Defining Yield Stress and Failure Stress (Strength)
[Pages:19]X. DEFINING YIELD STRESS AND FAILURE STRESS (STRENGTH)
One of the most obvious but still most difficult problems in dealing with matters of failure is that of defining the yield stress and the failure stress, commonly known as strength. These properties are needed to calibrate failure criteria. Such properties as modulus, yield stress, and strength are widely codified and quoted. Modulus E is straightforward but the terms yield stress and strength have a somewhat ambiguous history of use. In fact, there has not even been agreement on the proper designations for these properties. The terms yield point, proportional limit, yield strength have been used for the first property. For the failure stress such terms as ultimate strength, strength, rupture, and limiting stress and many more have been used. All of these have had rather different interpretations. None have been entirely satisfactory and none universally adopted.
Modern continuum mechanics does not offer any special insight on these matters nor does traditional mechanics of materials, which with considerable irony is also called strength of materials even though it has almost nothing to say about strength, Timoshenko [1]. In materials science, Cottrell [2] gives helpful discussions but does not give operational definitions. Hull and Bacon [3] state that "the yield stress is not unique" in recognition that the plastic deformation in metals due to dislocation flow is not a singular event but a diffuse process. Similarly for strength, the usual approach is to assign the stress at which the specimen ceases to function as being the strength. The term "ceases to function" usually remains undefined.
Perhaps as the result of these conceptual difficulties, modern usage has evolved into that of an arbitrary rule, the 0.2% strain offset rule for determining the yield stress of metals. For other materials there are not even arbitrary rules, there are only individual preferences and proclivities.
For perfectly brittle materials there is no problem. The yield stress is irrelevant and the strength is obvious. But for partially ductile or very ductile materials there is uncertainty and confusion about how to determine the yield stress and the strength.
It is quite apparent that to make the best use of failure criteria, it is necessary that they be implemented and supported by consistent and meaningful definitions of their calibrating properties and correspondingly of the interpretation of their results. To this end, rational definitions of yield stress and strength will now be sought. Yield Stress Definition Consider a typical, ductile material stress strain curve as shown in Fig. 1
Fig. 1 Stress strain curve The related constitutive form will be taken to be that of the strain hardening type and applicable to any standard test such as those for uniaxial tension, uniaxial compression, shear, or any proportional loading state. Now take the first and second derivatives of the stress strain curve in Fig. 1. These are shown schematically in Fig. 2
Fig. 2 Derivatives of stress strain curve
At the inflection point shown in Fig. 2a the second derivative in Fig. 2b reaches a maximum.
It is now seen that the strain ! = !y in Fig. 2b at which the magnitude
of the second derivative reaches a maximum is a transition point and the
associated stress "y in Fig. 1 is the yield stress. Thus, this definition of the yield stress, "y, is the single point on the stress strain curve at which the
tangent modulus, ET, is changing at the greatest rate with respect to increasing strain. The criterion for the yield stress is then
! ! !!!!!!"!!!
!!! !!!
! !"#$!%!!!!!!!!!!!!!!!!!!(1a)
or
!
!
!!!!!!"!!!
!!! !!!
!
!!!!!!!!!!!!!!!!!!!!!!!!!!!!!(1b)
This criterion for yield stress was given and examined rather recently by Christensen [4]. Surprisingly it apparently was never considered historically.
For ductile metals the location of the maximum of the second derivative is that condition at which the dislocation flow is sufficiently intense and varied as to cause this result. Such a process point involves both dislocation nucleation and the actual dynamics of the flow. For other materials such as glassy polymers, this point of the maximal second derivative correspondingly is caused by molecular rearrangement and damage at both the molecular and macroscopic scales.
The best way of viewing this yield behavior is that the first
derivative!!!"" versus ! is constantly decreasing for increasing ! but it has an inflection point that identifies the transition point "y. This single, unique
point then designates the transition from the previous nearly ideally elastic behavior to the following behavior approaching perfectly plastic flow. That the material may never truly attain the perfectly plastic state is usually caused by the intercession of the effects of flow anisotropy or localization etc.
To illustrate the process, an analytical form for typical stress strain curves will be taken so that the derivatives in (1) can be evaluated. Decomposing strain into elastic and plastic parts, take
! ! ! ! !"#
!
!!
! !!
!
!!!!!!!!!!!!!!!!!!!!!!!!!!!!!(2)
where a, m, and "0 are parameters to be specified. It can be shown that as
exponent m becomes very large (2) approaches that of the elastic-perfectly plastic case. Thus, except in this limiting case, the form (2) represents a continuous function with continuous derivatives in accordance with most physical observations.
Two examples will be given to show the evaluation of the yield stress using (1). The two examples with different values for exponent m are
(i)
E=70GPa "0=500MPa
a=0.01 m=5
(ii)
E=70GPa "0=500MPa
a=0.01 m=10
The corresponding second derivatives from (2) are shown in Fig. 3.
Fig. 3 Second derivatives for the examples
It is seen that these second derivatives give sharply defined maxima. The actual yield stresses were determined from (1b), the third derivative equal to zero
The full stress strain curves with the yield stresses determined by (1) are given in Fig. 4.
Fig. 4 Yield stresses for the examples
The yield stresses from (1) in the two examples are given by
! ! !!!!!!!!!!!!!! ! !"#!"#
! ! !"!!!!!!!!!!! ! !!"!"#
It is apparent from Fig. 4 that the yield stress values are larger than the values at which nonlinearity can first be observed, but it can also be shown that they are far less than the values from the 0.2% strain offset rule. If the exponent m=100 were taken in these examples, the result would be almost indistinguishable from the elastic-perfectly plastic case.
This new method for determining the yield stress complies with the original objective to find a rational criterion for the operation. However, it has a major disadvantage that renders it as almost unusable. Typical stress strain curves are actually just sequences of data points. Reliably determining second and/or third derivatives from such typical data sets is prohibitively difficult. So the situation appears to have reduced to the
common observation that "the operation was a success but the patient may not survive".
The practical means and method for determining the yield stress is still in an unsatisfactory and suspended state. Here is how to proceed further. The condition (1) is taken as the rigorous definition of the yield stress, even though it is difficult to implement. An approximation to the criterion (1) will be sought in a form that is easy and direct to use, but still retains the essential calibration of (1) in the stress strain problems of interest.
After examining several different forms the following was selected as a simple but reliable operational means of determining the yield stress. The yield stress is taken (designated) as that stress at which the actual strain is 5% greater than that of the linear elastic projection. This definition is
!
!
!!!!!!"!!!
!!!!! !!
!
!!!"!!!!!!!!!!!!!!!!!!!!!!!!!
(3)
with !L being the linear elastic range strain shown in Fig. 5.
Fig. 5 Strain deviation condition
In the two examples considered earlier, the rigorous yield stress given by (1) then gives the strain form in (3) as
!"#!!
!
!!!!!!!!!!!
!!
! !!
!!
!
!!!""
and
!"#!!
!
!"!!!!!!!!!!
!!
! !!
!!
!
!!!"#
These values are close to the 0.05 value of the 5% rule. The 5% strain deviation rule given by (3) provides a reasonable and easy to use criterion for determining the yield stress. It must be remembered however that it is only a convenient approximation to the rigorous definition of yield stress in (1). In the examples the approximate yield stresses given directly by the 5% strain deviation rule (3) are
!"#!! ! !!!!!!!!!!!!! ! !!"!"# !"#!! ! !"!!!!!!!!!!!! ! !"#!"#
Definition of Strength
How should one define strength? Is it simply the stress at which a specimen ruptures or fragments into multiple pieces? If the material were very brittle then the resulting failure stress is obvious. When the material is not perfectly brittle the problem becomes much more complex
................
................
In order to avoid copyright disputes, this page is only a partial summary.
To fulfill the demand for quickly locating and searching documents.
It is intelligent file search solution for home and business.
Related download
- techniques for estimating specific yield and usgs
- chapter 11 duration convexity and immunization
- calculating the effective interest rate
- simple interest compound interest and effective yield
- 7 revenue and yield management goodfellow publishers
- defining yield stress and failure stress strength
- this pdf is a selection from an out of print volume from
- yield calculations for treasury bills william l silber
Related searches
- stress and autoimmune disease
- stress and stress management pdf
- symptoms of stress and anxiety
- stress and cognitive dissonance
- stress and ears
- stress and ear pain
- emotional stress and hearing loss
- stress and anxiety symptoms in men
- women stress and health
- relationship between stress and illness
- stress and mental illness relationship
- psychological stress and disease