Filetype = GlazeChem Glazes



Host Bill van Gilder shares a few recipes for creating his favorite pottery glazes. These glaze recipes will work for cone 6 to cone 8 firings. Sieve each batch twice through an 80-mesh screen. A 10,000-gram dry weight batch will fill a five-gallon bucket when added to water.

Amber

A glossy semi-transparent glaze. Root beer color on brown clays; yellow amber on white clays. Good when applied over white slip.

Custer feldspar 2849 grams

Whiting 2415

Edgar’s Plastic Kaolin 711

Silica (325 mesh) 3439

Red iron oxide 1097

Rutile Green

A glossy opaque glaze. Best if applied thin. All-over light green if applied thick. Ron Roy base glaze recipe with oxide additions. Good when applied over or under Teal Blue glaze.

(All measurements are in grams.)

Custer feldspar 2200

Whiting 400

Talc 500

Ferro Frit (#3134) 2600

Edgar’s Plastic Kaolin 1700

Silica (325 mesh) 2600

Bentonite 100

Rutile (powdered) 600

Copper carbonate 400

Oribe Green

A pale to deep grass green, glossy glaze. Best when applied on white or light tone clay bodies. Good when applied over white slip. Cone 6 to cone 10.

(All measurements are in grams.)

Custer feldspar 3200

Whiting 2400

Silica (325 mesh) 2400

Kaolin (Tile #6) 1200

Zinc oxide 800

Copper carbonate 400

Teal Blue

A semi-gloss opaque glaze. Good when applied over or under Rutile Green glaze.

(All measurements are in grams.)

Custer feldspar 2000

Edgar’s Plastic Kaolin 2000

Ferro frit 3124 2000

Wollastonite 2000

Silica (325 mesh) 2000

Cobalt carbonate 100

Chrome oxide 50

Cream Rust

A semi-gloss opaque cream-breaking-rust glaze. Good over textured surfaces. Apply thin rather than thick.

(All measurements are in grams.)

Custer feldspar 2660

Strontium carbonate 330

Ferro frit (#3134) 3060

Wollastonite 1060

Silica (325 mesh) 1820

Edgar’s Plastic Kaolin 840

Talc 230

Red iron oxide 600

Tin oxide 1300

Glossy Black

A glossy, very black, opaque glaze. Ron Roy base glaze recipe with oxide additions.

(All measurements are in grams.)

Custer feldspar 2200

Whiting 400

Talc 500

Ferro frit #3134 (2600 grams)

Edgar’s Plastic Kaolin 1700

Silica (325 mesh) 2600

Bentonite 100

Cobalt carbonate 100

Red iron oxide 900

filetype = GlazeChem Glazes

version = 2

dbname = Mid-Range

I = |Imported 11 glazes from C:\Documents and Settings\Linda Arbuckle\My Documents\GlazChem\Feb 07 update2.txt

name = 1213P Calcium Matte

index =

date = 6/3/96

source =

type =

range = 5

firetype =

color =

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wollastonite

amount = 33.9

component = Ferro frit 3134

amount = 21.1

component = Kaolin

amount = 45

note = |Smooth, beautiful matte surface submitted by: Michelle Campbell

note = |e-mail: Lackacreek@ccinet.ab.ca source for original recipe: Plainsman

note = |Clays

name = 1213P Calcium Matte calc problem

index =

date = 6/3/96

source =

type =

range = 5

firetype =

color =

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wollastonite

amount = 36.6

component = Gerstley borate

amount = 10.7

component = Kaolin - theoretical

amount = 35.1

component = Custer feldspar

amount = 16.4

component = Silica

amount = 0.04

note = |Smooth, beautiful matte surface submitted by: Michelle Campbell

note = |e-mail: Lackacreek@ccinet.ab.ca source for original recipe: Plainsman

note = |Clays

name = 2nd Edition Indian Red

index =

date = 4/21/95

source =

type = Iron Saturate

range = 6

firetype = Ox. or Red.

color = iron red brown

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 40

component = Zinc oxide

amount = 4

component = Dolomite

amount = 3

component = Whiting

amount = 15

component = China clay

amount = 5

component = Silica

amount = 33

addition = chrome oxide

addamount = 0.5

addition = Red iron oxide

addamount = 4

note = |In oxidation at cone 6 a deep red iron oxide red. In reduction at

note = |cone 6 a deep brown with a slight green tint at close inspection.

note = |source for the original recipe: Emmanuel Coopers Glaze books

note = |submitted by: J.D. e-mail: CLAYJUNKIE@

name = 5-20's Tony Hansen

index =

date = 4/3/98

source =

type =

range = 6 - 8

firetype = oxidation

color = clear

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = EPK

amount = 20

component = Custer feldspar

amount = 20

component = Wollastonite

amount = 20

component = Frit 3134

amount = 20

component = Flint

amount = 20

note = |Chemical Analysis Na2O 0.14 Al2O3 0.38 SiO2 3.44 K2O 0.07 B2O3 0.22

note = |MgO 0.02 CaO 0.76 Alumina:Silica ratio is 1.00 : 9.08 Neutral:Acid

note = |ratio is 1.00 : 5.75 Alkali:Neutral:Acid ratio is 1.00 : 0.60 : 3.44

note = |Expansion coefficient: 69.2 x 10e-7 per degree C Oxides causing

note = |abnormal expansion effects: B2O3 John Post jp6mchp@ Sterling

note = |Heights, Michigan

name = 974 Kawai Celadon

index =

date = 3/26/96

source =

type = Celadon

range = 6 - 8

firetype = Reduction

color = Translucent Green

vistexture =

quality = shiny glossy

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 62.24

component = Whiting

amount = 7.61

component = China clay

amount = 4.97

component = Silica

amount = 25.18

addition = Black iron oxide

addamount = 1.52

note = |Original recipe called for limestone, substituted whiting, although

note = |using dolomite might be better. Add 2% Barium Carbonate for bluish

note = |celadon. Also can substitute red iron oxide for the black to get a

note = |yellow green celadon. submitted by: GURUSHAKTI@

name = Albany Black

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca Mg SlipGlaze

range = 5 - 6

firetype = Ox. or Red.

color = black

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany Slip

amount = 75

component = Nepheline syenite

amount = 20

component = Gerstley borate

amount = 5

addition = Cobalt oxide

addamount = 5

note = |Albany sub.= Yellow Banks Red #101 + Whiting 14% approx. + Dolomite

note = |2-3% approx.

name = Alfred Spodumene B.J.

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca Mg AlMatt

range = 6

firetype = Reduction

color = Tan/Brown/White

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 20

component = Custer feldspar

amount = 20

component = Spodumene

amount = 20

component = Dolomite

amount = 20

component = Whiting

amount = 5

component = Kaolin

amount = 15

addition = Tin oxide

addamount = 4

note = |This is the Alfred Spodumene glaze revised to C/6.

name = Almond St. Helens

index =

date = 6/24/97

source =

type = Zinc matt

range = 6

firetype = Oxidation

color = almond yellow

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer spar

amount = 40

component = Zinc oxide

amount = 8.6

component = Whiting

amount = 14.9

component = EPK

amount = 11.8

component = Flint

amount = 4.7

component = Volcanic ash - Mt. St. Helens

amount = 20

addition = Rutile

addamount = 8

note = |here are two glazes I have used successfully but not put thru any

note = |analysis. I got them at an art studio where I used to take classes.

note = |They are better if layered with other glazes. Wendy Hampton

note = | from Bainbridge Island WA

note = |Also see Blue St. Helen's

name = Amber

index =

date = 10/06/2002

source =

type =

range = 6-8

firetype = Oxidation

color = Amber

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 30.27

component = Whiting

amount = 25.65

component = Silica

amount = 36.53

component = EPK

amount = 7.55

addition = Red iron oxide

addamount = 11.66

note = |Clay Times May/June 2002. Root beer color on iron-bearing clays. Golden yellow on white clays. Layers well with oribe green on top or bottom. Good base for other oxide combinations.

name = Amber Ash Glaze

index =

date = 6/3/96

source =

type = Ash

range = 6

firetype = Oxidation

color = Amber

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cedar Heights Redart

amount = 40

component = Ferro frit 3124

amount = 30

component = Ash wood

amount = 30

addition = Rutile

addamount = 4

var = |Add 3% cobalt for a perfect Black Tested on Dillo White clay at a

var = |full ^6.

note = |I used sieved unwashed fireplace ash. An excellent honey gold gloss

note = | submitted by: Lori Wilkinson e-mail: lorwilk@

name = Amber Brown Dark Rich

index =

date = 08/03/2003

source =

type =

range = 6

firetype = Oxidation

color = Brown

vistexture =

quality =

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 46.7

component = EPK

amount = 22.9

component = Flint

amount = 30.4

component = Bone ash

amount = 0.2

addition = Red iron oxide

addamount = 10

var = |refire to cone 08 for opaque rust

name = Amber Honey

index =

date = 8/8/97

source =

type =

range = 5 - 6

firetype =

color = Amber

vistexture =

quality = glossy

transparency =

xtals = Small

bubbles = Some

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 20

component = Ferro frit 3134

amount = 20

component = Spodumene

amount = 20

component = Kentucky OM #4

amount = 20

component = Flint

amount = 20

addition = Bentonite

addamount = 2

addition = Manganese dioxide

addamount = 3

addition = Red iron oxide

addamount = 5

note = |Works at cone 5 or 6.

note = |Lovely amber with some tiny bubbles, floating dust crystals, nice

note = |surface Janet Price, Chief Information Officer Carroll College,

note = |Waukesha WI 53186 jprice@.edu or jprice@.edu

note = |414-524-7120

name = Amber New Tyler

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color = amber

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro Frit 3110

amount = 20

component = Red clay

amount = 60

component = Gerstley borate

amount = 20

note = |tested on white stoneware. AMBER WITH TINY BLACK FLECKS. SHINY.

note = |TRANSLUCENT. submitted by: Sharon LaRocca-Miranda e-mail:

note = |FMIRANDA@.OBERLIN.EDU , FMiranda@oberlin.edu source for

note = |original recipe: Zakin

name = Amber New Tyler

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color = amber

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro Frit 3110

amount = 20

component = Red clay

amount = 60

component = Gerstley borate

amount = 20

note = |tested on white stoneware. AMBER WITH TINY BLACK FLECKS. SHINY.

note = |TRANSLUCENT. submitted by: Sharon LaRocca-Miranda e-mail:

note = |FMIRANDA@.OBERLIN.EDU , FMiranda@oberlin.edu source for

note = |original recipe: Zakin

name = Apricot/Beige MMI

index =

date = 4/10/95

source =

type =

range = 6

firetype = Oxidation

color = apricot/beige

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 28.18

component = Whiting

amount = 18.18

component = Talc

amount = 9.09

component = Kaolin

amount = 26.36

component = Silica

amount = 9.09

component = Zinc oxide

amount = 9.09

addition = chrome oxide

addamount = 1.82

addition = Cobalt carbonate

addamount = 0.23

note = |Semi matt, apricot/beige, even, good. From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

name = Apricot/Tan MMM

index =

date = 4/10/95

source =

type =

range = 6

firetype = oxidation

color = apricot/tan

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 28.18

component = Whiting

amount = 18.18

component = Talc

amount = 9.09

component = Kaolin

amount = 26.36

component = Silica

amount = 9.09

component = Zinc oxide

amount = 9.09

addition = Iron oxide

addamount = 0.45

addition = chrome oxide

addamount = 1.82

note = |Semi matt, apricot/tan ok Darker than MMI From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

name = Aqua V.C. Karen Starshine

index =

date = 6/4/96

source =

type =

range = 6

firetype = Ox. or Red.

color = Blue Green

vistexture =

quality = Glossy or shiny

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = K-200 feldspar

amount = 46

component = Soda ash

amount = 5

component = Gerstley borate

amount = 12

component = Whiting

amount = 10

component = Barium carbonate

amount = 5

component = Lithium carbonate

amount = 2

component = Flint

amount = 20

addition = Macaloid

addamount = 2

addition = Titanium dioxide

addamount = 4

addition = Copper carbonate

addamount = 5

note = |AU Sp '92 tested by KG in OXIDATION at C/6 on dark brown clay body -

note = |a knockout glaze! The most interesting of the Starshine series to

note = |date tho the green hue was lost. Definitely RUNNY. Good in SODA. Now

note = |- how do we get this color at C/9-10? VC ed

name = Ash Barium Boron

index =

date = 4/3/98

source =

type =

range = 6 - 8

firetype =

color = base

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wood ash

amount = 24.07

component = Barnard clay

amount = 20.37

component = Custer feldspar

amount = 28.4

component = Gerstley borate

amount = 13.58

component = Barium carbonate

amount = 9.88

component = Zinc oxide

amount = 3.7

addition = Copper carbonate

addamount = 1.85

note = |Needs to be corrected for fit and pinholes but every clay body is a

note = |different can of worms. The barium/boron eutectic makes it hard to

note = |say what cone this fires to - the longer it is in kiln or the greater

note = |the thermal mass of the kiln the more it will flux. Formulated

note = |originally without the ash or slip clay it was semi-satin, semi-

note = |gloss somewhere around cone 2. Boron subdues the copper coloration.

note = |I'm not taking responsibility for anyone using these glazes, etc.

note = |Something is probably toxic. They are examples of my research and

note = |they work out in formulation. Which is what they are examples of. So

note = |go formulate your own non-toxic glazes, if that is possible. It's

note = |probably bad for the environment too. Email me with questions as to

note = |household performance, as that may be indicative of other problems.

note = |The badly crazed surfaces are not considered to be a continous-non

note = |porous sanitary surfaces. Eric Hansen, Lawrence, Kansas

note = |wabi_sabi@

name = Ash Behrends

index =

date = 6/3/96

source =

type = Ash

range = 6

firetype =

color =

vistexture = Striated

quality =

transparency =

xtals =

bubbles =

flow = Moderate

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Volcanic ash

amount = 65

component = Gerstley borate

amount = 35

note = |fluidity: very try useing 65% volcanic ash, 35% gerstly borate. This

note = |is a very fluid glaze, but does not run off the pot. It works very

note = |well over matt glazes. Good luck. submitted by: behrends e-mail:

note = |bluemoon@win.

name = Ash Behrends recalc

index =

date = 6/3/96

source =

type = Ash

range = 6

firetype =

color =

vistexture = Striated

quality =

transparency =

xtals =

bubbles =

flow = Moderate

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Feldspar

amount = 57.6

component = Gerstley borate

amount = 41.6

component = Dolomite

amount = 0.3

component = Whiting

amount = 0.5

note = |fluidity: very try useing 65% volcanic ash, 35% gerstly borate. This

note = |is a very fluid glaze, but does not run off the pot. It works very

note = |well over matt glazes. Good luck. submitted by: behrends e-mail:

note = |bluemoon@win.

name = Ash Behrens

index =

date = 6/3/96

source =

type = Ash

range = 6

firetype = oxidation

color =

vistexture =

quality =

transparency = Semi-opaque

xtals =

bubbles =

flow = Extreme

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Volcanic ash

amount = 65

component = Gerstley borate

amount = 35

note = |fluidity: very fluid try useing 65% volcanic ash, 35% gerstly borate.

note = |This is a very fluid glaze, but does not run off the pot. It works

note = |very well over matt glazes. Good luck. submitted by: behrends e-mail:

note = |bluemoon@win.

name = Ash Bush Fake

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = tan?

vistexture =

quality = runny, rivulet

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barnard clay

amount = 20

component = Ball clay

amount = 26

component = Wollastonite

amount = 30

component = Gerstley borate

amount = 24

addition = Rutile

addamount = 1

name = Ash Bush Fake NO GB

index =

date = 12/7/96

source =

type = Ash

range = 6

firetype = oxidation

color = tan?

vistexture =

quality = runny, rivulet

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin - theoretical

amount = 3.2

component = Dolomite

amount = 4.4

component = Whiting

amount = 26.1

component = Frit 3195

amount = 43.2

component = Silica

amount = 23.1

addition = Rutile

addamount = 1.6

addition = Manganese dioxide

addamount = 0.8

addition = Red iron oxide

addamount = 3

note = |Recalc to substitute for Gerstley borate

name = Ash Fake

index =

date = 6/3/96

source =

type = Fake ash

range = 6

firetype =

color =

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = Barnard clay

amount = 25

component = EPK

amount = 25

note = |Nice light glossy golden brown but not really a runny glaze Tested on

note = |Dillo White clay at a full ^6. submitted by: Lori Wilkinson e-mail:

note = |lorwilk@ I think this one is already in glazebase. r

name = Ash Fake - Mid Range rev.

index =

date = 10/29/94

source =

type = Fake ash

range = 6 - 8

firetype =

color = Translucent Green

vistexture =

quality = Shiny or Glossy drippy texture

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 17.08

component = Redart clay

amount = 37.16

component = Nepheline syenite

amount = 2.98

component = Whiting

amount = 31.01

component = Talc

amount = 2.83

component = Flint

amount = 2.54

component = Strontium carbonate

amount = 6.39

note = |Revised from a recipe that used Albany Slip and Barium Carbonate

note = |originally from Dale Huffman via GlazeBase. Richard Burkett 1994

name = Ash Fake - Mid Range rev.

index =

date = 10/29/94

source =

type = Ash

range = 6, 7, 8

firetype = Ox. or Red.

color = Translucent Green

vistexture =

quality = Shiny or Glossy drippy texture

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 17.1

component = Redart

amount = 37.2

component = Nepheline syenite

amount = 3

component = Whiting

amount = 31

component = Talc

amount = 2.8

component = Flint

amount = 2.5

component = Strontium carbonate

amount = 6.4

note = |Revised from a recipe that used Albany Slip and Barium Carbonate

note = |originally from Dale Huffman via GlazeBase. Richard Burkett 1994

name = Ash Fake - Mid Range rev. No GB

index =

date = 10/29/94

source =

type = Ash

range = 6, 7, 8

firetype = Ox. or Red.

color = Translucent Green

vistexture =

quality = Shiny or Glossy drippy texture

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 9.2

component = Whiting

amount = 23.3

component = Strontium carbonate

amount = 6.5

component = Kaolin - theoretical

amount = 17.8

component = Silica

amount = 8.7

component = Frit 3134

amount = 34.3

component = Bone ash

amount = 0.2

addition = Rutile

addamount = 0.5

addition = Red iron oxide

addamount = 2.8

note = |Revised from a recipe that used Albany Slip and Barium Carbonate

note = |originally from Dale Huffman via GlazeBase. Richard Burkett 1994

name = Ash Fake 2

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = Barnard clay

amount = 25

component = EPK

amount = 25

note = |Nice light glossy golden brown but not really a runny glaze Tested on

note = |Dillo White clay at a full ^6. submitted by: Lori Wilkinson e-mail:

note = |lorwilk@ I think this one is already in glazebase. r

name = Ash Fake 3

index =

date = 4/21/95

source =

type =

range = 6

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 20

component = Ferro Frit 3134

amount = 20

component = Custer feldspar

amount = 20

component = Barium carbonate

amount = 15

component = EPK

amount = 15

component = Gerstley borate

amount = 10

note = |add nickel oxide at 5% for an apple green pooling dark brown runs

note = |nicely and provides lots of interesting results on top of other

note = |glazes. Probably not for food surfaces. Works well with Randy's Red

note = |and Silky Black Matt clay body: Laguna B-mix a white stoneware

note = |submitted by: Iain Begg e-mail: begg@MPRGATE. MPR.CA

name = Ash Fake Clear - Mid Range rev.

index =

date = 10/29/94

source =

type =

range = 6, 7, 8

firetype = Ox. or Red.

color = Translucent Gray

vistexture =

quality = Shiny or Glossy drippy texture

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 17.48

component = Nepheline syenite

amount = 11.97

component = EPK

amount = 13.11

component = Whiting

amount = 31.74

component = Talc

amount = 4.81

component = Flint

amount = 14.35

component = Strontium carbonate

amount = 6.54

note = |Revised from a glaze using Albany Slip, originally from Dale Huffman

note = |via GlazeBase. Richard Burkett 1994

name = Ash Fake Clear - Mid Range rev.

index =

date = 10/29/94

source =

type = Fake ash

range = 6 - 8

firetype =

color = Translucent Gray

vistexture =

quality = Shiny or Glossy drippy texture

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 17.48

component = Nepheline syenite

amount = 11.97

component = EPK

amount = 13.11

component = Whiting

amount = 31.74

component = Talc

amount = 4.81

component = Flint

amount = 14.35

component = Strontium carbonate

amount = 6.54

note = |Revised from a glaze using Albany Slip, originally from Dale Huffman

note = |via GlazeBase. Richard Burkett 1994

name = Ash Fake Glaze

index =

date = 1/13/96

source =

type = Fake ash

range = 6

firetype =

color = yellow to brown

vistexture =

quality = Texture rivulets

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cedar Heights Redart

amount = 27.15

component = Dolomite

amount = 23.8

component = Barium sulfate

amount = 12.2

component = Tennessee #5 ball clay

amount = 20.4

component = Lithium carbonate

amount = 1.71

component = Gerstley borate

amount = 9.64

component = Bone ash

amount = 5.1

note = |Firing: firing type: oxidation or reduction Here is a cone 6 fake ash

note = |I used when I was taking classes with Kevin Hluch at Montgomery

note = |College in Maryland. It's fairly yellow with greenish runs in

note = |oxidation. Not usually as nice in reduction where it is quite brown

note = |although I liked it thin on certain things back then. You can

note = |probably figure from the decimal places that I copied this from a

note = |10,000 g batch recipie and that whoever figured it out first probably

note = |calculated the amounts rather than testing. Good luck. submitted by:

note = |Evan Dresel e-mail: PEDresel@

name = Ash Fake Glaze

index =

date = 1/13/96

source =

type =

range = 6

firetype = Ox. or Red.

color = yellow to brown

vistexture =

quality = Texture rivulets

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cedar Heights RedArt Clay

amount = 27.15

component = Dolomite

amount = 23.8

component = Barium sulfate

amount = 12.2

component = Tennessee #5 ball clay

amount = 20.4

component = Lithium carbonate

amount = 1.71

component = Gerstley borate

amount = 9.64

component = Bone ash

amount = 5.1

note = |Here is a cone 6 fake ash I used when I was taking classes with Kevin

note = |Hluch at Montgomery College in Maryland. It's fairly yellow with

note = |greenish runs in oxidation. Not usually as nice in reduction where it

note = |is quite brown although I liked it thin on certain things back then.

note = |You can probably figure from the decimal places that I copied this

note = |from a 10,000 g batch recipie and that whoever figured it out first

note = |probably calculated the amounts rather than testing. Good luck.

note = |submitted by: Evan Dresel e-mail: PEDresel@

name = Ash Fake Revised Galloway

index =

date = 06/04/2005

source =

type = Fake ash

range = 6

firetype = Salt - Soda

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 17

component = Kona F-4 feldspar

amount = 10

component = Ball clay

amount = 12

component = Silica

amount = 18

component = Dolomite

amount = 9

component = Whiting

amount = 26

component = Barium carbonate

amount = 9

addition = Rutile

addamount = 4

addition = Copper carbonate

addamount = 2

var = |Galloway says rutile 4-12, copper 2-6

note = |Clay Times May/Jn 2004. See Galloway web site for more glazes

name = Ash Frasca

index =

date = 12/26/2006

source =

type = Ash

range = 6

firetype = Oxidation

color = Turquoise

vistexture = Rivulet

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 11

component = Ash wood

amount = 56

component = Potash feldspar

amount = 11

component = Ball clay

amount = 11

component = Silica

amount = 11

addition = Copper carbonate

addamount = 4

note = |Works best dipped or sprayed over another glaze. Alone very dry.

note = |Variations -- blue = cobalt carb 2%

note = |

name = Ash Frasca

index =

date = 12/26/2006

source =

type = Ash

range = 6

firetype = Oxidation

color = Turquoise

vistexture = Rivulet

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 11

component = Ash wood

amount = 56

component = Potash feldspar

amount = 11

component = Ball clay

amount = 11

component = Silica

amount = 11

addition = Copper carbonate

addamount = 4

var = |blue = cobalt carb 2%

note = |Works best dipped or sprayed over another glaze. Alone very dry.

name = Ash Glaze

index =

date = 2/20/95

source =

type =

range = 5 - 6

firetype = Ox. or Red.

color =

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 13.6

component = Lithium carbonate

amount = 4.5

component = wood Ash

amount = 18.2

component = Whiting

amount = 18.2

component = Albany Slip

amount = 36.4

component = Kaolin

amount = 9.1

note = |eally hot Cone 6 ash glaze from: lowell baker on ClayArt Received:

note = |Thu, 16 Feb 1995 08:52:49

note = |

name = Ash Glaze cone 6

index =

date = 6/3/96

source =

type = Ash

range = 6

firetype = oxidation

color =

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cedar Heights Redart clay

amount = 40

component = Ferro Frit 3124

amount = 30

component = Ash wood

amount = 30

addition = Rutile

addamount = 4

note = |I used sieved unwashed fireplace ash. An excellent honey gold gloss

note = |Add 3% cobalt for a perfect Black Tested on Dillo White clay at a

note = |full ^6. submitted by: Lori Wilkinson e-mail: lorwilk@

name = Ash Glaze Rhodes revised

index =

date = 6/24/97

source =

type = Ash

range = 6 - 9

firetype =

color =

vistexture =

quality = stony/ satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Hardwood ash (washed)

amount = 28

component = G-200 feldspar

amount = 36

component = Dolomite

amount = 10

component = Kentucky OM #4

amount = 21

component = EPK kaolin

amount = 5

note = |use mixed hardwood ash + CMC Last year, with a lot of help from Tom

note = |Buck and some of the other Clayart gurus, I adjusted one of the old

note = |Daniel Rhodes ash glazes. Original recipe (Cone 9-10): Mixed hard

note = |wood ash 35 Oxford spar 35 China clay 15 Talc 15 I fire in an

note = |electric kiln. I would never describe it as a foolproof glaze, but if

note = |applied with care, it's so beautiful that it just knocks out all the

note = |reliable competition. I bisque at ^06 and am now firing at ^6. I have

note = |gone to ^9, but that seems to present more problems with pinholing

note = |and crazing. Also, I wash the ash. I have also used the same recipe

note = |with unwashed ash. The difference is that I would describe the

note = |unwashed ash glaze as stony matt and the washed ash glaze as opaque

note = |satin matt. Haven't tried this recipe at a lower temperature. You

note = |might want to give it a try. marjory r. kline

note = |

name = Ash Golden Fake

index =

date = 3/26/96

source =

type = Fake ash

range = 6

firetype =

color = Amber

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cedar Heights Redart

amount = 27.2

component = Dolomite

amount = 23.8

component = Barium sulfate

amount = 12.2

component = Ball clay

amount = 20.4

component = Lithium carbonate

amount = 1.7

component = Gerstley borate

amount = 9.6

component = Bone ash

amount = 5.1

addition = Bentonite

addamount = 1

note = |This is one I used at Montgomery College in Maryland.

note = |Yellow-tan in oxidation with greenish runs when applied thick. More

note = |orange and tricky to make look ok in reduction. You may want to test a strontium

note = |carbonate substitution for the barium sulfate for health and safety

note = |reasons. Good luck. Evan Dresel in Richland Washington where the

note = |latest news about leaking radioactive waste really isn't as new or

note = |bad as the press reports. pedresel@

name = Ash Golden Fake

index =

date = 12/7/96

source =

type = Ash

range = 6

firetype = oxidation

color = golden yellow

vistexture =

quality = runny, rivulet

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Redart clay

amount = 27

component = Dolomite

amount = 24

component = Barium carbonate

amount = 12

component = Ball clay

amount = 20

component = Lithium carbonate

amount = 2

component = Gerstley borate

amount = 10

component = Bone ash

amount = 5

note = |Two years ago I took a part-time job teaching

note = |ceramics at Navarro College in Corsicana, Texas. The college has only

note = |one kiln. It' an ancient Paragon High Fire. The design is square and

note = |toploading with very small cu. ft. It's been a real challenge to

note = |develop an attractive palette of clays and glazes for oxidation

note = |firing. I do majolica, colored clays, and cone 6 oxidation ( cone 7

note = |in the sitter). Rafael Molina Rmr3431@dcccd.edu

name = Ash Human Glaze -Su Standing Bear

index =

date = 08/12/2003

source =

type = Ash

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wollastonite

amount = 10

component = Silica

amount = 15

component = EPK

amount = 20

component = G-200 feldspar

amount = 20

component = Frit 3134

amount = 30

component = Bone ash

amount = 5

note = |This glaze is for human bone ash. From Bill Edwards

note = |on ClayArt

note = |

note = |The bone ash will need screened and in my case it took

note = |further pulverizing. Once I screen the content I took

note = |some of the larger particles and included it in the

note = |clay. The largest particles left over, and there most

note = |likely will be some, was put in the urns and sealed.

note = |So the finished product contained bone ash in the

note = |clay, in the glaze and in the end after final firing

note = |the cremains left over were sealed in each container

note = |and returned to the family.

note = |some of the small calcined

note = |(from cremation) fragments acted like iron bleeding in

note = |spots through the clay and glaze. It didn't run and I

note = |did add some colorants to this glaze. The results were

note = |nice!

name = Ash Levison

index =

date = 3/26/96

source =

type = Ash

range = 6

firetype =

color = grey blue

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wood ash

amount = 40

component = Custer feldspar

amount = 40

component = Ball clay

amount = 10

component = Silica

amount = 10

addition = Rutile

addamount = 4

addition = Cobalt carbonate

addamount = 2

note = |Original recipe called for washed ash. Glaze in blue/greyish mottled

note = |matt. I like it but I have not been able to have it bead-up and run.

note = |What chemical should I add to change its' melting characteristics?

note = |Should I fire to cone 7 or even 8? should I soak? I would also like

note = |to have an ash glaze in the green (forest) and brown/tan hues. Any

note = |suggestions? submitted by: Mitch Levison e-mail: Mitchlev@

name = Ash Levison

index =

date = 3/26/96

source =

type =

range = 6

firetype = oxidation

color = grey blue

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wood Ash

amount = 40

component = Custer feldspar

amount = 40

component = Ball clay

amount = 10

component = Silica

amount = 10

addition = Rutile

addamount = 4

addition = Cobalt carbonate

addamount = 2

note = |Original recipe called for washed ash. Glaze in blue/greyish mottled

note = |matt. I like it but I have not been able to have it bead-up and run.

note = |What chemical should I add to change its' melting characteristics?

note = |Should I fire to cone 7 or even 8? should I 'soak'? I would also like

note = |to have an ash glaze in the green (forest) and brown/tan hues. Any

note = |suggestions? submitted by: Mitch Levison e-mail: Mitchlev@

name = Ash Look

index =

date = 1/13/96

source =

type = Ash

range = 6

firetype = oxidation

color =

vistexture =

quality =

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro Frit 3195

amount = 46

component = Whiting

amount = 34

component = EPK

amount = 20

note = |A fake wood ash at cone 6 oxidation. It does

note = |run in those rivulets. I added 3% copper carbonate but I am sure some

note = |other colorants would be worth a try. submitted by: Suzanne Fuqua

note = |e-mail: Suzanne511@

name = Ash V.C. 4

index =

date = 11/15/98

source =

type = Ash

range = 5 - 6

firetype = Reduction

color =

vistexture =

quality = Rivulet

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Apple Wood Ash

amount = 50

component = Gerstley borate

amount = 20

component = Whiting

amount = 12

component = EPK

amount = 8

component = Flint

amount = 10

note = |Typical ash looking, drippy, webby, rivulets. Val, please name this

note = |series. Glaze Type: Ca B AshGlaze. Opacity: Mixed. Firing type:

note = |Reduction .

name = ash Zakin's GK

index =

date = 7/19/95

source =

type =

range = 5 - 6

firetype = Ox. or Red.

color =

vistexture =

quality = ash runny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro Frit 3124

amount = 18.18

component = Magnesium carbonate

amount = 7.07

component = Nepheline syenite

amount = 10.1

component = Strontium carbonate

amount = 11.11

component = Spodumene

amount = 15.15

component = EPK

amount = 10.1

component = Whiting

amount = 13.13

component = ash unwashed

amount = 15.15

addition = Opax

addamount = 12.12

addition = Bentonite

addamount = 2.02

note = |Use unwashed fireplace ash. Doesn't add to 100 because of the

note = |strontium/barium substitution, the bentonite, and the ash. This may

note = |be closer to cone 5 than cone 6 but seems to work over a range of a

note = |couple cones. This is Zakin's GK base with 15% unwashed, mixed

note = |fireplace ashes, with strontium substituted for barium and superpax

note = |for opax. By itself over porcelain, the glaze is not particularly

note = |interesting. But other glazes on top of it run and drip and blend

note = |together nicely. I've found that if I glaze the lower 2/3 or 3/4 of a

note = |pot with a well-behaved glossy glaze, brush a coat of this ZGK ash

note = |glaze on the top 1/3 or so and then brush or dip some third glaze on

note = |top of the ash glaze, I get a nice pattern of runs that don't go off

note = |the bottom of the pot onto the kiln shelf (usually). Different glazes

note = |give different kinds of runs and bands of different glazes are

note = |interesting too. The few times I tried a matte glaze on the bottom,

note = |the pots cracked. Could have been coincidence. But I've been sticking

note = |with glossy glazes on the bottom since then. submitted by: Janet

note = |Price e-mail: jprice@kzoo.edu

name = Aventurine Apple Green

index =

date = 03/11/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color =

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Fusion Frit F-15

amount = 70

component = Barium carbonate

amount = 30

addition = Chromium oxide

addamount = 1.8

addition = Macaloid

addamount = 1

note = |From Robert and Beatric Pearson in Clay Times Mar/Apr 07.NOT for food.

name = Aventurine Apple Green

index =

date = 07/15/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals = Small

bubbles =

flow = Moderate

durability =

flaws = Crazes

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Fusion Frit F-15

amount = 70

component = Barium carbonate

amount = 30

component = Silica

amount = 12

addition = Chrome oxide

addamount = 1.8

addition = Bentonite

addamount = 1

note = |Contains small metallic glitter crystals. Not for food use. Clay Times Mar/Apr. 07 p.50

name = Aventurine Blue Green

index =

date = 07/15/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = Green

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow = Moderate

durability =

flaws = Crazes

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Fusion Frit F-15

amount = 70

component = Barium carbonate

amount = 30

addition = Copper carbonate

addamount = 2

addition = Chrome oxide

addamount = 1.5

addition = Bentonite

addamount = 1

note = |Contains small metallic glitter crystals. Clay Times Mar/Apr. 07 p. 50. Minimally

note = |crazed. Should be applied thinly.Not for food use.

name = Aventurine Blue Green

index =

date = 03/11/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = Blue-green

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Fusion Frit F-15

amount = 70

component = Barium carbonate

amount = 30

addition = Copper carbonate

addamount = 2

addition = Chromium oxide

addamount = 1.5

addition = Macaloid

addamount = 1

note = |From Robert and Beatric Pearson in Clay Times Mar/Apr 07. Rare, minimally-crazed

note = |aventurine glaze. Apply thinly. Must be seen in bright light to see aventurine

note = |spangles.NOT for food.

name = Aventurine Blue-Green

index =

date = 03/11/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = blue-green

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Fusion Frit F-496

amount = 15

component = Custer feldspar

amount = 21

component = Whiting

amount = 17

component = Strontium carbonate

amount = 15

component = Kaolin

amount = 7

component = Silica

amount = 25

addition = Copper carbonate

addamount = 4.5

addition = Chromium oxide

addamount = 1.5

note = |From Robert and Beatric Pearson in Clay Times Mar/Apr 07. Calls for Spanish Red Iron

note = |Oxide.NOT for food.

name = Aventurine Chrome Copper Blue Green

index =

date = 07/15/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = Green

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow = Moderate

durability =

flaws = Crazes

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Fusion Frit F-496

amount = 15

component = Custer feldspar

amount = 21

component = Whiting

amount = 17

component = Strontium carbonate

amount = 15

component = Kaolin

amount = 7

component = Silica

amount = 25

addition = Copper carbonate

addamount = 4.5

addition = Chrome oxide

addamount = 1.5

note = |Contains small metallic glitter crystals. Clay Times Mar/Apr. 07, p. 51. Not for food

note = |use. Add CMC gum for better application.

name = Aventurine Chromium Green

index =

date = 03/11/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = Green

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Fusion Frit F-245

amount = 52

component = Custer feldspar

amount = 20

component = Barium carbonate

amount = 16

component = Silica

amount = 12

addition = Copper carbonate

addamount = 1.5

addition = Chromium oxide

addamount = 1

addition = Macaloid

addamount = 1

note = |From Robert and Beatric Pearson in Clay Times Mar/Apr 07.NOT for food.

name = Aventurine Circular Dot

index =

date = 03/11/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = Brown

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 24

component = Sodium bicarbonate

amount = 29

component = Whiting

amount = 11

component = Silica

amount = 36

component = Fluorspar

amount = 2

addition = Macaloid

addamount = 1

addition = Red iron oxide

addamount = 22

note = |From Robert and Beatric Pearson in Clay Times Mar/Apr 07. Calls for Spanish Red Iron

note = |Oxide. Due to soluble sodium bicarb, mix just before using and do not store.NOT for food.

name = Aventurine Circular Dot

index =

date = 03/11/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = Brown

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 24

component = Sodium bicarbonate

amount = 29

component = Whiting

amount = 11

component = Silica

amount = 36

component = Fluorspar

amount = 2

addition = Macaloid

addamount = 1

addition = Red iron oxide

addamount = 22

note = |From Robert and Beatric Pearson in Clay Times Mar/Apr 07. Calls for Spanish Red Iron

note = |Oxide. Due to soluble sodium bicarb, mix just before using and do not store.NOT for food.

name = Aventurine Iron

index =

date = 07/15/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = Brown

vistexture =

quality = Gloss

transparency =

xtals = Small

bubbles =

flow = Moderate

durability =

flaws = Crazes

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Sodium bicarbonate

amount = 47

component = Bentonite

amount = 20

component = Kona F-4 feldspar

amount = 10

component = Silica

amount = 23

addition = Red iron oxide

addamount = 22

note = |Contains small metallic glitter crystals.Clay Times Mar/Apr. 07 p.50. Soluble bicarb.

note = |Mix glaze fresh; don't store. Calls for Spanish Red Iron.

name = Aventurine Iron Variation

index =

date = 03/11/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = Brown

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Sodium bicarbonate

amount = 49

component = Bentonite

amount = 25

component = Whiting

amount = 4

component = Silica

amount = 22

addition = Red iron oxide

addamount = 21

note = |From Robert and Beatric Pearson in Clay Times Mar/Apr 07. Calls for Spanish Red Iron

note = |Oxide.Due to soluble sodium bicarb, mix just before using and do not store.NOT for food.

name = Aventurine Metallic Copper

index =

date = 03/11/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color =

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Fusion Frit F-79

amount = 40

component = Barium carbonate

amount = 48

component = Silica

amount = 12

component = Sodium bicarbonate

amount = 8

addition = Copper carbonate

addamount = 1

addition = Chromium oxide

addamount = 1.5

addition = Macaloid

addamount = 1

note = |From Robert and Beatric Pearson in Clay Times Mar/Apr 07.NOT for food.

name = Aventurine Sparkling Mint

index =

date = 03/11/2007

source =

type = Aventurine

range = 5

firetype = Oxidation

color = Green

vistexture =

quality = Gloss

transparency = Transparent

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3278

amount = 52

component = Barium carbonate

amount = 16

component = Kaolin

amount = 16

component = Silica

amount = 16

addition = Copper carbonate

addamount = 2

addition = Chromium oxide

addamount = 1.5

addition = Macaloid

addamount = 1

note = |From Robert and Beatric Pearson in Clay Times Mar/Apr 07.NOT for food.

name = Bacia's 20-30-40

index =

date = 1/13/96

source =

type =

range = 6

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 22.2

component = Whiting

amount = 33.3

component = Feldspar

amount = 44.4

note = |A variation for light color is to add a small am't (2%) MnCO3. I am

note = |breaking all rules with some of the high-fire stuff from 20 yrs. ago

note = |I couldn't bear to throw out. I use the 20-30-40 over highly textured

note = |clay, painted with either Barnard clay, one of my many old mixes

note = |containing Albany, or even over colored terra sig.s and FIRE TO CONE

note = |6. The terra sig's were never meant for this temp, but they work. The

note = |glaze at cone 6 looks more like an engobe but richer in the valleys

note = |of the texture. I remember how I used this glaze in high fire

note = |reduction and liked it a lot. It can turn gray in reduction. So

note = |experiment with opax. submitted by: Bacia Edelman e-mail:

note = |medelman@facstaff.wisc.edu

name = Ball Crawl

index =

date = 08/01/2001

source =

type =

range = 6

firetype = Ox. or Red.

color = Opaque White

vistexture =

quality = Texture crawl

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 50

component = Nepheline syenite

amount = 50

note = |> ClayArt Listserv recipe < If you find this glaze useful, please

note = |consider submitting it to the GlazeBase project with full

note = |documentation. Use one of the GlazeBase submission formats available

note = |on the CeramicsWeb web page.

note = |

note = |comments: There was also an article in ceramics Monthly, Feb 1990 on

note = |lichen glazes. I tried the Ball Crawl glaze. worked fairly well, but

note = |could be chipped off the pot too easily. this made me try putting it

note = |over another glaze. submitted by: Kathy Darby e-mail: kdarby@

note = |source for original recipe: Ceramics Monthly

name = Barium Boron Ash

index =

date = 4/3/98

source =

type =

range = 6 - 8

firetype =

color = base

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wood ash

amount = 24.07

component = Barnard clay

amount = 20.37

component = Custer feldspar

amount = 28.4

component = Gerstley borate

amount = 13.58

component = Barium carbonate

amount = 9.88

component = Zinc oxide

amount = 3.7

addition = Copper carbonate

addamount = 1.85

note = |Needs to be corrected for fit and pinholes but every clay body is a

note = |different can of worms. The barium/boron eutectic makes it hard to

note = |say what cone this fires to - the longer it is in kiln or the greater

note = |the thermal mass of the kiln the more it will flux. Formulated

note = |originally without the ash or slip clay it was semi-satin, semi-

note = |gloss somewhere around cone 2. Boron subdues the copper coloration.

note = |I'm not taking responsibility for anyone using these glazes, etc.

note = |Something is probably toxic. They are examples of my research and

note = |they work out in formulation. Which is what they are examples of. So

note = |go formulate your own non-toxic glazes, if that is possible. It's

note = |probably bad for the environment too. Email me with questions as to

note = |household performance, as that may be indicative of other problems.

note = |The badly crazed surfaces are not considered to be a continous-non

note = |porous sanitary surfaces. Eric Hansen, Lawrence, Kansas

note = |wabi_sabi@

name = Base

index =

date = 08/04/2003

source =

type =

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality =

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 47.3

component = Gerstley borate

amount = 14.2

component = Flint

amount = 27.5

component = Whiting

amount = 9.3

component = Zinc oxide

amount = 1.7

addition = Tin oxide

addamount = 1

addition = Copper carbonate

addamount = 0.3

var = |deep leaf green= + 5% copper carb

var = |soft green = + 1% chrome ox

var = |amber = + 5% RIO

name = Base 2 Overgloss Glaze

index =

date = 07/16/00

source =

type =

range = 4

firetype = Oxidation

color =

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 6.8

component = Gerstley borate

amount = 17.5

component = Talc

amount = 6.4

component = Zinc oxide

amount = 8.1

component = Custer feldspar

amount = 38.7

component = Flint

amount = 22.5

addition = Titanium dioxide

addamount = 3

addition = Red iron oxide

addamount = 3

var = |Overspray for mottled effects:

var = |ZnO 10

var = |3124 70

var = |Barnard 20

note = |CM May 2000 p101

name = Base 2 Overgloss Glaze No GB

index =

date = 07/16/00

source =

type =

range = 4

firetype = Oxidation

color =

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Strontium carbonate

amount = 4.9

component = Dolomite

amount = 10.8

component = Whiting

amount = 3.4

component = Zinc oxide

amount = 7.7

component = Custer feldspar

amount = 32.7

component = Silica

amount = 17.8

component = Frit 3185

amount = 19.9

component = Kaolin - theoretical

amount = 2.8

addition = Titanium dioxide

addamount = 2.9

addition = Red iron oxide

addamount = 2.9

var = |Overspray for mottled effects:

var = |ZnO 10

var = |3124 70

var = |Barnard 20

note = |CM May 2000 p101

name = Base Alec Karros

index =

date = 06/04/2005

source =

type =

range = 6

firetype = Salt - Soda

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 11

component = Nepheline syenite

amount = 21

component = EPK

amount = 10

component = Gerstley borate

amount = 12

component = Silica

amount = 40

component = Whiting

amount = 4

component = Wollastonite

amount = 8

component = Frit 3124

amount = 6

var = |Color combinations:

var = |Black stain 8 + Barnard 2

var = |Red stain 8-10 + RIO 2

var = |Orange stain 8-10 + rutile 2

var = |yellow stain 8-10 + rutile 2-6

var = |copper carb 2-6

var = |cobalt ox 2-12

var = |RIO 2 + rutile 4

note = |From Julia Galloway in Clay Times May/Jn 2004.

name = Base Ayumi/Lorio 20/80

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda ash

amount = 0.7

component = Dolomite

amount = 2.2

component = Kona F-4 feldspar

amount = 7.1

component = EPK

amount = 16.2

component = Strontium carbonate

amount = 3.9

component = Flint

amount = 1

component = Frit 3124

amount = 1

component = Custer feldspar

amount = 39.7

note = |From Sally Brogden.

name = Base Ayumi/Lorio 20/80 no soda ash

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 3.2

component = Whiting

amount = 0.2

component = Strontium carbonate

amount = 5.5

component = Custer feldspar

amount = 72.4

component = Kaolin - theoretical

amount = 14.7

component = Frit 3124

amount = 1.4

component = Alumina hydrate

amount = 2.7

note = |From Sally Brogden. Re-calc to eliminate soluble ingredients.

name = Base Bill Aycock's

index =

date = 3/26/96

source =

type =

range = 6

firetype = Ox. or Red.

color = Clear

vistexture =

quality = shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 29.6

component = Nepheline syenite

amount = 8.6

component = Strontium carbonate

amount = 4.9

component = Zinc oxide

amount = 3.3

component = Gerstley borate

amount = 20.7

component = Whiting

amount = 1.8

component = Silica

amount = 31.1

note = |The base glaze is shiny, almost clear, that is a little fluid at ^6+

note = |. My glazes that get the effect are all at ^6, and usually contain

note = |Boron- whether from Gerstley Borate, a frit, or Colemanite. I use a

note = |dark Rutile, and some zinc- which is a little contradictory, because

note = |of the effect of zinc on Iron colorant. Rutile has a secondary effect

note = |when blue is from Cobalt-- the color effect from Cobalt is somewhat

note = |transparent, and the opacifier effect of rutile gives the Cobalt blue

note = |something to show up against A nice 'hint' of blue can be the effect

note = |of a small amount of Cobalt in a transparent glaze with a fair amount

note = |of Rutile. and Iron wash under it can also cause interesting

note = |variations. This gives a good white with 5% rutile, with opalescent

note = |tones and, with luck and a good clay to work on, some blues. Try

note = |adding a small amount of Cobalt. This glaze seems to have a lot of

note = |ingredients, but I had to change spars, and readjust the recipe using

note = |a line blend to zero in on what I wanted. Note that there is no

note = |clay-- you may need to use a suspender, or add a little Bentonite.

note = |The Strontium I substituted for Barium is a little coarse and can

note = |settle. If you try it- please let me know the results. submitted by:

note = |Bill Aycock e-mail: baycock@

name = Base Blend Steve's/ Lorio A 80/20

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 30.53

component = Whiting

amount = 14.11

component = Dolomite

amount = 11.41

component = Magnesium carbonate

amount = 7.61

component = EPK

amount = 14.51

component = Flint

amount = 7.61

component = Gerstley borate

amount = 4.6

component = Custer feldspar

amount = 9.61

note = |From Sally Brogden.

name = Base Blend Steve's/ Lorio A 80/20 no GB

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 24.3

component = Whiting

amount = 6.3

component = Dolomite

amount = 26.9

component = Kaolin - theoretical

amount = 16.8

component = Silica

amount = 17.3

component = Frit 3134

amount = 7.8

note = |From Sally Brogden. Re-calculated w/o the gerstley borate.

name = Base Clear (Cone 5-10)

index =

date = 8/8/97

source =

type =

range = 5 - 10

firetype =

color = clear transparent

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = Kaolin

amount = 17.5

component = Flint

amount = 32.5

note = |works well over over slips Joan Slack-DeBrock/River Run Pottery

note = |P.O.Box 95 McNaughton, WI 54543 715-277-2773 riverrun@

name = Base Dave's

index =

date = 07/06/2006

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Tan

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 29.3

component = Flint

amount = 17.4

component = Frit 3134

amount = 53.3

addition = Tin oxide

addamount = 8.7

addition = Rutile

addamount = 4

addition = Red iron oxide

addamount = 3

name = Base F1

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 4.81

component = Kona F-4 feldspar

amount = 34.62

component = Dolomite

amount = 15.38

component = Soda ash

amount = 3.85

component = EPK

amount = 17.31

component = Strontium carbonate

amount = 14.42

component = Flint

amount = 5.77

component = Frit 3110

amount = 3.85

note = |From Sally Brogden

name = Base F5

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 4.8

component = Kona F-4 feldspar

amount = 34.6

component = Dolomite

amount = 15.4

component = Soda ash

amount = 3.9

component = EPK

amount = 17.3

component = Strontium carbonate

amount = 14.4

component = Flint

amount = 5.8

component = Lithium carbonate

amount = 3.9

note = |From Sally Brogden.

name = Base F5 no soda ash

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 5.8

component = Lithium carbonate

amount = 3.9

component = Dolomite

amount = 15.6

component = Strontium carbonate

amount = 14.4

component = Nepheline syenite

amount = 39.7

component = Kaolin - theoretical

amount = 6.8

component = Silica

amount = 11.2

note = |From Sally Brogden.

name = Base Franks G18-C

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 22.68

component = Whiting

amount = 18.56

component = EPK

amount = 5.15

component = Zinc oxide

amount = 8.25

component = NC-4 feldspar

amount = 45.36

note = |From Sally Brogden

name = Base Franks G18-C no NC4 spar

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 39.3

component = Whiting

amount = 20.4

component = Zinc oxide

amount = 8.3

component = Kaolin - theoretical

amount = 9.5

component = Silica

amount = 23.5

note = |From Sally Brogden. Re-calculated to replace NC-4 spar

name = Base Gareri

index =

date = 6/3/96

source =

type =

range = 4 - 8

firetype = oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 34.1

component = EPK

amount = 1.8

component = Colemanite

amount = 16.3

component = Silica

amount = 31.8

component = Whiting

amount = 3.9

component = Zinc oxide

amount = 6.1

component = Barium carbonate

amount = 5.9

addition = Bentonite

addamount = 2

note = |Gerstley Borate or Colemanite. submitted by: Charles Gareri e-mail:

note = |cgareri@ideanet.doe.state.in.us

name = Base Glaze

index =

date = 8/8/97

source =

type =

range = 6

firetype =

color = base

vistexture =

quality = semi-matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 20

component = Dolomite

amount = 20

component = Ferro frit 3124

amount = 20

component = Kentucky OM #4

amount = 20

component = Silica

amount = 20

note = |Note: the original article calls for Frit 3134. After having

note = |experimented with both 3124 and 3134, we found we liked 3124 better.

note = |I have used the following glaze with the Degussa stains and have

note = |achieved good results. The glaze appeared in an article written by

note = |Gerald Rowan in the December, 1981 issue of CM. It would be worth

note = |getting a copy of the article because there are many color variations

note = |suggested, many of which we've tested and had beautiful results. If

note = |you have trouble finding a copy, e-mail me directly with your address

note = |and I'll mail you one. With 5% tin it is a beautiful, fat white

note = |semi-mat glaze. The clay body you use makes a huge difference. When I

note = |have used the glaze over the GWU clay body (which fires from cones

note = |6-10), the glaze is yucky and transparent. When used over a cone 6

note = |temp clay made with Redart, it is beautiful. Good luck. Barbara

note = |barbara lewis

name = Base Hamada #2

index =

date = 06/04/2005

source =

type =

range = 6

firetype = Salt - Soda

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 53

component = Kona F-4 feldspar

amount = 8

component = Ball clay

amount = 2

component = Frit 3124

amount = 15

component = Whiting

amount = 9

component = Barium carbonate

amount = 16

component = Zinc oxide

amount = 9

var = |Recipe says 3124 0-15. Colors: copper carb 2-8; cobalt ox 1/4 -2; tin ox 4-10; RIO

var = |2-4; mang diox 2-6; grey stain 2-8; black stain 2-6

note = |From Julia Galloway in Clay Times May/Jn 2004.

name = Base Jamie's cone 6

index =

date = 08/04/2003

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 3.3

component = Barium carbonate

amount = 24

component = Silica

amount = 23

component = Gerstley borate

amount = 10

component = Ball clay

amount = 6

component = Whiting

amount = 3

component = Magnesium carbonate

amount = 1

var = |black 5% stain

var = |yellow 13-15% stain

var = |bermuda green + 13-15% Mason Bermuda stain

name = Base Jun 5

index =

date = 11/18/2002

source =

type = Boron opalescent

range = 6

firetype = Oxidation

color = White

vistexture = Opalescent

quality = Waxy

transparency = Semi-opaque

xtals = None

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Colemanite

amount = 12.4

component = Nepheline syenite

amount = 6

component = Spodumene - theoretical

amount = 4.8

component = Dolomite

amount = 9.9

component = Whiting

amount = 0.8

component = Zinc oxide

amount = 1.1

component = Kaolin - theoretical

amount = 16.3

component = Silica

amount = 46.4

component = Titanium dioxide

amount = 2.4

note = |Calculated from p. 88 Glazes Cone 6 by Michael Bailey

name = Base Kaplan's 3-6

index =

date = 12/6/96

source =

type =

range = 3 - 6

firetype = oxidation

color = white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = EPK

amount = 10.56

component = Whiting

amount = 17.43

component = Silica

amount = 22.75

component = Custer feldspar

amount = 39.36

component = Zinc oxide

amount = 9.9

addition = Zircopax

addamount = 9.9

note = |I use a cone 3-5, even cone 6 white versatile majolica (electric

note = |firings) for a major client and this glaze shows off its drips quite

note = |well. In fact, it is contributing to some unwanted seconds. The glaze

note = |is a great white, but the application is crutial and I am wondering

note = |about the glaze poise, or the set of the glaze on the ware. I think

note = |the glaze is adequately flocculated with a solution of bentonite and

note = |Flocs, and runs at an SG of about 1.6. We have experimented with

note = |various dipping strategies, to no avail.There are still streak marks,

note = |thick and thin marks, from dipping. The pots are mugs, all the same,

note = |and all glazed the same. Usign tongs with sharpened points, the mugs

note = |are dipped in an arc motion to glaze both the inside and the outside

note = |and as they are raised from the glaze bucket, on an angle, the

note = |interior glaze slowly decants out. There are still streaks and uneven

note = |parts on the ourside surface, but only on the side that the glaze

note = |runs off. The opposite side is perfect. submitted by: Jonathan Kaplan

note = |e-mail: jonathan@

name = Base Kaplan's Revised 3-5

index =

date = 12/6/96

source =

type =

range = 3 - 5

firetype = oxidation

color = white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 36

component = Whiting

amount = 16

component = Strontium carbonate

amount = 17

component = Kaolin

amount = 10

component = Silica

amount = 21

addition = Zircopax

addamount = 10

note = |(The following is in response to a glazeing problem that J. Kaplan

note = |was haveing with the original base.) It sounds like the problem is

note = |one of glaze formulation rather than of application. I would guess

note = |that the glaze has too high a surface tension because of the

note = |(relatively) high amount of zinc. Looking at it chemically it looks

note = |like a higher fire glaze that has been brought down in temperature by

note = |the addition of zinc, so the zinc can't just be left out. I guess the

note = |easiest solution is to substitute an oxide with a lower surface

note = |tension for the zinc. That would point to lead, barium and strontium.

note = |I assume that lead and barium are out of the question, so I did a

note = |quick substitution using strontium carbonate. The additions of

note = |bentonite and floccs would definitly help this glaze for dipping.

note = |submitted by: Pete Pinnell e-mail: ppinnell@unlinfo.unl.edu

name = Base Lorio A/8-A 98/2

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 47.1

component = Whiting

amount = 32

component = EPK

amount = 15.4

component = Gerstley borate

amount = 3.8

component = Frit 3110

amount = 0.9

component = Lithium carbonate

amount = 0.1

component = Barium carbonate

amount = 0.1

component = Flint

amount = 0.6

note = |From Sally Brogden.

name = Base Lorio A/8-A 98/2 no GB

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 45

component = Spodumene

amount = 0.6

component = Whiting

amount = 31.8

component = Kaolin - theoretical

amount = 15.4

component = Frit 3134

amount = 6.5

component = Silica

amount = 0.2

note = |From Sally Brogden. Re-calculated w/o Gerstley Borate

name = Base Lorio A/A 90/10

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 43.3

component = Whiting

amount = 29.4

component = EPK

amount = 15.5

component = Gerstley borate

amount = 3.5

component = Frit 3110

amount = 4.4

component = Lithium carbonate

amount = 0.4

component = Barium carbonate

amount = 0.7

component = Flint

amount = 2.8

note = |From Sally Brogden.

name = Base Lorio A/A 90/10 no GB

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 47.7

component = Spodumene

amount = 2.2

component = Whiting

amount = 29.6

component = Barium carbonate

amount = 0.7

component = Kaolin - theoretical

amount = 12.2

component = Frit 3134

amount = 6.5

component = Silica

amount = 1

note = |From Sally Brogden. Re-calculated w/o Gerstley Borate.

name = Base M-3

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 41.5

component = Barium carbonate

amount = 27.8

component = Lithium carbonate

amount = 4.9

component = Whiting

amount = 4.9

component = Flint

amount = 14.5

component = Gerstley borate

amount = 1.9

component = EPK

amount = 4.5

addition = Bentonite

addamount = 2

var = |Turquoise/Green Crystal + copper carb 2.87

note = |from Sally Brogden.

name = Base M-3 no GB

index =

date = 11/09/2002

source =

type = Crystalline

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 41.3

component = Spodumene

amount = 4

component = Strontium carbonate

amount = 20.8

component = Lithium carbonate

amount = 4.2

component = Whiting

amount = 5.4

component = Silica

amount = 13.3

component = Frit 3195

amount = 3.1

addition = Bentonite

addamount = 2

var = |Turquoise/Green Crystal opper carb 2.87

note = |from Sally Brogden.Re-calculated to eliminate Gerstley Borate and barium.

name = Base M2

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 21

component = Gerstley borate

amount = 5.25

component = Custer feldspar

amount = 15.75

component = Nepheline syenite

amount = 26.5

component = Ball clay

amount = 21

component = Flint

amount = 10.5

var = |Crystal Black + cobalt carb 6 + copper carb 6

note = |From Sally Brogden

name = Base Rob's/G.A. Blend- Wheeler

index =

date = 06/18/2004

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 34.6

component = Whiting

amount = 8.4

component = Gerstley borate

amount = 2.9

component = Strontium carbonate

amount = 9.3

component = Kona F-4 feldspar

amount = 23.2

component = Frit 3110

amount = 10.6

component = Flint

amount = 9.3

component = Lithium carbonate

amount = 1.7

addition = Bentonite

addamount = 3

note = |From Geoffrey Wheeler Geoffreywheeler@

name = Base Steve's #2

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 42.93

component = Barium carbonate

amount = 8.58

component = Magnesium carbonate

amount = 8.58

component = EPK

amount = 17.17

component = Wollastonite

amount = 8.58

component = Flint

amount = 8.49

component = Strontium carbonate

amount = 5.66

note = |From Sally Brogden.

name = Base U

index =

date = 07/06/2006

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 27.2

component = Whiting

amount = 27.6

component = Zinc oxide

amount = 12.8

component = EPK

amount = 22.6

component = Flint

amount = 8.2

component = Colemanite

amount = 1.5

name = Base Van Gilder

index =

date = 02/06/2007

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 20

component = Frit 3134

amount = 20

component = Wollastonite

amount = 20

component = Silica

amount = 20

component = EPK

amount = 20

name = Basic

index =

date = 6/4/96

source =

type = Ca 4-3-2-1

range = 5 - 6

firetype = Ox or Red

color = Variable

vistexture =

quality = Variable

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = K-200 Feldspar

amount = 43

component = EPK

amount = 14

component = Whiting

amount = 20

component = Flint

amount = 23

note = |A base mixture to which mustbe added 17 parts of any of the usual

note = |flux materials: zinc, barium, colemanite, dolomite, talc, wood ash,

note = |other alkalines. Base is C/9 Redtn. as is. Glaze Type: Ca 4-3-2-1.

note = |Firing type: Ox or Red. From Val Cushing. VC ed

note = |

name = Beady

index =

date = 06/07/00

source =

type = Bead

range = 5

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3134

amount = 10

component = Nepheline syenite

amount = 35

component = Wollastonite

amount = 10

component = Magnesium carb

amount = 35

component = EPK

amount = 10

note = |From Sandy Lance.

name = Beady Eyes 2

index =

date = 4/3/98

source =

type = Texture

range = 6 - 8

firetype = Ox. or Red.

color = white base

vistexture =

quality = texture glaze

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 25

component = Whiting

amount = 6

component = Magnesium carbonate

amount = 35

component = Kentucky OM #4

amount = 10

component = Flint

amount = 8

component = Ferro frit 3134

amount = 16

note = |This is not really a glaze, it is too high in secondary fluxes. It

note = |has a snake - alligator like crawling texture. This looks good over a

note = |black slip or over some velvet underglazes. Chemical Analysis Na2O

note = |0.07 Al2O3 0.12 SiO2 1.12 K2O 0.05 B2O3 0.09 TiO2 0.00 MgO 0.67 Fe2O3

note = |0.00 CaO 0.21 Alumina:Silica ratio is 1.00 : 9.09 Neutral:Acid ratio

note = |is 1.00 : 5.19 Alkali:Neutral:Acid ratio is 1.00 : 0.22 : 1.12

note = |Expansion coefficient: 67.2 x 10e-7 per degree C Oxides causing

note = |abnormal expansion effects: B2O3 Here's some recipes for a couple of

note = |crawling glazes. The high magnesium content of the glazes is what

note = |encourages the crawling action. The first one crawls into rounded

note = |bumps. Someone on the list sent it to me. The only problem that I

note = |have with this glaze (and I use the word glaze loosely in this case)

note = |is that after you dip your pieces into the glaze it tends to flake

note = |off before and sometimes during the firing. I usually brush Amaco

note = |Velvet Underglazes on the pots first and then dip them in glaze. The

note = |glaze application should be thick to encourage the crawling... happy

note = |testing, John Post jp6mchp@ Sterling Heights, Michigan

name = Beth's Shiny Green

index =

date = 6/3/96

source =

type =

range = 5 - 7

firetype =

color = light green

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 46.74

component = Silica

amount = 25

component = Gerstley borate

amount = 10.87

component = Ball clay

amount = 6.52

component = Dolomite

amount = 10.87

addition = Titanium dioxide

addamount = 7.61

addition = Bentonite

addamount = 1.09

addition = Copper carbonate

addamount = 1.63

note = |Hope this works for you. It is between a lime and chartreuse.

note = |submitted by: Beth Fusaro e-mail: elfusaro@freenet.scri.fsu.edu

note = |

name = Bill Aycock's Base

index =

date = 3/26/96

source =

type =

range = 6

firetype = Ox. or Red.

color = almost clear

vistexture =

quality = shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 29.56

component = Nepheline syenite

amount = 8.62

component = Strontium carbonate

amount = 4.91

component = Zinc oxide

amount = 3.31

component = Gerstley borate

amount = 20.74

component = Whiting

amount = 1.8

component = Silica

amount = 31.06

note = |The base glaze is shiny, almost clear, that is a little fluid at ^6+

note = |. My glazes that get the effect are all at ^6, and usually contain

note = |Boron- whether from Gerstley Borate, a frit, or Colemanite. I use a

note = |dark Rutile, and some zinc- which is a little contradictory, because

note = |of the effect of zinc on Iron colorant. Rutile has a secondary effect

note = |when blue is from Cobalt-- the color effect from Cobalt is somewhat

note = |transparent, and the opacifier effect of rutile gives the Cobalt blue

note = |something to show up against A nice 'hint' of blue can be the effect

note = |of a small amount of Cobalt in a transparent glaze with a fair amount

note = |of Rutile. and Iron wash under it can also cause interesting

note = |variations. This gives a good white with 5% rutile, with opalescent

note = |tones and, with luck and a good clay to work on, some blues. Try

note = |adding a small amount of Cobalt. This glaze seems to have a lot of

note = |ingredients, but I had to change spars, and readjust the recipe using

note = |a line blend to zero in on what I wanted. Note that there is no

note = |clay-- you may need to use a suspender, or add a little Bentonite.

note = |The Strontium I substituted for Barium is a little coarse and can

note = |settle. If you try it- please let me know the results. submitted by:

note = |Bill Aycock e-mail: baycock@

note = |

name = Bird Matt

index =

date = 1/13/96

source =

type =

range = 6

firetype = Ox. or Red.

color = silver white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 71.46

component = Dolomite

amount = 23.71

component = Ball clay

amount = 4.83

addition = Tin oxide

addamount = 9.55

addition = Bentonite

addamount = 2.81

note = |Ellen, about l978 Ruth Duckworth used a glaze in Banff that was

note = |called it with 5% Rutile or Ilemanite. I loved the glaze. Satiny

note = |silver-white, not blue though. submitted by: ELKE BLODGETT email:

note = |eiblodge@freenet.edmonton.ab.ca

note = |

name = Black

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = Black

vistexture =

quality = more matt thin, more glossy thick

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = K-200 feldspar

amount = 78.81

component = Gerstley borate

amount = 10.76

component = Whiting

amount = 5.46

component = EPK

amount = 4.97

addition = Copper carbonate

addamount = 3.31

addition = Cobalt carbonate

addamount = 1.99

addition = Manganese dioxide

addamount = 4.14

note = |kiln type: gas makes blue over the matt white, does interesting

note = |things over and under oxblood. submitted by: John Anthony e-mail:

note = |JTRAX@

note = |

name = Black Albany

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca Mg SlipGlaze

range = 5 - 6

firetype = Ox. or Red.

color = black

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 75

component = Nepheline syenite

amount = 20

component = Gerstley borate

amount = 5

addition = Cobalt oxide

addamount = 5

note = |Albany sub.= Yellow Banks Red #101 + Whiting 14% approx. + Dolomite

note = |2-3% approx.

name = Black Bright

index =

date = 08/03/2003

source =

type =

range = 5

firetype = Oxidation

color = Black

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 72

component = Spodumene

amount = 12

component = Gerstley borate

amount = 16

addition = Cobalt oxide

addamount = 2.4

name = Black crystal

index =

date = 11/19/2001

source =

type = Mid-fire

range = 5-6

firetype = Oxidation

color = Black

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 21

component = Gerstley borate

amount = 5.25

component = Custer feldspar

amount = 15.75

component = Nepheline syenite

amount = 26.5

component = Ball clay

amount = 21

component = Flint

amount = 10.5

addition = Cobalt carbonate

addamount = 6

addition = Copper carbonate

addamount = 6

note = |From Shannon Nelson

name = Black crystal no gb

index =

date = 11/19/2001

source =

type = Mid-fire

range = 5-6

firetype = Oxidation

color = Black

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 11

component = Whiting

amount = 10.5

component = Nepheline syenite

amount = 34.2

component = Kaolin - theoretical

amount = 17.5

component = Silica

amount = 16.3

component = Frit 3134

amount = 10.4

addition = Cobalt carbonate

addamount = 6

addition = Copper carbonate

addamount = 6

note = |From Shannon Nelson

name = Black Crystalline

index =

date = 12/7/96

source =

type = Crystalline

range = 6

firetype = oxidation

color = black

vistexture =

quality = matte

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 21

component = Gerstley borate

amount = 5.25

component = Custer feldspar

amount = 15.75

component = Nepheline syenite

amount = 26.5

component = Ball clay

amount = 21

component = Flint

amount = 10.5

addition = Cobalt carbonate

addamount = 6

addition = Copper carbonate

addamount = 6

note = |Too many ingredients (these ingredients are also to be added to the

note = |recipe) (can't remember who posted this originally, might've been me

note = |;) Mishy Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

note = |

name = Black Cushing

index =

date = 08/04/2003

source =

type =

range = 5-6

firetype =

color = Black

vistexture =

quality =

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 65

component = Barium carbonate

amount = 10

component = Nepheline syenite

amount = 10

component = Talc

amount = 15

addition = Chromium oxide

addamount = 1

addition = Manganese dioxide

addamount = 2

addition = Cobalt carbonate

addamount = 2

name = Black Granny's Shorts

index =

date = 3/26/96

source =

type =

range = 5 - 6

firetype = Ox. or Red.

color = Black

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = PV Clay

amount = 15

component = Custer spar

amount = 35

component = Flint

amount = 10

component = Whiting

amount = 10

component = Gerstley borate

amount = 30

addition = Black stain

addamount = 7

note = |(Granny's shorts with black stain) Beautiful black gloss, pulls away

note = |from edges, detail will be white, very nice. This is a good base

note = |glaze for trying many oxides and stains in. from Michelle Lowe,

note = |potter in the Phoenix desert mishlowe@

note = |mishlowe@aztec.asu.edu

name = Black IE

index =

date = 4/11/95

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = black / brown

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 17

component = Nepheline syenite

amount = 34

component = Kaolin

amount = 8

component = Silica

amount = 41

addition = Iron oxide

addamount = 13

note = |Shiny black/brown, ok. From Brian Kemp, (kempb@nievax.nie.ac.sg) via

note = |Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired

note = |at 100 degrees per hour to 600 degrees, then free for all to cone

note = |6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp, Nanyang Technological University, Block B,

note = |Room 216, 469 Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

name = Black Larry's

index =

date = 6/3/96

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = Black

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 46.7

component = Whiting

amount = 14.4

component = EPK

amount = 8.9

component = Barium carbonate

amount = 2.2

component = Silica

amount = 22.2

component = Lithium carbonate

amount = 5.6

addition = Cobalt carbonate

addamount = 3.3

addition = Iron oxide

addamount = 4.4

addition = Manganese dioxide

addamount = 2.2

note = |Here's a glaze I adapted from ^10 (just leave out the lithium for

note = |^10). It's a very glossy black black with a very long firing range in

note = |either oxidation or reduction. You may want to add just a touch of

note = |chrome oxide. I've handed this glaze out in my tile workshops for

note = |years, and I know a lot of people have had success with it. submitted

note = |by: Paul Lewing e-mail: PJLewing@

name = black Matt

index =

date = 4/10/95

source =

type = Mid-fire

range = 5

firetype = Oxidation

color = black

vistexture =

quality = matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barnard slip

amount = 90

component = Whiting

amount = 10

note = |Rob Wadey (robert wadey ) 9734B - 100 Ave

note = |Grande Prairie, Alberta t8V 0T6 Phone: (403) 538-3731 Fax: (403)

note = |538.3732

name = black Matt 2

index =

date = 4/10/95

source =

type =

range = 5

firetype = Oxidation

color = black

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barnard slip

amount = 90

component = Whiting

amount = 10

note = |Rob Wadey (robert wadey ) 9734B - 100 Ave Grande Prairie, Alberta t8V

note = |0T6 Phone: (403) 538-3731 Fax: (403) 538.3732

name = Black Matte

index =

date = 9/20/95

source =

type =

range = 6

firetype = Ox. or Red.

color = black

vistexture =

quality = matte

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Alberta slip

amount = 70

component = Ferro Frit 3124

amount = 20

component = Wollastonite

amount = 10

addition = Rutile

addamount = 5

addition = Mason stain 6600

addamount = 5

addition = Bentonite

addamount = 2

note = |Here's a recipe I used just recently for a dinnerset and it works

note = |very well. Has a nice matte finish and is good for food surfaces. I

note = |experimented with increasing amounts of black stain (I think that's a

note = |mason #?..in any event, not the stain with the cobalt base) up to an

note = |additional 10% and they were all good. submitted by: Dan Taylor

note = |e-mail: dataylor@mlc.

name = Black Matte

index =

date = 9/20/95

source =

type =

range = 6

firetype = Ox. or Red.

color = black

vistexture =

quality = matte

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Alberta slip

amount = 70

component = Ferro Frit 3124

amount = 20

component = Wollastonite

amount = 10

addition = Rutile

addamount = 5

addition = Mason stain 6600

addamount = 5

addition = Bentonite

addamount = 2

note = |Here's a recipe I used just recently for a dinnerset and it works

note = |very well. Has a nice matte finish and is good for food surfaces. I

note = |experimented with increasing amounts of black stain (I think that's a

note = |mason #?..in any event, not the stain with the cobalt base) up to an

note = |additional 10% and they were all good. submitted by: Dan Taylor

note = |e-mail: dataylor@mlc.

name = Black Metallic

index =

date = 3/26/96

source =

type = Metallic

range = 6

firetype = oxidation

color = Black

vistexture =

quality =

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 11

component = Whiting

amount = 5

component = Custer feldspar

amount = 79

component = EPK

amount = 5

addition = Cobalt oxide

addamount = 2

addition = Copper carbonate

addamount = 4

addition = Manganese dioxide

addamount = 4

note = |I use this ^6 black and love it. If you layer it with white glaze it

note = |turns a nice blue. submitted by: Barbara Webb e-mail:

note = |barbara@atl.

name = black metallic

index =

date = 12/7/96

source =

type = Metallic

range = 6

firetype = oxidation

color = metallic black

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 50

component = Gerstley borate

amount = 25

component = Flint

amount = 25

addition = Black iron oxide

addamount = 10

addition = Cobalt oxide

addamount = 2

addition = Copper carbonate

addamount = 4

note = |(wonderful!) Here are a few black cone 6 glazes I gleaned from

note = |clayart. If you sub Strontium carb for the Barium in the second they

note = |will all be food safe. From Sharon LaRocca-Miranda via Mishy Michelle

note = |Lowe, potter in the Phoenix desert mishlowe@

note = |mishlowe@aztec.asu.edu

name = Black Metallic

index =

date = 3/26/96

source =

type = Metallic

range = 6

firetype = Oxidation

color = Black

vistexture =

quality = Metallic

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 11

component = Whiting

amount = 5

component = Custer feldspar

amount = 79

component = EPK

amount = 5

addition = Cobalt oxide

addamount = 2

addition = Copper carbonate

addamount = 4

addition = Manganese dioxide

addamount = 4

note = |I use this ^6 black and love it. If you layer it with white glaze it

note = |turns a nice blue. submitted by: Barbara Webb e-mail:

note = |barbara@atl.

name = BLACK METALLIC 2

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = metallic black

vistexture =

quality = shiny glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 36

component = Whiting

amount = 9

component = Colemanite

amount = 5

component = Dolomite

amount = 5

component = Talc

amount = 16

component = Barium carbonate

amount = 8

component = Flint

amount = 16

component = Bentonite

amount = 5

addition = Black iron oxide

addamount = 3

addition = Zircopax

addamount = 15

addition = Rutile

addamount = 20

addition = Cobalt oxide

addamount = 3

note = |(Mishy suggests subbing Strontium 5 for the Barium) Here are a few

note = |black cone 6 glazes I gleaned from clayart. If you sub Strontium carb

note = |for the Barium in the second they will all be food safe. from Dan

note = |Taylor I have also added 3% #6600 Black Mason stain for an even more

note = |black glaze. Mishy Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

name = Black Metallic 3

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color = black

vistexture =

quality = matte

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 36.73

component = Whiting

amount = 9.18

component = Colemanite

amount = 5.1

component = Dolomite

amount = 5.1

component = Talc

amount = 16.33

component = Barium carbonate

amount = 8.16

component = Silica

amount = 16.33

component = Black iron oxide

amount = 3.06

addition = Bentonite

addamount = 5.1

addition = Zircopax

addamount = 15.31

addition = Rutile

addamount = 20.41

addition = Cobalt oxide

addamount = 3.06

note = |Here is one I have used for some time now and have found it to be

note = |very stable. It's not the simplest of recipes and probably could be

note = |simplified but I've never taken the time to do so because I don't use

note = |it that often so a batch lasts for a couple of years and reworking it

note = |doesn't seem to be on the top of my need-to list. So I'll give it to

note = |you like I have it in my grubby little book. I have also added 3%

note = |#6600 Black Mason stain for an even more black glaze. submitted by:

note = |Dan Taylor e-mail: dataylor@mlc.

name = Black Metallic 4

index =

date = 3/26/96

source =

type = Metallic

range = 6

firetype = oxidation

color = Black

vistexture =

quality =

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 11

component = Whiting

amount = 5

component = Custer feldspar

amount = 79

component = EPK

amount = 5

addition = Cobalt oxide

addamount = 2

addition = Copper carbonate

addamount = 4

addition = Manganese dioxide

addamount = 4

note = |I use this ^6 black and love it. If you layer it with white glaze it

note = |turns a nice blue. submitted by: Barbara Webb e-mail:

note = |barbara@atl.

name = Black Metallic Matt

index =

date =

source =

type = Metallic

range = 6 - 9

firetype =

color = Opaque metallic Black

vistexture =

quality = Matte

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wood ash

amount = 25

component = Nepheline syenite

amount = 37.5

component = Talc

amount = 18.75

component = Ball clay

amount = 18.75

addition = Iron oxide

addamount = 2.5

addition = Black copper oxide

addamount = 3.75

addition = Cobalt oxide

addamount = 2.92

var = |Other colors (delete black colorants): for matt brown with lots of

var = |texture add: Rutile 1.74 Iron Oxide 3.50 Manganese Dioxide 3.50 for

var = |matt blue breaking to something greenish add: Cobalt Carbonate 3.00

var = |Rutile 3.00

note = |I've been using the same wood ash formula for about 10

note = |years and have used wood ash from all kinds of known and unknown tree

note = |sources (washed and unwashed), fired to cone 6, 7, 8, 9 but mostly to

note = |cone 7 in an electric kiln. Write me if you have any questions about

note = |these glazes submitted by: Anne Fallis-Elliott e-mail: FallisT@

name = black metallic1

index =

date = 12/7/96

source =

type = Metallic

range = 6

firetype = oxidation

color = metallic black

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 50

component = Gerstley borate

amount = 25

component = Flint

amount = 25

addition = Black iron oxide

addamount = 10

addition = Cobalt oxide

addamount = 2

addition = Copper carbonate

addamount = 4

note = |(wonderful!) Here are a few black cone 6 glazes I gleaned from

note = |clayart. If you sub Strontium carb for the Barium in the second they

note = |will all be food safe. From Sharon LaRocca-Miranda via Mishy Michelle

note = |Lowe, potter in the Phoenix desert mishlowe@

note = |mishlowe@aztec.asu.edu

name = Black Mirror

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = black

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 38.18

component = Silica

amount = 23.64

component = Whiting

amount = 13.64

component = Kaolin

amount = 13.64

component = Zinc oxide

amount = 10.91

addition = Red iron oxide

addamount = 7.27

addition = Cobalt oxide

addamount = 0.91

note = |Here is a Cone 6 glaze that I have found to be very reliable This

note = |gives a shiny, mirror black. regards Brian Kemp. Simgapore

note = |kemob@nievax.nie.ac.sg

name = Black Mountain

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color =

vistexture =

quality = Satin matt

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Bainbridge spar

amount = 30

component = Whiting

amount = 20

component = Flint

amount = 20

component = Kaolin

amount = 10

component = Talc theoretical

amount = 20

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse. Original recipe just said "Bainbridge" - assumed to mean

note = |Bainbridge soda feldspar.

name = Black Patty's Metallic

index =

date = 03/02/2003

source =

type = Metallic

range = 6

firetype = Ox. or Red.

color = blue-black

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 5

component = Custer feldspar

amount = 79

component = Whiting

amount = 5

component = Colemanite

amount = 11

addition = Copper oxide

addamount = 2

addition = Copper carbonate

addamount = 3

addition = Manganese dioxide

addamount = 4

addition = Cobalt oxide

addamount = 2

note = |from Patty Block in Tupelo, MS. Very reliable, doesn't run or pit. More metallic

note = |in reduction.

name = Black Reed's Glossy

index =

date = 1/13/96

source =

type = Mid-fire

range = 6

firetype = oxidation

color = Black

vistexture =

quality = gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 11

component = EPK

amount = 5

component = Custer feldspar

amount = 79

component = Whiting

amount = 5

addition = Copper carbonate

addamount = 4

addition = Manganese dioxide

addamount = 4

addition = Cobalt oxide

addamount = 2

note = |I have used the following glaze with an electric kiln and found good

note = |results. The glaze 'Reed's Glossy Black' needs to be put on thick and

note = |does not seem to run. submitted by: Frank Helme e-mail: fhelme@

name = Black Reeds Glory

index =

date = 6/3/96

source =

type = Mid-fire

range = 6

firetype = oxidation

color = black

vistexture =

quality = glossy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 11

component = EPK

amount = 5

component = Custer feldspar

amount = 79

component = Whiting

amount = 5

addition = Copper carbonate

addamount = 4

addition = Manganese dioxide

addamount = 6

addition = Cobalt oxide

addamount = 2

addition = Red iron oxide

addamount = 1

note = |A true glossy black Tested on Dillo White clay at a full ^6.

note = |submitted by: Lori Wilkinson e-mail: lorwilk@

name = Black Rob Wadley's Barnard

index =

date = 4/7/95

source =

type =

range = 6

firetype = Oxidation

color = Black

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barnard clay

amount = 65

component = Feldspar

amount = 15

component = Whiting

amount = 10

component = Gerstley borate

amount = 10

note = |Test fired on Plainsman M340 (an off white clay) in an electric kiln. (I used

note = |Gerstley Borate for the Colemanite) Crawls if thick and can be used on greenware!! My

note = |tests were on bisque. It's dark brown, more runny, semi-gloss breaking to gloss where

note = |thick. BB3 I added 2% Manganese just for fun. This was a more intense version of BB2.

note = |Thanks Rob! From Vickie Sproule via clayart email: jsproule@mars. Kathy Darby

note = |sent two recipes, which I've called Darby 1&2

name = Black Shiny

index =

date = 3/26/96

source =

type = Mid-fire

range = 5 - 6

firetype = Oxidation

color = Black

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 43.21

component = Kaolin

amount = 9.88

component = Silica

amount = 23.46

component = Whiting

amount = 11.11

component = Gerstley borate

amount = 12.35

addition = Iron oxide

addamount = 9.88

note = |Shiny black, ok. from Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

name = Black Silky Matt

index =

date = 3/26/96

source =

type =

range = 5 - 6

firetype = Ox. or Red.

color = Opaque Black

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 7.51

component = Talc

amount = 5.42

component = Dolomite

amount = 3.34

component = Kona F-4 feldspar

amount = 16.69

component = Neph Sye

amount = 32.93

component = Whiting

amount = 7.12

component = Zinc oxide

amount = 6.45

component = EPK

amount = 12.57

component = Flint

amount = 7.96

addition = Cobalt oxide

addamount = 0.11

addition = Copper oxide

addamount = 0.33

addition = Red iron oxide

addamount = 0.33

addition = Bentonite

addamount = 0.11

note = |from Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

name = Black Silky Matt no GB

index =

date = 3/26/96

source =

type =

range = 5 - 6

firetype = Ox. or Red.

color = Opaque Black

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 5.4

component = Whiting

amount = 7.9

component = Zinc oxide

amount = 6

component = Nepheline syenite

amount = 40.8

component = Kaolin

amount = 16.8

component = Silica

amount = 9.6

component = Frit 3134

amount = 13.6

addition = Cobalt oxide

addamount = 0.09

addition = Copper oxide

addamount = 0.3

addition = Red iron oxide

addamount = 0.3

addition = Bentonite

addamount = 0.09

note = |from Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

name = Black Slip Glaze

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = black

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barnard clay

amount = 36.4

component = Frit 5301

amount = 54.5

component = Zinc oxide

amount = 9.1

addition = Bentonite

addamount = 2.7

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse. Can be used on greenware.

note = |

note = |

name = Black Tenmoku

index =

date = 08/01/2001

source =

type =

range = 6

firetype = Oxidation

color = jet black

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 375

component = Kaolin

amount = 50

component = Whiting

amount = 50

component = Gerstley borate

amount = 25

addition = Red iron oxide

addamount = 45

note = |> ClayArt Listserv recipe < If you find this glaze useful, please

note = |consider submitting it to the GlazeBase project with full

note = |documentation. Use one of the GlazeBase submission formats available

note = |on the CeramicsWeb web page.

note = | Originally specified Conish stone. comments: Semi matt jet black, no

note = |breaking to rust. ok. From Brian Kemp, (kempb@nievax.nie.ac.sg) via

note = |Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired

note = |at 100 degrees per hour to 600 degrees, then free for all to cone

note = |6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp, Nanyang Technological University, Block B,

note = |Room 216, 469 Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

note = |

name = Black With Gold

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color = Opaque Black with metallic gold

vistexture =

quality = satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kentucky ball clay

amount = 7

component = Redart

amount = 86

component = Silica

amount = 7

addition = Copper carbonate

addamount = 8.8

addition = Cobalt carbonate

addamount = 7

addition = Manganese dioxide

addamount = 64

note = |Dull satin black with a bronz cast. Tested on Dillo White clay at a

note = |full ^6. submitted by: Lori Wilkinson e-mail: lorwilk@

note = |NOT for foodware.

name = Blue Barium Jamie's

index =

date = 08/04/2003

source =

type = Barium matt

range = 6

firetype = Oxidation

color = Turquoise

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 65

component = Barium carbonate

amount = 35

component = EPK

amount = 1

addition = Copper carbonate

addamount = 2

addition = Bentonite

addamount = 1

note = |NOT for food surfaces. From Jamie Walker.

name = Blue Celadon

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = Blue celadon

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Volcanic ash

amount = 48.7

component = Wollastonite

amount = 12.17

component = Ball clay

amount = 10.43

component = Gerstley borate

amount = 8.7

component = Silica

amount = 6.96

component = Alberta slip

amount = 13.04

addition = Cobalt carbonate

addamount = 0.22

note = |kiln type: gas goes a little gray over stoneware, nicely translucent

note = |on procelain. submitted by: John Anthony e-mail: JTRAX@

note = |

name = Blue Cindy's

index =

date = 3/26/96

source =

type = Mid-fire

range = 6

firetype = oxidation

color = deep blue

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 20

component = Whiting

amount = 20

component = EPK

amount = 20

component = Silica

amount = 20

component = Ferro Frit 3124

amount = 20

addition = Bentonite

addamount = 2

addition = Cobalt carbonate

addamount = 5

note = |It is a nice, dark cobalt blue--Satin to

note = |glossy. I have to soak on medium for about 2 hrs. after the kiln

note = |sitter goes off to get it to smooth out. submitted by: Cindy P

note = |Russell e-mail: crussel@tenet.edu

name = Blue Dark Specks

index =

date = 08/04/2003

source =

type =

range = 6

firetype = Oxidation

color = Blue

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Silica

amount = 35

component = EPK

amount = 16

component = Gerstley borate

amount = 50

addition = Cobalt oxide

addamount = 1

name = Blue Deep Shiny

index =

date = 10/06/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Blue

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 44

component = EPK

amount = 2

component = Gerstley borate

amount = 20

component = Whiting

amount = 4

component = Barium carbonate

amount = 5

component = Flint

amount = 25

addition = Copper carbonate

addamount = 6

addition = Cobalt carbonate

addamount = 9

addition = Lithium carbonate

addamount = 4

name = Blue Deep Shiny

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = deep blue

vistexture =

quality = shiny glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 42.31

component = EPK

amount = 1.92

component = Colemanite

amount = 19.23

component = Whiting

amount = 3.85

component = Barium Carb

amount = 4.81

component = Flint

amount = 24.04

component = Lithium Carb

amount = 3.85

addition = Copper Carb

addamount = 5.77

addition = Cobalt oxide

addamount = 0.87

note = |I am using the following cone 6 recipe, which makes a gorgeous, shiny

note = |glaze. It contains only 5 percent barium, so I am hoping it is

note = |foodsafe. Does anyone know? Thanks, Ruth Jacobson skyceramic@

name = Blue Deep Shiny-Valerie's

index =

date = 03/25/2004

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Blue

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow = Extreme

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 22

component = Gerstley borate

amount = 10

component = Whiting

amount = 2

component = Barium carbonate

amount = 2.5

component = Flint

amount = 16.3

component = Frit 3124

amount = 8

component = Nepheline syenite

amount = 11.8

component = Dolomite

amount = 4.1

component = Wollastonite

amount = 12.3

component = EPK

amount = 11

addition = Copper carbonate

addamount = 4

addition = Cobalt carbonate

addamount = 4.8

addition = Lithium carbonate

addamount = 2

note = |Thin application is semi-opaque, thick is opaque. From Valerie Duncan

name = Blue Deep Shiny-Valerie's-no gb

index =

date = 03/25/2004

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Blue

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow = Extreme

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 21.9

component = EPK

amount = 11.5

component = Lithium carbonate

amount = 3.9

component = Whiting

amount = 2.3

component = Strontium carbonate

amount = 3.6

component = Silica

amount = 23.9

component = Frit 3134

amount = 32.8

addition = Copper carbonate

addamount = 5.8

addition = Cobalt carbonate

addamount = 8.8

note = |Thin application is semi-opaque, thick is opaque. From Valerie Duncan

name = Blue Emily's

index =

date = 6/3/96

source =

type =

range = 6

firetype = reduction

color =

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 36.56

component = Gerstley borate

amount = 19.35

component = OM-4 Ball Clay

amount = 11.83

component = Talc

amount = 15.05

component = Silica

amount = 10.75

component = Dolomite

amount = 6.45

addition = Zircopax

addamount = 4.3

addition = Cobalt carbonate

addamount = 3.23

note = |We use the second one at cone 6 in reduction, and it gives a

note = |beautiful bright purple. I have also done a series of color

note = |variations on the base glaze replacing the cobalt. The most promising

note = |of those was the one using 6% rutile. It gave a warm tan-yellow. The

note = |outstanding quality of the glaze (aside from the purple, of course)

note = |is the smooth texture and its reliability. submitted by: Rick

note = |Malmgren e-mail: r-malmgren@sjca.edu

name = Blue Green

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color =

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 30

component = Silica

amount = 30

component = Dolomite

amount = 20

component = EPK

amount = 20

addition = Chrome oxide

addamount = 2.5

addition = Cobalt oxide

addamount = 0.3

note = |submitted by: Cindy Russell e-mail: crussel@tenetedu

note = |

name = Blue Green IE 30 O Matt

index =

date = 4/11/95

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = blue green?

vistexture =

quality = Dry matte

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Strontium carbonate

amount = 27.5

component = Nepheline syenite

amount = 59.2

component = Ball clay

amount = 4.1

addition = Titanium dioxide

addamount = 3.6

addition = Cobalt carbonate

addamount = 0.5

note = |From Brian Kemp, (kempb@nievax.nie.ac.sg)

note = |via Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware

note = |Fired at 100 degrees per hour to 600 degrees, then free for all to

note = |cone 6-7. Brian Kemp, Nanyang Technological University, Block B,

note = |Room 216, 469 Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

name = Blue Green Slip glaze

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = blue green

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 60

component = Frit 5301

amount = 40

addition = Copper carbonate

addamount = 3

addition = Rutile

addamount = 4

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse.

note = |

note = |

name = Blue Julie's Water

index =

date = 11/15/99

source =

type = Alkaline

range = 5

firetype = Oxidation

color = Turquoise

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3110

amount = 3

component = Nepheline syenite

amount = 18

component = Whiting

amount = 2

component = Strontium carbonate

amount = 25

component = EPK

amount = 14

component = Flint

amount = 38

addition = Copper carbonate

addamount = 3

var = |blue = 3-7% Cu

var = |chartreuse = .5% Chrome

note = |2 coats if brushing. Gum recommended for brushing. Runs. From George Bowes.

note = |Recalcualted to substitute Strontium for Ba.

name = Blue matt

index =

date = 12/6/96

source =

type =

range = 6

firetype =

color = blue

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Volcanic ash

amount = 55

component = Whiting

amount = 25

component = Barium carbonate

amount = 10

component = Kentucky OM #4

amount = 10

addition = Cobalt oxide

addamount = 0.5

note = |(I used 7.5 of Stronium carb in place of the Barium and it worked OK)

note = |Lyn lyn peelle

note = |

name = Blue matt

index =

date = 12/6/96

source =

type =

range = 6

firetype =

color = blue

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Volcanic ash

amount = 55

component = Whiting

amount = 25

component = Barium carbonate

amount = 10

component = Kentucky OM #4

amount = 10

addition = Cobalt oxide

addamount = 0.5

note = |(I used 7.5 of Stronium carb in place of the Barium and it worked OK)

note = |Lyn lyn peelle

note = |

name = Blue Midnight

index =

date = 6/3/96

source =

type =

range = 5 - 8

firetype = Ox. or Red.

color = Blue

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Feldspar

amount = 44

component = Whiting

amount = 17

component = Ball clay

amount = 8

component = China clay

amount = 9

component = Silica

amount = 22

note = |translucency: Opaque Cobalt 5% for rich midnight blue. Superpax 10%

note = |for bright white, very good color response with on glaze stains.

note = |submitted by: Jo Ann Stevens e-mail: jstevens@ source for

note = |original recipe: Emanuel Cooper

name = Blue Opal

index =

date = 08/03/2003

source =

type =

range = 5-7

firetype = Oxidation

color = Blue

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Strontium carbonate

amount = 4

component = Gerstley borate

amount = 20.8

component = Whiting

amount = 1.5

component = Custer feldspar

amount = 44.3

component = EPK

amount = 2.1

component = Flint

amount = 24.9

component = Zinc oxide

amount = 3.3

addition = Tin oxide

addamount = 7.1

addition = Rutile

addamount = 3.1

addition = Cobalt carbonate

addamount = 2.6

name = Blue Pale Rutile

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color = pale blue

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 8.5

component = Magnesium carbonate

amount = 1.9

component = Whiting

amount = 15.3

component = Wood ash

amount = 14.5

component = Nepheline syenite

amount = 15.6

component = Kaolin

amount = 10.9

component = Flint

amount = 33.4

addition = Rutile

addamount = 1.7

note = |I fired cone 6 oxidation pretty exclusively for five years and worked

note = |with many glazes (being a glaze testing maniac). One that I really

note = |enjoyed using, for several years (and I still use it occasionally)

note = |was a Rutile Pale Blue that has no cobalt in it, yet goes most

note = |definitely blue in oxidation. It is a tan mat if it isn't fired high

note = |enough and glossy pale translucent blue (almost celadon-like) at

note = |temp. Usually crazes... Mishy, enjoying an unusually cold and rainy

note = |Sonoran desert Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

note = |

name = Blue Slip glaze

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = blue

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 60

component = Frit 5301

amount = 40

addition = Cobalt carbonate

addamount = 3

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse.

note = |

note = |

name = Blue Spot Glaze

index =

date = 02/17/2006

source =

type = Crystalline

range = 5

firetype = Oxidation

color = tan with blue spots

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 20.5

component = Sodium bicarbonate

amount = 18

component = Zinc oxide

amount = 19

component = Kaolin

amount = 8

component = Flint

amount = 34.5

addition = Nickel carbonate

addamount = 2

note = |Clay Times NOv/Dec. 2005 p.51. No firing directions were given, but I assume slow

note = |cooling is needed. This is a very high Zn, low Al glaze, and probably is very runny.

name = Blue Spruce

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = blue-green

vistexture =

quality = semi-gloss to gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 18.18

component = Ferro frit 3124

amount = 22.73

component = Nepheline syenite

amount = 22.73

component = Kaolin

amount = 13.64

component = Flint

amount = 13.64

component = Zircopax (or Ultrox)

amount = 9.09

addition = Copper carbonate

addamount = 1.82

addition = Cobalt carbonate

addamount = 1.82

addition = Rutile

addamount = 4.55

note = |Frank Helme sent me the correct recipe for Blue Spruce. ( I fire with

note = |a ^ 7 in sitter) The recipe published in ClayTimes left out the

note = |Cobalt Carb. I remixed and retested and it is an improvement over the

note = |lime-green (with no copper carbonate). A semi-gloss to glossy

note = |texture. The color is a soft blue gray with some visual

note = |texture/mottling. I also fire it in a ^ 7 Soda in reduction and its a

note = |more intense blue. Good luck! Rafael Molina-Rodriguez

note = |rmr3431@dcccd.edu

note = |

name = Blue St. Helens

index =

date = 6/24/97

source =

type = Zinc matt

range = 6

firetype = Oxidation

color = blue

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer spar

amount = 39.6

component = Flint

amount = 5.4

component = Whiting

amount = 14.1

component = EPK

amount = 11.6

component = Zinc oxide

amount = 8.2

component = Dolomite

amount = 0.4

component = Colemanite

amount = 0.9

component = Volcanic ash - Mt. St. Helens

amount = 19.9

addition = Cobalt oxide

addamount = 0.1

note = |This makes 3 gallons of glaze here are two glazes I have used

note = |successfully but not put thru any analysis. I got them at an art

note = |studio where I used to take classes. They are better if layered with

note = |other glazes. Wendy Hampton from Bainbridge Island

note = |WA

note = |A

name = Blue Tamaras

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = blue

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 39

component = Silica

amount = 9

component = EPK

amount = 7

component = Whiting

amount = 17

component = Zinc oxide

amount = 8

component = Mount St. Helens Volcanic Ash

amount = 20

addition = Cobalt oxide

addamount = 1.5

note = |recipe Makes 1 gal. Good luck! Wendy from Bainbridge Island WA

note = |whampton@

name = Blue Yellow slip glaze

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = blue, yellow streaks?

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 60

component = Frit 5301

amount = 40

addition = Cobalt carbonate

addamount = 3

addition = Manganese dioxide

addamount = 2

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse.

note = |

name = blue-grey speckled Gloss

index =

date = 4/10/95

source =

type =

range = 6 - 8

firetype = Oxidation

color = speckled blue-grey

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 47.37

component = Potash feldspar

amount = 28.42

component = Flint

amount = 9.47

component = Zinc oxide

amount = 9.47

component = Whiting

amount = 5.26

addition = Rutile

addamount = 5.26

note = |Rob Wadey (robert wadey ) 9734B - 100 Ave Grande Prairie, Alberta t8V

note = |0T6 Phone: (403) 538-3731 Fax: (403) 538.3732

name = Bob Wicks Base

index =

date = 3/26/96

source =

type =

range = 6

firetype = oxidation

color = see comments

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 47

component = Colemanite

amount = 27

component = EPK

amount = 6

component = Silica

amount = 20

note = |I have a simplecone 6 base glaze that exhibits some very fine

note = |qualities. Then I add the following coloring agents in given

note = |percentages. Zircopax 12% makes the base glaze white Copper Carbonate

note = |makes a nice green I suggest you use both of these together and it

note = |will give you a nice gloss irredecent green in an oxidation fire.

note = |submitted by: Bob Wicks e-mail: BobWicks@

note = |

name = BQ Matt

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 10.87

component = Wollastonite

amount = 18.12

component = Nepheline syenite

amount = 36.23

component = EPK

amount = 18.12

component = Gerstley borate

amount = 16.67

note = |add 5% zircopax and 8% mason st. 6485 for a light, delicate yellow. I

note = |use a fairly dark clay body so your results may be quite different.

note = |good luck with the yellows. submitted by: Mary Kuilema e-mail:

note = |kuil@k2.

note = |

name = Bright Pink

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = mauve

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 43.33

component = Whiting

amount = 20

component = Lithium carbonate

amount = 16.67

component = Barium carbonate

amount = 5

component = Gerstley borate

amount = 8.33

component = Silica

amount = 6.67

addition = Tin oxide

addamount = 8.33

addition = Chrome oxide

addamount = 0.42

note = |Semi matt mauve, nice. From Brian Kemp, (kempb@nievax.nie.ac.sg) via

note = |Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired

note = |at 100 degrees per hour to 600 degrees, then free for all to cone

note = |6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp, Nanyang Technological University, Block B,

note = |Room 216, 469 Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

note = |

name = Brilliant Matt Purple

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = purple

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 20.43

component = Silica

amount = 10.75

component = Barium carbonate

amount = 43.01

component = Lithium carbonate

amount = 5.38

component = Kaolin

amount = 20.43

addition = Copper carbonate

addamount = 7.53

note = |Whoever was looking for a Turquoise Glaze. I have 2 recipes for

note = |glazes a pottery teacher gave me. We call them Brilliant Matt Purple

note = |and Brilliant Matt Turquoise. They are volatile so be very careful

note = |with your kiln shelves. There is Barium Carbonate in the recipes, so

note = |they are poisonous whilst in the raw state. Please wear masks and

note = |gloves and if possible work at an extractor fan. I just put a normal

note = |fan pointing out the window and work behind it. I hear from

note = |production potters that Barium can leach thru your skin. Be careful

note = |and practise Good Safety Habits. As you can see they both use the

note = |same ingredients, but in different proportions. I have a friend /

note = |customer (they usually become friends) who is a production potter

note = |(with a 200 cubic foot parafin fired kiln), who uses the BMT and is

note = |delighted with it. He fires to cone 6 (1200/1220 C)You have to watch

note = |your application thickness to get the result you want. We have fired

note = |the BMP from 950 C to almost 1300 C with different results but always

note = |pleasantly surprised. Do not expect consistancy with these glazes.

note = |submitted by: Ralph Loewenthal e-mail: fayralph@sprintlink.co.za

note = |

name = Brilliant Matt Turquoise

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = turquoise

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 57.29

component = Silica

amount = 7.29

component = Barium carbonate

amount = 27.08

component = Lithium carbonate

amount = 2.08

component = Kaolin

amount = 6.25

addition = Copper carbonate

addamount = 4.17

note = |Firing: firing type: oxidation, reduction Whoever was looking for a

note = |Turquoise Glaze. I have 2 recipes for glazes a pottery teacher gave

note = |me. We call them Brilliant Matt Purple and Brilliant Matt Turquoise.

note = |They are volatile so be very careful with your kiln shelves. There is

note = |Barium Carbonate in the recipes, so they are poisonous whilst in the

note = |raw state. Please wear masks and gloves and if possible work at an

note = |extractor fan. I just put a normal fan pointing out the window and

note = |work behind it. I hear from production potters that Barium can leach

note = |thru your skin. Be careful and practise Good Safety Habits. As you

note = |can see they both use the same ingredients, but in different

note = |proportions. I have a friend / customer (they usually become friends)

note = |who is a production potter (with a 200 cubic foot parafin fired

note = |kiln), who uses the BMT and is delighted with it. He fires to cone 6

note = |(1200/1220 C)You have to watch your application thickness to get the

note = |result you want. We have fired the BMP from 950 C to almost 1300 C

note = |with different results but always pleasantly surprised. Do not expect

note = |consistancy with these glazes. submitted by: Ralph Loewenthal e-mail:

note = |fayralph@sprintlink.co.za

note = |

name = Broken gloss/matt broken dark browns

index =

date = 4/10/95

source =

type =

range = 5

firetype =

color = dark brown

vistexture =

quality = gloss to matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barnard slip

amount = 60

component = Whiting

amount = 20

component = Gerstley borate

amount = 20

note = |Rob Wadey (robert wadey ) 9734B - 100 Ave

note = |Grande Prairie, Alberta t8V 0T6 Phone: (403) 538-3731 Fax: (403)

note = |538.3732

note = |

name = Bronze Aqua Lana Wilson

index =

date = 12/26/2006

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Strontium carbonate

amount = 50

component = Nepheline syenite

amount = 50

component = Gerstley borate

amount = 2.5

addition = Bentonite

addamount = 3

addition = Copper carbonate

addamount = 4

note = |Thin application = aqua, thick = bronze. Runs if thick, so make thin

note = |toward bottom. For a better bronze, apply over a thin application of

note = |Lichen Bell's glaze.

note = |

name = Bronze Aqua Lana Wilson

index =

date = 12/26/2006

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Strontium carbonate

amount = 50

component = Nepheline syenite

amount = 50

component = Gerstley borate

amount = 2.5

addition = Bentonite

addamount = 3

addition = Copper carbonate

addamount = 4

note = |Thin application = aqua, thick = bronze. Runs if thick, so make thin toward bottom. For a better bronze, apply over a thin application of Lichen Bell's glaze.

name = Bronze cone 2-6

index =

date = 03/02/00

source =

type = Metallic

range = 2-6

firetype = Oxidation

color = bronze metallic

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Manganese dioxide

amount = 60

component = Copper oxide

amount = 10

component = Redart

amount = 20

component = EPK

amount = 10

note = |NOT FOOD SAFE!!!

note = |This was very bronze looking. I was amazed. But it is not for food

note = |containers. I believe you mentioned that you wanted it for tiles?

note = |>

note = |> Celia in NC

note = |> cwike@

note = |>Nottingham center for the Arts

name = Bronze Metallic Gold Luster

index =

date = 05/19/2002

source =

type = Metallic

range = 6

firetype = Oxidation

color = bronze metallic

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = China clay

amount = 100

addition = Cobalt oxide

addamount = 33

addition = Copper oxide

addamount = 33

addition = Manganese dioxide

addamount = 266

note = |Soft black-gold color. From Glazes Cone 6 by Michael Bailey. NOT food safe.

name = Bronze Ogden

index =

date = 12/6/96

source =

type = Metallic

range = 6

firetype = Oxidation

color = bronze metallic

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Red clay

amount = 66.67

component = China clay

amount = 33.33

addition = Manganese dioxide

addamount = 200

addition = Black copper oxide

addamount = 33.33

note = |(fire to cone 7 in sitter) I use Redart and EPK. Note: A thick coat

note = |yields best results. rafael molina-rodriguez re:

note = |blistering of this type of glazes - I've had the same problem when

note = |firing this type of glaze on the bottom of an ancient Paragon

note = |High-fire kiln ( square, top-loading ). This kiln has approximately

note = |one cone differential from top to bottom. I solved the problem of

note = |already fired pieces by refiring them in a hotter zone of the kiln.

note = |The blisters disappearred. Now I place all bronze glazed pieces at or

note = |near the top.

name = Bronze Sandy

index =

date = 12/6/96

source =

type = Metallic

range = 6

firetype = Oxidation

color = Bronze metallic

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ball clay

amount = 100

addition = Manganese dioxide

addamount = 400

addition = Copper carbonate

addamount = 100

note = |(fire to cone 7 in sitter) Note: Thin application for best color.

note = |rafael molina-rodriguez re: blistering of this type of glazes - I've

note = |had the same problem when firing this type of glaze on the bottom of

note = |an ancient Paragon High-fire kiln ( square, top-loading ). This kiln

note = |has approximately one cone differential from top to bottom. I solved

note = |the problem of already fired pieces by refiring them in a hotter zone

note = |of the kiln. The blisters disappearred. Now I place all bronze glazed

note = |pieces at or near the top.

name = BROWN BUTTER

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = dark brown w/ black flecks

vistexture =

quality = waxy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Volcanic ash

amount = 44.79

component = Spodumene

amount = 19.47

component = Dolomite

amount = 9.74

component = Talc

amount = 9.74

component = Ball clay

amount = 9.74

component = Borax

amount = 3.89

addition = Iron chromate

addamount = 2.63

addition = Rutile

addamount = 2.63

addition = Ilmenite

addamount = 2.63

note = |(a waxy surfaced, very regular and predictable glaze. Pleasant dark

note = |brown with black flecks. Takes overdipping with more reactive glazes

note = |very nicely - e.g. the oatmeal. The Borax means it shouldn't be left

note = |to hang around too long before being used) Here are a couple of

note = |standards from the Richmond Potters Club, and a few of my own

note = |formulation that have worked well in ^6 oxidation. They aren't

note = |revolutionary (my exciting ones have things like barium in them, or

note = |are less predictable for a classroom situation) but they have been

note = |reliable, and allow for some play. They all calculate out to well

note = |within the INSIGHT limit formulas for maturity at ^6. If anyone tests

note = |these and comes up with problems, new ideas, good variations etc.

note = |could they let me know? I'll look forward to a larger list being

note = |posted to clayart. Veronica Shelford e-mail: shelford@

note = |s-mail: P.O. Box 6-15 Thetis Island, BC V0R 2Y0 Tel: (250) 246-1509

name = Brown Matt

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = brown

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 18.35

component = Custer feldspar

amount = 51.38

component = EPK

amount = 16.51

component = Flint

amount = 5.5

component = Zinc oxide

amount = 8.26

addition = Rutile

addamount = 6.42

addition = Red iron oxide

addamount = 2.13

addition = Nickel oxide

addamount = 3.19

note = |I have recently been using a nice matt brown in cone 6 oxidation that

note = |looks nice on its own and over many other glazes. It is: Enjoy! Lori

note = |Cole Kitchener, Ontario

name = Brown Persimmon

index =

date = 4/21/95

source =

type = Iron Saturate

range = 6

firetype = reduction

color = deep brown

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Silica

amount = 37.63

component = Nepheline syenite

amount = 21.51

component = Whiting

amount = 16.13

component = EPK

amount = 13.98

component = Gerstley borate

amount = 10.75

addition = Red iron oxide

addamount = 16.13

note = |kiln type: gas very nice, deep brown with occasional lighter

note = |speckling submitted by: John Anthony e-mail: JTRAX@

name = Brown Pleasant

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = brown

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Alberta slip

amount = 62.5

component = Gerstley borate

amount = 20.83

component = Potash feldspar

amount = 8.33

component = EPK

amount = 8.33

addition = Tin oxide

addamount = 3.33

note = |This is quite a pleasant sort of mid brown glaze for ^6 oxidation How

note = |nice to be able to share something from my books, I have been so

note = |pleased with some of the recipes that I have tested from other

note = |clayart subscribers. I only wish that I could give proper credit to

note = |the originators of these but I am afraid I was amiss in recording

note = |such info. Sue on a rainy day in British Columbia - how unusual sue

note = |hutchen

name = brown Rowe

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = brown

vistexture =

quality = semi-gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Colemanite

amount = 50

component = EPK

amount = 20

component = Flint

amount = 30

addition = Manganese dioxide

addamount = 5

addition = Red iron oxide

addamount = 10

note = |Hello Anne, This is a neat brown semi-gloss for cone 6. I beleive it

note = |came from CM, June/81 page 78. It is called Rowe brown How are things

note = |in Ontario? Frank Simons fsimons@

name = Bullfrog Green

index =

date = 4/3/98

source =

type =

range = 5

firetype = oxidation

color = green

vistexture =

quality = stoney matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 47

component = Whiting

amount = 7.5

component = Barium carbonate

amount = 10.5

component = Zinc oxide

amount = 6

component = Kentucky OM #4

amount = 5

component = EPK

amount = 5

component = Flint

amount = 19

addition = Copper carbonate

addamount = 4

note = |I like a lot of green. But this ain't no Kermit green. Very stony

note = |matte with very hard surface. I suspect it was a tile glaze. Joe

note = |Zeller supplied the base, I went ape with the copper. I'm not taking

note = |responsibility for anyone using these glazes, etc. Something is

note = |probably toxic. They are examples of my research and they work out in

note = |formulation. Which is what they are examples of. So go formulate your

note = |own non-toxic glazes, if that is possible. It's probably bad for the

note = |environment too. Email me with questions as to household performance,

note = |as that may be indicative of other problems. The badly crazed

note = |surfaces are not considered to be a continous-non porous sanitary

note = |surfaces. Eric Hansen, Lawrence, Kansas wabi_sabi@

note = |

name = Burgundy

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 53

component = Silica

amount = 20

component = Whiting

amount = 15

component = Barium carbonate

amount = 6

component = EPK

amount = 6

addition = Mason Deep Crimson Stain

addamount = 10

note = |I use 4.5 of Strontium in place of Barium. I have had several request

note = |for this glaze recipe. It is a cone 6 Oxidation glaze. It is more

note = |opaque than some may want. It is satin to semi-glossy. submitted by:

note = |Cindy P Russell e-mail: crussel@tenet.edu

name = Burgundy Ozona

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = deep brick red

vistexture =

quality = stony slip or engobe

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = A.P. Green fireclay

amount = 80

component = GoldArt

amount = 20

addition = Chrome oxide

addamount = 1

addition = Iron oxide

addamount = 2

note = |I've applied them to bone dry sculptural work, bisqued them and then

note = |have rubbed stains or oxides into the recesses, sponging off, then

note = |fired again for permanence. They are quite versatile. These recipes

note = |are from Zakin's book on Electric Kiln Ceramics. Some of the clays

note = |used in the recipe are coarse and the slip should not be strined. The

note = |result will be a coarse, sandy-textured surface, not for functional

note = |pieces. They may be applied by dipping, spraying or brushing. They

note = |may be applied to greenware or bisqued ware. They may be used alone

note = |or with stains and glazes. The appearance when fired is soft and

note = |sandy. Candice Roeder

name = Bush Fake Ash

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = tan?

vistexture =

quality = runny, rivulet

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barnard clay

amount = 20

component = Ball clay

amount = 26

component = Wollastonite

amount = 30

component = Gerstley borate

amount = 24

addition = Rutile

addamount = 1

note = |A wood-fired surface is another story. I'm not sure it's possible to

note = |simulate the wood ash texture in oxidation. The best results I've

note = |achieved are from the following: These are nice sufaces, but if you

note = |want Richard Aerni-like wood ash texture again I'm not sure it's

note = |possible. Good luck! Two years ago I took a part-time job teaching

note = |ceramics at Navarro College in Corsicana, Texas. The college has only

note = |one kiln. It' an ancient Paragon High Fire. The design is square and

note = |toploading with very small cu. ft. It's been a real challenge to

note = |develop an attractive palette of clays and glazes for oxidation

note = |firing. I do majolica, colored clays, and cone 6 oxidation ( cone 7

note = |in the sitter). Rafael Molina Rmr3431@dcccd.edu

note = |

name = Butterscotch

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = butterscotch yellow

vistexture =

quality = satin matte?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 80

component = Whiting

amount = 15

component = Barium carbonate

amount = 12

component = Zinc oxide

amount = 12

component = Kaolin

amount = 10

component = Ball clay

amount = 8

component = Silica

amount = 36

addition = Rutile

addamount = 10.4

addition = Ochre

addamount = 5.2

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse.

note = |

name = BUTTERSCOTCH GLOSSY

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = orangey tinted clear

vistexture =

quality = glossy shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 29.47

component = Nepheline syenite

amount = 20

component = Flint

amount = 20

component = Gerstley borate

amount = 17.89

component = Zinc oxide

amount = 5.26

component = Whiting

amount = 4.21

component = Lithium carbonate

amount = 3.16

addition = Manganese dioxide

addamount = 3.16

addition = Red iron oxide

addamount = 2.11

addition = Zircopax

addamount = 4.21

note = |(An orangey tinted clear glaze - I like it for stone ginger bottles

note = |and other old-timey things) Here are a couple of standards from the

note = |Richmond Potters Club, and a few of my own formulation that have

note = |worked well in ^6 oxidation. They aren't revolutionary (my exciting

note = |ones have things like barium in them, or are less predictable for a

note = |classroom situation) but they have been reliable, and allow for some

note = |play. They all calculate out to well within the INSIGHT limit

note = |formulas for maturity at ^6. If anyone tests these and comes up with

note = |problems, new ideas, good variations etc. could they let me know?

note = |I'll look forward to a larger list being posted to clayart. Veronica

note = |Shelford e-mail: shelford@ s-mail: P.O. Box 6-15 Thetis

note = |Island, BC V0R 2Y0 Tel: (250) 246-1509

note = |

name = C. Gareri Base

index =

date = 7/19/95

source =

type =

range = 4 - 8

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 34.13

component = EPK

amount = 1.8

component = Gerstley borate

amount = 16.32

component = Silica

amount = 31.83

component = Whiting

amount = 3.9

component = Zinc oxide

amount = 6.11

component = Barium carbonate

amount = 5.91

addition = Bentonite

addamount = 2

note = |I have never ommitted Barium in this ^4-^8 oxidation glaze actually i

note = |have not used the glaze in years. But it is a great oxidation glaze

note = |and I considered using it next year at the school where I teach.

note = |However, the barium scared me. IF barium Carb can not be ommited is

note = |there a safe substitute? submitted by: Charles Gareri e-mail:

note = |cgareri@ideanet.doe.state.in.us

note = |

name = Calcium Alumina Transparent Matte

index =

date = 12/6/96

source =

type =

range = 5 - 6

firetype = Ox. or Red.

color = translucent clear

vistexture =

quality = transparent semi-matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wollastonite

amount = 30

component = Ferro Frit 3134

amount = 21.5

component = Kaolin

amount = 25.5

component = Calcined kaolin

amount = 19

component = Silica

amount = 4

note = |part of a series I did to produce a saturated calcia matte glaze

note = |using wollastonite instead of whiting. Note you need to split the

note = |kaolin with calcined kaolin. If you don't the glaze will shrink too

note = |much and crack during drying, then crawl during firing. You can make

note = |your own calcined kaolin by bisque firing a planter full of raw

note = |kaolin. Remember to use 12% less calcined because of the LOI. I also

note = |tried high alumina low silica and sure enough, that gives a matte

note = |too, just like the textbooks say. However the best results came with

note = |both high CaO and high Al2O3 as follows: (this is still under

note = |development) submitted by: Tony Hansen email: thansen@mlc.

note = |

name = CDG Base 1 Peach

index =

date = 07/16/00

source =

type =

range = 4

firetype = Oxidation

color =

vistexture =

quality =

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Strontium carbonate

amount = 5.182

component = Whiting

amount = 9.6

component = Zinc oxide

amount = 10.41

component = Custer feldspar

amount = 73.08

addition = Copper carbonate

addamount = 0.99

addition = Rutile

addamount = 6.02

note = |Ceramic Mo May 2000 p.101. Untested w/SrCO3. Orig is 6.91 BaCO3

name = Celadon

index =

date = 12/7/96

source =

type =

range = 6

firetype = Reduction

color = translucent green

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow = Moderate

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Colemanite

amount = 61.22

component = EPK

amount = 8.16

component = Whiting

amount = 2.04

component = Silica

amount = 28.57

addition = Red iron oxide

addamount = 2.04

addition = Bentonite

addamount = 2.04

note = |Here is a CEladon, works well a bit runny though. from omer artun

note = |

name = Celadon 974 Kawai

index =

date = 3/26/96

source =

type = Celadon

range = 6 - 8

firetype = Reduction

color = Green

vistexture =

quality = shiny glossy

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 62.24

component = Whiting

amount = 7.61

component = China clay

amount = 4.97

component = Silica

amount = 25.18

addition = Black iron oxide

addamount = 1.52

note = |Original recipe called for limestone, substituted whiting, although

note = |using dolomite might be better. Add 2% Barium Carbonate for bluish

note = |celadon. Also can substitute red iron oxide for the black to get a

note = |yellow green celadon. submitted by: GURUSHAKTI@

name = Celadon 974 Kawai

index =

date = 3/26/96

source =

type = Mid-fire

range = 6 - 8

firetype = reduction

color = Green

vistexture =

quality = Gloss

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 62.24

component = Whiting

amount = 7.61

component = China clay

amount = 4.97

component = Silica

amount = 25.18

addition = Black iron oxide

addamount = 1.52

note = |Original recipe called for limestone, substituted whiting, although

note = |using dolomite might be better. Add 2% Barium Carbonate for bluish

note = |celadon. Also can substitute red iron oxide for the black to get a

note = |yellow green celadon. submitted by: GURUSHAKTI@

name = Celadon Blue

index =

date = 4/21/95

source =

type = Mid-fire

range = 6

firetype = reduction

color = celadon Blue

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Volcanic ash

amount = 48.7

component = Wollastonite

amount = 12.17

component = Ball clay

amount = 10.43

component = Gerstley borate

amount = 8.7

component = Silica

amount = 6.96

component = Alberta slip

amount = 13.04

addition = Cobalt carbonate

addamount = 0.22

note = |kiln type: gas goes a little gray over stoneware, nicely translucent

note = |on procelain. submitted by: John Anthony e-mail: JTRAX@

name = Celadon Faux

index =

date = 6/3/96

source =

type =

range = 6

firetype = Oxidation

color = Green

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 50

component = Wollastonite

amount = 20

component = China clay

amount = 10

component = Silica

amount = 10

component = Gerstley borate

amount = 10

addition = Copper carbonate

addamount = 0.5

addition = Black Stain

addamount = 0.2

note = |I've been using a Cone 6-9 oxidation Faux Celadon glaze on porcelain

note = |(Standard Ceramics). It looks quite a bit like a real celadon except

note = |a bit darker. It was fine until about a year ago when I started

note = |getting pinholes AND there would be a slight crawling in some places

note = |on the pot. The pot needed to be refired each time, then the crawling

note = |healed. I tried applying the glaze more thinly, but that didn't

note = |matter, I still got the strange bald spots. Thinking it might be oil

note = |or dirt on the surface, I went over each surface with a dry Scrubbie,

note = |then wiped them down with a damp sponge. I still had bald spots.

note = |Pinholes appeared on the bottom of the pots. (My pots have carved

note = |feet which raise the bottoms of the pots and the bottoms get glazed.)

note = |For a while I thought it was just me, but a colleague of mine used

note = |the same batch of glaze and had the same problem. I work in a

note = |cooperative studio and don't mix my own glazes, or do my own firing,

note = |but the firing schedules haven't changed since I've been working

note = |there (about 5 years). Help! I have developed a line of pots with

note = |this glaze that sell pretty well. submitted by: Sandy e-mail:

note = |SANDRA@ICICB.NCI.

name = Celadon Faux

index =

date = 6/3/96

source =

type = Mid-fire

range = 6

firetype = oxidation

color = Green

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 50

component = Wollastonite

amount = 20

component = China clay

amount = 10

component = Silica

amount = 10

component = Gerstley borate

amount = 10

addition = Copper carbonate

addamount = 0.5

addition = Black Stain

addamount = 0.2

note = |I've been using a Cone 6-9 oxidation Faux Celadon glaze on porcelain

note = |(Standard Ceramics). It looks quite a bit like a real celadon except

note = |a bit darker. It was fine until about a year ago when I started

note = |getting pinholes AND there would be a slight crawling in some places

note = |on the pot. The pot needed to be refired each time, then the crawling

note = |healed. I tried applying the glaze more thinly, but that didn't

note = |matter, I still got the strange bald spots. Thinking it might be oil

note = |or dirt on the surface, I went over each surface with a dry Scrubbie,

note = |then wiped them down with a damp sponge. I still had bald spots.

note = |Pinholes appeared on the bottom of the pots. (My pots have carved

note = |feet which raise the bottoms of the pots and the bottoms get glazed.)

note = |For a while I thought it was just me, but a colleague of mine used

note = |the same batch of glaze and had the same problem. submitted by: Sandy e-mail:

note = |SANDRA@ICICB.NCI.

name = Celadon Glossy

index =

date = 12/7/96

source =

type =

range = 6

firetype = Reduction

color = Green

vistexture =

quality = Gloss

transparency = Translucent

xtals =

bubbles =

flow = Moderate

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Colemanite

amount = 61.22

component = EPK

amount = 8.16

component = Whiting

amount = 2.04

component = Silica

amount = 28.57

addition = Red iron oxide

addamount = 2.04

addition = Bentonite

addamount = 2.04

note = |Here is a CEladon, works well a bit runny though. from omer artun

note = |

name = Celadon Kawaii Revised

index =

date = 11/15/98

source =

type = Celadon

range = 5 - 6

firetype = Reduction

color = Blue

vistexture =

quality = Satin

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline Sye

amount = 4357

component = Whiting

amount = 792

component = EPK

amount = 475

component = Flint

amount = 1822

component = Talc

amount = 554

note = |Lovely. Crazes. Very high alkaline glaze. This is the original

note = |Kawaii Celadon formula and revising to Cone 6. There is no Talc in

note = |the original glaze. Glaze Type: Ca Na Mg Celadon. Opacity: . Firing

note = |type: Reduction .

name = Celadon to Teal

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Wollastonite

amount = 8

component = Nepheline syenite

amount = 30

component = Kaolin

amount = 10

component = Silica

amount = 31

note = |for celadon add cobalt carbonate 0.125% and chrome oxide 0.125%, for

note = |teal blue add cobalt carbonate 0.5% and chrome oxide 0.3%, for teal

note = |green add cobalt carbonate 0.5% and chrome oxide 0.5%. submitted by:

note = |Iain Begg e-mail: begg@MPRGATE.MPR.CA

note = |

name = Celedon Satin

index =

date = 10/06/2002

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 46.3

component = Flint

amount = 19.7

component = EPK

amount = 2.4

component = Whiting

amount = 8.2

component = Gerstley borate

amount = 13.6

component = Zinc oxide

amount = 3.9

component = Dolomite

amount = 5.9

var = |Copper Carb .28 Nice faux blue celedon glaze. Pretty shiny.

var = |Rich plum- 9 Red Degusa stain

var = | .25 Cobalt Carb.

var = |Shiny red- 9 Red Degusa stain

name = Chappel Boron Lithium

index =

date = 7/19/95

source =

type =

range = 6

firetype =

color = green

vistexture =

quality = glassy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 51

component = Gerstley borate

amount = 26

component = Silica

amount = 23

addition = Copper carbonate

addamount = 5

addition = Red iron oxide

addamount = 0.5

addition = Bentonite

addamount = 1

note = |I was looking for something like Warren MacKenzie's Glassy Green that

note = |would fire at ^6 instead of ^4. The Boron Lithium in Chappel's glaze

note = |book looked close so I added the same oxides as MacKenzie uses in his

note = |^4. MacKenzie doesn't use his ^4 anymore, but found a ^1 glassy green

note = |he uses instead. This is also a nice transparent ^6 without

note = |colorants. submitted by: Lee Love e-mail: leelove@mill2.

note = |

name = Charcoal

index =

date = 12/7/96

source =

type =

range = 5 - 6

firetype = oxidation

color = greenish charcoal gray

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Lithium carbonate

amount = 1

component = Strontium carbonate

amount = 20

component = Nepheline syenite

amount = 60

component = OM-4 Ball Clay

amount = 10

component = Flint,325 mesh

amount = 9

addition = Manganese dioxide

addamount = 2

addition = Copper carbonate

addamount = 5

note = |For my black I added these colorants, rather than those above:

note = |Chrome.......1.14 Cobalt Carb 4.55 Red Iron Ox..3.41 I am having a

note = |problem with a glaze. It is a cone 6 oxidation glaze, charcoal

note = |variation of Pinnell Strontium Matt Glaze. I am trying to achieve a

note = |(cobalt)bla variation, rather than the greenish black that the

note = |Charcoal version produces. I took colorants from a favorite black

note = |glaze recipe and used those percentages i Strontium Matt base. The

note = |results were black, but very dry and underfired lookin fire this

note = |glaze to cone 7, BTW) Could the colorants I added have a refractory

note = |effect, and if so, how do I correc problem? Any ideas? I'd appreciate

note = |help on this one. Thanks. Candice Roeder croeder@worldnet.

note = |living in the sticks in Michigan

note = |

name = Chartreuse Elyse's Matt

index =

date = 03/06/01

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Chartreuse

vistexture =

quality = Matt

transparency = Semi-opaque

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 3

component = Magnesium carb

amount = 3

component = Whiting

amount = 22

component = Nepheline syenite

amount = 23

component = Kaolin

amount = 20

component = Flint

amount = 29

var = |Chartreuse: 8% Drakenfield yellow (bright yellow stain)

var = | + 0.5% copper carb

var = |Deep Plum: + 10% Standard Ceramics Orchid stain

var = |Deep Purple-blue: + 8% Royal purple (Standard Ceramics).

note = |From Elyse Burja. Based on Dixon Satin.

name = Chartreuse Matt Elyse's

index =

date = 03/22/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Chartreuse

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 3

component = Magnesium carbonate

amount = 3

component = Whiting

amount = 22

component = Nepheline syenite

amount = 23

component = Kaolin

amount = 20

component = Flint

amount = 29

var = |Chartreuse: 8% Drakenfield yellow (bright yellow stain) + 0.5% copper carb

var = |Deep Plum: + 10% Standard Ceramics Orchid stain

var = |Deep Purple-blue: + 8% Royal purple (Standard Ceramics).

note = |From Elyse Burja

name = Chartreuse Matt Elyse's no GB

index =

date = 03/22/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Chartreuse

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Talc

amount = 5

component = Whiting

amount = 21

component = Custer feldspar

amount = 28

component = Kaolin - theoretical

amount = 18

component = Silica

amount = 18

component = Frit 3124

amount = 10

component = Bone ash

amount = 0.1

component = Rutile

amount = 0.08

component = Iron oxide

amount = 0.1

var = |Chartreuse: 8% Drakenfield yellow (bright yellow stain) + 0.5% copper carb

var = |Deep Plum: + 10% Standard Ceramics Orchid stain

var = |Deep Purple-blue: + 8% Royal purple (Standard Ceramics).

note = |From Elyse Burja

name = Chartreuse Matt Elyse's no GB

index =

date = 03/22/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = chartreuse

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 6.629

component = Whiting

amount = 19.134

component = Nepheline syenite

amount = 23.006

component = Kaolin - theoretical

amount = 16.738

component = Silica

amount = 28.782

component = Frit 3195

amount = 5.711

var = |Chartreuse: 8% Drakenfield yellow (bright yellow stain) + 0.5% copper carb

var = |Deep Plum: + 10% Standard Ceramics Orchid stain

var = |Deep Purple-blue: + 8% Royal purple (Standard Ceramics).

note = |From Elyse Burja

name = Chocolate Super-Hiway

index =

date = 4/3/98

source =

type =

range = 6 - 8

firetype = oxidation

color = brown

vistexture =

quality = textured (w/added clay)

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 50.72

component = Gerstley borate

amount = 24.64

component = Barium carbonate

amount = 17.39

component = Zinc oxide

amount = 7.25

note = |plus as much local dark red clay as I can get into it. Then I layer

note = |over it with the same glaze without the clay. This gets a highly

note = |pitted chocolate cake look with a cratered & pinholed glossy surface.

note = |I don't like any of the above glazes inside a bowl. I kinda like more

note = |of a feldspathic glaze for eating/drinking surface. I'm not taking

note = |responsibility for anyone using these glazes, etc. Something is

note = |probably toxic. They are examples of my research and they work out in

note = |formulation. Which is what they are examples of. So go formulate your

note = |own non-toxic glazes, if that is possible. It's probably bad for the

note = |environment too. Email me with questions as to household performance,

note = |as that may be indicative of other problems. The badly crazed

note = |surfaces are not considered to be a continous-non porous sanitary

note = |surfaces. Eric Hansen, Lawrence, Kansas wabi_sabi@

name = Cindy's Blue

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color = deep blue

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 20

component = Whiting

amount = 20

component = EPK

amount = 20

component = Silica

amount = 20

component = Ferro frit 3124

amount = 20

addition = Bentonite

addamount = 2

addition = Cobalt carbonate

addamount = 5

note = |I'm just now getting around to the cone 6 oxidation cobalt blue glaze

note = |that several of you ask for. It is a nice, dark cobalt blue--Satin to

note = |glossy. I have to soak on medium for about 2 hrs. after the kiln

note = |sitter goes off to get it to smooth out. submitted by: Cindy P

note = |Russell e-mail: crussel@tenet.edu

note = |

name = Clay Black VC

index =

date = 06/27/2003

source =

type = Clay

range = 5-6

firetype = Ox. or Red.

color = Black

vistexture =

quality = Unglazed

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ocmulgee

amount = 50

component = Pine Lake

amount = 15

component = GoldArt

amount = 15

component = Ball clay

amount = 10

component = Barnard clay

amount = 10

component = Grog

amount = 6

addition = Red iron oxide

addamount = 3

name = Clay Casting Slip

index =

date = 10/17/2003

source =

type = Clay (casting slip)

range = 6

firetype = Ox. or Red.

color = Tan

vistexture =

quality = unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 4000

component = GoldArt

amount = 3000

component = Redart

amount = 1000

component = Kaolin

amount = 5800

component = Ball clay

amount = 3000

component = Flint

amount = 3200

addition = Darvan 7

addamount = 140

note = |Add 10,000 water. for easy weighing of Darvan add to last 500 gms of water.

note = |

note = |From Colleen

note = |colleens@

name = Clay casting Wally's wonderslip

index =

date = 07/24/2003

source =

type = Clay casting

range = 5-9

firetype = Ox. or Red.

color = White

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = GoldArt

amount = 21

component = Tennessee ball clay

amount = 10

component = EPK

amount = 12

component = Custer feldspar

amount = 26

component = Whiting

amount = 1

component = Flint

amount = 30

note = |Add 199 ml sodium silicate + 199 ml Darvan and 41.7 lbs water

name = Clay Casting White Rozman

index =

date = 06/02/2004

source =

type = Clay casting

range = 2-4

firetype = Oxidation

color = White

vistexture =

quality =

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Talc

amount = 5

component = Nepheline syenite

amount = 30

component = EPK

amount = 23

component = Kentucky OM #4

amount = 22

component = Flint

amount = 20

addition = Barium carbonate

addamount = 0.03

addition = Soda ash

addamount = 0.03

addition = Sodium silicate

addamount = 0.25

note = |Start 38% water, then add more if required. From Paul Rozman in CM.

name = Clay Don's Porcellaneous

index =

date = 01/27/2003

source =

type = Clay (Porcelain)

range = 5-7

firetype = Ox. or Red.

color = White

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Tennessee ball clay

amount = 22

component = Tile 6 clay

amount = 10

component = EPK

amount = 10

component = Nepheline syenite

amount = 33

component = G-200 feldspar

amount = 9

component = Silica

amount = 9

var = |add 2% V-gum T

note = |From Don Davis

name = Clay for outdoor use from Ted Randall

index =

date = 08/23/2007

source =

type = Clay

range = 6

firetype =

color = Brown

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = PBX

amount = 20

component = Pine Lake

amount = 10

component = A.P. Green

amount = 15

component = Wollastonite

amount = 15

addition = Molochite

addamount = 5

addition = Grog

addamount = 25

addition = Red iron oxide

addamount = 1.5

note = |via Jamie McKinnon.It calls for Fiberous Wollastonite, not powedered. Wet to fired

note = |shrinkage 8%. Can add more grog to total of 30% in mixed particle sizes. Color cited

note = |as deep cinnamon.

name = clay Pinnell porcelain

index =

date = 01/27/2003

source =

type = Clay (Porcelain)

range = 6

firetype = Ox. or Red.

color = White

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Tennessee ball clay

amount = 25

component = Tile 6 clay

amount = 25

component = Silica

amount = 25

component = Custer feldspar

amount = 25

addition = Bentonite

addamount = 1

note = |soak bentonite in water before adding.

name = Clay Red Rozman Throwing

index =

date = 06/02/2004

source =

type = Clay

range = 2-4

firetype = Oxidation

color = Red

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wollastonite

amount = 3

component = Nepheline syenite

amount = 14

component = Ball clay

amount = 25

component = GoldArt

amount = 25

component = Redart

amount = 25

component = Flint

amount = 8

note = |From Paul Rozman in CM. Note the neph sy will deflocculate the body.

name = clay VC Off-White dense stoneware

index =

date = 01/27/2003

source =

type = Clay (Stoneware)

range = 6

firetype = Ox. or Red.

color = White

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Tile 6 clay

amount = 20

component = EPK

amount = 15

component = Kentucky OM #4

amount = 20

component = GoldArt

amount = 25

component = Nepheline syenite

amount = 10

component = Flint

amount = 10

addition = Bentonite

addamount = 2

name = Clay VC Orange-Brown Throwing

index =

date = 06/27/2003

source =

type = Clay

range = 5-6

firetype = Ox. or Red.

color = Brown-orange

vistexture =

quality = Lichen

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = GoldArt

amount = 30

component = Pine Lake

amount = 30

component = Ocmulgee

amount = 40

name = Clay Warm Brown RISD 96

index =

date = 10/17/2003

source =

type = Clay (Stoneware)

range = 6

firetype = Oxidation

color = brown

vistexture =

quality = unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ocmulgee

amount = 15

component = GoldArt

amount = 14

component = Redart

amount = 14

component = XX Sagger

amount = 13

component = Flint

amount = 12

component = Kentucky OM #4

amount = 11

component = Custer feldspar

amount = 11

component = Tile 6 clay

amount = 10

addition = Bentonite

addamount = 3

var = |+ handful Epsom salts

note = |Warm brown, good thermal shock resistance, good for throwing and handbuilding.

note = |Revised by Larry Bush.

name = Clay White Casting c6

index =

date = 02/16/99

source =

type = Casting slip

range = 5-6

firetype = Oxidation

color = White

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Nepheline syenite

amount = 12.5

component = Custer feldspar

amount = 25

component = Flint

amount = 17.5

component = EPK

amount = 20

component = Kentucky OM #4

amount = 25

note = |Adapted from M Corney's cone 10 casting slip.

note = |10,000 gm batch:

note = |3,500 water, 10 gms soda ash, 58 gms sodium silicate.

name = Clay White Plastic VC

index =

date = 06/27/2003

source =

type = Clay

range = 5-6

firetype = Ox. or Red.

color = White

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Tile 6 clay

amount = 20

component = EPK

amount = 10

component = XX Sagger

amount = 20

component = Kentucky ball clay

amount = 10

component = Kona F-4 feldspar

amount = 20

component = Flint

amount = 20

addition = Bentonite

addamount = 2

addition = Macaloid

addamount = 1

note = |NOt translucent. Throws like porcelain.

name = Clay White Throwing

index =

date = 06/27/2003

source =

type = Clay (Stoneware)

range = 5-6

firetype = Reduction

color = White

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Grolleg

amount = 50

component = Kona F-4 feldspar

amount = 25

component = Pyrax

amount = 13

component = Flint

amount = 12

addition = Bentonite

addamount = 2

addition = Macaloid

addamount = 2

name = Clay: Revised Steve's White

index =

date = 03/06/01

source =

type = Clay (Mid-Range)

range = 5-6

firetype = Ox. or Red.

color = White

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = EPK

amount = 20

component = Tile 6 clay

amount = 20

component = GoldArt

amount = 14

component = XX Sagger

amount = 10

component = A.P. Green

amount = 10

component = Custer feldspar

amount = 14

component = Talc

amount = 3

component = Flint

amount = 10

addition = Bentonite

addamount = 3

name = Clear

index =

date = 4/21/95

source =

type =

range = 6

firetype = reduction

color = clear in oxidation, greyish in

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Silica

amount = 31

component = Nepheline syenite

amount = 30

component = Gerstley borate

amount = 21

component = EPK

amount = 10

component = Wollastonite

amount = 8

note = |kiln type: gas Color: clear in oxidation, greyish in reduction

note = |submitted by: John Anthony e-mail: JTRAX@

note = |

name = Clear

index =

date = 6/3/96

source =

type =

range = 4 - 8

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Wollastonite

amount = 8

component = Nepheline syenite

amount = 30

component = Kaolin

amount = 10

component = Silica

amount = 31

note = |I've been using this on underglaze decorated porcelain though

note = |recommendations stated that it fits most stoneware bodies. It gives a

note = |nice smooth clear finish. There has been some minor crazing on ^10

note = |porcelain fired to ^6, but little to no problems on ^6 porcelain fire

note = |to ^6, for obvious reasons of clay maturity. I'm also curious whether

note = |it scratches easily. submitted by: Carol Durnford e-mail:

note = |durnford@selway.umt.edu source for original recipe: Ceramics Monthly

note = |

name = Clear

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = clear in oxidation, greyish in

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Silica

amount = 31

component = Nepheline syenite

amount = 30

component = Gerstley borate

amount = 21

component = EPK

amount = 10

component = Wollastonite

amount = 8

note = |kiln type: gas Color: clear in oxidation, greyish in reduction

note = |submitted by: John Anthony e-mail: JTRAX@

note = |

name = Clear (Huddleston)

index =

date = 12/6/96

source =

type =

range = 5 - 6

firetype = oxidation

color = transparent clear

vistexture =

quality = glossy, shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro Frit 3134

amount = 50

component = EPK

amount = 30

component = Silica

amount = 20

note = |It didn't craze but the colors were not quite as bright as others but

note = |it is a nice glaze and subing Ferro frit 3124, I found a nice clear

note = |matt. I hope these help. They're all I could find. Joyce Basking in

note = |the sun in the Mojave joyce lee, jim lee

note = |

name = Clear (Ian Begg)

index =

date = 12/6/96

source =

type =

range = 5 - 6

firetype =

color =

vistexture =

quality = glossy, shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Flint

amount = 26

component = Kona F-4 spar

amount = 32

component = Wollastonite

amount = 6

component = Kentucky OM #4

amount = 10

component = Pemco frit P-54

amount = 16

component = Whiting

amount = 10

note = |In response to questions about cone 5-6 clear glazes crazing over

note = |underglazes...I am ever tweaking this recipe, which is coming closer

note = |to a no-craze, nice soft surface on Hagi porcelain. It is still not

note = |perfect with the tiniest evidence of crazing where thick, and I'll

note = |continue to work with it, suggestions welcome. In the meantime,

note = |Laguna's MS-29 crazes NOT, but its limitations aside from cost and

note = |unknown recipe is in developing a rich color pallette. Curt

note = |Huddleston joyce lee, jim lee

name = Clear 184 Gloss Bowes

index =

date = 11/15/98

source =

type = Mid-fire

range = 5

firetype = Oxidation

color = Transparent Clear

vistexture =

quality = Glossy or shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = F-4 feldspar

amount = 45.5

component = Flint

amount = 20

component = Gerstley borate

amount = 13.3

component = Whiting

amount = 8.3

component = Dolomite

amount = 6.4

component = Zinc oxide

amount = 4

component = EPK

amount = 2.5

note = |Good with stains & oxides except pinks and purples. Apply 2 coats if

note = |brushed for colors, 1 for clear. Use gum if brushing (e.g. Amaco

note = |pre-mix). From George Bowes.

name = Clear 184 Gloss Bowes NO GB

index =

date = 11/15/98

source =

type = Mid-fire

range = 5

firetype = Oxidation

color = Transparent Clear

vistexture =

quality = Glossy or shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 28.2

component = Silica

amount = 15.1

component = Dolomite

amount = 8.3

component = Whiting

amount = 5.5

component = Zinc oxide

amount = 3.9

component = Tile 6 clay

amount = 13

component = Frit 3134

amount = 25.9

var = |Light green- 5 drakenfield yellow, 4 rutile, 1 copper carb

note = |Good with stains & oxides except pinks and purples. Apply 2 coats if

note = |brushed for colors, 1 for clear. Use gum if brushing (e.g. Amaco

note = |pre-mix). From George Bowes.

name = Clear 184 Gloss Bowes NO GB No Crazing

index =

date = 11/15/98

source =

type = Mid-fire

range = 5

firetype = Oxidation

color = Transparent Clear

vistexture =

quality = Glossy or shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 39

component = Dolomite

amount = 12

component = Whiting

amount = 8

component = Zinc oxide

amount = 5

component = Frit 3134

amount = 36

component = Flint

amount = 3

component = Lithium carbonate

amount = 1

note = |Good with stains & oxides except pinks and purples. Apply 2 coats if

note = |brushed for colors, 1 for clear. Use gum if brushing (e.g. Amaco

note = |pre-mix). From George Bowes.

note = |

note = |Catherine Boswell test to eliminate crazing.

name = clear 3 part

index =

date = 4/3/98

source =

type =

range = 5 - 6

firetype = oxidation

color = Clear

vistexture =

quality = glossy

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = EPK

amount = 15

component = Flint

amount = 35

var = |.5% cobalt makes a nice transparent blue.

note = |Nice clear, when applied thicker it gets milky. sue hintz

name = Clear 5-6

index =

date = 12/6/96

source =

type = Mid-fire

range = 5 - 6

firetype = Ox. or Red.

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = F-4 spar

amount = 40

component = Gerstley borate

amount = 30

component = Ball clay

amount = 20

component = Silica

amount = 10

note = |Boy, do I have a fabulous clear glaze for you!! This glaze is

note = |incredibly forgiving - doesn't show drips, overdips, differences in

note = |thickness, is glassy clear w/o yellow, and doesn't craze.

note = |It only has 4 ingredients, too. I use this over slips and underglazes

note = |and it's fine. I also use lusters over it with great results.

note = |What can I say? This is THE PERFECT clear glaze. Laura in Oregon

note = |(robert speirs, m.d. 766 x4450 )

name = clear absolutely

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color = clear, transparent

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 40

component = Gerstley borate

amount = 30

component = Kentucky OM #4

amount = 20

component = Flint

amount = 10

note = |Results beautiful except my blue (cobalt) slip went black under this

note = |clear. Slip applied to leather-hard piece, bisqued, then dipped in

note = |clear. Anybody with an answer to whats happening? Is the iron in the

note = |OM-4 ball clay joining the cobalt to make black? Am I the guest

note = |recipient of a voodoo curse? What are all those cows chewing on when

note = |they're just laying around? I hate to have to abandon this glaze

note = |because, like me, its so cheap and simple. Dale McCleskey, Nashville,

note = |TN, USA, Confused.

name = Clear Base

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color = Transparent Clear

vistexture =

quality = shiny glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 20

component = Wollastonite

amount = 10

component = Nepheline syenite

amount = 30

component = EPK

amount = 10

component = Silica (325m)

amount = 30

note = |For 2 years I struggled with this concept & finally gave up. The fuel

note = |savings (?) were not worth the effort. The results don't compare to

note = |^10. I agree with Peter Pinnell- sell another mug to pay for the

note = |difference in firing costs. add- 10% iron for temmoku or- 2% tin

note = |oxide & 1% copper carb. for red Due to the lower sintering point of

note = |^6 glazes- you have to start reduction fairly early- at least by

note = |stoneware standards. Try ^010 as a starting point & go from there. I

note = |also used a clay body that had a higher iron content than my present

note = |^10 body- it seemed to make a difference. submitted by: Tom Gray

note = |e-mail: tgraypots@

note = |

name = Clear Base (Cone 5-10)

index =

date = 8/8/97

source =

type =

range = 5 - 10

firetype = Oxidation

color = clear transparent

vistexture =

quality = glossy

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = Kaolin

amount = 17.5

component = Flint

amount = 32.5

note = |works well over over slips Joan Slack-DeBrock/River Run Pottery

note = |P.O.Box 95 McNaughton, WI 54543 715-277-2773 riverrun@

name = Clear Base Bob Wicks

index =

date = 3/26/96

source =

type =

range = 6

firetype = oxidation

color = Clear

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 47

component = Colemanite

amount = 27

component = EPK

amount = 6

component = Silica

amount = 20

var = |Zircopax 12% makes the base glaze white Copper Carbonate

var = |makes a nice green I suggest you use both of these together and it

var = |will give you a nice gloss irredecent green in an oxidation fire.

note = |I have a simple cone 6 base glaze that exhibits some very fine

note = |qualities.

note = |submitted by: Bob Wicks e-mail: BobWicks@

name = Clear Buttery Grandey

index =

date = 07/16/00

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Waxy

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = F-4 spar

amount = 50

component = Dolomite

amount = 15.5

component = Magnesium carb

amount = 6.8

component = EPK

amount = 15

component = Flint

amount = 9.3

component = Frit 3124

amount = 3.5

addition = Tin oxide

addamount = 3.5

note = |From Katherine Grandey @ Univ of FL

name = Clear Dinah's

index =

date = 12/6/96

source =

type = Mid-fire

range = 5

firetype = Ox. or Red.

color = Clear

vistexture =

quality = gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro frit 3292

amount = 39.9

component = Frit 3124

amount = 39.9

component = Kentucky OM #4

amount = 9.98

component = Silica

amount = 9.98

component = Magnesium carbonate

amount = 0.25

addition = Epsom salts

addamount = 0.5

var = |Add: CMC 0.25

note = |Mix to specific gravity of 1.5. I found another glaze that was

note = |developed a couple of years back by Dinah Collopy

note = |(dinah@GN2.). She wanted a clear that handled underglazes

note = |well as I recall.

note = |

note = | Iain Iain Begg

note = |begg@mpr.ca Bearsden Studio, Vancouver, BC

name = Clear Dinah's Transparent

index =

date = 12/6/96

source =

type =

range = 5

firetype = Oxidation

color = Clear

vistexture =

quality = gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro frit 3292

amount = 39.9

component = Ferro frit 3124

amount = 39.9

component = Kentucky OM #4

amount = 10

component = Silica (325m)

amount = 10

component = Magnesium carbonate

amount = 0.3

addition = CMC

addamount = 0.3

addition = Epsom salts

addamount = 0.5

note = |Mix to specific gravity of 1.5. I found another glaze that was

note = |developed a couple of years back by Dinah Collopy

note = |(dinah@GN2.). She wanted a clear that handled underglazes

note = |well as I recall. I know she did countless tests. Her comments were

note = |as follows: There were two commercial glazes that worked

note = |well--Laguna's MS29 and Ceramichrome NG 100 (the latter says it

note = |contains lead aluminum silicate but if fired over cone2 meets FDA

note = |health requirments for lead release). These commercial glazes need to

note = |be applied VERY thinly. What I will end up using is the following:

note = |Maybe that explains why the colours are so vibrant.... Iain Iain Begg

note = |begg@mpr.ca Bearsden Studio, Vancouver, BC

name = Clear Glaze

index =

date = 12/6/96

source =

type =

range = 5 - 6

firetype = Oxidation

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Minspar Soda Feldspar

amount = 40

component = Gerstley borate

amount = 30

component = Ball clay

amount = 20

component = Silica

amount = 10

note = |This glaze is incredibly forgiving - doesn't show drips, overdips,

note = |differences in thickness, is glassy clear w/o yellow, and doesn't

note = |craze. I use this over slips and underglazes and it's fine. I also use

note = |lusters over it with great results. This is THE

note = |PERFECT clear glaze. Laura in Oregon

name = Clear Glaze

index =

date = 12/6/96

source =

type =

range = 5 - 6

firetype = Oxidation

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Minspar Soda Feldspar

amount = 40

component = Gerstley borate

amount = 30

component = Ball clay

amount = 20

component = Silica

amount = 10

note = |This glaze is incredibly forgiving - doesn't show drips, overdips,

note = |differences in thickness, is glassy clear w/o yellow, and doesn't

note = |craze. I use this over slips and underglazes and it's fine. I also use

note = |lusters over it with great results. This is THE

note = |PERFECT clear glaze. Laura in Oregon

name = Clear Glaze 5-6

index =

date = 12/6/96

source =

type =

range = 5 - 6

firetype =

color = clear transparent

vistexture =

quality = glossy, shiny

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Minspar Soda Feldspar

amount = 40

component = Gerstley borate

amount = 30

component = Ball clay

amount = 20

component = Silica

amount = 10

note = |Boy, do I have a fabulous clear glaze for you!! I tested about 15

note = |clears last year and only came up with 2 that I would consider using.

note = |This glaze is incredibly forgiving - doesn't show drips, overdips,

note = |differences in thickness, is glassy clear w/o yellow, and doesn't

note = |craze. Can you believe it? I couldn't either, but it's true and I am

note = |absolutely thrilled with this glaze. It only has 4 ingredients, too.

note = |I use this over slips and underglazes and it's fine. I also use

note = |lusters over it with great results. What can I say? This is THE

note = |PERFECT clear glaze. Have fun. Laura in Oregon )

name = Clear Glaze 5-6 recalc

index =

date = 12/6/96

source =

type =

range = 5 - 6

firetype =

color = clear transparent

vistexture =

quality = glossy, shiny

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 4.7

component = Whiting

amount = 2

component = Silica

amount = 2.7

component = Kona F-4 feldspar

amount = 33.6

component = Frit 3195

amount = 56.9

addition = Bentonite

addamount = 2

note = |Boy, do I have a fabulous clear glaze for you!! I tested about 15

note = |clears last year and only came up with 2 that I would consider using.

note = |This glaze is incredibly forgiving - doesn't show drips, overdips,

note = |differences in thickness, is glassy clear w/o yellow, and doesn't

note = |craze. Can you believe it? I couldn't either, but it's true and I am

note = |absolutely thrilled with this glaze. It only has 4 ingredients, too.

note = |I use this over slips and underglazes and it's fine. I also use

note = |lusters over it with great results. What can I say? This is THE

note = |PERFECT clear glaze. Have fun. Laura in Oregon )

name = Clear Gloss

index =

date = 08/03/2003

source =

type =

range = 5-7

firetype = Oxidation

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = Flint

amount = 32.5

component = EPK

amount = 17.5

name = Clear Gronborg

index =

date = 12/6/96

source =

type =

range = 5

firetype =

color = Clear

vistexture =

quality = gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 39

component = Gerstley borate

amount = 20

component = Zinc oxide

amount = 3

component = Barium carbonate

amount = 6

component = Whiting

amount = 2

component = EPK

amount = 8

component = Silica

amount = 22

note = |Parker Gloss and Gronborg Clear are very similar. I include both

note = |because the coefficient of expansion is just different enough for you

note = |to tell which way to go if they do not fit your body. And, yes, I

note = |know they all have barium in them. Not much, though, so you could

note = |probably substitute 3/4 as much strontium carb, and not affect them

note = |much, or possibly just leave it out. I hope this helps. Paul Lewing

note = | pjlewing@

name = Clear Gronborg

index =

date = 12/6/96

source =

type = Mid-fire

range = 5

firetype = Ox. or Red.

color = clear transparent

vistexture =

quality = gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 39

component = Gerstley borate

amount = 20

component = Zinc oxide

amount = 3

component = Barium carbonate

amount = 6

component = Whiting

amount = 2

component = EPK

amount = 8

component = Silica

amount = 22

note = |Parker Gloss and Gronborg Clear are very similar. I include both

note = |because the coefficient of expansion is just different enough for you

note = |to tell which way to go if they do not fit your body. And, yes, I

note = |know they all have barium in them. Not much, though, so you could

note = |probably substitute 3/4 as much strontium carb, and not affect them

note = |much, or possibly just leave it out. I hope this helps. Paul Lewing

note = | pjlewing@

name = Clear GTB

index =

date = 7/19/95

source =

type =

range = 6

firetype = Ox. or Red.

color = Clear

vistexture =

quality =

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 39

component = Gerstley borate

amount = 27

component = Silica

amount = 18

component = Whiting

amount = 8

component = EPK

amount = 8

note = |Slips (use GTB over these)(Coppen Light is a ball clay from HC

note = |Spinks) UBL-33 Black Coppen Light 50 Frit 3134 20 Mason 6600 30

note = |UBL-18 Blue Black Coppen Light 50 Neph Sy 10 Mason 6616 30

note = |Wollastonite 10 UBL-17 Seal Brown Coppen Light 40 Neph Sy 20 Mason

note = |6152 30 Wollastonite 10 UB-20 Cobalt Blue Coppen Light 60 Flint 20

note = |Mason 6316 20 UPR-13 Pansy Purple Coppen Light 40 Neph Sy 10 Mason

note = |6385 37.5 Wollastonite 12.5 UB-18 Teal Blue Coppen Light 60 Frit 3134

note = |30 Mason 6305 10 UG-35 French Green Coppen Light 50 Frit 3134 15

note = |Wollastonite 10 Mason 6219 25 UG-13 Coppen Green Coppen Light 40 Neph

note = |Sy 30 Copper Carb 15 Flint 10 Wollastonite 5 UG-18 Deep Turquoise

note = |Coppen Light 40 Neph Sy 10 Mason 6390 40 Wollastonite 10 UR-21

note = |Crimson Coppen Light 40 Frit 3134 20 Mason 6006 30 Wollastonite 10

note = |UPR-27 Lavender Coppen Light 50 Frit 3134 30 Mason 6319 20 UY-28

note = |TYitanium Yellow Coppen Light 50 Neph Sy 10 Frit 3134 10 Mason 6485

note = |30 UY-24 Yellow Coppen Light 50 Neph Sy 12.5 Mason 6481 25

note = |Wollastonite 12.5 UP-45 Hot Pink Coppen Light 50 Frit 3134 30 Mason

note = |6020 20 UP-33 Coral Coppen Light 50 Frit 3134 30 Neph Sy 5 Mason 6090

note = |35 UGR-9 Gray Coppen Light 40 Neph Sy 5 Wollastonite 10 Frit 3134 5

note = |Mason 6530 40 UW-1 White Coppen Light 30 Neph Sy 20 Frit 3134 10

note = |Wollastonite 10 Mason 6700 30 submitted by: Jonathan Kaplan e-mail:

note = |74034.3566@ source for original recipe: Wayne Bates

name = Clear Katherine's 6

index =

date = 11/15/96

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture = None

quality = Gloss

transparency = Transparent

xtals = None

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 30

component = Wollastonite

amount = 8

component = Gerstley borate

amount = 21

component = EPK

amount = 10

component = Strontium carbonate

amount = 15

component = Flint

amount = 41

note = |add CMC for brushing application. From Katherine Grandy

name = Clear kitten's

index =

date = 10/06/2002

source =

type =

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 10.01

component = Dolomite

amount = 2.4

component = Whiting

amount = 0.4

component = Strontium carbonate

amount = 11.7

component = EPK

amount = 18.1

component = Silica

amount = 25

component = Frit 3134

amount = 32.2

note = | No Gerstley Borate Clear Base. Tends to run.

name = Clear Kitten's

index =

date = 10/29/2001

source =

type = Mid-fire

range = 5-6

firetype = Oxidation

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 24

component = Wollastonite

amount = 6.4

component = Gerstley borate

amount = 16.8

component = EPK

amount = 8

component = Flint

amount = 32.8

component = Strontium carbonate

amount = 12

note = |From Kathy King. Gem-like clear.

name = Clear Kitten's No GB

index =

date = 10/29/2001

source =

type = Mid-fire

range = 5-6

firetype = Oxidation

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 10.1

component = Dolomite

amount = 2.4

component = Whiting

amount = 0.4

component = Strontium carbonate

amount = 11.7

component = EPK

amount = 18.1

component = Silica

amount = 25

component = Frit 3134

amount = 32.2

note = |From Kathy King. Gem-like clear.

name = Clear Kitten's Sally's

index =

date = 04/07/2005

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 26

component = Wollastonite

amount = 7

component = Gerstley borate

amount = 18

component = EPK

amount = 9

component = Flint

amount = 27

component = Strontium carbonate

amount = 13

name = Clear Kona Gloss

index =

date = 08/04/2003

source =

type =

range = 6

firetype = Reduction

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 30

component = Gerstley borate

amount = 24

component = Wollastonite

amount = 15

component = EPK

amount = 8

component = Silica

amount = 23

var = |Striated green = + talc 3 + rutile 5 + strontium carb 10 + copper ox. 0.5 +

var = |zircopax 7

var = |Periwinkle Terazzo (solid thick, speckled thin) + tin 7.1 + zinc 3.3

var = |+ cobalt xo 2.6 + dark rutile 3.1

var = |Brown Aventurine (brown mauve thick,

var = |gold-speckled thin) + zinc 3.3 + dk rutile 2 + mang diox. 5.1

note = |From Sandy Potash

name = Clear Les Lawrence

index =

date = 1/13/96

source =

type =

range = 6

firetype = Oxidation

color = clear

vistexture =

quality =

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 44.64

component = EPK

amount = 26.79

component = Silica

amount = 28.57

note = |Here is a simple cone 6 oxidation glaze I have used often. I haven't

note = |tried it with colorants though. It is from Les Lawrence in Ceramics

note = |Monthly. submitted by: Suzanne Fuqua e-mail: Suzanne511@

name = Clear Les Lawrence

index =

date = 1/13/96

source =

type =

range = 6

firetype = oxidation

color = clear

vistexture =

quality =

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 44.64

component = EPK

amount = 26.79

component = Silica

amount = 28.57

note = |here is a simple cone 6 oxidation glaze I have used often. I haven't

note = |tried it with colorants though. It is from Les Lawrence in Ceramics

note = |Monthly. submitted by: Suzanne Fuqua e-mail: Suzanne511@

name = Clear Parker Gloss 5

index =

date = 12/6/96

source =

type =

range = 5

firetype = Ox. or Red.

color = Clear

vistexture =

quality = gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 43

component = Gerstley borate

amount = 20

component = Whiting

amount = 2

component = Zinc oxide

amount = 3

component = Barium carbonate

amount = 6

component = EPK

amount = 2

component = Silica

amount = 24

note = |Parker Gloss and Gronborg Clear are very similar. I include both

note = |because the coefficient of expansion is just different enough for you

note = |to tell which way to go if they do not fit your body. And, yes, I

note = |know they all have barium in them. Not much, though, so you could

note = |probably substitute 3/4 as much strontium carb, and not affect them

note = |much, or possibly just leave it out. I hope this helps. Paul Lewing

note = | pjlewing@

name = Clear Patti's Crystal

index =

date = 12/6/96

source =

type =

range = 5 - 7

firetype =

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Whiting

amount = 8

component = Nepheline syenite

amount = 30

component = Kaolin

amount = 10

component = Flint

amount = 31

note = |Does anyone have a good crystal clear cone 5 glaze recipe they could

note = |share? I like Patti's Crystal Clear ^5-7 from Clayart a few years

note = |ago. Janice Lipuma Lexington KY jan lipuma

name = Clear Patti's Crystal 5-7

index =

date = 12/6/96

source =

type =

range = 5 - 7

firetype = Ox. or Red.

color = Clear

vistexture =

quality = glossy shiny

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Whiting

amount = 8

component = Nepheline syenite

amount = 30

component = Kaolin

amount = 10

component = Flint

amount = 31

note = |Does anyone have a good crystal clear cone 5 glaze recipe they could

note = |share? I like Patti's Crystal Clear ^5-7 from Clayart a few years

note = |ago. Janice Lipuma Lexington KY jan lipuma

name = Clear Patty's Crystal 2

index =

date = 11/15/98

source =

type =

range = 5

firetype = Oxidation

color = Clear

vistexture =

quality = Shiny or Glossy

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = gerstley borate

amount = 10.5

component = Whiting

amount = 4

component = neph sy

amount = 15

component = Kaolin

amount = 5

component = Flint

amount = 15.5

addition = Bentonite

addamount = 2

note = |Kathy Whipple likes this clear. Rate for cone 5-7

name = Clear semi-mat Glaze

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color = Clear

vistexture =

quality = Satin matt

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Pemco frit P-626

amount = 20.6

component = Nepheline syenite

amount = 23.9

component = Wollastonite

amount = 13.9

component = Whiting

amount = 4.6

component = EPK

amount = 6.8

component = Silica

amount = 30.3

addition = Bentonite

addamount = 1.9

note = |Candice Roeder - (for me it was shiny clear) originally SG-42 from

note = |Chappell book (I used 325 mesh flint, and amorphous silica - which

note = |stopped crazing) This was used on a stoneware (Standard 182G) and

note = |primarily on porcelain 135 from A.R.T.... Fired to cone 6 (standard

note = |cone)....same schedule of firing each time. Candice in 0 degree rural

note = |Michigan croeder1@

name = Clear Tracy Wilson's

index =

date = 3/26/96

source =

type = Mid-fire

range = 5 - 6

firetype = Ox. or Red.

color = clear

vistexture =

quality = shiny

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 45

component = Colemanite

amount = 25

component = Kaolin

amount = 15

component = Silica

amount = 15

addition = Bentonite

addamount = 3

note = |The clear was lovely over the white slip but pinholed majorly over

note = |the blue. The blue had been poured on over my cream clay body

note = |plainsman M-340. Well if anyone can let me know why the pinholing on

note = |the blue that would be great (I suspect it must be a cobalt annoyance

note = |or something because the clear glaze was o.k on the white slip and on

note = |the regular clay itself). Also if anyone has another recipe to try

note = |that would be helpful. submitted by: Cheryl Brown e-mail:

note = |cbrown@terranet.ab.ca

name = Clear Transparent Dinah's

index =

date = 12/6/96

source =

type =

range = 5

firetype =

color = Clear

vistexture =

quality = gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro frit 3292

amount = 39.9

component = Ferro frit 3124

amount = 39.9

component = Kentucky OM #4

amount = 9.98

component = Silica (325m)

amount = 9.98

component = Magnesium carbonate

amount = 0.25

addition = CMC

addamount = 0.25

addition = Epsom salts

addamount = 0.5

note = |Mix to specific gravity of 1.5. I found another glaze that was

note = |developed a couple of years back by Dinah Collopy

note = |(dinah@GN2.). She wanted a clear that handled underglazes

note = |well as I recall. I know she did countless tests. Her comments were

note = |as follows: There were two commercial glazes that worked

note = |well--Laguna's MS29 and Ceramichrome NG 100 (the latter says it

note = |contains lead aluminum silicate but if fired over cone2 meets FDA

note = |health requirments for lead release). These commercial glazes need to

note = |be applied VERY thinly. What I will end up using is the following:

note = |Maybe that explains why the colours are so vibrant.... Iain Iain Begg

note = |begg@mpr.ca Bearsden Studio, Vancouver, BC

name = Clear V.C. 2

index =

date = 11/15/98

source =

type = Ca Na B

range = 5 - 6

firetype = Ox or Red

color = White

vistexture =

quality = Glossy

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Cornwall Stone

amount = 47.4

component = Gerstley borate

amount = 47.4

component = Ball clay

amount = 5.3

addition = Zircopax

addamount = 5.3

note = |Val, please name this series. Glaze Type: Ca Na B. Opacity:

note = |Transparent. Firing type: Ox or Red .

name = Colemanite White Glaze

index =

date = 4/21/95

source =

type =

range = 5

firetype = oxidation

color = mottled cream

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Colemanite

amount = 31

component = Dolomite

amount = 14

component = Kaolin

amount = 19

component = Silica

amount = 36

note = |a very nice shiny, mottled cream color that has given me some

note = |interesting effects over dark slips. Gerstley Borate used for

note = |Colemanite. source of original recipe: Ceramics Monthly, March '94

note = |p.60 submitted by: Sumi Dick e-mail: Sumi@

name = cone 6 Ash Glaze

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color =

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cedar Heights Redart

amount = 40

component = Ferro frit 3124

amount = 30

component = Ash

amount = 30

addition = Rutile

addamount = 4

note = |I used sieved unwashed fireplace ash. An excellent honey gold gloss

note = |Add 3% cobalt for a perfect Black Tested on Dillo White clay at a

note = |full ^6. submitted by: Lori Wilkinson e-mail: lorwilk@

note = |

name = Copper Red

index =

date = 3/26/96

source =

type =

range = 6

firetype = Reduction

color = Opaque Red

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 59.81

component = Frit 3110

amount = 11.34

component = Zinc oxide

amount = 5.15

component = Talc

amount = 4.12

component = Whiting

amount = 16.49

component = EPK

amount = 3.09

addition = Copper carbonate

addamount = 1.03

addition = Tin oxide

addamount = 2.06

note = |In use RLC. Note: 1/2 cup Epsom Salts / 10000gm. eliminates settling.

note = |Frit 3195 may be substituted for 3110. Good reduction yields blood

note = |red. Oxidation is celadon-like green. Apply medium / thin won't be

note = |red / thick it crawls. If overlapped on another glaze - may crawl.

note = |Here is a formula that has recently been used here at Richland

note = |College, Dallas, Tx. I can't give you much information about the

note = |firing itself, since it was done by one of the other instructors.

note = |What I can tell you is that the colors seemed to go from Fire-engine

note = |red to red with blackish areas. Did not seem to run a lot. Possible

note = |Health Hazards: Talc: wear a NIOSH approved dust mask when handling

note = |dry material Unity Formula for Copper Red: 0.171 K2O??0.290

note = |Al2O3?2.183 SiO2? 0.141 Na2O?0.010 B2O3??7.5:1 Si:Al Ratio 0.448 CaO?

note = |0.082 MgO? 0.158 ZnO? Percentage Analysis: 57.63 % SiO2 13.01 % Al2O3

note = |0.31 % B2O3 7.08 % K2O 3.82 % Na2O 11.03 % CaO 1.45 % MgO 5.67 % ZnO

note = |Hope this can be of some assistance......Fred Sweet

note = |

name = Copper Red

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 43.9

component = Flint

amount = 16.3

component = Whiting

amount = 14.3

component = Ferro frit 3134

amount = 13.3

component = EPK

amount = 5.1

component = Zinc oxide

amount = 4.1

component = Talc

amount = 3.1

addition = Tin oxide

addamount = 2

addition = Black copper oxide

addamount = 1

note = |I am looking for a cone 6, reduction Copper Red glaze recipe, and

note = |would appreciate any suggestions or ideas. The one that we are

note = |currently using is a bit too runny at cone 6. We tried a line blend

note = |with a copper red that I have used at cone 10, but the color went to

note = |a pink as soon as we moved it up the scale enough to not make it so

note = |runny. Thanks, Rick Malmgren RMalmgren@

name = Cornball White

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color = white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 49.23

component = Kentucky OM #4

amount = 22.96

component = Talc

amount = 7.26

component = Whiting

amount = 7.72

component = Barium carbonate

amount = 12.82

note = |I'm not taking responsibility for anyone using these glazes, etc.

note = |Something is probably toxic. They are examples of my research and

note = |they work out in formulation. Which is what they are examples of. So

note = |go formulate your own non-toxic glazes, if that is possible. It's

note = |probably bad for the environment too. Email me with questions as to

note = |household performance, as that may be indicative of other problems.

note = |The badly crazed surfaces are not considered to be a continous-non

note = |porous sanitary surfaces. Eric Hansen, Lawrence, Kansas

note = |wabi_sabi@

note = |

name = Crater glaze

index =

date = 7/19/95

source =

type = Texture

range = 6

firetype =

color =

vistexture =

quality = texture, craters

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Talc

amount = 25

component = Cryolite

amount = 15

component = Silica

amount = 30

component = EPK

amount = 30

addition = Bentonite

addamount = 2

note = |Does not crater in oxidation, why? submitted by: Eliz Drachman

note = |e-mail: PhysandClay@

name = Craters test

index =

date = 04/07/98

source =

type = Crater

range = 6

firetype = Oxidation

color =

vistexture = Lava

quality = Crater

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Cornwall Stone

amount = 25.812

component = Gerstley borate

amount = 1.562

component = Lithium carbonate

amount = 4.753

component = Dolomite

amount = 16.364

component = Fluorspar

amount = 31.73

component = EPK

amount = 1.588

component = Flint

amount = 18.191

name = Crawl Bone Ash

index =

date = 01/10/01

source =

type = Crawl

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Bone ash

amount = 74.4

component = Cryolite

amount = 13.2

component = Barium carbonate

amount = 4.1

component = F-4 spar

amount = 8.3

var = |try each:

var = |CuCO3 4%

var = |rutile 8 %

var = |CoCO3 3

var = |CrO 2%

note = |Virginia Scotchie

name = Crawl CM Ball

index =

date = 9/20/95

source =

type = Crawl

range = 6

firetype = Ox. or Red.

color = White

vistexture =

quality = Texture

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 50

component = Nepheline syenite

amount = 50

note = |There was also an article in ceramics Monthly, Feb 1990 on lichen

note = |glazes. I tried the Ball Crawl glaze. worked fairly well, but could

note = |be chipped off the pot too easily. this made me try putting it over

note = |another glaze. submitted by: Kathy Darby e-mail: kdarby@

note = |source for original recipe: Ceramics Monthly

name = Crawl Jamie's

index =

date =

source =

type = Crawl

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 70

component = Magnesium carbonate

amount = 30

var = |10-15% rutile for beige

note = |From Jamie Walker

name = Cream Breaking Red

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color = cream

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 46.7

component = Kona F-4 feldspar

amount = 20

component = Whiting

amount = 13.3

component = Barium carbonate

amount = 6.7

component = Silica

amount = 13.3

addition = Tin oxide

addamount = 17.3

addition = Red iron oxide

addamount = 2.7

note = |I substitute Strontium 3.75 for the Barium. I've benefited from the

note = |recipes and advise you all have given, and I have a successful cone 6

note = |glaze to share. It is from (of all places) a Reader's Digest craft

note = |book. It is a nice fat cream to beige glaze. Glossy but not garish.

note = |Breaks to reddish brown where thin. If your clay body has much iron

note = |in it, the reddish breaking is quite pronounced, with speckles. I use

note = |it on white stoneware up to cone 7, and sometimes on porcelain,

note = |(though on porcelain it is less earthy looking). It is a nice neutral

note = |earth tone. Stores well, coats well. Well behaved and forgiving. Dark

note = |slips used underneath will show through. BTW, it does not add up to

note = |100. I've fired it as low as 5 and as high as 7. submitted by:

note = |Candice Roeder e-mail: CRoeder1@ source for original recipe:

note = |Readers Digest Craft Book

name = CREAM BREAKING RED

index =

date =

source =

type =

range = 6

firetype = Oxidation

color = buff stoneware

vistexture =

quality = Semi-gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 46.7

component = Kona F-4 feldspar

amount = 20

component = Whiting

amount = 13.3

component = Barium carbonate

amount = 6.7

component = Flint

amount = 13.3

addition = Tin oxide

addamount = 17.3

addition = Red iron oxide

addamount = 4

note = |one Type: Orton Clay Color/Type: Buff Stoneware Clarity:

note = |Semi-translucent Crystals: none Bubbles Within Glaze No Glaze Flow:

note = |Moderate flow Glaze Type: MEASURED Thermal Expansion: - What Makes

note = |This Glaze Unique: diversity of coloration - Reliability of glaze:

note = |100% reliable - Firing data: cone 6 oxidation yields beautiful

note = |results/normal firing cycle. - Surface quality variations: smooth

note = |melting - kiln manufacture and type: Norman kiln-top loader - Effects

note = |of firing to different cones: good results cones 4-6 - Coloring

note = |oxides, stains and opacifiers tested: - Known glaze flaws: - Apparent

note = |viscosity for pouring and dipping: - Application thickness:1 coat -

note = |Effects on different clay bodies: - Interactive effect with other

note = |glazes:beautiful with coblat glazes - Specific gravity of glaze for

note = |pouring and dipping: half and half cream - Water pH/composition: -

note = |Calculated unity formula: - Analyses for any rare or unusual

note = |ingredients used in this glaze: Glaze Contributor:G.Pollock Test

note = |Site:Pittsburgh, PA Source for the Original Recipe: .

name = Creme of Mushroom

index =

date = 8/8/97

source =

type =

range = 6

firetype =

color = semi trans light tan

vistexture =

quality = very glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 10.7

component = Nepheline syenite

amount = 40.7

component = Whiting

amount = 9.6

component = Flint

amount = 23.3

component = Gerstley borate

amount = 7.6

component = Dolomite

amount = 4.8

component = Zinc oxide

amount = 3.4

addition = Rutile

addamount = 4

addition = Red iron oxide

addamount = 1

addition = Bentonite

addamount = 1.5

addition = Zircopax

addamount = 10.2

note = |Here is an interesting cone 6 that is very glossy, semi transparent

note = |in the light tan range. Some fine particle speckling too. Dan

note = |Saultman, Colorado clay-art@

note = |

name = Crystal Matt

index =

date = 08/03/2003

source =

type = Crystalline

range = 5-8

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Feldspar

amount = 36

component = Whiting

amount = 9

component = Dolomite

amount = 22

component = Flint

amount = 28

addition = Bentonite

addamount = 5

var = |+ 10% rutile in oxidation = glassy white w/pink crystals. In reduction = blue

var = |w/white and pink crystals

name = Crystalline Black

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = black

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 21

component = Gerstley borate

amount = 5.25

component = Custer feldspar

amount = 15.75

addition = Cobalt carbonate

addamount = 6

addition = Copper carbonate

addamount = 6

note = |Too many ingredients (these ingredients are also to be added to the

note = |recipe): (can't remember who posted this originally, might've been me

note = |;) Mishy Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

note = |

note = |

name = Crystalline Manganese

index =

date = 04/12/99

source =

type = Crystalline

range = 5-6

firetype = Ox. or Red.

color = Black

vistexture =

quality = Metallic

transparency = Opaque

xtals = Medium (clustered)

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Feldspar

amount = 51.1

component = EPK

amount = 15.6

component = Flint

amount = 15.6

component = Whiting

amount = 17.8

addition = Red iron oxide

addamount = 4.4

addition = Manganese dioxide

addamount = 6.7

note = |From Hamer, A Potters Dictionary of Materials and Techniques 3rd ed.p210-11

name = cullet glaze

index =

date = 4/3/98

source =

type =

range = 2 - 6

firetype = oxidation

color = green

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cullet (container glass)

amount = 49.01

component = Redart clay

amount = 6.24

component = EPK

amount = 9.47

component = Dolomite

amount = 2.68

component = Whiting

amount = 21.19

component = Silica

amount = 11.42

note = |Total 100.01 Molecular Formula: 0.279 KNa0 0.122 Al2O3 1.985 SiO2

note = |0.590 CaO 0.007 Fe2O3 0.003 TiO2 0.128 MgO This recipe is simlar in

note = |terms of unity to one in use in Thailand. I have no idea about its

note = |durability. Perhaps some one else can speak to this. Certainly there

note = |is a lot of variation in container glass. Louis louis katz

note = |

name = Cyndi's Revision 5-A

index =

date = 11/16/98

source =

type = Magnesium matt

range = 5-6

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Gerstley borate

amount = 7

component = Nepheline syenite

amount = 19

component = Dolomite

amount = 5

component = EPK

amount = 12

component = Wollastonite

amount = 34

component = Flint

amount = 23

name = Cyndi's Revision 5-C

index =

date = 11/16/98

source =

type = Magnesium matt

range = 5-6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Gerstley borate

amount = 5

component = Nepheline syenite

amount = 18

component = EPK

amount = 14

component = Dolomite

amount = 13

component = Wollastonite

amount = 23

component = Flint

amount = 28

note = |Higher silica

name = D.K. 11

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca Liner MidRoad

range = 5 - 6

firetype = Ox. or Red.

color = white

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 63

component = Whiting

amount = 18

component = Zinc oxide

amount = 5

component = Talc

amount = 5

component = EPK

amount = 9

addition = Zircopax

addamount = 12

var = |May use 8 - 12% Zircopax for white.

note = |See also D.K. 11 Revised

name = D.K. 11 Revised

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca Liner MidRoad

range = 5 - 6

firetype = Ox. or Red.

color = white

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 62

component = Whiting

amount = 14

component = Zinc oxide

amount = 6

component = Talc

amount = 8

component = EPK

amount = 10

addition = Zircopax

addamount = 8

note = |Revised by V.C. Whiter & more toward satin than D.K. 11.

name = Darby 1

index =

date = 08/01/2001

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 17

component = Nepheline syenite

amount = 29

component = Barnard clay

amount = 54

note = |> ClayArt Listserv recipe < If you find this glaze useful, please

note = |consider submitting it to the GlazeBase project with full

note = |documentation. Use one of the GlazeBase submission formats available

note = |on the CeramicsWeb web page.

note = |

note = |Comments: Test fired on Plainsman M340 (an off white clay) in an

note = |electric kiln. This was dark brown, well behaved semi-gloss. It's

note = |semi-transparent where thin. From Kathy Darby From Vickie Sproule via

note = |clayart email: jsproule@mars.

name = Darby 2

index =

date = 4/7/95

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 17.96

component = Nepheline syenite

amount = 22.26

component = Barnard clay

amount = 35.73

component = Flint

amount = 23.85

component = Soda ash

amount = 0.2

note = |Test fired on Plainsman M340 (an off white clay) in an electric kiln.

note = |I didn't have any soda ash, so I didn't add it. This was a dark brown

note = |glossy glaze very much like Alberta slip in cone 9, but darker. From

note = |Kathy Darby Thanks Kathy! From Vickie Sproule via clayart email:

note = |jsproule@mars.

note = |

name = Dark Brown Gloss

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = dark brown

vistexture =

quality = glossy, shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Flint

amount = 21.35

component = Potash feldspar

amount = 39.33

component = Whiting

amount = 16.85

component = Ball clay

amount = 11.24

component = Volcanic ash

amount = 11.24

addition = Red iron oxide

addamount = 12.36

addition = Bentonite

addamount = 2.25

addition = Titanium dioxide

addamount = 2.25

note = |I also have a dark brown gloss recipe for ^6 but have not yet tested

note = |it How nice to be able to share something from my books, I have been

note = |so pleased with some of the recipes that I have tested from other

note = |clayart subscribers. I only wish that I could give proper credit to

note = |the originators of these but I am afraid I was amiss in recording

note = |such info. Sue on a rainy day in British Columbia - how unusual sue

note = |hutchen

note = |

name = Dark Brown Matt

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = dark brown

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 24.88

component = Nepheline syenite

amount = 17.91

component = Colemanite

amount = 6.97

component = Whiting

amount = 14.93

component = Kaolin

amount = 22.39

component = Flint

amount = 12.94

addition = Manganese dioxide

addamount = 7.96

addition = Black copper oxide

addamount = 1.49

note = |from Plainsman Clay (Alberta) here's a brown that we have used for

note = |years in our studio: Apart from being dark, brown and matt, this

note = |glaze goes on well, covers well and looks good with many other

note = |glazes. Hope it's one you add to your recipe book. Geri Huntley

note = |Kamloops BC jhuntley@cariboo.bc.ca

note = |

name = DR

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = dark blue to turquoise

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 20.43

component = Barium carbonate

amount = 43.01

component = Lithium carbonate

amount = 5.38

component = Silica

amount = 10.75

component = Kaolin

amount = 20.43

addition = Copper carbonate

addamount = 7.53

note = |Semimatt dark blue breaking to turquoise. ok From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = Eggshell

index =

date = 12/26/2006

source =

type = Zinc matt

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 9.5

component = Zinc oxide

amount = 5.5

component = Frit 3124

amount = 44.5

component = Custer feldspar

amount = 20

component = Bentonite

amount = 7.5

component = EPK

amount = 5

component = Silica

amount = 8

addition = Tin oxide

addamount = 9

addition = Red iron oxide

addamount = 3

note = |From Central Carolina CC via Ceramics Mo.07 Buyer's Guide supplement.

note = |

name = Eggshell

index =

date = 12/26/2006

source =

type = Zinc matt

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 9.5

component = Zinc oxide

amount = 5.5

component = Frit 3124

amount = 44.5

component = Custer feldspar

amount = 20

component = Bentonite

amount = 7.5

component = EPK

amount = 5

component = Silica

amount = 8

addition = Tin oxide

addamount = 9

addition = Red iron oxide

addamount = 3

note = |From Central Carolina CC via Ceramics Mo.07 Buyer's Guide supplement.

name = Eggshell David Hewitt's

index =

date = 9/20/95

source =

type = Magnesium matt

range = 6

firetype = Oxidation

color = White

vistexture =

quality = satin matt

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 48

component = China clay

amount = 16

component = Dolomite

amount = 15

component = Whiting

amount = 10

component = Silica

amount = 5

component = PotteryCrafts Frit P2960

amount = 5.5

component = Zinc oxide

amount = 0.5

note = |This gives a white satin finish 'eggshell' glaze. coloured slip

note = |applied to the leather hard pot come through the glaze very

note = |successfully. submitted by: David Hewitt e-mail:

note = |david@DHPOT.DEMON.CO.UK

name = Eggshell recalc

index =

date = 12/26/2006

source =

type = Zinc matt

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 16

component = Dolomite

amount = 0.9

component = Zinc oxide

amount = 5.3

component = Frit 3195

amount = 24.8

component = Potash feldspar - theoretical

amount = 32.8

component = Kaolin - theoretical

amount = 0.3

component = Silica

amount = 19.9

addition = Tin oxide

addamount = 9

addition = Red iron oxide

addamount = 3

note = |From Central Carolina CC via Ceramics Mo.07 Buyer's Guide supplement.

note = |Recalculated to use less frit and be cheaper. Untested.

note = |

name = Eggshell recalc

index =

date = 12/26/2006

source =

type = Zinc matt

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 16

component = Dolomite

amount = 0.9

component = Zinc oxide

amount = 5.3

component = Frit 3195

amount = 24.8

component = Potash feldspar - theoretical

amount = 32.8

component = Kaolin - theoretical

amount = 0.3

component = Silica

amount = 19.9

addition = Tin oxide

addamount = 9

addition = Red iron oxide

addamount = 3

note = |From Central Carolina CC via Ceramics Mo.07 Buyer's Guide supplement. Recalculated to

note = |use less frit and be cheaper. Untested.

name = Ellen's Halloween

index =

date = 11/15/98

source =

type = Ca Ba AlMatt

range = 5 - 7

firetype = Reduction

color = Yellow brown green

vistexture =

quality = Satin to Matt/Soft Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 4240

component = Whiting

amount = 1760

component = Barium carbonate

amount = 1280

component = EPK

amount = 720

addition = Yellow ochre

addamount = 400

addition = Rutile

addamount = 160

note = |Soft matt. Yellowish, brownish, greenish."Multi-colored

note = |yellow-browns, etc. Beautiful." Glaze Type: Ca Ba AlMatt. Opacity:

note = |Opaque. Firing type: Reduction .

note = |

name = Engobe Black Vitreous

index =

date = 9/20/95

source =

type = Slip

range = 6

firetype = Ox. or Red.

color = black

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 16.7

component = Calcined kaolin

amount = 38.9

component = Talc theoretical

amount = 5.6

component = Nepheline syenite

amount = 16.7

component = Silica

amount = 16.7

component = Borax

amount = 5.6

addition = Zircopax

addamount = 11.1

addition = Red iron oxide

addamount = 16.7

addition = Manganese dioxide

addamount = 16.7

addition = Chrome oxide

addamount = 16.7

note = |Colorants can range from 10.5 to 21, but 15 is entered as an average.

note = |A few years ago I participated in a workshop with Randy Brodnax who

note = |work with lichen glazes, among other techniques. His recipes follow.

note = |We covered the bisqued pot with the black englobe, (brushed on) and

note = |then dipped the pot in the lichen glaze. Then colored commercial

note = |underglazes were sprayed on the glaze. Wonderful effects. The black

note = |engobe gives better contrast with the lichen glaze. I also tried the

note = |lichen glaze both over and under my regualr cone six glazes, some

note = |very interesting, very nice effects. try it. submitted by: Kathy

note = |Darby e-mail: kdarby@ source for original recipe: Randy Brodnax

name = Floating Blue (Clayart)

index =

date = 12/6/96

source =

type =

range = 6

firetype =

color = blue to green

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 47.3

component = Gerstley borate

amount = 27

component = Silica

amount = 20.3

component = EPK

amount = 5.4

addition = Red iron oxide

addamount = 2

addition = Cobalt oxide

addamount = 1

addition = Milled rutile

addamount = 4

note = |I come to your rescue. I just tried 2 slightly different Floating

note = |Blue's last night. One of them is from Clayart database the other

note = |from my RISD notebook RISD Floating Blue is much much nicer, as it

note = |has better coverage and less runny, and the blue is accented much

note = |better. I hope this helps. OMER BERAT ARTUN Institute for Brain and

note = |tel: 401 421 2879 (home) Neural Systems, 401 863 3920 (office)

note = |Department of Physics 401 863 3494 (fax) Box 1843 Brown University

note = |URL: Providence RI 02912

note = |e-mail: artun@cns.brown.edu

note = |

name = Floating Blue (RISD)

index =

date = 12/6/96

source =

type =

range = 6

firetype = oxidation

color = blue to green

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 47.3

component = Colemanite

amount = 27

component = Flint

amount = 20.3

component = Kaolin

amount = 5.4

addition = Red iron oxide

addamount = 2

addition = Cobalt oxide

addamount = 1

addition = Rutile

addamount = 4

note = |I come to your rescue. I just tried 2 slightly different Floating

note = |Blue's last night. One of them is from Clayart database the other

note = |from my RISD noteboo RISD Floating Blue is much much nicer, as it has

note = |better coverage and less runny, and the blue is accented much better.

note = |I hope this helps. OMER BERAT ARTUN Institute for Brain and tel: 401

note = |421 2879 (home) Neural Systems, 401 863 3920 (office) Department of

note = |Physics 401 863 3494 (fax) Box 1843 Brown University URL:

note = | Providence RI 02912 e-mail:

note = |artun@cns.brown.edu

note = |

name = Floating Blue (RISD) test question

index =

date = 12/6/96

source =

type =

range = 6

firetype = oxidation

color = blue to green

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 47.3

component = Colemanite

amount = 27

component = Flint

amount = 20.3

component = Kaolin

amount = 5.4

addition = Red iron oxide

addamount = 2

addition = Cobalt oxide

addamount = 1

addition = Rutile

addamount = 4

note = |I come to your rescue. I just tried 2 slightly different Floating

note = |Blue's last night. One of them is from Clayart database the other

note = |from my RISD noteboo RISD Floating Blue is much much nicer, as it has

note = |better coverage and less runny, and the blue is accented much better.

note = |I hope this helps. OMER BERAT ARTUN Institute for Brain and tel: 401

note = |421 2879 (home) Neural Systems, 401 863 3920 (office) Department of

note = |Physics 401 863 3494 (fax) Box 1843 Brown University URL:

note = | Providence RI 02912 e-mail:

note = |artun@cns.brown.edu

name = Floating Blue Glaze

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 47.31

component = Gerstley borate

amount = 27

component = Silica

amount = 20.3

component = EPK

amount = 5.4

addition = Red iron oxide

addamount = 2

addition = Cobalt oxide

addamount = 1

addition = CMC

addamount = 1

addition = Rutile (milled)

addamount = 4

note = |I substitute Cobalt Carb 2.0. I noticed that the Floating Blue has

note = |popped up again. It is a glaze I'm familiar with since I've been

note = |using it for about 3 years. What caught my eye, was the description

note = |of it as slate blue, which doesn't fit my results. So, I picked up

note = |the original recipe, and it differs from the one Sharon posted. If

note = |you're interested, you might try this version in your tests. It is

note = |called Floating Blue...from James Chappell's book, Clay and Glazes.

note = |This glaze produces a deep blue-brown background of great depth with

note = |lighter mottled blues that seem to float on the surface of the

note = |background glaze. The glaze has more of the lighter mottled blues

note = |where the application is thickest. Watch thickness near the bottom of

note = |the pot. The C.M.C. measurement refers to a premixed CMC and water

note = |solution. For the Silica, I use 325 mesh Flint. The rutile, is just

note = |powdered rutile from the ceramics supply. It fires best on the light

note = |side of cone 6 (standard cone just bending), seems to get greener and

note = |more fluid the higher you go. Cone 5 works well, too. I do not find a

note = |need for bentonite. The book says to weigh the ingredients very

note = |carefully, use distilled water or water that is known to have a low

note = |mineral content. Mix then add the CMC solution. Sieve two or three

note = |times through a 60 to 80 mesh sieve to thoroughly disperse the

note = |cobalt, iron, and rutile. The book warns that the glaze is fickle,

note = |and recommends against firing this glaze in the same kiln with glazes

note = |that contain copper, chrome, nickel or manganese. Mineral content of

note = |the water is an important factor. I have noticed an adverse effect as

note = |the author noted, and now fire an entire kiln load of this glaze. The

note = |glaze should be stirred occasionally during application because the

note = |iron has a tendency to settle. Chappell's Suggested variations:

note = |Stipple on additional glaze with brush or apply with sponge for an

note = |even more mottled effect. Or: lightly sponge a thin wash of 3 grams

note = |of chrome oxide to 100 grams of water plus a tablespoon of CMC over

note = |the top to produce a floating blue glaze with subtle green tints. Or:

note = |Over the glaze, sponge lightly with a rutile wash consisting of 2

note = |grams rutile per 100g of water for a floating blue glaze with

note = |slightly tan crystalline tints on the surface. submitted by: Candice

note = |Roeder e-mail: CRoeder1@ source for original recipe: James

note = |Chappell

note = |

name = Frit 25

index =

date = 6/3/96

source =

type =

range = 5 - 7

firetype =

color = clear

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 34.9

component = Pemco frit P-25

amount = 25.3

component = Silica

amount = 25.3

component = Whiting

amount = 5.8

component = Gerstley borate

amount = 5.1

component = Kentucky Ball Clay

amount = 3.6

note = |transparency: transparent used frit 3269. Apply thin, I added 5% more

note = |flint---see text for colour options. Superpax 10%--really bright

note = |white--good colour response with stains except pinks. submitted by:

note = |Jo Ann Stevens e-mail: jstevens@

note = |

name = G 1

index =

date = 11/15/98

source =

type = Li Ba

range = 5

firetype = Ox or Red

color =

vistexture =

quality = Semi-matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Buckingham feldspar

amount = 34.78

component = Barium

amount = 17.39

component = Frit Pb

amount = 8.7

component = Frit

amount = 8.7

component = Zinc

amount = 4.35

note = |White semi-opaque semi-mat smooth dull glaze. Colors tested: Iron 7%,

note = |Copper 4%, Rutile 7%, Nickle 4% and Nickle 4 plus Iron 7. More

note = |notes??? Glaze Type: Li Ba. Opacity: Semi-opaque. Firing type: Ox or

note = |Red .

note = |

name = G-200 Matt

index =

date = 11/15/98

source =

type =

range = 5

firetype = Oxidation

color = Translucent White

vistexture =

quality = Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash spar

amount = 150

component = Zinc oxide

amount = 150

component = Flint

amount = 90

component = Whiting

amount = 40

component = barium carb

amount = 36.5

component = EPK

amount = 27

component = Dolomite

amount = 6.5

note = |Good w/stains & oxides about 10%. Cobalt 1% = electric blue. 2 coats

note = |if brushed. Use gum if brushing. From George Bowes.

note = |

name = GDR6

index =

date = 8/8/97

source =

type =

range = 6

firetype =

color = Translucent white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 32

component = Whiting

amount = 14

component = Talc

amount = 6

component = Ferro frit 3134

amount = 6

component = Kentucky OM #4

amount = 17

component = Silica

amount = 25

note = |Can use either Custer or G-200 Feldspar. Ratio 9.84 Expansion 457.43

note = |Here is a foodsafe glaze made up for me by Ron Roy. It is a balanced

note = |glaze and has passed the 24 hour in the freezer to boiling water test

note = |without any crazing or cracking. Translucent white. Transparent where

note = |thin, whiter where thicker. Lynn Barth Cherry Valley Pottery

note = |LABARTH@worldnet.

note = |

name = Gibby's Rutile

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = tan/yellow

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Lithium carbonate

amount = 10.5

component = Bone ash

amount = 10.5

component = Nepheline syenite

amount = 61.5

component = #6 Tile clay

amount = 17.5

addition = Rutile

addamount = 10

note = |fired to ^ 6 Ox (^ 7 in sitter.) (I used EPK instead of #6 Tile

note = |Kaolin) Very nice matt, light tan/yellow with orange specks. From

note = |Gibby and Dave Gibson Rafael Molina-Rodriguez

note = |

name = Gloss broken cool browns

index =

date = 4/10/95

source =

type =

range = 6 - 8

firetype =

color = broken cool browns

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 50

component = Spodumene

amount = 50

note = |Rob Wadey (robert wadey ) 9734B - 100 Ave

note = |Grande Prairie, Alberta t8V 0T6 Phone: (403) 538-3731 Fax: (403)

note = |538.3732

note = |

name = Gloss Clear

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona Feldspar

amount = 18.56

component = Dolomite

amount = 0.36

component = Gerstley borate

amount = 39.56

component = EPK

amount = 22.29

component = Silica

amount = 19.24

note = |(optional zircopax) 8% --for a white glaze. This works well with many

note = |different colorants. Yellow is a sunny /bright that pools in the

note = |crevices with 6% titanium dioxide. I have also added up to 10% more

note = |EPK for a less runny glaze, but I fire closer to ^7 than to ^5.

note = |submitted by: Mary Kuilema e-mail: kuil@k2.

note = |

name = Gloss Off-White

index =

date = 03/06/01

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = F-4 spar

amount = 45

component = Flint

amount = 24

component = Gerstley borate

amount = 13.3

component = Whiting

amount = 8.3

component = Dolomite

amount = 6.4

component = Zinc oxide

amount = 4

component = EPK

amount = 2.5

var = |+ 8% Mason #6129 Golden Ambrosia

name = Gloss Parker

index =

date = 12/6/96

source =

type =

range = 5

firetype = Oxidation

color = Clear

vistexture =

quality = gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 43

component = Gerstley borate

amount = 20

component = Whiting

amount = 2

component = Zinc oxide

amount = 3

component = Barium carbonate

amount = 6

component = EPK

amount = 2

component = Silica

amount = 24

note = |Parker Gloss and Gronborg Clear are very similar. I include both

note = |because the coefficient of expansion is just different enough for you

note = |to tell which way to go if they do not fit your body. And, yes, I

note = |know they all have barium in them. Not much, though, so you could

note = |probably substitute 3/4 as much strontium carb, and not affect them

note = |much, or possibly just leave it out. I hope this helps. Paul Lewing

note = | pjlewing@

name = Gloss speckled blue-grey

index =

date = 4/10/95

source =

type =

range = 6 - 8

firetype = Oxidation

color = speckled blue-grey

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany Slip

amount = 47.37

component = Potash feldspar

amount = 28.42

component = Flint

amount = 9.47

component = Zinc oxide

amount = 9.47

component = Whiting

amount = 5.26

addition = Rutile

addamount = 5.26

note = |Rob Wadey (robert wadey ) 9734B - 100 Ave Grande Prairie, Alberta t8V

note = |0T6 Phone: (403) 538-3731 Fax: (403) 538.3732

note = |

name = GLOSS TRANSPARENT

index =

date = 4/10/95

source =

type =

range = 6

firetype = oxidation

color = clear transparent

vistexture =

quality = gloss, shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = EPK Kaolin

amount = 17.5

component = Flint

amount = 32.5

note = |I use this over slips and there has never been any crazing. Where it

note = |is a little thick it shows white. For a blue I added: Cobalt

note = |Carbonate .5 % Manganese Carbonate 5.0% For a beautiful blue-gray:

note = |Chrome Oxide 4% Tin Oxide 5% In response to request for cone 6

note = |glazes...This glaze was in a former post from someone else, but I

note = |have been using it for years. Some results of my testing are below. I

note = |fire in electric and use a commercial brown/black clay. This glaze is

note = |simple and dependable from firing to firing. Phyllis Nelson Baker

note = |University NELSON@george.bakeru.edu

note = |

name = Gloss White

index =

date = 12/7/96

source =

type =

range = 4 - 5 - 6 - 7 - 8

firetype = oxidation

color = white

vistexture =

quality = glossy, shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 12.59

component = Nepheline syenite

amount = 29.95

component = Whiting

amount = 11.37

component = Flint

amount = 27.51

component = Gerstley borate

amount = 8.93

component = Dolomite

amount = 5.69

component = Zinc oxide

amount = 3.96

addition = Bentonite

addamount = 1.52

addition = Zircopax

addamount = 10.15

note = |For Pat Chesney- I use a gloss white glaze that it supposed to mature

note = |at cone 4 -8. I fire it to 6-7, so I haven't personally tested it at

note = |4. I got the recipe from Eastern Ill. Univ. Hope this helps. from

note = |rebecca mott

note = |

name = Glossy

index =

date = 6/4/96

source =

type = Ca Mg AlMatt

range = 5 - 6

firetype = Ox or Red

color = Opaque White

vistexture =

quality = Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 Spar

amount = 19

component = Custer feldspar

amount = 19

component = Nepheline syenite

amount = 19

component = Dolomite

amount = 25

component = Whiting

amount = 6

component = Kaolin

amount = 12

addition = Tin oxide

addamount = 7.5

note = |A glossier version of Polished Matt. Glaze Type: Ca Mg AlMatt. Firing

note = |type: Ox or Red. From Val Cushing. VC ed

note = |

name = GNB11

index =

date = 4/10/95

source =

type =

range = 6

firetype =

color = pale blue w/ darker flecks

vistexture =

quality = dry matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 55.56

component = Barium carbonate

amount = 41.41

component = Zinc oxide

amount = 3.03

addition = Cobalt carbonate

addamount = 0.25

addition = Chrome oxide

addamount = 0.25

note = |Dry, pale blue with darker flecks From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs CLAY COLOR/TYPE: Buff

note = |Stoneware Fired at 100 degrees per hour to 600 degrees, then free for

note = |all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the

note = |UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University Block B,

note = |Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore CLAY COLOR/TYPE: Buff Stoneware

note = |Fired at 100 degrees per hour to 600 degrees, then free for all to

note = |cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp Nanyang Technological University Block B,

note = |Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

note = |

name = GNB7

index =

date = 4/10/95

source =

type =

range = 6

firetype = oxidation

color = cornflower blue/green

vistexture =

quality = dry

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 55.56

component = Barium carbonate

amount = 41.41

component = Zinc oxide

amount = 3.03

addition = Titanium dioxide

addamount = 4.04

addition = Cobalt carbonate

addamount = 0.51

note = |Dry, cornflower blue/green with yellow flecks, nice. From Brian Kemp,

note = |Singapore, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = GNB9

index =

date = 4/10/95

source =

type =

range = 6

firetype = oxidation

color = mid grey/blue

vistexture =

quality = dry matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 55.56

component = Barium carbonate

amount = 41.41

component = Zinc oxide

amount = 3.03

addition = Cobalt carbonate

addamount = 1.01

addition = Rutile

addamount = 5.05

addition = Copper carbonate

addamount = 2.02

note = |Dry, mid grey/blue with yellow green flecks, good. From Brian Kemp,

note = |Singapore, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = Gold Klinesville (Jeff Dietrich)

index =

date = 4/7/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = Amber

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 4.5

component = Whiting

amount = 20.2

component = Wollastonite

amount = 5.6

component = Nepheline syenite

amount = 56.2

component = Cedar Heights Redart Clay

amount = 13.5

addition = Red iron oxide

addamount = 6.7

addition = Zircopax

addamount = 12.4

note = |Golden glaze to round out the palette and add warmth. This applied

note = |smoothly - was a smooth satin matt - color similar to old gold. They

note = |are dependable firing to firing in Cone 6 electric on dark clay. From

note = |Jeff Dietrich in Ceramics Montly, April 1991 & sent via ClayArt by

note = |Phyllis Nelson Baldwin City, Kansas E-mail: NELSON@george.bakeru.edu

name = Gold Metallic

index =

date = 4/11/95

source =

type = Metallic

range = 6

firetype = Oxidation

color = black thin, crinkled gold thick

vistexture =

quality = matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Red clay

amount = 86.7

component = Ball clay

amount = 6.7

component = Silica

amount = 6.7

addition = Manganese dioxide

addamount = 65

addition = Copper oxide

addamount = 6.7

addition = Cobalt oxide

addamount = 4.2

note = |Matt black where thin, crinkled gold where thick, ok. From Brian

note = |Kemp, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv.

note = |CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

name = Gold Metallic Reynold's

index =

date = 02/20/2006

source =

type = Metallic

range = 6-10

firetype = Ox. or Red.

color = Metallic Bronze

vistexture = Mottled

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow = Extreme

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Redart

amount = 60

component = Ball clay

amount = 5

component = Flint

amount = 5

addition = Manganese dioxide

addamount = 45

addition = Copper oxide

addamount = 5

addition = Cobalt oxide

addamount = 5

note = |From Craig Reynolds. Runs a lot at cone 10, but lovely waxy to matt surface. NOT

note = |for food. Calls for black copper oxide.

name = Gray Gunmetal

index =

date = 8/8/97

source =

type =

range = 6

firetype =

color = Metallic grey

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 42.9

component = Flint

amount = 27.8

component = EPK

amount = 8

component = Whiting

amount = 13.9

component = Zinc oxide

amount = 7.4

addition = Cobalt oxide

addamount = 2.8

addition = Red iron oxide

addamount = 4

addition = Manganese dioxide

addamount = 2.8

note = |(Manganese dioxide is toxic in dust form. Came from Alex Combs, Anchorage

note = |Community College, circa 1973.

note = |Ric Ric Swenson, Bennington College, Route 67-A, Bennington, Vermont,

note = |05201-6001 USA. telephone 802 442 - 5401 vox X 262 fax X 237 direct

note = |fax line 802 442 - 6164 email rswenson@bennington.edu

note = |------------------------------

name = Green Beth's Shiny

index =

date = 6/3/96

source =

type = Mid-fire

range = 5 - 7

firetype = oxidation

color = light green

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 46.7

component = Silica

amount = 25

component = Gerstley borate

amount = 10.9

component = Ball clay

amount = 6.5

component = Dolomite

amount = 10.9

addition = Titanium dioxide

addamount = 7.6

addition = Bentonite

addamount = 1.1

addition = Copper carbonate

addamount = 1.6

note = |It is between a lime and chartreuse.

note = |submitted by: Beth Fusaro e-mail: elfusaro@freenet.scri.fsu.edu

name = Green black matt - Brandeis

index =

date = January 25, 1994

source =

type =

range = 6 - 10

firetype = Oxidation

color = green black

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 74.26

component = Zinc oxide

amount = 1.98

component = Dolomite

amount = 4.95

component = Whiting

amount = 2.97

component = EPK

amount = 6.93

component = Flint (325m)

amount = 8.91

addition = Copper carbonate

addamount = 3.96

addition = Cobalt oxide

addamount = 2.97

addition = Rutile

addamount = 9.9

note = |one Type: Orton Clay Color/Type: Brown stoneware Clarity: Opaque

note = |Crystals: None Clustered, Dispersed Bubbles Within Glaze: No Glaze

note = |Flow: Little flow Glaze Type: What Makes This Glaze Unique:

note = |It is an extremely intriguing glaze because

note = |of the variety of color and surface quality that it yields depending

note = |on the clay color, thickness of the glaze and whether or not it

note = |overlaps another glaze.

note = |Firing data: only tested at cone 6 and 7 -

note = |Surface quality variations: Applied thickly, the color is almost a

note = |gun metal black with a waxy to satin matt finish over buff, brown and

note = |porcelain clays. Lighter coats, especially over buff clays yield

note = |greens and blues and almost a glossy surface. - Kiln size,

note = |manufacture and type: Skutt 1027 - Effects of firing to different

note = |cones: - Coloring oxides, stains and opacifiers tested: - Known glaze

note = |flaws: - Apparent viscosity for pouring and dipping: - Application

note = |thickness: Depends on the desired effect. It can be dipped, but

note = |brushing yields more interesting effects and greater color variety. -

note = |Effects on different clay bodies: See above - Interactive effect with

note = |other glazes: One of the most exciting effects develops when using

note = |this over a white glaze covering porcelain clay. An extremely light

note = |coat brushed on yields bright sea blues and greens with patches of

note = |almost gold. Over the same white glaze on buff clay, the cobalt blue

note = |dominates. (The white glaze I use tends to turn virtually clear over

note = |buff or brown clay, leaving a glossy, faintly white blue finish.) -

note = |Specific gravity of glaze for pouring and dipping: - Water

note = |pH/composition: - Calculated unity formula: - Analyses for any rare

note = |or unusual ingredients used in this glaze: Original recipe called for

note = |Atomite brand whiting Glaze Contributor: Madeleine Hall-Arber Test

note = |Site: Newton, Massachusetts Source for the Original Recipe: Xeroxed

note = |typewritten pages without an notation of author, found at the student

note = |pottery center at Brandeis University.

name = Green Bullfrog

index =

date = 4/3/98

source =

type =

range = 5

firetype = oxidation

color = green

vistexture =

quality = stoney matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 47

component = Whiting

amount = 7.5

component = Barium carbonate

amount = 10.5

component = Zinc oxide

amount = 6

component = Kentucky OM #4

amount = 5

component = EPK

amount = 5

component = Flint

amount = 19

addition = Copper carbonate

addamount = 4

note = |I like a lot of green. But this ain't no Kermit green. Very stony

note = |matte with very hard surface. I suspect it was a tile glaze. Joe

note = |Zeller supplied the base, I went ape with the copper. I'm not taking

note = |responsibility for anyone using these glazes, etc. Something is

note = |probably toxic. They are examples of my research and they work out in

note = |formulation. Which is what they are examples of. So go formulate your

note = |own non-toxic glazes, if that is possible. It's probably bad for the

note = |environment too. Email me with questions as to household performance,

note = |as that may be indicative of other problems. The badly crazed

note = |surfaces are not considered to be a continous-non porous sanitary

note = |surfaces. Eric Hansen, Lawrence, Kansas wabi_sabi@

name = Green Dragon Matt

index =

date = 12/26/2006

source =

type = Zinc matt

range = 6

firetype = Oxidation

color = Turquoise

vistexture =

quality = Matt

transparency =

xtals = None

bubbles =

flow = Extreme

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 18

component = Zinc oxide

amount = 8

component = Cornwall Stone

amount = 22

component = Soda spar

amount = 44

component = EPK

amount = 3

component = Bentonite

amount = 5

addition = Titanium dioxide

addamount = 4

addition = Copper carbonate

addamount = 4

note = |Good with Ash Fresca over Green Dragon.

name = Green Dragon Matt

index =

date = 12/26/2006

source =

type = Zinc matt

range = 6

firetype = Oxidation

color = Turquoise

vistexture =

quality = Matt

transparency =

xtals = Small

bubbles =

flow = Extreme

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 18

component = Zinc oxide

amount = 8

component = Cornwall Stone

amount = 22

component = Soda spar

amount = 44

component = EPK

amount = 3

component = Bentonite

amount = 5

addition = Titanium dioxide

addamount = 4

addition = Copper carbonate

addamount = 4

note = |Good with Ash Fresca over Green Dragon.

note = |

name = Green Emerald

index =

date = 6/3/96

source =

type =

range = 6

firetype = Oxidation

color = Green

vistexture =

quality = gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 48

component = EPK

amount = 18.6

component = Silica

amount = 31.4

component = Soda ash

amount = 2

addition = Chrome oxide

addamount = 2

addition = Cobalt oxide

addamount = 1

note = |submitted by: Cindy Russell e-mail: crussel@tenetedu

name = Green Forrest

index =

date = 6/3/96

source =

type = Magnesium matt

range = 6

firetype = oxidation

color = Green

vistexture =

quality = satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 19

component = Whiting

amount = 3

component = Nepheline syenite

amount = 35

component = Ball clay

amount = 24

component = Silica

amount = 19

addition = chrome oxide

addamount = 2

addition = Cobalt carbonate

addamount = 1

note = |submitted by: Cindy Russell e-mail: crussel@tenetedu

name = Green Forrest

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color = Green

vistexture =

quality = satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 19

component = Whiting

amount = 3

component = Nepheline syenite

amount = 35

component = Ball clay

amount = 24

component = Silica

amount = 19

addition = Chrome oxide

addamount = 2

addition = Cobalt carbonate

addamount = 1

note = |submitted by: Cindy Russell e-mail: crussel@tenetedu

name = Green Glaze

index =

date = 01/19/2006

source =

type = Zinc matt

range = 5

firetype = Oxidation

color = Green

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 60

component = Calcium carbonate

amount = 8

component = Zinc oxide

amount = 16

component = Flint

amount = 16

addition = Macaloid

addamount = 1

addition = Nickel carbonate

addamount = 2

addition = Rutile

addamount = 4

note = |Clay Times NOv/Dec.05 p.52. OK for food.

note = |Use light rutile.

name = Green Hunter

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = Green

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Silica

amount = 8

component = Nepheline syenite

amount = 46

component = Spodumene

amount = 10

component = Kaolin

amount = 12

component = Dolomite

amount = 10

component = Gerstley borate

amount = 10

component = Zinc oxide

amount = 4

addition = Copper carbonate

addamount = 2.5

note = |cone 6? Electric Kiln Ceramics (latest volume). Marilyn at the Warwick

note = |Pottery Studio u1004425@

name = Green IE4E

index =

date = 4/3/95

source =

type =

range = 6

firetype = Ox. or Red.

color = Green

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 29.7

component = Silica

amount = 29.7

component = Barium carbonate

amount = 17.8

component = Gerstley borate

amount = 9.9

component = Ball clay

amount = 5.9

component = Whiting

amount = 4

component = Zinc oxide

amount = 0.5

component = Lithium carbonate

amount = 2.5

addition = Copper carbonate

addamount = 3

addition = Rutile

addamount = 5

addition = Zirconium silicate

addamount = 8.9

note = |omments: Shiny palmer green, darker where thick. ok. From Brian Kemp,

note = |Singapore, (kempb@nievax.nie.ac.sg)

name = GREEN MANNING

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = dark green

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Volcanic ash

amount = 34.91

component = Gerstley borate

amount = 7.55

component = Nepheline syenite

amount = 18.87

component = Whiting

amount = 16.04

component = Kaolin

amount = 16.98

component = Flint

amount = 5.66

addition = Copper oxide

addamount = 3.77

note = |(Richmond Potters' Club standard, unknown origin) (a very dark green

note = |matt - usually boring on it's own but excellent for over-dipping or

note = |otherwise slurping around. Also a good base glaze - the copper can be

note = |replaced with judicious amounts of other colourants, and they all

note = |make pleasant matt glazes.) Here are a couple of standards from the

note = |Richmond Potters Club, and a few of my own formulation that have

note = |worked well in ^6 oxidation. They aren't revolutionary (my exciting

note = |ones have things like barium in them, or are less predictable for a

note = |classroom situation) but they have been reliable, and allow for some

note = |play. They all calculate out to well within the INSIGHT limit

note = |formulas for maturity at ^6. If anyone tests these and comes up with

note = |problems, new ideas, good variations etc. could they let me know?

note = |I'll look forward to a larger list being posted to clayart. Veronica

note = |Shelford e-mail: shelford@ s-mail: P.O. Box 6-15 Thetis

note = |Island, BC V0R 2Y0 Tel: (250) 246-1509

name = Green Matt

index =

date = 12/7/96

source =

type =

range = 5

firetype =

color = green

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 40

component = Wollastonite

amount = 25

component = Spodumene

amount = 12

component = EPK

amount = 12

component = Silica

amount = 11

addition = Copper carbonate

addamount = 4

addition = Bentonite

addamount = 2

note = |The other day a matt turquoise glaze was posted on Clayart. I am

note = |suggesting that midfire potters not use this Maryland glaze for food

note = |containers. It doesn't have enough silica to keep the copper properly

note = |bound when faced with food acids. Adapting the same Seger formula,

note = |this recipe is more balanced. Only tests will show if these yield an

note = |acceptable colour and surface on your claybody. submitted by: Tom

note = |Buck e-mail: Tom.Buck@freenet.hamilton.on.ca or

note = |

note = |

name = Green Metal Patina Reynolds

index =

date = 08/04/2003

source =

type = Metallic

range = 6

firetype = Oxidation

color = Green metallic

vistexture =

quality =

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Lithium carbonate

amount = 39.02

component = Frit 3124

amount = 29.27

component = Flint

amount = 9.76

addition = Superpax

addamount = 19.51

addition = Copper carbonate

addamount = 2

name = Green Mexico Point

index =

date = 7/19/95

source =

type = Mid-fire

range = 6

firetype = Ox. or Red.

color = green

vistexture =

quality = matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 42.5

component = Spodumene

amount = 17.5

component = Pioneer kaolin

amount = 7.5

component = Dolomite

amount = 17.5

component = Gerstley borate

amount = 15

addition = Zircopax

addamount = 25

addition = Copper carbonate

addamount = 3.12

addition = Bentonite

addamount = 1.25

note = |It's cone 6, from

note = |Coopers Electric Kiln Ceramics, Vol.2, p122. Called 'Mexico Point

note = |Green'. It's a lovely soft matte green on the white burning stoneware

note = |I use. submitted by: Dan Taylor e-mail: dataylor@mlc.

name = Green Mexico Point

index =

date = 7/19/95

source =

type = Mid-fire

range = 6

firetype = Ox. or Red.

color = green

vistexture =

quality = matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 42.5

component = Spodumene

amount = 17.5

component = Pioneer kaolin

amount = 7.5

component = Dolomite

amount = 17.5

component = Gerstley borate

amount = 15

addition = Zircopax

addamount = 25

addition = Copper carbonate

addamount = 3.12

addition = Bentonite

addamount = 1.25

note = |It's cone 6, from

note = |Coopers Electric Kiln Ceramics, Vol.2, p122. Called 'Mexico Point

note = |Green'. It's a lovely soft matte green on the white burning stoneware

note = |I use. submitted by: Dan Taylor e-mail: dataylor@mlc.

name = Green Phila

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = green pools black

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 58

component = Strontium carbonate

amount = 26

component = Ball clay

amount = 10

component = Silica

amount = 5

component = Lithium carbonate

amount = 1

addition = Rutile

addamount = 4

addition = Copper carbonate

addamount = 4

addition = Bentonite

addamount = 4

addition = Epsom salts

addamount = 1

note = |kiln type: gas green pools black with some purplish highlights

note = |submitted by: John Anthony e-mail: JTRAX@

name = Green Phila

index =

date = 4/21/95

source =

type =

range = 6

firetype = reduction

color = green pools black

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 58

component = Strontium carbonate

amount = 26

component = Ball clay

amount = 10

component = Silica

amount = 5

component = Lithium carbonate

amount = 1

addition = Rutile

addamount = 4

addition = Copper carbonate

addamount = 4

addition = Bentonite

addamount = 4

addition = Epsom salts

addamount = 1

note = |kiln type: gas green pools black with some purplish highlights

note = |submitted by: John Anthony e-mail: JTRAX@

name = Green Randy's

index =

date = 4/3/98

source =

type =

range = 5 - 6

firetype = oxidation

color = dark green

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = F-4 feldspar

amount = 19.08

component = Potash feldspar

amount = 22.76

component = Kentucky OM #4

amount = 10.91

component = Silica

amount = 17.45

component = Strontium carbonate

amount = 13.63

component = Whiting

amount = 9.54

component = Dolomite

amount = 6.62

addition = Tin oxide

addamount = 4

addition = Copper carbonate

addamount = 6

note = |I got this copy of Randys Green at a workshop, where it was described

note = |as a C 10 glaze. It works very well as is at C 5-6 and is a deep

note = |forest green, slightly translucent. Occasionally I have underfired it

note = |to C4, where it becomes matte and slightly metallic and looks very

note = |nice. I hope this helps. Leslie lesaint1@

name = Green Sana (C6 revision)

index =

date = 12/7/96

source =

type = Magnesium matt

range = 6

firetype = Oxidation

color = yellowish green

vistexture =

quality = satin matte

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Feldspar

amount = 30

component = Whiting

amount = 10

component = Gerstley borate

amount = 12

component = Strontium carbonate

amount = 8

component = Magnesium carbonate

amount = 3

component = EPK

amount = 5

component = Silica

amount = 32

addition = Tin oxide

addamount = 3

addition = Copper carbonate

addamount = 5

addition = Rutile

addamount = 5

addition = Bentonite

addamount = 2

note = |Nice satin finish soft yellowish green

note = |that fit my clay body very well. It has a pretty low coefficient of

note = |expansion, and looks good, though not as yellowish, without the

note = |rutile. I know this doesn't add up to 100, but that's the way it was

note = |posted. Here it is. Good Luck, Paul Lewing, Seattle pjlewing@

note = |

name = Green Sana's (original formula)

index =

date = 12/7/96

source =

type = Magnesium matt

range = 6 - 10

firetype = Oxidation

color = green

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 30.01

component = Whiting

amount = 9.99

component = Colemanite

amount = 12

component = Barium carbonate

amount = 8

component = Magnesium carbonate

amount = 3

component = EPK

amount = 5

component = Silica

amount = 32

addition = Tin oxide

addamount = 3

addition = Copper carbonate

addamount = 5

addition = Rutile

addamount = 5

addition = Bentonite

addamount = 2.06

note = |A few people asked me for the *original* Sana's Green recipe, so here

note = |it is. Richard Gralnik

name = Green Sana's rev.

index =

date = 12/7/96

source =

type =

range = 4 - 7

firetype = ox. or red.

color = green

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 30.9

component = Whiting

amount = 10.3

component = Colemanite

amount = 12.4

component = Strontium carbonate

amount = 5.3

component = Magnesium carbonate

amount = 3.1

component = EPK

amount = 5.1

component = Silica

amount = 32.9

addition = Tin oxide

addamount = 3.1

addition = Copper carbonate

addamount = 5.1

addition = Rutile

addamount = 5.1

addition = Bentonite

addamount = 2.1

note = |glaze archive queen Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

note = |

name = Green Soft with Pink Flecks

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color = light green

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 67

component = Dolomite

amount = 10

component = EPK

amount = 8

component = Silica

amount = 9

component = Zinc oxide

amount = 6

addition = Copper carbonate

addamount = 3

note = |Exquisite light green gloss but no pink flecks Tested on Dillo White

note = |clay at a full ^6. submitted by: Lori Wilkinson e-mail:

note = |lorwilk@

name = Green Sombright 3

index =

date = 11/09/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Green

vistexture =

quality = Satin matt

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 42.45

component = Whiting

amount = 6.6

component = Strontium carbonate

amount = 29.25

component = Ball clay

amount = 12.26

component = Zinc oxide

amount = 9.43

note = |From Sally Brogden. Re-calc of Jeff Oestreich's cone 10 Sombright Green for cone 6.

name = Green Translucent Deep

index =

date = 4/21/95

source =

type =

range = 5 - 6

firetype = oxidation

color = deep green

vistexture =

quality =

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 50.24

component = Silica

amount = 25.12

component = Whiting

amount = 9.05

component = Dolomite

amount = 5.03

component = Gerstley borate

amount = 7.54

component = Zinc oxide

amount = 3.02

addition = Copper carbonate

addamount = 7.04

note = |originally suggested 7-10% copper carbonate. a deep green translucent

note = |that I like over white glazes, for a mottled, opaque effect. Also

note = |nice layered with cobalt blue glazes. I have found that many cone 10

note = |glazes will at least do something interesting at cone 6. Try it!

note = |source of original recipe: I adapted this off the base for Tom

note = |Coleman's cone 10 red. purple. submitted by: Sumi Dick e-mail:

note = |Sumi@

name = Green, Randy's

index =

date = 4/3/98

source =

type =

range = 5 - 6

firetype = oxidation

color = dark green

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = F-4 feldspar

amount = 19.08

component = Potash feldspar

amount = 22.76

component = Kentucky OM #4

amount = 10.91

component = Silica

amount = 17.45

component = Strontium carbonate

amount = 13.63

component = Whiting

amount = 9.54

component = Dolomite

amount = 6.62

addition = Tin oxide

addamount = 4

addition = Copper carbonate

addamount = 6

note = |I got this copy of Randys Green at a workshop, where it was described

note = |as a C 10 glaze. It works very well as is at C 5-6 and is a deep

note = |forest green, slightly translucent. Occasionally I have underfired it

note = |to C4, where it becomes matte and slightly metallic and looks very

note = |nice. I hope this helps. Leslie lesaint1@

name = Green-Black Pete's

index =

date = 02/29/2004

source =

type =

range = 6

firetype = Oxidation

color = Green

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3134

amount = 4.3

component = Nepheline syenite

amount = 29.3

component = Spodumene

amount = 27.2

component = Strontium carbonate

amount = 17.8

component = Grolleg

amount = 12

component = Silica

amount = 8

component = Lithium carbonate

amount = 1.4

addition = Copper carbonate

addamount = 5

addition = Titanium dioxide

addamount = 5

var = |3% copper + 5 % Ti = more green

var = |5% copper + 5% Ti = more black

note = |Variation on Pete Pinnell's Weathered Bronze. Black crystals, breaks black over

note = |edges and texture. A bit more matte. See Clay Times Mar/Apr. 2004 for article p.19.

name = Grey

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = grey

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = G-200 feldspar

amount = 47.9

component = Whiting

amount = 7.2

component = Barium carbonate

amount = 9

component = Zinc oxide

amount = 7.2

component = Talc

amount = 2.4

component = Ball clay

amount = 4.8

component = Silica

amount = 21.6

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse.

note = |

name = GTB Clear

index =

date = 7/19/95

source =

type =

range = 6

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 39

component = Gerstley borate

amount = 27

component = Silica

amount = 18

component = Whiting

amount = 8

component = EPK

amount = 8

note = |Slips (use GTB over these)(Coppen Light is a ball clay from HC

note = |Spinks) UBL-33 Black Coppen Light 50 Frit 3134 20 Mason 6600 30

note = |UBL-18 Blue Black Coppen Light 50 Neph Sy 10 Mason 6616 30

note = |Wollastonite 10 UBL-17 Seal Brown Coppen Light 40 Neph Sy 20 Mason

note = |6152 30 Wollastonite 10 UB-20 Cobalt Blue Coppen Light 60 Flint 20

note = |Mason 6316 20 UPR-13 Pansy Purple Coppen Light 40 Neph Sy 10 Mason

note = |6385 37.5 Wollastonite 12.5 UB-18 Teal Blue Coppen Light 60 Frit 3134

note = |30 Mason 6305 10 UG-35 French Green Coppen Light 50 Frit 3134 15

note = |Wollastonite 10 Mason 6219 25 UG-13 Coppen Green Coppen Light 40 Neph

note = |Sy 30 Copper Carb 15 Flint 10 Wollastonite 5 UG-18 Deep Turquoise

note = |Coppen Light 40 Neph Sy 10 Mason 6390 40 Wollastonite 10 UR-21

note = |Crimson Coppen Light 40 Frit 3134 20 Mason 6006 30 Wollastonite 10

note = |UPR-27 Lavender Coppen Light 50 Frit 3134 30 Mason 6319 20 UY-28

note = |TYitanium Yellow Coppen Light 50 Neph Sy 10 Frit 3134 10 Mason 6485

note = |30 UY-24 Yellow Coppen Light 50 Neph Sy 12.5 Mason 6481 25

note = |Wollastonite 12.5 UP-45 Hot Pink Coppen Light 50 Frit 3134 30 Mason

note = |6020 20 UP-33 Coral Coppen Light 50 Frit 3134 30 Neph Sy 5 Mason 6090

note = |35 UGR-9 Gray Coppen Light 40 Neph Sy 5 Wollastonite 10 Frit 3134 5

note = |Mason 6530 40 UW-1 White Coppen Light 30 Neph Sy 20 Frit 3134 10

note = |Wollastonite 10 Mason 6700 30 submitted by: Jonathan Kaplan e-mail:

note = |74034.3566@ source for original recipe: Wayne Bates

note = |

name = Gun Metal

index =

date = 08/03/2003

source =

type = Metallic

range = 6

firetype = ?

color = grey metallic

vistexture =

quality = metallic

transparency = opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit P-25

amount = 27

component = Gerstley borate

amount = 15

component = Spodumene

amount = 40

component = EPK

amount = 18

addition = Tin oxide

addamount = 6.8

addition = Copper carbonate

addamount = 4.8

name = Happy

index =

date = 06/07/00

source =

type = Mid-fire

range = 5

firetype = Oxidation

color = White

vistexture = Mottled

quality = Gloss

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 50

component = Ball clay

amount = 12

component = Dolomite

amount = 20

component = Bone ash

amount = 10

component = Lithium carbonate

amount = 8

addition = Rutile

addamount = 4

addition = Zircopax

addamount = 4

note = |From Shannon Nelson at Univ. of FL.

name = Honey Amber

index =

date = 8/8/97

source =

type =

range = 5 - 6

firetype =

color = clear yellow

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 20

component = Ferro frit 3134

amount = 20

component = Spodumene

amount = 20

component = Kentucky OM #4

amount = 20

component = Flint

amount = 20

addition = Bentonite

addamount = 2

addition = Manganese dioxide

addamount = 3

addition = Red iron oxide

addamount = 5

note = |I like this amber glaze. Works at cone 5 or 6. Originally came from

note = |the list I think. The tiny bubbles would add to the brew image.

note = |Lovely amber with some tiny bubbles, floating dust crystals, nice

note = |surface Janet Price, Chief Information Officer Carroll College,

note = |Waukesha WI 53186 jprice@.edu or jprice@.edu

note = |414-524-7120

note = |

name = Honey Lucas

index =

date = 06/04/2005

source =

type =

range = 6

firetype = Salt - Soda

color = Brown

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 11.8

component = Ball clay

amount = 29.4

component = Silica

amount = 29.4

component = Whiting

amount = 29.4

addition = Red iron oxide

addamount = 17.6

note = |From Julia Galloway in Clay Times May/Jn 2004.

name = HOPS #2

index =

date = 12/6/96

source =

type =

range = 6

firetype =

color = varies

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 30

component = Silica (325m)

amount = 20

component = Whiting (Hubercarb)

amount = 15

component = EPK

amount = 10

component = Gerstley borate

amount = 25

addition = Superpax (Tam)

addamount = 10

note = |^6 in sitter- average bend; on buff stoneware; no soaking; nice glaze

note = |but not too white, seemed more of a tan esp. where thin. not the rich

note = |fat white that would imitate majolica. my overglazes seemed to run

note = |and or bleed together alittle, can definitely see movement in them.

note = |glaze fits fine. these results were consistent on all 4 tiles. my

note = |overglazes were -by volume sea green stain 1 gerstley borate 1 deep

note = |crimson stain 1 gerstley borate 1 ball clay 1 Saturn orange stain 3

note = |gerst. borate 3 ball clay 1 the overglazes tend to seperate more when

note = |the base glaze is thicker on both test and at 04 at 04 they are

note = |excellent submitted by: Ed Brownlee e-mail: edware@umich.edu

note = |

name = IE 13 A

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = pale green/tan, darker

vistexture =

quality = Shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 36.36

component = Dolomite

amount = 18.18

component = Silica

amount = 18.18

component = Kaolin

amount = 18.18

component = Bone ash

amount = 5.45

component = Zinc oxide

amount = 3.64

addition = Copper carbonate

addamount = 1.82

note = |Very pale green/tan, darker where pooled, very nice. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 130 D

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = pale blue w/speckles

vistexture =

quality = dry matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 36.73

component = Nepheline syenite

amount = 59.19

component = Ball clay

amount = 4.08

addition = Tin oxide

addamount = 10.2

addition = Cobalt oxide

addamount = 0.51

note = |Dry glaze, pale blue with vivid blue speckles. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 149

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = brilliant pale yellow

vistexture =

quality = Dry matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 34.69

component = Silica

amount = 41.84

component = Whiting

amount = 17.35

component = Ball clay

amount = 6.12

addition = Praseodymium oxide

addamount = 10.2

addition = Zircon

addamount = 5.1

note = |Dry, brilliant pale yellow, good as a dry glaze. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 149

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = brilliant pale yellow

vistexture =

quality = Dry matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 34.69

component = Silica

amount = 41.84

component = Whiting

amount = 17.35

component = Ball clay

amount = 6.12

addition = Praseodymium oxide

addamount = 10.2

addition = Zircon

addamount = 5.1

note = |Dry, brilliant pale yellow, good as a dry glaze. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 157 PINK

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = red/pink, purple/mauve

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Nepheline syenite

amount = 16

component = Kaolin

amount = 11

component = Whiting

amount = 20

component = Silica

amount = 32

addition = Tin oxide

addamount = 5

addition = Chrome Oxide

addamount = 0.15

note = |Excellent red/pink, purple/mauve where thick. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 157 PINK

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = red/pink, purple/mauve

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Nepheline syenite

amount = 16

component = Kaolin

amount = 11

component = Whiting

amount = 20

component = Silica

amount = 32

addition = Tin oxide

addamount = 5

addition = Chrome Oxide

addamount = 0.15

note = |Excellent red/pink, purple/mauve where thick. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 2 A

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = cornflower blue, speckles

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 35.99

component = Barium carbonate

amount = 22.62

component = Silica

amount = 14.4

component = Gerstley borate

amount = 10.28

component = Zirconium silicate

amount = 9.25

component = Kaolin

amount = 5.14

component = Lithium carbonate

amount = 2.06

component = Zinc oxide

amount = 0.26

addition = Cobalt oxide

addamount = 1.54

addition = Rutile

addamount = 0.51

note = |Very nice semi matt mid to cornflower blue, speckles, paler blue

note = |where thinner, very good. From Brian Kemp, (kempb@nievax.nie.ac.sg)

note = |via Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware

note = |Fired at 100 degrees per hour to 600 degrees, then free for all to

note = |cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp, Nanyang Technological University, Block B,

note = |Room 216, 469 Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

note = |

name = IE 30 B

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = pale blue w/ speckles

vistexture =

quality = dry matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 36.73

component = Nepheline syenite

amount = 59.19

component = Ball clay

amount = 4.08

addition = Cobalt oxide

addamount = 0.51

note = |Dry, adhered, pale blue with vivid mid blue speckles. From Brian

note = |Kemp, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv.

note = |CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 30 F

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = off white to pale turquoise

vistexture =

quality = dry matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 36.73

component = Nepheline syenite

amount = 59.19

component = Ball clay

amount = 4.08

addition = Copper carbonate

addamount = 2.04

note = |Dry, adhered, pale off white to pale turquoise where thicker. From

note = |Brian Kemp, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp,

note = |Nanyang Technological University, Block B, Room 216, 469 Bukut Timah

note = |Rd., Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = IE 30 O

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = blue green?

vistexture =

quality = Dry matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 36.73

component = Nepheline syenite

amount = 59.19

component = Ball clay

amount = 4.08

addition = Titanium dioxide

addamount = 3.57

addition = Cobalt carbonate

addamount = 0.51

note = |No notes on this one. rd From Brian Kemp, (kempb@nievax.nie.ac.sg)

note = |via Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware

note = |Fired at 100 degrees per hour to 600 degrees, then free for all to

note = |cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp, Nanyang Technological University, Block B,

note = |Room 216, 469 Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

note = |

name = IE 30M

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = grey, green / orange yellow if

vistexture =

quality = Dry matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 36.73

component = Nepheline syenite

amount = 59.19

component = Ball clay

amount = 4.08

addition = Copper carbonate

addamount = 3.06

addition = Rutile

addamount = 3.06

note = |Dry glaze, grey, green tint, darker where thicker. Orange yellow

note = |where thin. Moderate aplication. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 30N

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = mid blue to dark blue

vistexture =

quality = Dry matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 38

component = Nepheline syenite

amount = 58

component = Ball clay

amount = 4

addition = Titanium dioxide

addamount = 3.5

addition = Cobalt oxide

addamount = 1.5

note = |Dry glaze, mid blue to dark blue where thick. Pale yellow where thin.

note = |From Brian Kemp, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp,

note = |Nanyang Technological University, Block B, Room 216, 469 Bukut Timah

note = |Rd., Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = IE 35

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = cream white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 45

component = Whiting

amount = 10

component = Zinc oxide

amount = 10

component = Kaolin

amount = 10

component = Silica

amount = 25

note = |Nice cream white, no craze, very nice. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 4

index =

date = 4/11/95

source =

type =

range = 6

firetype = oxidation

color = with 0.25 Cobalt Carbonate = st

vistexture =

quality = shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 27.4

component = Gerstley borate

amount = 9.13

component = Barium carbonate

amount = 16.44

component = Ball clay

amount = 5.48

component = Whiting

amount = 3.65

component = Lithium carbonate

amount = 1.83

component = Silica

amount = 27.4

component = Zinc oxide

amount = 0.46

component = Zirconium silicate

amount = 8.22

note = |kiln type: electric Color: with 0.25 Cobalt Carbonate = streaky

note = |cornflower blue, with 0.5 Cobalt Carbonate = strong streaky blue

note = |pleasant From Brian Kemp, Singapore, (kempb@nievax.nie.ac.sg) via

note = |Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired

note = |at 100 degrees per hour to 600 degrees, then free for all to cone

note = |6-7.

note = |CONTRIBUTOR: Brian Kemp Nanyang Technological University Block B,

note = |Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

name = IE 4 E

index =

date = 4/11/95

source =

type =

range = 6

firetype = oxidation

color = frosty, pastel, pale blue

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 38.46

component = Gerstley borate

amount = 9.62

component = Whiting

amount = 3.85

component = Lithium carbonate

amount = 1.92

component = Barium carbonate

amount = 17.31

component = Silica

amount = 28.85

addition = Copper carbonate

addamount = 1.92

addition = Tin oxide

addamount = 7.69

addition = Zirconium silicate

addamount = 11.54

note = |kiln type: electric nice From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 4 E

index =

date = 4/11/95

source =

type =

range = 6

firetype = oxidation

color = frosty, pastel, pale blue

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 38.46

component = Gerstley borate

amount = 9.62

component = Whiting

amount = 3.85

component = Lithium carbonate

amount = 1.92

component = Barium carbonate

amount = 17.31

component = Silica

amount = 28.85

addition = Copper carbonate

addamount = 1.92

addition = Tin oxide

addamount = 7.69

addition = Zirconium silicate

addamount = 11.54

note = |kiln type: electric nice From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 40

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = white

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 25.45

component = Zinc oxide

amount = 13.64

component = Gerstley borate

amount = 11.82

component = Kaolin

amount = 7.27

component = Silica

amount = 32.73

component = Magnesium carbonate

amount = 9.09

note = |Semi matt white, no craze, good. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 40

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = white

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 25.45

component = Zinc oxide

amount = 13.64

component = Gerstley borate

amount = 11.82

component = Kaolin

amount = 7.27

component = Silica

amount = 32.73

component = Magnesium carbonate

amount = 9.09

note = |Semi matt white, no craze, good. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 41

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = very white

vistexture =

quality = shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 38.46

component = Magnesium carbonate

amount = 4.4

component = Zinc oxide

amount = 14.29

component = Kaolin

amount = 3.3

component = Silica

amount = 39.56

note = |Very white, shiny, no craze, excellent. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 42

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = white

vistexture =

quality = shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 49

component = Lithium carbonate

amount = 3

component = Zinc oxide

amount = 11

component = Whiting

amount = 5

component = Kaolin

amount = 16

component = Silica

amount = 16

note = |Shiny white, no craze, good. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 43

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = pale coffee brown

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 26.32

component = Barium carbonate

amount = 41.05

component = Zinc oxide

amount = 15.79

component = Lithium carbonate

amount = 2.11

component = Silica

amount = 14.74

addition = Nickel Oxide

addamount = 4.21

note = |Semi matt, pale coffee brown with blue patches. good. From Brian

note = |Kemp, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv.

note = |CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 44

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = dark blue with paler blue

vistexture =

quality = Shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 27.37

component = Barium carbonate

amount = 25.26

component = Zinc oxide

amount = 28.42

component = Lithium carbonate

amount = 2.11

component = Silica

amount = 16.84

addition = Nickel Oxide

addamount = 4.21

note = |Shiny, nice dark blue with paler blue speckles, rust on edges, very

note = |nice. Uses nickel oxide? or carbonate? From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 45

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = beige/blue w/dark red/brown

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 21.88

component = Zinc oxide

amount = 21.88

component = Barium carbonate

amount = 31.25

component = Lithium carbonate

amount = 4.17

component = Kaolin

amount = 3.12

component = Silica

amount = 17.71

addition = Nickel Oxide

addamount = 4.17

note = |Semi matt, beige/blue with dark red/brown areas. Lighter blue

note = |speckles. Very nice, apply thickly for blue. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 49

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = white

vistexture =

quality = Shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 34.69

component = Whiting

amount = 17.35

component = Ball clay

amount = 6.12

component = Silica

amount = 41.84

note = |Shiny, clear white (on white clay) no craze, very good. From Brian

note = |Kemp, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv.

note = |CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 50

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = clear, transparent

vistexture =

quality = Shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 38.18

component = Zinc oxide

amount = 10.91

component = Kaolin

amount = 13.45

component = Silica

amount = 24.09

component = Whiting

amount = 13.36

note = |Very nice, clear shiny glaze, no craze, very good. From Brian Kemp,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp, Nanyang

note = |Technological University, Block B, Room 216, 469 Bukut Timah Rd.,

note = |Singapore, 1025 TEST SITE: Nanyang Technological University, Singapore

note = |

name = IE 52

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = dark green/blue

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 19

component = Whiting

amount = 3

component = Nepheline syenite

amount = 35

component = Ball clay

amount = 24

component = Silica

amount = 19

addition = Chromium oxide

addamount = 2

addition = Cobalt carbonate

addamount = 1

note = |Semi matt, dark green/blue with chocolate speckles, chocolate on

note = |edges, nice. From Brian Kemp, (kempb@nievax.nie.ac.sg) via Rose Downs

note = |on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100

note = |degrees per hour to 600 degrees, then free for all to cone 6-7. Kiln

note = |Size, Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian

note = |Kemp, Nanyang Technological University, Block B, Room 216, 469 Bukut

note = |Timah Rd., Singapore, 1025 TEST SITE: Nanyang Technological

note = |University, Singapore

note = |

name = IE 6

index =

date = 4/4/95

source =

type =

range = 6

firetype = oxidation

color = pale blue with darker flecks, da

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 33.15

component = Wollastonite

amount = 22.1

component = Gerstley borate

amount = 19.89

component = Ball clay

amount = 11.05

component = Barium carbonate

amount = 11.05

component = Lithium carbonate

amount = 2.76

addition = Zirconium silicate

addamount = 9.94

addition = Cobalt oxide

addamount = 1.1

note = |Kiln Type: kiln type: electric Color: pale blue with darker flecks,

note = |darker blue where pooled or thicker. From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE 68

index =

date = 4/4/95

source =

type =

range = 6

firetype = oxidation

color = nice coffee, pale brown with cr

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 56.18

component = Red clay

amount = 13.48

component = Wollastonite

amount = 5.62

component = Whiting

amount = 20.23

component = Magnesium carbonate

amount = 4.49

addition = Zirconium silicate

addamount = 12.36

addition = Red iron oxide

addamount = 6.74

note = |Kiln Type: electric Color: nice coffee, pale brown with cream

note = |speckles. very good From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE 76

index =

date = 4/4/95

source =

type =

range = 6

firetype =

color = very pale pink

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 46.43

component = Whiting

amount = 21.43

component = Gerstley borate

amount = 8.93

component = Lithium carbonate

amount = 17.86

component = Barium carbonate

amount = 5.36

addition = Silica

addamount = 78.55

addition = Tin oxide

addamount = 7.14

addition = Rutile

addamount = 5.36

note = |Kiln Type: electric From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE 77

index =

date = 4/4/95

source =

type =

range = 6

firetype = oxidation

color = dark orange brown.

vistexture =

quality = shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 40

component = Zinc oxide

amount = 4

component = Dolomite

amount = 3

component = Whiting

amount = 15

component = Kaolin

amount = 5

component = Silica

amount = 33

addition = Red iron oxide

addamount = 4

addition = Chrome Oxide

addamount = 0.5

note = |Kiln Type: electric good From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE 78

index =

date = 4/4/95

source =

type =

range = 6

firetype = oxidation

color = Cream white

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 46.67

component = Whiting

amount = 20

component = Zinc oxide

amount = 11.11

component = Dolomite

amount = 5.56

component = Kaolin

amount = 11.11

component = Silica

amount = 5.56

addition = Tin oxide

addamount = 4.44

note = |Kiln Type: electric nice. nice surface From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE 8

index =

date = 4/4/95

source =

type =

range = 6

firetype = oxidation

color = pale blue with darker flecks, t

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 32.26

component = Ball clay

amount = 21.51

component = Wollastonite

amount = 19.35

component = Gerstley borate

amount = 10.75

component = Barium carbonate

amount = 10.75

component = Zinc oxide

amount = 3.23

component = Lithium carbonate

amount = 2.15

addition = Zirconium silicate

addamount = 7.53

addition = Copper carbonate

addamount = 2.15

note = |Kiln Type: electric Color: pale blue with darker flecks, turquoise

note = |where thick From Brian Kemp, Singapore, (kempb@nievax.nie.ac.sg) via

note = |Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired

note = |at 100 degrees per hour to 600 degrees, then free for all to cone

note = |6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp Nanyang Technological University Block B,

note = |Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

note = |

name = IE 82

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = dark blue, even darker where th

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 39

component = Kaolin

amount = 5

component = Zinc oxide

amount = 18

component = Barium carbonate

amount = 28

component = Silica

amount = 10

addition = Nickel oxide

addamount = 1.5

note = |kiln type: electric good From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE 84

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = off white with a faint hint of

vistexture =

quality = shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 38.18

component = Kaolin

amount = 13.64

component = Whiting

amount = 13.64

component = Zinc oxide

amount = 10.91

component = Silica

amount = 23.64

addition = Tin oxide

addamount = 9.09

addition = Chrome oxide

addamount = 0.45

note = |kiln type: electric nice base glaze From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE 9

index =

date = 4/4/95

source =

type =

range = 6

firetype =

color = very pale off white-tan, orange

vistexture =

quality = semi matt/ matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 33.33

component = Wollastonite

amount = 22.22

component = Ball clay

amount = 22.22

component = Gerstley borate

amount = 10

component = Barium carbonate

amount = 8.89

component = Zinc oxide

amount = 0.56

component = Lithium carbonate

amount = 2.78

addition = Zirconium silicate

addamount = 11.11

addition = Copper carbonate

addamount = 2.22

note = |Kiln Type: electric Color: very pale off white-tan, orange specks

note = |where thin, pale green where thick, flashing on the edges. From Brian

note = |Kemp, Singapore, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = IE Black

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = black / brown

vistexture =

quality = shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 17

component = Nepheline syenite

amount = 34

component = Kaolin

amount = 8

component = Silica

amount = 41

addition = Iron oxide

addamount = 13

note = |Shiny black/brown, ok. From Brian Kemp, (kempb@nievax.nie.ac.sg) via

note = |Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired

note = |at 100 degrees per hour to 600 degrees, then free for all to cone

note = |6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp, Nanyang Technological University, Block B,

note = |Room 216, 469 Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

note = |

name = IE Red

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = pale yellow, green yellow

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 55.57

component = Whiting

amount = 24.44

component = Zinc oxide

amount = 4.44

component = Kaolin

amount = 11.11

component = Silica

amount = 4.44

addition = Iron Oxide

addamount = 3.33

addition = Rutile

addamount = 3.33

note = |Semi matt pale yellow, green yellow where thicker, tiny brown flecks,

note = |ok. From Brian Kemp, (kempb@nievax.nie.ac.sg) via Rose Downs on

note = |ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100

note = |degrees per hour to 600 degrees, then free for all to cone 6-7. Kiln

note = |Size, Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian

note = |Kemp, Nanyang Technological University, Block B, Room 216, 469 Bukut

note = |Timah Rd., Singapore, 1025 TEST SITE: Nanyang Technological

note = |University, Singapore

note = |

name = IE105H

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = duck egg blue

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 60

component = Barium carbonate

amount = 24

component = Lithium carbonate

amount = 5

component = Kaolin

amount = 6

component = Silica

amount = 5

addition = Cobalt carbonate

addamount = 0.25

addition = Tin oxide

addamount = 8

note = |Semi matt, very nice buttery surface. Duck egg blue with darker

note = |specks From Brian Kemp, (kempb@nievax.nie.ac.sg) via Rose Downs on

note = |ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100

note = |degrees per hour to 600 degrees, then free for all to cone 6-7. Kiln

note = |Size, Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian

note = |Kemp, Nanyang Technological University, Block B, Room 216, 469 Bukut

note = |Timah Rd., Singapore, 1025 TEST SITE: Nanyang Technological

note = |University, Singapore

note = |

name = IE170

index =

date = 4/10/95

source =

type =

range = 6

firetype =

color = white

vistexture =

quality = semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 33.9

component = Dolomite

amount = 16.95

component = Bone ash

amount = 5.08

component = Zinc oxide

amount = 3.39

component = Kaolin

amount = 8.47

component = Silica

amount = 19.49

component = Whiting

amount = 4.24

component = Zirconium silicate

amount = 8.47

note = |A nice, stable, semi matt white. A typical dolomite response to gosu-

note = |grey with yellow speckles in places, good From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE27A/H

index =

date = 4/3/95

source =

type =

range = 6

firetype = Ox. or Red.

color = very pale, warm green w/pink flecks

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 67

component = Dolomite

amount = 10

component = Kaolin

amount = 8

component = Silica

amount = 9

component = Zinc oxide

amount = 6

addition = Iron Oxide

addamount = 2

addition = Copper carbonate

addamount = 1.5

note = |omments: very pale, warm green with pink flecks. From Brian Kemp,

note = |Singapore, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = IE27A/I

index =

date = 4/3/95

source =

type =

range = 6

firetype = Ox. or Red.

color = medium tan

vistexture =

quality = shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 67

component = Dolomite

amount = 10

component = Kaolin

amount = 8

component = Silica

amount = 9

component = Zinc oxide

amount = 6

addition = Iron Oxide

addamount = 2

addition = Chrome Oxide

addamount = 1

note = |omments: shiny, mid tan. From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE27A/O

index =

date = 4/3/95

source =

type =

range = 6

firetype =

color = medium blue w/ pink flecks

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 67

component = Dolomite

amount = 10

component = Kaolin

amount = 8

component = Silica

amount = 9

component = Zinc oxide

amount = 6

addition = Copper carbonate

addamount = 1.5

addition = Cobalt oxide

addamount = 0.25

note = |Mid blue with Pink flecks. I began to notice some similar glazes, so,

note = |I will list the main glaze recipe and the variations in the comments

note = |section. From Brian Kemp, Singapore, (kempb@nievax.nie.ac.sg) via

note = |Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired

note = |at 100 degrees per hour to 600 degrees, then free for all to cone

note = |6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp Nanyang Technological University Block B,

note = |Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

note = |

name = IE3

index =

date = 4/3/95

source =

type =

range = 6

firetype = Ox. or Red.

color = variable (see comments)

vistexture =

quality = semi-matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 38.72

component = Whiting

amount = 29.04

component = Barium carbonate

amount = 13.55

component = Kaolin

amount = 11.62

component = Ball clay

amount = 4.84

component = Zinc oxide

amount = 0.29

component = Lithium carbonate

amount = 1.94

addition = Zirconium silicate

addamount = 8.71

note = |The base appears to be a semi matt. From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv.

note = |variations: IE3 A/4 - Copper Carbonate 3.0 -pale turquoise with

note = |green-brown flecks IE3 A/6 - Cobalt Oxide 0.5 - Blue White IE3 A/7 -

note = |Manganese Dioxide 2.0 - Pink Mauve IE3 A/C - Copper Carbonate 1.5 -

note = |Nice blue-green, pale w/ tan-yellow flck IE3 A/H - Iron Oxide 2.0,

note = |copper carbonate 1.5 - pale green w/ orange-brown flecks IE3 A/M -

note = |Rutile 2.0, Chrome Oxide 1.0 - mauve with deeper mauve flecks IE3 A/O

note = |- Copper Carbonate 1.5, Cobalt Oxide 0.25 - green blue breaking to

note = |pale blue IE3 A/R - Copper Carbonate 1.5, Manganese Dioxide 1 - tan

note = |green with brown flecks IE3 A/U - Cobalt Oxide 0.25, Manganese

note = |Dioxide 1 - pale grey blue with blue and pink flecks. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE30K

index =

date = 4/3/95

source =

type =

range = 6

firetype = Ox. or Red.

color = pink

vistexture =

quality = dry, matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 37.5

component = Nepheline syenite

amount = 58.33

component = Ball clay

amount = 4.17

addition = Blythe Red Glaze Stain

addamount = 10.42

note = |omments: Dry pink, ok. From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE4C

index =

date = 4/3/95

source =

type =

range = 6

firetype =

color = pale yellow

vistexture =

quality = shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 29.7

component = Silica

amount = 29.7

component = Barium carbonate

amount = 17.82

component = Gerstley borate

amount = 9.9

component = Ball clay

amount = 5.94

component = Whiting

amount = 3.96

component = Zinc oxide

amount = 0.5

component = Lithium carbonate

amount = 2.48

addition = Praseodymium oxide

addamount = 9.9

addition = Zirconium silicate

addamount = 8.91

note = |omments: shiny, pale yellow. good. From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = IE81

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = tan/brown with blue flecks, som

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 26

component = Barium carbonate

amount = 41.7

component = Lithium carbonate

amount = 3.1

component = Zinc oxide

amount = 12.5

component = Silica

amount = 16.7

addition = Bentonite

addamount = 4.2

note = |Color: tan/brown with blue flecks, some bright

note = |pink flecks. From Brian Kemp, Singapore, (kempb@nievax.nie.ac.sg) via

note = |Rose Downs on ClayArt listserv.

name = Indian Red

index =

date = 4/11/95

source =

type =

range = 6

firetype = Oxidation

color = brown

vistexture =

quality = Shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 40

component = Zinc oxide

amount = 4

component = Dolomite

amount = 3

component = Whiting

amount = 15

component = Kaolin

amount = 5

component = Silica

amount = 33

addition = Chrome Oxide

addamount = 0.5

addition = Iron Oxide

addamount = 4

note = |Shiny brown, quite nice. From Brian Kemp, (kempb@nievax.nie.ac.sg)

note = |via Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware

note = |Fired at 100 degrees per hour to 600 degrees, then free for all to

note = |cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp, Nanyang Technological University, Block B,

note = |Room 216, 469 Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

note = |

name = Indian Red 2nd Edition

index =

date = 4/21/95

source =

type =

range = 6

firetype = Oxidation

color = iron red brown

vistexture =

quality =

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 40

component = Zinc oxide

amount = 4

component = Dolomite

amount = 3

component = Whiting

amount = 15

component = China clay

amount = 5

component = Silica

amount = 33

addition = chrome oxide

addamount = 0.5

addition = Red iron oxide

addamount = 4

note = |In oxidation at cone 6 a deep red iron oxide red. In reduction at

note = |cone 6 a deep brown with a slight green tint at close inspection.

note = |source for the original recipe: Emmanuel Coopers Glaze books

note = |submitted by: J.D. e-mail: CLAYJUNKIE@

name = Indian Red 2nd Edition

index =

date = 4/21/95

source =

type =

range = 6

firetype = ox. or red.

color = iron red brown

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 40

component = Zinc oxide

amount = 4

component = Dolomite

amount = 3

component = Whiting

amount = 15

component = China clay

amount = 5

component = Silica

amount = 33

addition = chrome oxide

addamount = 0.5

addition = Red iron oxide

addamount = 4

note = |In oxidation at cone 6 a deep red iron oxide red. In reduction at

note = |cone 6 a deep brown with a slight green tint at close inspection.

note = |source for the original recipe: Emmanuel Coopers Glaze books

note = |submitted by: J.D. e-mail: CLAYJUNKIE@

name = Iron Red

index =

date = 12/7/96

source =

type = Iron Saturate

range = 6

firetype = Oxidation

color = iron red opaque

vistexture =

quality = gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 54.88

component = Talc

amount = 14.63

component = Flint

amount = 30.49

addition = Red iron oxide

addamount = 21.95

note = |Here is an Ox Blood Red that I've used in the past. Apply it HEAVILY

note = |for the best results. Cone 6 Oxidation. andrew s lubow

note = |

name = Jade Green

index =

date = 07/16/00

source =

type = Mid-fire

range = 4

firetype = Oxidation

color = Green

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 20

component = Gerstley borate

amount = 10

component = Talc

amount = 10

component = Whiting

amount = 10

component = Custer feldspar

amount = 40

component = Flint

amount = 10

addition = Copper carbonate

addamount = 5

note = |CM May 2000 p.102

name = Jade Green Base cone 5

index =

date = 09/11/98

source =

type =

range = 5-6

firetype = Oxidation

color = Clear

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 41

component = Strontium carbonate

amount = 20

component = EPK

amount = 10

component = Flint

amount = 10

component = Gerstley borate

amount = 10

component = Zinc oxide

amount = 9

var = |5% copper

var = |1% cobalt

var = |3% mn

name = Jade Green Matt

index =

date = 11/15/98

source =

type = Ba

range = 5

firetype = Oxidation

color = Opaque Blue Green

vistexture =

quality = Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash spar

amount = 40.1

component = barium carb

amount = 20

component = Kaolin

amount = 10.1

component = Flint

amount = 10

component = Gerstley borate

amount = 10

component = Zinc oxide

amount = 9.9

note = |Thin = brown/green. Thicker beautiful green. Also try stains. Not

note = |great for purples, bad for pinks. From George Bowes.

name = Jade Matte

index =

date = 10/06/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Green

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 40.4

component = Strontium carbonate

amount = 19.9

component = EPK

amount = 10

component = Silica

amount = 9.9

component = Gerstley borate

amount = 9.9

component = Zinc oxide

amount = 9.8

var = |vanadium ms 10

note = |Soft opaque satin matte. Good with other colorants. Tested with Laguna Borate

note = |subst for GB, and looks very similar.

name = JDB73

index =

date = 4/3/95

source =

type =

range = 6

firetype =

color = orange brown to light tan if thick

vistexture =

quality = shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro frit 3110

amount = 30

component = Soda feldspar

amount = 35

component = Whiting

amount = 10

component = Kaolin

amount = 10

component = Silica

amount = 10

component = Zinc oxide

amount = 5

addition = Tin oxide

addamount = 10

addition = Iron oxide

addamount = 4

note = |nice, shiny orange brown, light tan where thick. very nice From Brian

note = |Kemp, Singapore, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = JDB81

index =

date = 4/3/95

source =

type =

range = 6

firetype = Ox. or Red.

color = black

vistexture =

quality = shiny to semi-matt?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 47.06

component = Dolomite

amount = 17.65

component = Kaolin

amount = 11.76

component = Silica

amount = 23.53

addition = Manganese dioxide

addamount = 3.53

addition = Cobalt carbonate

addamount = 4.71

addition = Chrome Oxide

addamount = 1.18

addition = Iron Oxide

addamount = 1.18

note = |semi matt, shiny black. good From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = JDB84

index =

date = 4/3/95

source =

type =

range = 6

firetype = Ox. or Red.

color = blue

vistexture =

quality = shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 35.71

component = Whiting

amount = 12.24

component = Zinc oxide

amount = 24.49

component = Silica

amount = 22.45

component = Kaolin

amount = 5.1

addition = Cobalt carbonate

addamount = 1.53

note = |shiny, pleasant blue, darker where thicker. good From Brian Kemp,

note = |Singapore, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = JDB84A

index =

date = 4/3/95

source =

type =

range = 6

firetype = Ox. or Red.

color = dark blue green, darker blue thicker

vistexture =

quality = glossy, shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 35.71

component = Whiting

amount = 12.24

component = Zinc oxide

amount = 24.49

component = Silica

amount = 22.45

component = Kaolin

amount = 5.1

addition = Cobalt carbonate

addamount = 1.53

addition = Nickel (ox or carb?)

addamount = 1.53

note = |omments: dark blue-green, glossy. darker blue where thicker. good

note = |From Brian Kemp, Singapore, (kempb@nievax.nie.ac.sg) via Rose Downs

note = |on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100

note = |degrees per hour to 600 degrees, then free for all to cone 6-7. Kiln

note = |Size, Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian

note = |Kemp Nanyang Technological University Block B, Room 216 469 Bukut

note = |Timah Rd. Singapore, 1025 TEST SITE: Nanyang Technological

note = |University, Singapore

note = |

name = Karen's cone 6

index =

date = 10/14/98

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality = Gloss

transparency =

xtals =

bubbles = Many

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Flint

amount = 25.3

component = Strontium carbonate

amount = 4.9

component = Gerstley borate

amount = 21.1

component = Whiting

amount = 1.5

component = Custer spar

amount = 45

component = Grolleg clay

amount = 2.1

name = Karen's Glaze

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color = Turquoise

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 40

component = Dolomite

amount = 20

component = Flint

amount = 20

component = Kaolin

amount = 10

component = Bone ash

amount = 6

component = Zinc oxide

amount = 4

addition = Copper carbonate

addamount = 2

note = |Candice croeder1@

name = Karen't Starshine Cone 6

index =

date = 05/05/2006

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = K-200 feldspar

amount = 46

component = Soda ash

amount = 5

component = Gerstley borate

amount = 12

component = Whiting

amount = 10

component = Barium carbonate

amount = 5

component = Lithium carbonate

amount = 2

component = Flint

amount = 20

addition = Bentonite

addamount = 2

addition = Titanium dioxide

addamount = 4

addition = Copper carbonate

addamount = 5

note = |Cone 6 variation of high-fire glaze from Val Cushing.

name = Karen't Starshine Cone 6 no GB

index =

date = 05/05/2006

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda ash

amount = 10.758

component = Lithium carbonate

amount = 2

component = Wollastonite

amount = 10.581

component = Barium carbonate

amount = 5

component = Silica

amount = 39.417

component = Frit 3134

amount = 20.246

component = Alumina

amount = 8.215

addition = Bentonite

addamount = 2

addition = Titanium dioxide

addamount = 4

addition = Copper carbonate

addamount = 5

note = |Cone 6 variation of high-fire glaze from Val Cushing.

name = Kemp 1

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = cream white

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 45

component = Whiting

amount = 10

component = Zinc oxide

amount = 10

component = Kaolin

amount = 10

component = Silica

amount = 25

note = |A nice cream. No crazing. Very nice Brian Kemp. Singapore

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 10

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = Tan / orange

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 38.18

component = Zinc oxide

amount = 10.91

component = Kaolin

amount = 13.64

component = Silica

amount = 23.64

component = Whiting

amount = 13.64

addition = Chrome Oxide

addamount = 0.91

addition = Rutile

addamount = 0.91

note = |Shiny Tan/orange. Nice Brian Kemp. Singapore - kempb@nievax.nie.ac.sg

note = |tested on white stoneware CLAY COLOR/TYPE: Buff Stoneware Fired at

note = |100 degrees per hour to 600 degrees, then free for all to cone 6-7.

note = |Kiln Size, Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR:

note = |Brian Kemp Nanyang Technological University Block B, Room 216 469

note = |Bukut Timah Rd. Singapore, 1025 TEST SITE: Nanyang Technological

note = |University, Singapore

note = |

name = Kemp 11

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = Turquoise green

vistexture =

quality = Semi-Matte or Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 50

component = Spodumene

amount = 40

component = Gerstley borate

amount = 10

addition = Bentonite

addamount = 3

addition = Copper carbonate

addamount = 3

note = |Semi matt. Turquoise green. Paler on edges Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 12

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = white

vistexture =

quality = Semi-Matte or Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 37.74

component = Dolomite

amount = 18.87

component = Bone ash

amount = 5.66

component = Zinc oxide

amount = 3.77

component = Kaolin

amount = 12.26

component = Silica

amount = 21.7

note = |Semi matt white. Buttery surface Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 13

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = Yellow green

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 38.18

component = Zinc oxide

amount = 10.91

component = Kaolin

amount = 13.64

component = Silica

amount = 23.64

component = Whiting

amount = 13.64

addition = Titanium dioxide

addamount = 5

addition = Chrome Oxide

addamount = 1

note = |Yellow green. Paler on edges. Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 14

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = almost iron red to orange

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 32.5

component = Silica

amount = 24.17

component = Zinc oxide

amount = 8.33

component = Gerstley borate

amount = 8.33

component = Dolomite

amount = 15.83

component = Bone ash

amount = 10.83

addition = Red iron oxide

addamount = 10.83

note = |Almost an iron red. Orange where thick. Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 15

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = Pale blue w/ speckles

vistexture =

quality = dry matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 36.73

component = Nepheline syenite

amount = 59.19

component = Ball clay

amount = 4.08

addition = Cobalt oxide

addamount = 0.51

note = |Dry. Adhered well Pale blue with vivid mid blue speckles. Great for

note = |sculpture Brian Kemp. Singapore - kempb@nievax.nie.ac.sg tested on

note = |white stoneware CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees

note = |per hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = Kemp 16

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = white breaking to orange

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 45.45

component = Silica

amount = 33.33

component = Whiting

amount = 4.04

component = Talc

amount = 7.07

component = Kaolin

amount = 5.05

component = Soda ash

amount = 5.05

addition = Tin oxide

addamount = 10.1

note = |A nice 'shino-like' white breaking to orange Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 17

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype =

color = red / pink to Purple/mauve

vistexture =

quality = shiny glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Nepheline syenite

amount = 16

component = Kaolin

amount = 11

component = Whiting

amount = 20

component = Silica

amount = 32

addition = Tin oxide

addamount = 5

addition = Chrome oxide

addamount = 0.15

note = |Excellent red/pink. Purple/mauve where thick Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 18

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = pale blue to a turquoise

vistexture =

quality = dry matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 55.56

component = Barium carbonate

amount = 41.41

component = Zinc oxide

amount = 3.03

addition = Copper carbonate

addamount = 2.02

note = |A very nice dry glaze. Great for sculpture. Varying from a pale blue

note = |tint to a turquoise tint. Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 19

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = Mid grey/blue w/ yellow green flecks

vistexture =

quality = Dry Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 55.56

component = Barium carbonate

amount = 41.41

component = Zinc oxide

amount = 3.03

addition = Copper carbonate

addamount = 2.02

addition = Cobalt carbonate

addamount = 1.01

addition = Rutile

addamount = 5.05

note = |Dry. Mid grey/blue with yellow green flecks. Good for sculpture Brian

note = |Kemp. Singapore - kempb@nievax.nie.ac.sg tested on white stoneware

note = |CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = Kemp 2

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = white

vistexture =

quality = Semi-Matte or Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 25.45

component = Magnesium carbonate

amount = 9.09

component = Zinc oxide

amount = 13.64

component = Gerstley borate

amount = 11.82

component = Kaolin

amount = 7.27

component = Silica

amount = 32.73

note = |Semi matt white. No craze Excellent Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 20

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = pale blue where thin

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 5.05

component = Gerstley borate

amount = 10.1

component = Magnesium carbonate

amount = 5.05

component = Whiting

amount = 11.11

component = Potash feldspar

amount = 16.16

component = Soda feldspar

amount = 16.16

component = Ball clay

amount = 5.05

component = Silica

amount = 31.31

addition = Cobalt carbonate

addamount = 0.51

addition = Rutile

addamount = 3.03

note = |Shiny pale blue where thin. Nice streaky blue where thicker. Brian

note = |Kemp. Singapore - kempb@nievax.nie.ac.sg tested on white stoneware

note = |CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = Kemp 3

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = white w/ yellow patches

vistexture =

quality = stoney Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 33.33

component = Whiting

amount = 33.33

component = Ball clay

amount = 33.33

note = |Matt. Stony white with yellow patches. Orange flashing on the edges.

note = |Brian Kemp. Singapore - kempb@nievax.nie.ac.sg tested on white

note = |stoneware CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = Kemp 4

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = orange / tan

vistexture =

quality = Semi-Matte or Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 50

component = Dolomite

amount = 22.5

component = Kaolin

amount = 15

component = Bone ash

amount = 7.5

component = Lithium carbonate

amount = 2.5

component = Zinc oxide

amount = 2.5

addition = Iron Oxide

addamount = 2.5

addition = Chromium oxide

addamount = 1.25

note = |Semi matt orange/tan Brian Kemp. Singapore - kempb@nievax.nie.ac.sg

note = |tested on white stoneware CLAY COLOR/TYPE: Buff Stoneware Fired at

note = |100 degrees per hour to 600 degrees, then free for all to cone 6-7.

note = |Kiln Size, Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR:

note = |Brian Kemp Nanyang Technological University Block B, Room 216 469

note = |Bukut Timah Rd. Singapore, 1025 TEST SITE: Nanyang Technological

note = |University, Singapore

note = |

name = Kemp 5

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = soft green w/ pink flecks

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 67

component = Dolomite

amount = 10

component = Kaolin

amount = 8

component = Silica

amount = 9

component = Zinc oxide

amount = 6

addition = Copper carbonate

addamount = 3

note = |Shiny. Soft green with pink flecks. Very good Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 6

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = Green/ble breaking to pale blue

vistexture =

quality = Semi-Matte or Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 35.62

component = Whiting

amount = 26.71

component = Barium carbonate

amount = 12.47

component = Zinc oxide

amount = 0.27

component = Kaolin

amount = 10.69

component = Zirconium silicate

amount = 8.01

component = Ball clay

amount = 4.45

component = Lithium carbonate

amount = 1.78

addition = Copper carbonate

addamount = 1.34

addition = Manganese dioxide

addamount = 1.34

addition = Cobalt oxide

addamount = 0.22

note = |Semi matt. Green/ble breaking to pale blue Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kemp 7

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = Pale blue with darker flecks

vistexture =

quality = Semi-Matte or Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 22.35

component = Wollastonite

amount = 22.35

component = Gerstley borate

amount = 20.11

component = Ball clay

amount = 11.17

component = Barium carbonate

amount = 11.17

component = Zirconium silicate

amount = 10.06

component = Lithium carbonate

amount = 2.79

addition = Cobalt oxide

addamount = 1.12

note = |Semi matt. Pale blue with darker flecks. Darker blue where pooled or

note = |thick Brian Kemp. Singapore - kempb@nievax.nie.ac.sg tested on white

note = |stoneware CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = Kemp 8

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype =

color = dark orange/brown

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 40

component = Zinc oxide

amount = 4

component = Dolomite

amount = 3

component = Whiting

amount = 15

component = Kaolin

amount = 5

component = Silica

amount = 33

addition = Red iron oxide

addamount = 4

note = |Shiny dark orange/brown Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

note = |

name = Kemp 9

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype =

color = strong pink

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 34

component = Silica

amount = 41

component = Whiting

amount = 17

component = Kaolin

amount = 8

addition = Tin oxide

addamount = 10

addition = Chrome oxide

addamount = 0.5

note = |Shiny strong pink. Very good Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

note = |

name = Kendall Matt

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color = tan/orange

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 66.09

component = Lithium carbonate

amount = 2.91

component = Whiting

amount = 8.74

component = Talc

amount = 11.65

component = Magnesium carbonate

amount = 3.85

component = Gerstley borate

amount = 6.76

addition = Bentonite

addamount = 3.85

note = |For orange add 4.0% Rutile. Here a the glazes we've found work out

note = |OK, and are currently studio shop glazes. We have noticed that a

note = |slightly heavier reduction is needed for cone 6 than in cone 9/10.

note = |submitted by: Candice Roeder e-mail: CRoeder1@

note = |

name = Klinesville Gold (Jeff Dietrich)

index =

date = 4/7/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 4.49

component = Whiting

amount = 20.23

component = Wollastonite

amount = 5.62

component = Nepheline syenite

amount = 56.18

component = Cedar Heights Redart Clay

amount = 13.48

addition = Red iron oxide

addamount = 6.74

addition = Zircopax

addamount = 12.36

note = |Golden glaze to round out the palette and add warmth. This applied

note = |smoothly - was a smooth satin matt - color similar to old gold. They

note = |are dependable firing to firing in Cone 6 electric on dark clay. From

note = |Jeff Dietrich in Ceramics Montly, April 1991 & sent via ClayArt by

note = |Phyllis Nelson Baldwin City, Kansas E-mail: NELSON@george.bakeru.edu

note = |

name = Lavender Satin

index =

date = 6/24/97

source =

type =

range = 6 - 7

firetype =

color = lavender

vistexture =

quality = satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Flint

amount = 29.59

component = Gerstley borate

amount = 21.11

component = Nepheline syenite

amount = 12.32

component = Talc

amount = 11.83

component = Dolomite

amount = 11.83

component = Kentucky OM #4

amount = 8.28

component = Spodumene

amount = 5.03

addition = Cobalt carbonate

addamount = 2

note = |Nice differences tween thick and thin applications, and sort of

note = |periwinkle where it breaks over carved edges. Bob Kavanaugh, do you

note = |recognize this? It's the white satin you sent me about a year ago.

note = |I've been playing with it! Thanks for the recipe! Kat Neely-Jones

note = |Salem, Oregon solvejgma@

note = |

name = Lewing 5CL

index =

date = 12/6/96

source =

type =

range = 5

firetype = Ox. or Red.

color = clear transparent

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 26.18

component = Silica

amount = 25.28

component = EPK

amount = 14.04

component = Frit 3134

amount = 14.04

component = Whiting

amount = 10.23

component = Dolomite

amount = 5.62

component = Barium carbonate

amount = 4.61

note = |Parker Gloss and Gronborg Clear are very similar. I include both

note = |because the coefficient of expansion is just different enough for you

note = |to tell which way to go if they do not fit your body. And, yes, I

note = |know they all have barium in them. Not much, though, so you could

note = |probably substitute 3/4 as much strontium carb, and not affect them

note = |much, or possibly just leave it out. I hope this helps. Paul Lewing

note = | pjlewing@

note = |

name = Lichen Bell's

index =

date = 12/26/2006

source =

type = Lichen

range = 6-8

firetype = Oxidation

color =

vistexture =

quality = Lichen

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 31

component = Talc theoretical

amount = 8

component = Zinc oxide

amount = 6

component = Frit P-25

amount = 6

component = Soda spar

amount = 30

component = Kaolin

amount = 19

note = |To achieve a cracked-earth effect, some cracks should show before

note = |firing.

note = |

name = Lichen Bell's

index =

date = 12/26/2006

source =

type = Lichen

range = 6-8

firetype = Oxidation

color =

vistexture =

quality = Lichen

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 31

component = Talc theoretical

amount = 8

component = Zinc oxide

amount = 6

component = Frit P-25

amount = 6

component = Soda spar

amount = 30

component = Kaolin

amount = 19

note = |To achieve a cracked-earth effect, some cracks should show before firing.

name = Lichen Glaze

index =

date = 9/20/95

source =

type =

range = 6

firetype = Ox. or Red.

color = Opaque White

vistexture =

quality = Texture

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 30

component = Magnesium carbonate

amount = 30

component = Ferro Frit 3134

amount = 10

component = Talc

amount = 10

component = Kaolin

amount = 20

note = |A few years ago I participated in a workshop with Randy Brodnax who

note = |works with lichen glazes, among other techniques. His recipes follow.

note = |We covered the bisqued pot with the black englobe, (brushed on) and

note = |then dipped the pot in the lichen glaze. Then colored commercial

note = |underglazes were sprayed on the glaze. Wonderful effects. The black

note = |engobe gives better contrast with the lichen glaze. I also tried the

note = |lichen glaze both over and under my regualr cone six glazes, some

note = |very interesting, very nice effects. try it. submitted by: Kathy

note = |Darby e-mail: kdarby@ source for original recipe: Randy Brodnax

note = |

name = Light Blue

index =

date = 12/6/96

source =

type =

range = 5, 6, 7, 8

firetype = Ox. or Red.

color =

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro Frit 3124

amount = 75

component = EPK

amount = 12.5

component = Potash feldspar

amount = 12.5

addition = Zircopax

addamount = 25

addition = Cobalt carbonate

addamount = 0.62

note = |submitted by: Ken on Cape Cod e-mail: ktighe@

note = |

name = Light Peach

index =

date = 6/3/96

source =

type =

range = 6

firetype = Ox. or Red.

color = pale pink, peach

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 46

component = EPK

amount = 16

component = Silica

amount = 38

addition = Rutile

addamount = 10

note = |Used powdered rutile. Here's a peach I've developed; maybe it will

note = |give you a starting point. Be sure to try it at different

note = |thicknesses. I've fired it from cone 5-8 with best results at a high

note = |cone 6 or low 7. Can get runny at 7 if applied too thick. Good luck!

note = |submitted by: Darlene Yarnetsky -- Mudcat Pottery Madison IN e-mail:

note = |jyarnet@ideanet.doe.state.in.us

note = |

name = Lisa's Favorite

index =

date = 12/7/96

source =

type =

range = 6

firetype = Ox. or Red.

color =

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 47.3

component = Gerstley borate

amount = 27

component = Silica

amount = 20.3

component = EPK

amount = 5.4

addition = Red iron oxide

addamount = 2

addition = Cobalt oxide

addamount = 1

addition = Rutile

addamount = 4

note = |I'd like to take my favorite ^6 glaze and translate it to ^06 or ^04,

note = |but I don't really know how. Would some of y'all who have recipe

note = |software try this one and see what you come out with? Thanks. TIA

note = |from Greensboro, NC lisa

note = |

name = Lois Marcet

index =

date = 11/15/98

source =

type = Ca Li

range = 4 - 5

firetype = Oxidation

color = White

vistexture =

quality = Smooth Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Lepidolite

amount = 1200

component = Oxford spar

amount = 4000

component = Calcined kaolin

amount = 800

component = Whiting

amount = 1200

component = Flint

amount = 800

note = |Satin, silky smooth semi opaque white. (doubtful) 5/9/61 Glaze Type:

note = |Ca Li. Opacity: Semi-Opaque. Firing type: Oxidation .

note = |

note = |

name = Lydahl 1

index =

date = 11/15/98

source =

type = Ba Ca

range = 5

firetype = Ox or Red

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 Spar

amount = 53

component = Whiting

amount = 6

component = Strontium carbonate

amount = 19

component = Frit 3124

amount = 5

component = Clay

amount = 5

component = Flint

amount = 11

addition = Copper Carb

addamount = 2

note = |Smooth polished marble type base, semi-opaque. Copper gives

note = |blue, Manganese a pink violet and iron a yellow straw.

note = |

note = |Colors in Ox or Red? Glaze Type: Ba Ca. Opacity: Semi-opaque. Firing

note = |type: Ox or Red .

name = Lydahl 2

index =

date = 11/15/98

source =

type = Ca Pb RawLead AlMatt

range = 5

firetype = Oxidation

color = white base

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 Spar

amount = 1778

component = Whiting

amount = 445

component = White Lead

amount = 3555

component = Kaolin

amount = 1334

component = Flint

amount = 889

note = |Semi-opaque. Tends to go a little shiny where thin and almost

note = |transparent. Very good matt where thicker. Glaze Type: Ca Pb RawLead

note = |AlMatt. Opacity: Semi-opaque. Firing type: Oxidation .

note = |

name = Lydahl 2 LEAD

index =

date = 11/15/98

source =

type = Ca Pb RawLead AlMatt

range = 5

firetype = Oxidation

color = white base

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 spar

amount = 22.2

component = Whiting

amount = 5.6

component = White lead

amount = 44.4

component = Kaolin

amount = 16.7

component = Flint

amount = 11.1

note = |Semi-opaque. Tends to go a little shiny where thin and almost

note = |transparent. Very good matt where thicker. Glaze Type: Ca Pb RawLead

note = |AlMatt. Opacity: Semi-opaque. Firing type: Oxidation .

name = Lydahl 3

index =

date = 11/15/98

source =

type = Ca Zn Mg Na AlMatt

range = 5

firetype = Ox or Red

color =

vistexture =

quality = Smooth Dry Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline Sye

amount = 50

component = Dolomite

amount = 15

component = Whiting

amount = 2

component = Zinc oxide

amount = 8

component = Clay

amount = 15

component = Flint

amount = 10

note = |White opaque smooth dry mat. Color tends to go flat, very dense

note = |glaze.

note = |

note = |Glaze name originally listed as "Lydahl???" Is it really a Lydahl

note = |glaze? TD Glaze Type: Ca Zn Mg Na AlMatt. Opacity: Opaque. Firing

note = |type: Ox or Red .

name = Majolica c5 version H

index =

date = 11/25/98

source =

type = Majolica

range = 5

firetype = Oxidation

color = White

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Gerstley borate

amount = 10

component = Frit 3134

amount = 14

component = Custer spar

amount = 28

component = Wollastonite

amount = 20

component = EPK

amount = 28

addition = Zircopax

addamount = 18.072

addition = Bentonite

addamount = 2.41

name = Majolica Cone 5 VersionA

index =

date = 11/25/98

source =

type = Majolica

range = 5-6

firetype = Oxidation

color = White

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 10

component = Frit 3134

amount = 10

component = Custer spar

amount = 25

component = Silica

amount = 19

component = EPK

amount = 18

component = Dolomite

amount = 6

component = Wollastonite

amount = 12

addition = Zircopax

addamount = 15

note = |From Suzanne Storer in Ogden, UT sstorer@utah-

name = Majolica cone 6

index =

date = 01/31/01

source =

type = Majolica

range = 6

firetype = Oxidation

color = White

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Gerstley borate

amount = 16.5

component = Nepheline syenite

amount = 13

component = EPK

amount = 9.1

component = Whiting

amount = 15.6

component = Flint

amount = 25.7

component = Zircopax

amount = 20

note = |Add CMC gum if needed to harden the surface. Reported to fit cone 10

note = |porcelain fired to cone 6. Use 50 stain/50 frit over. Add CMC or

note = |liquid starch for better brushing.

note = |

note = |On Arbuckle majolica handout.

name = Majolica cone 6 No GB

index =

date = 01/31/01

source =

type = Majolica

range = 6

firetype = Oxidation

color = White

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Whiting

amount = 13.4

component = Custer feldspar

amount = 3.5

component = EPK

amount = 7.4

component = Flint

amount = 13.9

component = Zircopax

amount = 20

component = Frit 3124

amount = 32.6

note = |Re-calculated to eliminate GB. Untested.

note = |

note = |Add CMC gum if needed to harden the surface. Reported to fit cone 10

note = |porcelain fired to cone 6. Use 50 stain/50 frit over. Add CMC or

note = |liquid starch for better brushing.

note = |

note = |On Arbuckle majolica handout.

name = Majolica Midrange 2

index =

date = 11/15/98

source =

type = Ca B Majolica

range = 5 - 6

firetype = Oxidation

color = White

vistexture =

quality = Semi-Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Pemco frit P-54

amount = 27.3

component = Nepheline syenite

amount = 4.1

component = Calcined kaolin

amount = 8.6

component = EPK

amount = 10.1

component = Whiting

amount = 19.7

component = Flint

amount = 30.1

addition = Zircopax

addamount = 25

note = |Variation of Mid-range Majolica that replaces Gerstley borate with a

note = |frit to eliminate surface blemishes of the overglaze majolica

note = |colorants. Ferro Frit 3134 can be substituted for Pemco Frit P-54.

note = |Good as a majolica-like opaque white glaze with oxides and stains

note = |brushed over it. Very stable - does not run, applies well with a

note = |brush or by other methods. Doesn't craze on cone 10 porcelain fired

note = |to cone 6 - test on cone 6 body. Tested on Aardvark stoneware clays:

note = |(listed best to worst for smooth surface) Porcelain, Hopkins White

note = |60, Joe Soldate 60, Rio Red (the last two may have a fairly gritty

note = |surface, even at cone 6). Possible Glaze Flaws: This glaze is fairly

note = |powdery without any binder. It will crawl slightly if applied too

note = |thickly followed by a wash of color on the raw glaze. YOU MUST add

note = |CMC to glaze batch to harden the raw surface of this glaze. Use about

note = |one tablespoon of CMC powder (soaked in a pint of hot water

note = |overnight) per 3000 gram batch. Colors: Use mason stains mixed 50/50

note = |with Pemco frit P-25 or Ferro Frit 3124, or use 70 stain/30 gerstley

note = |borate in a watery mix for colors over glaze or some combination of

note = |gerstley borate and frit. Using too much gerstley borate may make the

note = |stain change color or become pastel. Purple stains may need to have

note = |more flux added up to 3 parts flux to 1 part stain. If you use all

note = |frit, add liquid starch or CMC to colors for easier brushing and to

note = |minimize smearing before they're fired. A small amount of bentonite

note = |may also help to keep the all-frit mixture from settling out. These

note = |binders are not as necessary with the gerstley borate. Use these

note = |Duncan EZ-stroke transparent underglazes as overglaze wash for color:

note = |EZ003, EZ004, EZ007, EZ012, EZ014, EZ019, EZ020, EZ021, EZ024, EZ025,

note = |EZ027, EZ028, EZ030, EZ032, EZ161. Almost all the other EZstrokes

note = |will work, especially if thinned slightly. The dark blue and the

note = |orange EZstrokes will wrinkle and get rough if applied too thickly.

note = |Cover coat CC 154 should work as well. Most other Cover Coat colors

note = |will work when thinly applied, but may be dry if thick. Try adding a

note = |teaspoonful of frit or gerstley borate to a jar of CC underglaze for

note = |glossier color. Other color possibilities include washes of the

note = |common colorants (mix chrome and rutile 50/50 with gerstley borate or

note = |frit). A thin red iron or red earthenware slip or possibly a red

note = |terra sigillata on the foot or other exposed clay areas makes a nice

note = |contrast if used on a white clay body. Richard Burkett 1991. Other

note = |color possibilities: A nice dark blue green with: 2% cobalt carb + 3%

note = |chrome oxide + 2% black iron oxide added to the glaze. SDSU 1992

name = Majolica Midrange 96

index =

date = 12/31/96

source =

type = Majolica

range = 5-7

firetype = Oxidation

color = White

vistexture =

quality = Gloss

transparency = Opaque

xtals = None

bubbles = None

flow = None

durability = Good

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 5.3

component = Nepheline syenite

amount = 33.1

component = EPK

amount = 4.6

component = Dolomite

amount = 2.3

component = Whiting

amount = 9.4

component = Flint

amount = 45.3

addition = Zircopax

addamount = 10.1

addition = Bentonite

addamount = 3.3

addition = Epsom salts

addamount = 0.6

note = | From Linda Litteral - SDSU Glaze class 1996. She called it 'A-7

note = |Chinese.' Tested for new Midrange majolica for class use. Almost

note = |boron free - good for stain colors that are subject to dissolving in

note = |boron glazes.

note = | Very stable, does not move during firing unless quite thick. Will

note = |crawl slightly if very thick. Applies well either by dipping or

note = |brushing.

note = | Works well with almost all Duncan EZ-Stroke underglaze colors as

note = |majolica washes, as do Amaco velvet red versions of the zirconium

note = |encapsulted red stains. Probably most stains would work well also.

note = |Color possibities: Use mason stains mixed 50/50 with Pemco frit P-25

note = |or Ferro Frit 3124, or use 70 stain/30 gerstley borate in a watery

note = |mix for colors over glaze or some combination of gerstley borate and

note = |frit. Using too much gerstley borate may make the stain change color

note = |or become pastel. Purple stains may need to have more flux added up

note = |to 3 parts flux to 1 part stain. If you use all frit, add liquid

note = |starch or CMC to colors for easier brushing and to minimize smearing

note = |before they're fired. Use these Duncan EZ-stroke transparent

note = |underglazes as overglaze wash for color: EZ003, EZ004, EZ007, EZ012,

note = |EZ014, EZ019, EZ020, EZ021, EZ024, EZ025, EZ027, EZ028, EZ030, EZ032,

note = |EZ161. Almost all the other EZstrokes will work, especially if

note = |thinned slightly. The darker blues EZstrokes will wrinkle and get

note = |rough if applied too thickly. CoverCoat CC 154 should work as well.

note = |Most other CoverCoat colors will work when thinly applied, but may be

note = |dry if thick. Try adding a teaspoonful of frit or gerstley borate to

note = |a jar of CC underglaze for glossier color.

note = | Other color possibilities include washes of the common colorants

note = |(mix chrome and rutile 50/50 with gerstley borate or frit). A thin

note = |red iron or red earthenware slip or possibly a red terra sigillata on

note = |the foot or other exposed clay areas makes a nice contrast if used on

note = |a white clay body.

note = |

note = |*Variations:

note = | Other color possibilities: A nice dark blue green with: 2% cobalt

note = |carb + 3% chrome oxide + 2% black iron oxide added to the glaze. Or

note = |almost any commercial stain added to the glaze in 5-12% amounts.

note = |

note = |*How long have you been using this glaze?

note = | About a year.

note = |

note = |*Where is it used?

note = | San Diego State University

note = |

note = |*Where did this recipe come from?

note = | From Linda Litteral - SDSU Glaze class 1996. She called it 'A-7

note = |Chinese.'

note = |

note = |*What do you like most about this glaze?

note = | very stable, good support for most stain colors

note = |

note = |*Is this glaze reliable?

note = | very, but like many majolica glazes it may crawl if applied too

note = |thickly.

note = |

note = |*Does this glaze tend to craze/crawl/pinhole/etc.?

note = | like many majolica glazes it may crawl if applied too thickly.

note = |

note = |*How do different firing temperatures/atmospheres affect the glaze?

note = | should work in oxidation or reduction firings, but not with all

note = |stain colors.

note = |

note = |*How does the glaze behave on different clay bodies?

note = | best on finer textured clays or smooth, well-ribbed surfaces if used

note = |on more heavily grogged clay bodies.

note = |

note = |*How thickly should the glaze be applied to the pot?

note = | medium (average) application for best opacity. may crawl if too

note = |thick.

note = |

note = |*How does this glaze interact with other glazes?

note = | should work with most other glazes like any typical white gloss

note = |glaze, due to the low boron content

note = |

note = |*What is your kiln type and size?

note = | Alpine Globar, approx 8 cu. ft.

note = |

note = |*How do you typically fire?

note = | 6-8 hour heating, 24-36 hour cooling, no soak.

note = |

note = |*Do you experience problems with the raw glaze?

note = | may settle badly without the bentonite/epsom salt addition. Adding a

note = |small amount of CMC gum solution may also help a bit and harden the

note = |raw glaze surface.

note = |

note = |*GlazeBase Glaze*

note = | Submitted by: Richard Burkett (richard.burkett@sdsu.edu)

note = | Ice Cream Flavor: Ben and Jerry's Pistachio

note = |

note = | --------------------------------------------------------------------

note = |----

name = Majolica Midrange 96 Revised

index =

date = 12/31/00

source =

type = Majolica

range = 5-7

firetype = Oxidation

color = White

vistexture =

quality = Gloss

transparency = Opaque

xtals = None

bubbles = None

flow = None

durability = Good

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 2.3

component = Whiting

amount = 8.7

component = Feldspar

amount = 35.8

component = EPK

amount = 5.8

component = Flint

amount = 35.7

component = Frit 3124

amount = 10.5

addition = Zircopax

addamount = 12

addition = Bentonite

addamount = 2

addition = Epsom salts

addamount = 0.6

note = |Revised to avoid using Gerstley Borate (no longer mined) and Neph Sy

note = |(deflocculates glaze)

note = |

note = |From Linda Litteral - SDSU Glaze class 1996. She called it 'A-7

note = |Chinese.' Tested for new Midrange majolica for class use. Almost

note = |boron free - good for stain colors that are subject to dissolving in

note = |boron glazes.

note = | Very stable, does not move during firing unless quite thick. Will

note = |crawl slightly if very thick. Applies well either by dipping or

note = |brushing.

note = | Works well with almost all Duncan EZ-Stroke underglaze colors as

note = |majolica washes, as do Amaco velvet red versions of the zirconium

note = |encapsulted red stains. Probably most stains would work well also.

note = |Color possibities: Use mason stains mixed 50/50 with Pemco frit P-25

note = |or Ferro Frit 3124, or use 70 stain/30 gerstley borate in a watery

note = |mix for colors over glaze or some combination of gerstley borate and

note = |frit. Using too much gerstley borate may make the stain change color

note = |or become pastel. Purple stains may need to have more flux added up

note = |to 3 parts flux to 1 part stain. If you use all frit, add liquid

note = |starch or CMC to colors for easier brushing and to minimize smearing

note = |before they're fired. Use these Duncan EZ-stroke transparent

note = |underglazes as overglaze wash for color: EZ003, EZ004, EZ007, EZ012,

note = |EZ014, EZ019, EZ020, EZ021, EZ024, EZ025, EZ027, EZ028, EZ030, EZ032,

note = |EZ161. Almost all the other EZstrokes will work, especially if

note = |thinned slightly. The darker blues EZstrokes will wrinkle and get

note = |rough if applied too thickly. CoverCoat CC 154 should work as well.

note = |Most other CoverCoat colors will work when thinly applied, but may be

note = |dry if thick. Try adding a teaspoonful of frit or gerstley borate to

note = |a jar of CC underglaze for glossier color.

note = | Other color possibilities include washes of the common colorants

note = |(mix chrome and rutile 50/50 with gerstley borate or frit). A thin

note = |red iron or red earthenware slip or possibly a red terra sigillata on

note = |the foot or other exposed clay areas makes a nice contrast if used on

note = |a white clay body.

note = |

note = |*Variations:

note = | Other color possibilities: A nice dark blue green with: 2% cobalt

note = |carb + 3% chrome oxide + 2% black iron oxide added to the glaze. Or

note = |almost any commercial stain added to the glaze in 5-12% amounts.

note = |

note = |*How long have you been using this glaze?

note = | About a year.

note = |

note = |*Where is it used?

note = | San Diego State University

note = |

note = |*Where did this recipe come from?

note = | From Linda Litteral - SDSU Glaze class 1996. She called it 'A-7

note = |Chinese.'

note = |

note = |*What do you like most about this glaze?

note = | very stable, good support for most stain colors

note = |

note = |*Is this glaze reliable?

note = | very, but like many majolica glazes it may crawl if applied too

note = |thickly.

note = |

note = |*Does this glaze tend to craze/crawl/pinhole/etc.?

note = | like many majolica glazes it may crawl if applied too thickly.

note = |

note = |*How do different firing temperatures/atmospheres affect the glaze?

note = | should work in oxidation or reduction firings, but not with all

note = |stain colors.

note = |

note = |*How does the glaze behave on different clay bodies?

note = | best on finer textured clays or smooth, well-ribbed surfaces if used

note = |on more heavily grogged clay bodies.

note = |

note = |*How thickly should the glaze be applied to the pot?

note = | medium (average) application for best opacity. may crawl if too

note = |thick.

note = |

note = |*How does this glaze interact with other glazes?

note = | should work with most other glazes like any typical white gloss

note = |glaze, due to the low boron content

note = |

note = |*What is your kiln type and size?

note = | Alpine Globar, approx 8 cu. ft.

note = |

note = |*How do you typically fire?

note = | 6-8 hour heating, 24-36 hour cooling, no soak.

note = |

note = |*Do you experience problems with the raw glaze?

note = | may settle badly without the bentonite/epsom salt addition. Adding a

note = |small amount of CMC gum solution may also help a bit and harden the

note = |raw glaze surface.

note = |

note = |*GlazeBase Glaze*

note = | Submitted by: Richard Burkett (richard.burkett@sdsu.edu)

note = | Ice Cream Flavor: Ben and Jerry's Pistachio

note = |

note = | --------------------------------------------------------------------

note = |----

name = Majolica Rozman

index =

date = 06/02/2004

source =

type = Majolica

range = 2-4

firetype = Oxidation

color = Clear

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 5

component = Frit 3124

amount = 40

component = Kona F-4 feldspar

amount = 15

component = Nepheline syenite

amount = 15

component = EPK

amount = 12

component = Flint

amount = 13

addition = Superpax

addamount = 12

addition = CMC

addamount = 10

note = |CMC gum is added as a solution of 15 grams CMA gum in 1 liter of water.

name = Majolica Vina's

index =

date = 10/11/2006

source =

type = Majolica

range = 6

firetype = Oxidation

color = White

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 34

component = Wollastonite

amount = 20

component = Kentucky OM #4

amount = 10

component = Gerstley borate

amount = 16

component = Flint

amount = 20

addition = Zircopax Plus

addamount = 15

var = |In place of zircopax, you can use 10% tin oxide. May cause chrome-tin pinking

var = |w/chrome colors

note = |From Vina Schemer VinaClay@

name = Maroon Cyndi's Satin

index =

date = 03/06/01

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Maroon

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ball clay

amount = 20

component = F-4 spar

amount = 50

component = Gerstley borate

amount = 10

component = Whiting

amount = 15

component = Flint

amount = 5

var = |Maroon: 10% Mason Blackberry Wine stain

note = |From Cyndi Gehr @ Univ. of FL

name = Mason Stain Mixture

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = UnderglazeStain

range = 5 - 6

firetype = Ox. or Red.

color = Varies

vistexture =

quality = Varies

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Mason Stain

amount = 60

component = Frit 3124

amount = 40

note = |From a handout bearing Anne Kraus' name. 'Stain can be painted on

note = |bisque ware, clear sprayed over.'

name = Matt Alkaline Base

index =

date = 06/27/2003

source =

type = Alkaline

range = 5-6

firetype = Ox. or Red.

color = White

vistexture =

quality = Matt

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 30

component = Frit 3110

amount = 25

component = Barium carbonate

amount = 10

component = Whiting

amount = 15

component = EPK

amount = 10

component = Flint

amount = 10

var = |Lt. Blue 1% copper carb

var = |Yellow w/Orange-greenish streaks (reduct) 5% RIO

var = |Pinkish-purple + 1% Mn Diox.

name = Matt base

index =

date = 12/7/96

source =

type =

range = 6

firetype = ox. or red.

color =

vistexture =

quality = waxy matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Neph Syenite

amount = 60

component = Barium carbonate

amount = 24

component = Lithium carbonate

amount = 5

component = EPK

amount = 6

component = Flint

amount = 5

note = |additions: Base no Additions White Matt Red Iron Oxide 3% Yellow Matt

note = |Copper Carb 2% Turqoise Matt Colbalt Carb 1% Sky Blue Matt Manganese

note = |Diox 2% Purple Matt Chrome Ox 2% Green (oxidized copper) Matt Nickel

note = |Ox 2% Grey Matt

note = |

name = Matt Base 5

index =

date = 6/4/96

source =

type = Ca Mg

range = 5 - 6

firetype = Ox or Red

color = SemiOpaque White

vistexture =

quality = Satin Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 40

component = Frit 3124

amount = 9

component = Talc

amount = 9

component = Whiting

amount = 16

component = EPK

amount = 10

component = Flint

amount = 16

note = |Glaze Type: Ca Mg. Firing type: Ox or Red. From Val Cushing. VC ed

note = |

name = Matt Base Hatch

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 40

component = Zinc oxide

amount = 15

component = China clay

amount = 20

component = Whiting

amount = 25

note = |Here are a couple of C 6 glazes that I use with my speckled

note = |brownstone in ox. A very even matt when well applied. Below C6 can be

note = |dry and scaly. The success of this glaze depends on the clay body. As

note = |stated from the book. I like the way it looks with Randy's Red and I

note = |have used it in combination with other colored glazes with good luck.

note = |submitted by: Jan Henkel e-mail: jhenkel@ source for

note = |original recipe: Electric Pottery by E. Cooper.

name = Matt BQ

index =

date = 6/3/96

source =

type = Magnesium matt

range = 6

firetype = oxidation

color =

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 10.9

component = Wollastonite

amount = 18.1

component = Nepheline syenite

amount = 36.2

component = EPK

amount = 18.1

component = Gerstley borate

amount = 16.7

var = |add 5% zircopax and 8% mason st. 6485 for a light, delicate yellow.

note = |I use a fairly dark clay body so your results may be quite different. good luck

note = |with the yellows. submitted by: Mary Kuilema e-mail: kuil@k2.

name = Matt Clear

index =

date = 12/6/96

source =

type =

range = 6 - 9

firetype =

color = translucent clear

vistexture =

quality = semi-matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 45.05

component = EPK

amount = 19.82

component = Dolomite

amount = 20.72

component = Whiting

amount = 5.41

component = Talc

amount = 9.01

note = |% Weight Ananlysis SiO2 56.94, P2O5 0.29, Al2O3 17.58, Fe2O3 0.29,

note = |MgO 8.82, CaO 12.07, Na2O 1.77, K2O 2.38. I regularly use a glaze at

note = |cone 8 over coloured slips which is matt but lets the coloured slips

note = |show through. This is in oxidation over a buff stoneware glaze. In

note = |case this sounds what you are after and interesting to you, I give

note = |the recipe below, which I have translated from the UK sourced

note = |materials that I use, into North American materials. Actually the

note = |difference is very small. submitted by: David Hewitt e-mail:

note = |david@dhpot.demon.co.uk

note = |

name = Matt Kendall

index =

date = 3/26/96

source =

type =

range = 6

firetype = reduction

color = tan/orange

vistexture =

quality = matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 66.09

component = Lithium carbonate

amount = 2.91

component = Whiting

amount = 8.74

component = Talc

amount = 11.65

component = Magnesium carbonate

amount = 3.85

component = Gerstley borate

amount = 6.76

addition = Bentonite

addamount = 3.85

var = |For orange add 4.0% Rutile.

note = | Here a the glazes we've found work out

note = |OK, and are currently studio shop glazes. We have noticed that a

note = |slightly heavier reduction is needed for cone 6 than in cone 9/10.

note = |submitted by: Candice Roeder e-mail: CRoeder1@

name = Matt Mammo

index =

date = 08/04/2003

source =

type = Magnesium matt

range = 5-6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 49

component = EPK

amount = 20

component = Whiting

amount = 4

component = Dolomite

amount = 19

component = Gerstley borate

amount = 17

addition = Zircopax

addamount = 10

var = |COLORANTS TO TRY:

var = |2 chrome ox

var = |1 cobalt

var = |1 manganese diox.

var = |2 iron

name = Matt purple/black

index =

date = 4/10/95

source =

type =

range = 5

firetype =

color = purple to black

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 75

component = Cornwall Stone

amount = 25

addition = Red iron oxide

addamount = 25

note = |Rob Wadey (robert wadey ) 9734B - 100 Ave

note = |Grande Prairie, Alberta t8V 0T6 Phone: (403) 538-3731 Fax: (403)

note = |538.3732

note = |

name = Matt Satin VC

index =

date = 06/27/2003

source =

type =

range = 5-6

firetype = Ox. or Red.

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 25

component = Frit 3124

amount = 25

component = Whiting

amount = 20

component = EPK

amount = 15

component = Flint

amount = 15

note = |Good base for color tests.

name = MATT SOFT ONE

index =

date = 4/10/95

source =

type =

range = 5 - 6

firetype = Oxidation

color = White

vistexture =

quality = matt

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 8.18

component = Flint

amount = 11.82

component = Gerstley borate

amount = 10

component = Kaolin

amount = 10

component = Lithium carbonate

amount = 4.55

component = Nepheline syenite

amount = 49.09

component = Zinc oxide

amount = 1.82

component = Cryolite

amount = 4.55

addition = Tin oxide

addamount = 1.82

addition = Zircopax

addamount = 4.55

note = |This produces a soft white matt glaze. One might wish to substitute

note = |strontium carbonate for the barium especially for use on functional

note = |ware. This glaze contains a great deal

note = |of lithium, such glazes may flake off of the ware and one should not

note = |use more then 5%. This is a high alumina glaze which

note = |shall have a rather modest glaze flow. It will be a soft white matt

note = |or a satin matt. Without barium it may be more towards the satin matt

note = |texture. Harold J. McWHINNIE Email:Harold_J_McWHINNIE@umail.umd.edu

name = Matt Stoney Base

index =

date = 06/02/2004

source =

type = Mid-fire

range = 2-4

firetype = Oxidation

color = White

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 20

component = Frit 3124

amount = 20

component = Tin oxide

amount = 30

component = EPK

amount = 15

component = Flint

amount = 15

var = |yellow = +5 iron

var = |blue-green= + .03 cobalt carb + 2 copper carb

note = |From Paul Rozman in CM

name = Matt Stony

index =

date = 08/04/2003

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 10

component = EPK

amount = 20

component = Zinc oxide

amount = 30

component = Dolomite

amount = 20

component = Kona F-4 feldspar

amount = 30

var = |Cream= RIO 1 + rutile 2

var = |Blue = rutile 2 + cobalt ox 0.5

var = |blue-green= rutile 2 + cobalt ox 0.5 + copper carb 3

note = |From Sandy Potash

name = Matt Super Dry

index =

date = 02/26/2002

source =

type = Mid-fire

range = 6

firetype = Ox. or Red.

color = Green

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 60

component = Strontium carbonate

amount = 15

component = Calcined kaolin

amount = 8

component = Flint

amount = 6

component = Lithium carbonate

amount = 6

component = Gerstley borate

amount = 5

addition = Copper carbonate

addamount = 3

var = |blue: cobalt 2

note = |from Mary Barranger

name = Matt Super Dry no GB

index =

date = 02/26/2002

source =

type = Mid-fire

range = 6

firetype = Ox. or Red.

color = Green

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 58.5

component = Strontium carbonate

amount = 14.8

component = Lithium carbonate

amount = 5.9

component = Kaolin

amount = 7.9

component = Flint

amount = 2.6

component = Frit 3195

amount = 9.3

addition = Copper carbonate

addamount = 3

var = |blue: cobalt 2

note = |from Mary Barranger

name = Matt V.C. 3

index =

date = 11/15/98

source =

type = Ca Zn AlMatt

range = 5 - 6

firetype = Ox or Red

color = Clear

vistexture =

quality = Satin Matt

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Custer feldspar

amount = 52

component = Whiting

amount = 19

component = Zinc oxide

amount = 9

component = EPK

amount = 14

component = Flint

amount = 6

note = | Glaze Type: Ca Zn AlMatt. Opacity: Semi-transparent. Firing type: Ox

note = |or Red .

name = Matt V.C. Polished

index =

date = 6/4/96

source =

type = Magnesium matt

range = 5 - 6

firetype = Ox or Red

color = Clear

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 20

component = Custer feldspar

amount = 20

component = Spodumene

amount = 20

component = Dolomite

amount = 20

component = Whiting

amount = 5

component = Kaolin

amount = 15

addition = Tin oxide

addamount = 6

note = |Nice. Glaze Type: Ca Mg AlMatt. Firing type: Ox or Red. From Val

note = |Cushing. VC ed

name = Matt Val's KK Revised True

index =

date = 11/25/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws = Crawls

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 2.9

component = Whiting

amount = 22.3

component = Nepheline syenite

amount = 22.6

component = EPK

amount = 25.3

component = Flint

amount = 15

component = Frit 3124

amount = 11.7

name = Matt Val's KK Revised True Revised

index =

date = 11/25/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws = Crawls

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 6.1

component = Whiting

amount = 19.2

component = Custer feldspar

amount = 32.5

component = Calcined kaolin

amount = 9.1

component = Kaolin - theoretical

amount = 15.9

component = Silica

amount = 9.8

component = Frit 3134

amount = 7.5

note = |Glaze in original form crawled. Revised to use dolomite instead of mag carb and to

note = |use part calcined kaolin.

name = Matte 1213P Calcium

index =

date = 6/3/96

source =

type = Mid-fire

range = 5

firetype = Ox. or Red.

color =

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wollastonite

amount = 33.88

component = Ferro Frit 3134

amount = 21.1

component = Kaolin

amount = 45.01

note = |Smooth, beautiful matte surface submitted by: Michelle Campbell

note = |e-mail: Lackacreek@ccinet.ab.ca source for original recipe: Plainsman

note = |Clays

name = Matte Black

index =

date = 9/20/95

source =

type =

range = 6

firetype =

color = black

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Alberta slip

amount = 70

component = Ferro frit 3124

amount = 20

component = Wollastonite

amount = 10

addition = Rutile

addamount = 5

addition = Mason Stain 6600

addamount = 5

addition = Bentonite

addamount = 2

note = |Here's a recipe I used just recently for a dinnerset and it works

note = |very well. Has a nice matte finish and is good for food surfaces. I

note = |experimented with increasing amounts of black stain (I think that's a

note = |mason #?..in any event, not the stain with the cobalt base) up to an

note = |additional 10% and they were all good. submitted by: Dan Taylor

note = |e-mail: dataylor@mlc.

name = Matte Deep Mauve

index =

date = 01/14/2003

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Lavender

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 48

component = Barium carbonate

amount = 25

component = Zinc oxide

amount = 15

component = Silica

amount = 6

component = Whiting

amount = 6

addition = Bentonite

addamount = 2

addition = Green nickel oxide

addamount = 2

note = |From Lana Wilson in Clay Times Jan/Feb. 2001 p 43. Mauve purple thick, navy

note = |blue specks where thin. richer on red clay. Refire to cone 06 to get gray and

note = |purple.

name = Matte Kathy King Satin

index =

date = 10/18/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 2.9

component = Magnesium carb

amount = 2.9

component = Whiting

amount = 22.4

component = Nepheline syenite

amount = 22.7

component = EPK

amount = 20.3

component = Flint

amount = 20

component = Frit 3124

amount = 8.8

var = |Grass green- 8 drakenfield yellow(or MS preseod yellow), 2 copper carb

var = |Medium green- 8 drakenfield yelow, 4 copper

var = |Pale green- 2 preseodemium yellow MS, .5 copper

var = |Pale yellow- 1 drakenfield yellow, .5 turquoise MS

var = |Pale blue- 1 sky blue MS, .2 copper carb

var = |Pale orange- .25 bright orange degusa stain

var = |Medium purple- 5 alpine rose MS, 4 cerulian MS

var = |(washes of MS and water are nice under the pale colors)

note = |Excellent base glaze. More shiny than matte. For true matte see Val's revised KK base

name = matte original c6

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = F-4 feldspar

amount = 45

component = Whiting

amount = 18

component = Kentucky OM #4

amount = 25

component = Zinc oxide

amount = 12

note = |FORMULA & ANALYSIS ------------------ *CaO........ .46 12.04%

note = |*MgO........ .01 .11% *K2O........ .06 2.53% *Na2O....... .12 3.50%

note = |*ZnO........ .36 13.49% Fe2O3...... .00 .32% TIO2....... .01 .42%

note = |AL2O3...... .37 17.61% SiO2....... 1.79 49.97% P2O5....... RATIO 4.82

note = |EXPAN 592.94 WEIGHT 214.43 I have test results for the original

note = |simple glaze and Ron's 2 complicated versions. All 3 glazes were

note = |tested on white and red stoneware, vertical and horizontal tiles.

note = |They were all fired in the bottom half of my Skutt to cone 6

note = |electric. The firing took approzimately 12 hours with a 1 hour soak

note = |at top temp. I added 2% rutile to all the glazes to test for color

note = |response, and used OM4 ball clay (instead of bell dark). I was

note = |somewhat surprised at how similar the glazes came out. The vertical

note = |tiles were virtually identical. All three were a soft gray opaque

note = |matt. My white stoneware has a little granular illmenite in it, and

note = |small spots bleed through. I double dipped 1/2 of each tile, and the

note = |glaze ran just a little. There was no discernable crazing. The

note = |horizontal tiles had noticable differences. These tiles were more

note = |mottled than the vertical ones, kind of like on oatmeal effect. The

note = |original glaze was a warmer gray than either of the 2 complex

note = |versions. The second complex version, where thick, was dry and

note = |sugary, and more silvery than either of the other 2. On all tiles,

note = |the red stoneware was more of a tan color than the white. Terri

note = |Storer storer@ Variations by Ron Roy: complicated

note = |version #1 ----------------- F4 SPAR 22.00 22.00% CUSTER SPAR 22.00

note = |22.00% WHITING 18.50 18.50% OM-4 Ball Clay 11.50 11.50% EPK 11.50

note = |11.50% ZINC OXIDE 12.00 12.00% SILICA 2.50 2.50% ---------- 100.00

note = |FORMULA & ANALYSIS ------------------ *CaO........ .46 12.02%

note = |*MgO........ .00 .09% *K2O........ .09 3.79% *Na2O....... .09 2.47%

note = |*ZnO........ .36 13.57% Fe2O3...... .00 .29% TIO2....... .01 .23%

note = |AL2O3...... .37 17.53% SiO2....... 1.80 49.98% P2O5....... .00 .02%

note = |RATIO 4.85 EXPAN 597.19 WEIGHT 215.75 My complicated version #2

note = |----------------- F4 SPAR............. 20.00 20.00% NEPH

note = |SY............. 20.00 20.00% WHITING............. 18.00 18.00% BELL

note = |DARK........... 11.00 11.00% EPK................. 11.00 11.00% ZINC

note = |OXIDE.......... 12.00 12.00% SILICA.............. 8.00 8.00%

note = |---------- 100.00 FORMULA & ANALYSIS ------------------ *CaO........

note = |.45 11.72% *MgO........ .01 .11% *K2O........ .05 2.21% *Na2O.......

note = |.13 3.77% *ZnO........ .36 13.53% Fe2O3...... .00 .26% TIO2.......

note = |.01 .22% AL2O3...... .38 17.68% SiO2....... 1.82 50.49% P2O5.......

note = |.00 .01% COST/KG 1.42 RATIO 4.85 EXPAN 584.18 WEIGHT 216.41 You post

note = |these to the list if you want - before or after you test them - what

note = |ever you like - but let me know what happenes and include all the

note = |recipes cause I don't keep em. Ron Roy 93 Pegasus Trail

note = |Scarborough,Canada M1G 3N8 Evenings, call 416 439 2621 Fax, 416 438

note = |7849 Studio: 416-752-7862. Email ronroy@astral.magic.ca Home page

note = |

name = Matte Robert Silverman

index =

date = 11/25/2001

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Green

vistexture =

quality = Matt

transparency = Opaque

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 57.1

component = Strontium carbonate

amount = 10.5

component = Barium carbonate

amount = 10.5

component = Lithium carbonate

amount = 4.8

component = Spodumene

amount = 4.8

component = Ball clay

amount = 7.6

component = Flint

amount = 4.8

addition = Copper carbonate

addamount = 2

addition = Chromium oxide

addamount = 3

note = |From Valerie Duncan. Glittery green over texture.

name = Matte Val's Awsome KK Revised

index =

date = 10/18/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 2.9

component = Magnesium carb

amount = 2.9

component = Whiting

amount = 22.4

component = Nepheline syenite

amount = 22.7

component = EPK

amount = 25.3

component = Flint

amount = 15

component = Frit 3124

amount = 8.8

var = |Eggshell- 2 rutile

var = |Dark purple- .5 cobalt, 4 Blackberry wine MS

var = |Sunny Yellow- 6 Preseodemium Yellow MS, 2.5 Bright orange degusa stain

var = |Cherry Red- 9 Red degusa stain

note = |Beautiful, rich, semi-translucent matte. Use same colorants as KK

name = Matte White

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = very white

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 38.7

component = Wollastonite

amount = 15.2

component = Barium carbonate

amount = 15.2

component = Silica

amount = 10.5

component = EPK

amount = 10.2

component = Gerstley borate

amount = 10.2

note = |kiln type: gas very white in oxidation, duller in reduction submitted

note = |by: John Anthony e-mail: JTRAX@

note = |

name = metallic black

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = metallic black

vistexture =

quality = shiny glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 50

component = Gerstley borate

amount = 25

component = Flint

amount = 25

addition = Black iron oxide

addamount = 10

addition = Cobalt oxide

addamount = 2

addition = Copper carbonate

addamount = 4

note = |(wonderful!) Here are a few black cone 6 glazes I gleaned from

note = |clayart. If you sub Strontium carb for the Barium in the second they

note = |will all be food safe. From Sharon LaRocca-Miranda via Mishy Michelle

note = |Lowe, potter in the Phoenix desert mishlowe@

note = |mishlowe@aztec.asu.edu

note = |

note = |

name = metallic black

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = metallic black

vistexture =

quality = shiny glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 50

component = Gerstley borate

amount = 25

component = Flint

amount = 25

addition = Black iron oxide

addamount = 10

addition = Cobalt oxide

addamount = 2

addition = Copper carbonate

addamount = 4

note = |(wonderful!) Here are a few black cone 6 glazes I gleaned from

note = |clayart. If you sub Strontium carb for the Barium in the second they

note = |will all be food safe. From Sharon LaRocca-Miranda via Mishy Michelle

note = |Lowe, potter in the Phoenix desert mishlowe@

note = |mishlowe@aztec.asu.edu

note = |

note = |

name = Metallic Matt Black

index =

date =

source =

type =

range = 6 - 9

firetype =

color = Opaque metallic Black

vistexture =

quality = Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wood ash

amount = 25

component = Nepheline syenite

amount = 37.5

component = Talc

amount = 18.75

component = Ball clay

amount = 18.75

addition = Iron oxide

addamount = 2.5

addition = Black copper oxide

addamount = 3.75

addition = Cobalt oxide

addamount = 2.92

note = |Other colors (delete black colorants): for matt brown with lots of

note = |texture add: Rutile 1.74 Iron Oxide 3.50 Manganese Dioxide 3.50 for

note = |matt blue breaking to something greenish add: Cobalt Carbonate 3.00

note = |Rutile 3.00 I've been using the same wood ash formula for about 10

note = |years and have used wood ash from all kinds of known and unknown tree

note = |sources (washed and unwashed), fired to cone 6, 7, 8, 9 but mostly to

note = |cone 7 in an electric kiln. Write me if you have any questions about

note = |these glazes submitted by: Anne Fallis-Elliott e-mail: FallisT@

name = Metallic Pewter Luster

index =

date = 05/19/2002

source =

type = Metallic

range = 6

firetype = Oxidation

color = Metallic pewter

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = China clay

amount = 100

addition = Copper oxide

addamount = 66

addition = Manganese dioxide

addamount = 300

note = |NOT food safe. From Glazes Cone 6 by Michael Bailey

name = Mexico Point Green

index =

date = 7/19/95

source =

type =

range = 6

firetype =

color = green

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 42.5

component = Spodumene

amount = 17.5

component = Pioneer kaolin

amount = 7.5

component = Dolomite

amount = 17.5

component = Gerstley borate

amount = 15

addition = Zircopax

addamount = 25

addition = Copper carbonate

addamount = 3.12

addition = Bentonite

addamount = 1.25

note = |I'm sending this to the group rather than directly because it's such

note = |a nice glaze some others might like to have it too. It's cone 6, from

note = |Coopers Electric Kiln Ceramics, Vol.2, p122. Called Mexico Point

note = |Green. It's a lovely soft matte green on the white burning stoneware

note = |I use. submitted by: Dan Taylor e-mail: dataylor@mlc.

note = |

name = Midnight Blue

index =

date = 6/3/96

source =

type =

range = 5 - 8

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Feldspar

amount = 44

component = Whiting

amount = 17

component = Ball clay

amount = 8

component = China clay

amount = 9

component = Silica

amount = 22

note = |translucency: Opaque Cobalt 5% for rich midnight blue. Superpax 10%

note = |for bright white, very good color response with on glaze stains.

note = |submitted by: Jo Ann Stevens e-mail: jstevens@ source for

note = |original recipe: Emanuel Cooper

note = |

name = Mirror Black

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color = mirror black

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 38.18

component = Zinc oxide

amount = 10.91

component = EPK

amount = 13.64

component = Silica

amount = 23.64

component = Whiting

amount = 13.64

addition = Red iron oxide

addamount = 7.27

addition = Cobalt carbonate

addamount = 1.82

note = |Yes, I know this does not equal 100%. A true glossy mirror black.

note = |Tested on Dillo White clay at a full ^6. submitted by: Lori Wilkinson

note = |e-mail: lorwilk@

note = |

name = MME

index =

date = 4/10/95

source =

type =

range = 6

firetype =

color = Pale pink

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 28.18

component = Whiting

amount = 18.18

component = Talc

amount = 9.09

component = Kaolin

amount = 26.36

component = Silica

amount = 9.09

component = Zinc oxide

amount = 9.09

addition = Tin oxide

addamount = 4.55

addition = Chrome oxide

addamount = 1.82

note = |Semi matt, Pale pink, good From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = MMI

index =

date = 4/10/95

source =

type =

range = 6

firetype =

color = apricot/beige

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 28.18

component = Whiting

amount = 18.18

component = Talc

amount = 9.09

component = Kaolin

amount = 26.36

component = Silica

amount = 9.09

component = Zinc oxide

amount = 9.09

addition = Chrome oxide

addamount = 1.82

addition = Cobalt carbonate

addamount = 0.23

note = |Semi matt, apricot/beige, even, good. From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = MMM

index =

date = 4/10/95

source =

type =

range = 6

firetype = oxidation

color = apricot/tan

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 28.18

component = Whiting

amount = 18.18

component = Talc

amount = 9.09

component = Kaolin

amount = 26.36

component = Silica

amount = 9.09

component = Zinc oxide

amount = 9.09

addition = Iron oxide

addamount = 0.45

addition = Chrome oxide

addamount = 1.82

note = |Semi matt, apricot/tan ok Darker than MMI From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = MMN

index =

date = 4/10/95

source =

type =

range = 6

firetype =

color = off white

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 28.18

component = Whiting

amount = 18.18

component = Talc

amount = 9.09

component = Kaolin

amount = 26.36

component = Silica

amount = 9.09

component = Zinc oxide

amount = 9.09

addition = Tin oxide

addamount = 4.55

addition = Manganese dioxide

addamount = 0.91

note = |Semi matt, off white, faint blue tinge where thicker, good From Brian

note = |Kemp, Singapore, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = MMO

index =

date = 4/10/95

source =

type =

range = 6

firetype = oxidation

color = pale yellow

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 28.18

component = Whiting

amount = 18.18

component = Talc

amount = 9.09

component = Kaolin

amount = 26.37

component = Silica

amount = 9.09

component = Zinc oxide

amount = 9.09

addition = Tin oxide

addamount = 4.55

addition = Praseodymium

addamount = 7.27

note = |Praseodymium not specified: oxide or stain? Very pale yellow on

note = |edges, stronger yellow tint where thicker From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

note = |

name = Mt St Helens Almond

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = yellowish

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 40

component = Zinc oxide

amount = 8.6

component = Whiting

amount = 14.9

component = EPK

amount = 11.8

component = Flint

amount = 4.7

component = Mount St. Helens Volcanic

amount = 20

addition = Rutile

addamount = 8

note = |The following is a Mt. St. Helens ash glaze from the Seattle area.

note = |recipe Makes 1 gal. Good luck! Wendy from Bainbridge Island WA

note = |whampton@

note = |

name = Mt. St. Helens Blue

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = blue

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 39.59

component = Flint

amount = 5.35

component = Whiting

amount = 14.08

component = EPK

amount = 11.57

component = Zinc oxide

amount = 8.17

component = Dolomite

amount = 0.44

component = Colemanite

amount = 0.88

component = Mount St. Helens Volcanic Ash

amount = 19.92

addition = Cobalt oxide

addamount = 0.1

note = |5000g recipe Makes 3 gal. Good luck! Wendy from Bainbridge Island WA

note = |whampton@

note = |

name = Mud Crack

index =

date = 12/6/96

source =

type = Texture

range = 3

firetype = oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 50

component = Nepheline syenite

amount = 20

component = Ferro Frit 3134

amount = 20

component = Gerstley borate

amount = 10

note = |Sharon Palmatory is seeking Coleman's crawl glaze, which he terms

note = |Mudcrack glaze. I have the answer, which is in Piepenburg's latest

note = |book: The Spirit of Clay. (see p. 126 if you can get hold of it.) I

note = |quote: The piece was first glaze fired to cone 5; re-glazed with a

note = |thick application of his Mud Crack overglaze (50 % magnesium

note = |carbonate, 20 % neph. syenite, 20% Ferro Frit 3134, and 10% Gerstley

note = |borate) and fired to cone 3. My suggestions are: try over a matte

note = |surface glaze. You mentioned a slip. I think it would have to be a

note = |very vitreous slip to work. Depending on your kiln, I have had better

note = |luck with a cone 2 in the sitter. or witness cone 3 at 9 oclock.. But

note = |all depends on the glaze underneath. Also, thick application means

note = |THICK or the texture is absorbed into the glaze. If spraying the

note = |mudcrack glaze, it is possible that it will crack and fall off the

note = |existing fired glaze!!. submitted by: Bacia Edelman e-mail:

note = |medelman@facstaff.wisc.edu source for original recipe: Robert

note = |Pipenburg

name = Name 1

index =

date = 11/15/98

source =

type = Ca B

range = 5 - 6

firetype = Ox or Red

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3124

amount = 60

component = Gerstley borate

amount = 10

component = Flint

amount = 10

component = EPK

amount = 10

component = Whiting

amount = 10

note = | Glaze Type: Ca B. Opacity: . Firing type: Ox or Red .

name = Name 2

index =

date = 11/15/98

source =

type = Na Ca Ba AlMatt

range = 5 - 6

firetype = Ox or Red

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline Sye

amount = 4000

component = Barium carbonate

amount = 800

component = Frit 3124

amount = 400

component = Whiting

amount = 400

component = Petalite

amount = 400

component = EPK

amount = 800

component = Flint

amount = 1200

note = |Copper Carbonate (2.0%) produces blue green, Chrome ( 1.0%) produces

note = |yellow green. Glaze Type: Na Ca Ba AlMatt. Opacity: . Firing type: Ox

note = |or Red .

note = |

name = Name 3

index =

date = 11/15/98

source =

type = Ca B

range = 5 - 6

firetype = Oxidation

color = Bright Yellow

vistexture =

quality = Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 4000

component = Barnard clay

amount = 2000

component = EPK

amount = 2000

note = | Glaze Type: Ca B. Opacity: Transparent. Firing type: Oxidation .

note = |

note = |

name = Name 4

index =

date = 11/15/98

source =

type = Ca B SlipGlaze

range = 5 - 6

firetype = Ox or Red

color =

vistexture =

quality = Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 4000

component = Albany

amount = 2000

component = EPK

amount = 2000

note = | Glaze Type: Ca B SlipGlaze. Opacity: Transparent. Firing type: Ox or

note = |Red .

note = |

note = |

name = NDVC

index =

date = 6/4/96

source =

type = Ca Li AlMatt

range = 5 - 6

firetype = Reduction

color = Semi-opaque greyish breaks white

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 40

component = Frit 3110

amount = 6

component = Dolomite

amount = 12

component = Whiting

amount = 14

component = EPK

amount = 12

component = Flint

amount = 16

note = |Iron (5.0%) gives yellow-brown, cobalt carbonate (1.0%) yields

note = |green-lavender to off-white. Glaze Type: Ca Li AlMatt. Firing type:

note = |Reduction. From Val Cushing. VC ed

note = |

name = new glaze

index =

date = 11/18/2002

source =

type =

range =

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

name = new glaze

index =

date = 12/26/2006

source =

type =

range =

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

name = new glaze

index =

date = 12/26/2006

source =

type =

range =

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

name = No. 92

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca Pb FritLead

range = 4 - 6

firetype = Oxidation

color =

vistexture =

quality = Glossy or shiny

transparency = Transparent to semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3304

amount = 29

component = Frit 3124

amount = 22

component = Custer feldspar

amount = 18

component = Whiting

amount = 12

component = Georgia kaolin

amount = 8

component = Flint

amount = 11

note = |Val Cushing: TESTED OK FOR FOOD.

name = No. 98

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca B MidRoad

range = 4 - 6

firetype = Ox. or Red.

color =

vistexture =

quality = Gloss

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Zinc oxide

amount = 3

component = Barium carbonate

amount = 9

component = Custer feldspar

amount = 37

component = Georgia kaolin

amount = 9

component = Flint

amount = 21

addition = Zircopax

addamount = 1.5

addition = Iron oxide

addamount = 1.5

addition = Milled Ilmenite

addamount = 1.5

note = |Val Cushing: TESTED OK FOR FOOD.

name = Nutmeg Richard Busch's

index =

date = 06/03/2005

source =

type = Lithium Matt

range = 6

firetype = Oxidation

color = Orange

vistexture = Speckled

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 23.3

component = Dolomite

amount = 23.3

component = Kentucky OM #4

amount = 23.3

component = Silica

amount = 23.3

component = Frit 3134

amount = 6.8

addition = Red iron oxide

addamount = 1.07

addition = Yellow ochre

addamount = 3.24

addition = Tin oxide

addamount = 4.85

addition = Bentonite

addamount = 2

note = |Clay Times Jan/Feb 05 p. 55. Apply thickly.

name = Nutmeg Richard's

index =

date = 02/06/2007

source =

type = Magnesium matt

range = 6

firetype = Oxidation

color = Brown

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 23.3

component = Spodumene

amount = 23.3

component = Kentucky OM #4

amount = 23.3

component = Silica

amount = 23.3

component = Frit 3134

amount = 6.8

addition = Red iron oxide

addamount = 1.1

addition = Yellow ochre

addamount = 3.2

addition = Tin oxide

addamount = 4.9

addition = Bentonite

addamount = 1.9

note = |From Bill Van Gilder

note = |

name = Oatmeal Pike's

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color = Tan

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 37.3

component = Colemanite

amount = 12.7

component = Dolomite

amount = 6.4

component = Talc

amount = 13.6

component = Kaolin

amount = 4.5

component = Silica

amount = 22.7

component = Zinc oxide

amount = 2.7

note = |Our Guild has a cone 6 recipe (originally from Connie Pike) which

note = |turns very purple if you add 2% cobalt oxide to it. You might try

note = |adapting it for higher temperatures. Good luck - purple and lilac

note = |sound very Eastery and springlike, which it is NOT, here in

note = |Yellowknife, NWT. submitted by: Autumn Downey e-mail:

note = |downeya@ source for original recipe: Connie Pike

name = Off-White Gloss

index =

date = 03/06/01

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = F-4 spar

amount = 45

component = Flint

amount = 24

component = Gerstley borate

amount = 13.3

component = Whiting

amount = 8.3

component = Dolomite

amount = 6.4

component = Zinc oxide

amount = 4

component = EPK

amount = 2.5

var = |+ 8% Mason #6129 Golden Ambrosia

name = Oil Spot

index =

date = 4/3/98

source =

type =

range = 5 - 9

firetype = oxidation

color = black

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = EPK

amount = 4.91

component = Feldspar

amount = 78.86

component = Whiting

amount = 5.48

component = Gerstley borate

amount = 10.75

addition = Copper carbonate

addamount = 4.13

addition = Manganese dioxide

addamount = 4.13

addition = Cobalt oxide

addamount = 2.07

note = |Nice shiny black, works nicely with other glazes to get interest

note = |effects. Try WG white with this one. I have spent about a year

note = |reading all of the good things you all have had to share and thought

note = |it is my turn to do some of the giving. Here are some formulas that I

note = |have gathered from the studio. I don't know who the original creators

note = |of these are. Hope you all enjoy them: sue hintz

note = |

name = Old Gold Albany

index =

date = 11/15/98

source =

type = Li Ca Mg Zr SlipGlaze

range = 5 - 6

firetype = Ox or Red

color = Gold?

vistexture =

quality = Satin-Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 6240

component = Lithium carbonate

amount = 800

component = Zircopax

amount = 960

note = |Are there more ingredients? The end of the recipe is obliterated.

note = |Glaze Type: Li Ca Mg Zr SlipGlaze. Opacity: Opaque. Firing type: Ox

note = |or Red .

note = |

note = |

name = Orange Brown Speckled Tan number 288

index =

date = 3/26/96

source =

type = Mid-fire

range = 6 - 8

firetype = reduction

color =

vistexture =

quality = Texture

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 53

component = Whiting

amount = 22

component = Barium carbonate

amount = 16

component = EPK

amount = 9

note = |Lots of surface texture. Add: Rutile 2-3% submitted by:

note = |GURUSHAKTI@

name = Orange Brown Speckled Tan number 288

index =

date = 3/26/96

source =

type = Mid-fire

range = 6 - 8

firetype = reduction

color =

vistexture =

quality = Texture

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 53

component = Whiting

amount = 22

component = Barium carbonate

amount = 16

component = EPK

amount = 9

note = |Lots of surface texture. Add: Rutile 2-3% submitted by:

note = |GURUSHAKTI@

name = Orange Red

index =

date = 12/28/2004

source =

type = Iron saturate

range = 6

firetype = Oxidation

color = Red

vistexture =

quality = Gloss

transparency = Opaque

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 46.7

component = EPK

amount = 4

component = Bone ash

amount = 15

component = Lithium carbonate

amount = 4

component = Talc

amount = 16.9

component = Flint

amount = 11.4

addition = Red iron oxide

addamount = 11

addition = Bentonite

addamount = 2

var = |rio 11-17%

note = |source: Michael Bailey, Glazes Cone 6 This is a "kaki" (plum) saturated iron red.

note = |It can be a brilliant red-orange with just the right amount of iron. It does

note = |better if you do a controlled cooling as it is a crystalline glaze and needs the

note = |slow cool for the crystals to grow (fast cool will yield a chocolate brown

note = |gloss).You have to do a line blend on this one to get it right as iron oxides are

note = |never the same. I use Spanish red iron oxide. Generally increments of 1% RIO will

note = |be fine. But, you really need to do the line blend to get the best red and to

note = |fully appreciate the range of colors in that small range of RIO additions.

note = |From Bill Buckner bbuckner@

name = Orange-Red Base

index =

date = 10/23/2002

source =

type = Iron Saturate

range = 6

firetype = Oxidation

color = Orange-brown

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 46.7

component = Kaolin

amount = 4

component = Bone ash

amount = 15

component = Lithium carbonate

amount = 4

component = Talc

amount = 16.9

component = Flint

amount = 11.4

addition = Bentonite

addamount = 2

addition = Red iron oxide

addamount = 11.5

note = |From Glazes Cone 6 by Michael Bailey p. 89

name = Orange/Brown gloss Kemp 8

index =

date = 1/26/95

source =

type =

range = 6 - 7

firetype = Ox. or Red.

color = dark orange/brown

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 40

component = Zinc oxide

amount = 4

component = Dolomite

amount = 3

component = Whiting

amount = 15

component = Kaolin

amount = 5

component = Silica

amount = 33

addition = Red iron oxide

addamount = 4

note = |Shiny dark orange/brown Brian Kemp. Singapore -

note = |kempb@nievax.nie.ac.sg tested on white stoneware CLAY COLOR/TYPE:

note = |Buff Stoneware Fired at 100 degrees per hour to 600 degrees, then

note = |free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft. Manufactured

note = |in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological University

note = |Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST SITE:

note = |Nanyang Technological University, Singapore

name = original c6 matte

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = F-4 feldspar

amount = 45

component = Whiting

amount = 18

component = Kentucky OM #4

amount = 25

component = Zinc oxide

amount = 12

note = |FORMULA & ANALYSIS ------------------ *CaO........ .46 12.04%

note = |*MgO........ .01 .11% *K2O........ .06 2.53% *Na2O....... .12 3.50%

note = |*ZnO........ .36 13.49% Fe2O3...... .00 .32% TIO2....... .01 .42%

note = |AL2O3...... .37 17.61% SiO2....... 1.79 49.97% P2O5....... RATIO 4.82

note = |EXPAN 592.94 WEIGHT 214.43 I have test results for the original

note = |simple glaze and Ron's 2 complicated versions. All 3 glazes were

note = |tested on white and red stoneware, vertical and horizontal tiles.

note = |They were all fired in the bottom half of my Skutt to cone 6

note = |electric. The firing took approzimately 12 hours with a 1 hour soak

note = |at top temp. I added 2% rutile to all the glazes to test for color

note = |response, and used OM4 ball clay (instead of bell dark). I was

note = |somewhat surprised at how similar the glazes came out. The vertical

note = |tiles were virtually identical. All three were a soft gray opaque

note = |matt. My white stoneware has a little granular illmenite in it, and

note = |small spots bleed through. I double dipped 1/2 of each tile, and the

note = |glaze ran just a little. There was no discernable crazing. The

note = |horizontal tiles had noticable differences. These tiles were more

note = |mottled than the vertical ones, kind of like on oatmeal effect. The

note = |original glaze was a warmer gray than either of the 2 complex

note = |versions. The second complex version, where thick, was dry and

note = |sugary, and more silvery than either of the other 2. On all tiles,

note = |the red stoneware was more of a tan color than the white. Terri

note = |Storer storer@ Variations by Ron Roy: complicated

note = |version #1 ----------------- F4 SPAR 22.00 22.00% CUSTER SPAR 22.00

note = |22.00% WHITING 18.50 18.50% OM-4 Ball Clay 11.50 11.50% EPK 11.50

note = |11.50% ZINC OXIDE 12.00 12.00% SILICA 2.50 2.50% ---------- 100.00

note = |FORMULA & ANALYSIS ------------------ *CaO........ .46 12.02%

note = |*MgO........ .00 .09% *K2O........ .09 3.79% *Na2O....... .09 2.47%

note = |*ZnO........ .36 13.57% Fe2O3...... .00 .29% TIO2....... .01 .23%

note = |AL2O3...... .37 17.53% SiO2....... 1.80 49.98% P2O5....... .00 .02%

note = |RATIO 4.85 EXPAN 597.19 WEIGHT 215.75 My complicated version #2

note = |----------------- F4 SPAR............. 20.00 20.00% NEPH

note = |SY............. 20.00 20.00% WHITING............. 18.00 18.00% BELL

note = |DARK........... 11.00 11.00% EPK................. 11.00 11.00% ZINC

note = |OXIDE.......... 12.00 12.00% SILICA.............. 8.00 8.00%

note = |---------- 100.00 FORMULA & ANALYSIS ------------------ *CaO........

note = |.45 11.72% *MgO........ .01 .11% *K2O........ .05 2.21% *Na2O.......

note = |.13 3.77% *ZnO........ .36 13.53% Fe2O3...... .00 .26% TIO2.......

note = |.01 .22% AL2O3...... .38 17.68% SiO2....... 1.82 50.49% P2O5.......

note = |.00 .01% COST/KG 1.42 RATIO 4.85 EXPAN 584.18 WEIGHT 216.41 You post

note = |these to the list if you want - before or after you test them - what

note = |ever you like - but let me know what happenes and include all the

note = |recipes cause I don't keep em. Ron Roy 93 Pegasus Trail

note = |Scarborough,Canada M1G 3N8 Evenings, call 416 439 2621 Fax, 416 438

note = |7849 Studio: 416-752-7862. Email ronroy@astral.magic.ca Home page

note = |

note = |

name = OSB

index =

date = 4/3/95

source =

type =

range = 6

firetype = Ox. or Red.

color = white to orange

vistexture =

quality = shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 45.45

component = Silica

amount = 33.33

component = Whiting

amount = 4.04

component = Talc

amount = 7.07

component = Kaolin

amount = 5.05

component = Soda ash

amount = 5.05

addition = Tin oxide

addamount = 10.1

note = |omments: Nice shino white breaking to orange. From Brian Kemp,

note = |Singapore, (kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt

note = |listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at 100 degrees per

note = |hour to 600 degrees, then free for all to cone 6-7. Kiln Size,

note = |Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR: Brian Kemp

note = |Nanyang Technological University Block B, Room 216 469 Bukut Timah

note = |Rd. Singapore, 1025 TEST SITE: Nanyang Technological University,

note = |Singapore

note = |

name = Oxblood

index =

date = 4/21/95

source =

type =

range = 6

firetype = reduction

color = copper red

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 55.33

component = Gerstley borate

amount = 12.61

component = Whiting

amount = 10.71

component = Silica

amount = 21.35

addition = Copper Oxide

addamount = 0.39

addition = Tin oxide

addamount = 0.99

note = |kiln type: gas green in oxidation, red in reduction submitted by:

note = |John Anthony e-mail: JTRAX@

note = |

name = Ozona gritty slip variations

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = tan - add color

vistexture =

quality = stony slip or engobe

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = A.P. Green fireclay

amount = 70

component = GoldArt

amount = 20

component = Ball clay

amount = 10

note = |Tan Gray-green add: Chrome oxide 3 Tan Gray-blue add: Cobalt oxide 1

note = |Iron oxide 1 I've applied them to bone dry sculptural work, bisqued

note = |them and then have rubbed stains or oxides into the recesses,

note = |sponging off, then fired again for permanence. They are quite

note = |versatile. These recipes are from Zakin's book on Electric Kiln

note = |Ceramics. Some of the clays used in the recipe are coarse and the

note = |slip should not be strined. The result will be a coarse,

note = |sandy-textured surface, not for functional pieces. They may be

note = |applied by dipping, spraying or brushing. They may be applied to

note = |greenware or bisqued ware. They may be used alone or with stains and

note = |glazes. The appearance when fired is soft and sandy. Candice Roeder

note = |

note = |

name = Ozona White

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = stony white

vistexture =

quality = stony slip or engobe

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = A.P. Green fireclay

amount = 70

component = Cedar Heights Goldart

amount = 20

component = Ball clay

amount = 10

note = |I've applied them to bone dry sculptural work, bisqued them and then

note = |have rubbed stains or oxides into the recesses, sponging off, then

note = |fired again for permanence. They are quite versatile. These recipes

note = |are from Zakin's book on Electric Kiln Ceramics. Some of the clays

note = |used in the recipe are coarse and the slip should not be strined. The

note = |result will be a coarse, sandy-textured surface, not for functional

note = |pieces. They may be applied by dipping, spraying or brushing. They

note = |may be applied to greenware or bisqued ware. They may be used alone

note = |or with stains and glazes. The appearance when fired is soft and

note = |sandy. Candice Roeder

note = |

name = Pale Rutile Blue

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color = pale blue

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 8.45

component = Magnesium carbonate

amount = 1.86

component = Whiting

amount = 15.3

component = Wood ash

amount = 14.54

component = Nepheline syenite

amount = 15.55

component = Kaolin

amount = 10.91

component = Flint

amount = 33.39

addition = Rutile

addamount = 1.69

note = |I fired cone 6 oxidation pretty exclusively for five years and worked

note = |with many glazes (being a glaze testing maniac). One that I really

note = |enjoyed using, for several years (and I still use it occasionally)

note = |was a Rutile Pale Blue that has no cobalt in it, yet goes most

note = |definitely blue in oxidation. It is a tan mat if it isn't fired high

note = |enough and glossy pale translucent blue (almost celadon-like) at

note = |temp. Usually crazes... Mishy, enjoying an unusually cold and rainy

note = |Sonoran desert Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

note = |

note = |

name = Parker Gloss

index =

date = 12/6/96

source =

type =

range = 5

firetype =

color = clear transparent

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 43

component = Gerstley borate

amount = 20

component = Whiting

amount = 2

component = Zinc oxide

amount = 3

component = Barium carbonate

amount = 6

component = EPK

amount = 2

component = Silica

amount = 24

note = |Parker Gloss and Gronborg Clear are very similar. I include both

note = |because the coefficient of expansion is just different enough for you

note = |to tell which way to go if they do not fit your body. And, yes, I

note = |know they all have barium in them. Not much, though, so you could

note = |probably substitute 3/4 as much strontium carb, and not affect them

note = |much, or possibly just leave it out. I hope this helps. Paul Lewing

note = | pjlewing@

note = |

name = Patti's Crystal Clear

index =

date = 12/6/96

source =

type =

range = 5 - 7

firetype =

color = transparent clear

vistexture =

quality = glossy shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Whiting

amount = 8

component = Nepheline syenite

amount = 30

component = Kaolin

amount = 10

component = Flint

amount = 31

note = |Does anyone have a good crystal clear cone 5 glaze recipe they could

note = |share? I like Patti's Crystal Clear ^5-7 from Clayart a few years

note = |ago. Janice Lipuma Lexington KY jan lipuma

name = Paul's White

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 15.7

component = Talc

amount = 8.6

component = Whiting

amount = 12

component = Custer feldspar

amount = 43

component = EPK

amount = 8.6

component = Flint

amount = 12.1

addition = Zircopax

addamount = 8.1

note = |There's a White that i tested from Ceramics Monthly Answers to

note = |Potters Questions. I have done tests with it but haven't used it yet

note = |on anything major. It appeared to be something I would like. I want

note = |to work more with it when I get the time. Cheryl Fisher Sarasota, FL

note = |cfisher995@

note = |

name = Pearly

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = pearly orange w/yellow

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Flint

amount = 32.7

component = Whiting

amount = 19.7

component = EPK

amount = 12.1

component = Zinc oxide

amount = 6.6

component = Magnesium carbonate

amount = 2.7

component = K-200 feldspar

amount = 26.3

addition = Rutile

addamount = 10

note = |Glossy pearly white to orange with yellow highlights where thick.

note = |Best when applied thickly. Be careful it might run some. Steve

note = |Williams sawilliams@ ------------------------------

name = Permanent Tan

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color = tan

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wollastonite

amount = 30.33

component = Talc

amount = 8.88

component = Spodumene

amount = 49.77

component = EPK

amount = 11.02

note = |I'm not taking responsibility for anyone using these glazes, etc.

note = |Something is probably toxic. They are examples of my research and

note = |they work out in formulation. Which is what they are examples of. So

note = |go formulate your own non-toxic glazes, if that is possible. It's

note = |probably bad for the environment too. Email me with questions as to

note = |household performance, as that may be indicative of other problems.

note = |The badly crazed surfaces are not considered to be a continous-non

note = |porous sanitary surfaces. Eric Hansen, Lawrence, Kansas

note = |wabi_sabi@ As I remember they were all quite nice. But

note = |these and about half a dozen other tests went into a bucket of

note = |mystery glaze liner to which I added even more Custer, Kona F-4, EPK,

note = |then came in later with scoops of Gerstley and zircopax for a really

note = |nice satin with no problems. I need to find a Mac up at KU that has

note = |the HyperglazeIIx on it with my files to reconstruct. But it may not

note = |be worth it. That concept is simple if ya know how to use the program

note = |and maximize the feldspars, lithium, KNaO and get plenty of other

note = |fluxes in each glaze. Also I did not know Clayart has 1995 archives

note = |under the subject: cone 6 chit-chat. With several hundred recipes.

note = |I'm editing out all the headers and putting in titles and a single

note = |style much like this here. Some very lively conversation is recorded

note = |in the archives about cone 6 favorites. I am enjoying reading it now.

note = |Basically that was what I was after but if anyone wants to bounce

note = |some ideas, info, I will play. One more:

note = |

name = Persimmon

index =

date = 4/10/95

source =

type =

range = 6

firetype = Ox. or Red.

color = red brown

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 46.08

component = Kaolin

amount = 22.55

component = Silica

amount = 29.41

component = Soda ash

amount = 1.96

addition = Red iron oxide

addamount = 9.8

note = |An even better electric kiln glaze at cone 6 for refiring at cone 06

note = |yto to get a rich red. fire at cone 6 and do nothing but take it out

note = |of the kiln and look disappointed and then put in and refire at cone

note = |06. Next direction, take out and enthuse over change and improvement.

note = |Hope this is of interest. Lana Wilson lana@chem.ucsd.edu

note = |

name = Peter's Metallic Black

index =

date = 3/26/96

source =

type =

range = 5 - 10

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 78.84

component = Colemanite

amount = 10.69

component = Whiting

amount = 5.51

component = EPK

amount = 4.96

addition = Copper carbonate

addamount = 4.19

addition = Manganese dioxide

addamount = 4.19

addition = Cobalt carbonate

addamount = 2.09

note = |A really great glossy black. from Michelle Lowe, potter in the

note = |Phoenix desert mishlowe@ mishlowe@aztec.asu.edu

name = PG-2 Transparent Gloss

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = clear

vistexture =

quality = satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 40.17

component = Gerstley borate

amount = 24.35

component = Silica

amount = 17.74

component = EPK

amount = 17.74

addition = Bentonite

addamount = 0.87

note = |a clear, satin glaze. You may need to adjust the silica up a bit to

note = |prevent crazing, depending on your clay. source of original recipe:

note = |James Chappell's Complete Compendium of Clays and Glazes for the

note = |Potter submitted by: Sumi Dick e-mail: Sumi@

note = |

name = Pink

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = pink

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Nepheline syenite

amount = 16

component = Kaolin

amount = 11

component = Whiting

amount = 20

component = Silica

amount = 32

addition = Tin oxide

addamount = 5

addition = Chromium oxide

addamount = 0.15

note = |Brian Kemp. Singapore kempb@nievax.nie.ac.sg

note = |

name = Pink Base

index =

date = 6/3/96

source =

type =

range = 5

firetype =

color = Translucent White

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro frit 3134

amount = 20.59

component = Kaolin

amount = 22.79

component = Silica

amount = 42.65

component = Whiting

amount = 13.97

note = |submitted by: Michelle Campbell e-mail: Lackacreek@ccinetabca

note = |

name = Pink Bright

index =

date = 4/11/95

source =

type = Lithium Matt

range = 6-7

firetype = Oxidation

color = mauve

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 43.3

component = Whiting

amount = 20

component = Lithium carbonate

amount = 16.7

component = Barium carbonate

amount = 5

component = Gerstley borate

amount = 8.3

component = Silica

amount = 6.7

addition = Tin oxide

addamount = 8.3

addition = chrome oxide

addamount = 0.4

note = |Semi matt mauve, nice. From Brian Kemp, (kempb@nievax.nie.ac.sg) via

note = |Rose Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired

note = |at 100 degrees per hour to 600 degrees, then free for all to cone

note = |6-7. Kiln Size, Cromarty 25 cu ft. Manufactured in the UK.

note = |CONTRIBUTOR: Brian Kemp, Nanyang Technological University, Block B,

note = |Room 216, 469 Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang

note = |Technological University, Singapore

name = Pink Cr-Sn Matt

index =

date = 08/01/2001

source =

type = Chrome-tin pink

range = 6

firetype = oxidation

color = Pale pink

vistexture =

quality = Semi matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 140.9

component = Whiting

amount = 90.9

component = Talc

amount = 45.5

component = Kaolin

amount = 131.8

component = Silica

amount = 45.5

component = Zinc oxide

amount = 45.5

addition = Tin oxide

addamount = 22.8

addition = Chrome oxide

addamount = 9.1

note = |> ClayArt Listserv recipe < If you find this glaze useful, please

note = |consider submitting it to the GlazeBase project with full

note = |documentation. Use one of the GlazeBase submission formats available

note = |on the CeramicsWeb web page.

note = |

note = |comments: Semi matt, Pale pink, good From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

name = Pink Cr-Sn MME

index =

date = 4/10/95

source =

type =

range = 6

firetype =

color = Pale pink

vistexture =

quality = Semi matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 28.2

component = Whiting

amount = 18.2

component = Talc

amount = 9.1

component = Kaolin

amount = 26.4

component = Silica

amount = 9.1

component = Zinc oxide

amount = 9.1

addition = Tin oxide

addamount = 4.6

addition = chrome oxide

addamount = 1.8

note = |Semi matt, Pale pink, good From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

name = Pink Glaze

index =

date = 01/19/2006

source =

type = Zinc matt

range = 5

firetype = Oxidation

color = Pink

vistexture =

quality =

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 140

amount = 48

component = Zinc oxide

amount = 24

component = Kaolin

amount = 28

addition = Chrome oxide

addamount = 2

var = |additions of .25% RIO make the glaze more orange.

var = |1% RIO = terracotta

note = |B & R Pearson, Clay Times Nov/Dec 05 p.51. NOt for food.

name = Pink Nickel

index =

date = 7/19/95

source =

type = Mid-fire

range = 6

firetype = oxidation

color = plum

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Lithium carbonate

amount = 3.12

component = Barium carbonate

amount = 41.67

component = Zinc oxide

amount = 12.5

component = Nepheline syenite

amount = 26.04

component = Silica

amount = 16.67

addition = Bentonite

addamount = 4.17

addition = Nickel oxide

addamount = 1.56

note = |Here's a neat plum glaze, rather misnamed 'Nickel Pink.' It's 6^ ox.

note = |and comes from Emanual Coopers recipe file. Was printed in Ceramic

note = |Review May/June/87. When it is applied rather thickly, it is a

note = |beautiful rich plum color, breaking on the edges to a leather brown.

note = |submitted by: Dan Taylor e-mail: dataylor@mlc.

name = Pink Pale Matt

index =

date = 4/10/95

source =

type = Mid-fire

range = 6

firetype = oxidation

color = Pale pink

vistexture =

quality = Semi matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 28.18

component = Whiting

amount = 18.18

component = Talc

amount = 9.09

component = Kaolin

amount = 26.36

component = Silica

amount = 9.09

component = Zinc oxide

amount = 9.09

addition = Tin oxide

addamount = 4.55

addition = Chrome oxide

addamount = 1.82

note = |Semi matt, Pale pink, good From Brian Kemp, Singapore,

note = |(kempb@nievax.nie.ac.sg) via Rose Downs on ClayArt listserv. CLAY

note = |COLOR/TYPE: Buff Stoneware Fired at 100 degrees per hour to 600

note = |degrees, then free for all to cone 6-7. Kiln Size, Cromarty 25 cu ft.

note = |Manufactured in the UK. CONTRIBUTOR: Brian Kemp Nanyang Technological

note = |University Block B, Room 216 469 Bukut Timah Rd. Singapore, 1025 TEST

note = |SITE: Nanyang Technological University, Singapore

name = Pink Powder Box

index =

date = 4/3/98

source =

type = Mid-fire

range = 5 - 6

firetype = oxidation

color = pink

vistexture =

quality = matte

transparency =

xtals =

bubbles = Many

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kentucky OM #4

amount = 15.79

component = Ferro frit 3134

amount = 52.63

component = Whiting

amount = 5.26

component = Silica (300m)

amount = 26.32

addition = Bentonite

addamount = 2.11

addition = Titanium dioxide

addamount = 1.05

note = |(Mimi Obstler's Out of the Earth Into the Fire p147) Here's the

note = |recipe, fired to about cone 5.4 or 6.2 (depending on which cone you

note = |want to read). Or fired to 1200C at 50C/hr. I added 1%

note = |TiO2 which gives a nice blush of crystalline effects, without the

note = |yellowish orange you get from rutile. Where this glaze is thicker

note = |though and right together with the crystals/bubbles, there's a foamy

note = |texture inside the glaze. I can tell because I fire on stilts and

note = |when the stilts come off, a little circular crust of glass stays on

note = |the stilt pin and the interior of the glaze where the stilt pulled

note = |off the surface looks like froth. Foam. (P.S. is this behavior an

note = |indicator of a fit problem?) So the glaze goes onto greenware and

note = |gets put in the kiln on stilts. Fired. Tons of what I thought were

note = |crystals but maybe they really are bubbles, as revealed by the froth.

note = |The presence of some sharp-edged pinholes argues that my crystals are

note = |bubbles maybe. Conventional wisdom I: soak more or cool more slowly.

note = |Done that I: Goes up to temp at 60C/hr, soaks 25 minutes, cools at

note = |150C/hr to 900, then at 60C/hr to 700. If it gets any slower than

note = |that, won't I be a laughing stock? Conventional wisdom II: try

note = |refiring to convince yourself that it needs to soak some more. Done

note = |that II: Refired a set of pieces. Foam is still there. Some of the

note = |sharp edged pinholes have closed up. I have used this same recipe

note = |with 8% rutile (lovely effect by the way if your rutile is finely

note = |enough ground). It doesn't exhibit the same problem as far as I can

note = |see. A few pinholes where quite thick but nothing like this. So. Is

note = |this because titanium actually makes a glaze more refractory? I'm

note = |kinda puzzled about calculating how to make something melt more

note = |smoothly. Especially since it already seems totally loaded up with

note = |melter, all that boron. Thanks for any pointers to enlightenment Jan

note = |Walker Cambridge MA USA jwalker@world.

name = Pinnell Strontium Matt Glaze

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color =

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Lithium carbonate

amount = 1

component = Strontium carbonate

amount = 20

component = Nepheline syenite

amount = 60

component = Ball clay

amount = 10

component = Silica

amount = 9

note = |White add Titanium Dioxide 5%. Weathered Bronze Green add Titanium

note = |Dioxide 5% and Copper Carbonate 5%. Periwinkle Blue add Cobalt

note = |Carbonate .15% and Copper Carbonate 4%. Dark Mottled Green add Copper

note = |Carbonate 8%. Cream/Tan add Rutile 6%. Charcoal add Manganese Dioxide

note = |2% and Copper Carbonate 5%. I have found several yellow ^ 6 glazes

note = |you might be interested in. The Pinnell Strontium matt was still very

note = |matt with 5% added G. Borate (maybe needs even more) The glaze must

note = |be thickly applied. It breaks to darker gold and white with 6% mason

note = |stain 6485/ titanium yellow. submitted by: Mary Kuilema e-mail:

note = |kuil@k2.

note = |

name = Plainsman Clear

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color = clear

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro frit 3134

amount = 50

component = Kaolin

amount = 30

component = Silica

amount = 20

note = |I have had success with a clear developed by Plainsman Clays,

note = |Lethbridge Alberta, Canada. Find it has a broad range, but must glaze

note = |carefully, as it can turn a bit cloudy if it is too thick. (my

note = |pencil, partly wrapped with wire, acts as my hydrometer) I have used

note = |over the underglazes you mention. Have applied the underglazes to

note = |both greenware and to the bisque. This glaze does not craze!

note = |submitted by: Carolyn DiPasquale e-mail: sdipo@ source for

note = |original recipe: Plainsman Clays

note = |

name = Pleasant Brown

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = brown

vistexture =

quality = shiny glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Alberta slip

amount = 62.5

component = Gerstley borate

amount = 20.83

component = Potash feldspar

amount = 8.33

component = EPK

amount = 8.33

addition = Tin oxide

addamount = 3.33

note = |This is quite a pleasant sort of mid brown glaze for ^6 oxidation How

note = |nice to be able to share something from my books, I have been so

note = |pleased with some of the recipes that I have tested from other

note = |clayart subscribers. I only wish that I could give proper credit to

note = |the originators of these but I am afraid I was amiss in recording

note = |such info. Sue on a rainy day in British Columbia - how unusual sue

note = |hutchen

note = |

name = Plum Ed's

index =

date = 12/6/96

source =

type = Chrome-tin pink

range = 6

firetype =

color = light pink

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 50.6

component = Gerstley borate

amount = 8.8

component = EPK

amount = 4.6

component = Whiting

amount = 22.1

component = Flint

amount = 13.8

addition = Bentonite

addamount = 0.9

addition = Tin oxide

addamount = 8.3

addition = Potassium bichromate

addamount = 0.9

note = | Andy

note = |Lubow andrew s lubow

name = Plum Ed's

index =

date = 12/6/96

source =

type = Chrome-tin pink

range = 6

firetype = Ox. or Red.

color = light pink

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 50.6

component = Gerstley borate

amount = 8.8

component = EPK

amount = 4.6

component = Whiting

amount = 22.1

component = Flint

amount = 13.8

addition = Bentonite

addamount = 0.9

addition = Tin oxide

addamount = 8.3

addition = Potassium bichromate

addamount = 0.9

note = |They use this glaze a lot at a community college I go to. I'm curious

note = |if anyone can tell me if it's safe used for a food container? Andy

note = |Lubow andrew s lubow

name = Plum Ed's 6

index =

date = 12/6/96

source =

type =

range = 6

firetype = Oxidation

color = light pink

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = neph sy

amount = 50.64

component = Gerstley borate

amount = 8.84

component = EPK

amount = 4.61

component = Whiting

amount = 22.1

component = Flint

amount = 13.81

addition = Bentonite

addamount = 0.92

addition = Tin oxide

addamount = 8.28

addition = Potassium dichromate

addamount = 0.92

note = |They use this glaze a lot at a community college I go to. I'm curious

note = |if anyone can tell me if it's safe used for a food container? Andy

note = |Lubow andrew s lubow

name = PMSP 4 Base

index =

date = 4/3/98

source =

type =

range = 6 - 8

firetype = oxidation

color = clear

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3134

amount = 25.4

component = Nepheline syenite

amount = 8

component = Wollastonite

amount = 19.6

component = EPK

amount = 22.5

component = Flint

amount = 24.5

note = |Chemical Analysis Na2O 0.18 Al2O3 0.35 SiO2 3.26 K2O 0.01 B2O3 0.27

note = |MgO 0.02 CaO 0.79 Alumina:Silica ratio is 1.00 : 9.41 Neutral:Acid

note = |ratio is 1.00 : 5.30 Alkali:Neutral:Acid ratio is 1.00 : 0.62 : 3.26

note = |Expansion coefficient: 68.0 x 10e-7 per degree C Oxides causing

note = |abnormal expansion effects: B2O3 The question that I have for Ron is

note = |about the expansion of the glazes listed below. A while back you told

note = |me that the expansion for the PMSP-4 glaze was a little low. You sent

note = |me a revised version which had a slightly higher expansion. I then

note = |looked at Tony Hansen's 5-20 glaze and found it to be pretty close to

note = |my PMSP-4. What range do you think the expansion should be in for a

note = |cone 6 oxidation glaze? PMSP-4 Expansion coefficient: 68.0 x 10e-7

note = |per degree C Ron Roy's version of PMSP-4 Expansion coefficient: 71.1

note = |x 10e-7 per degree C Tony Hansen's 5-20's glaze Expansion

note = |coefficient: 69.2 x 10e-7 per degree C In terms of my experience

note = |firing these glazes, I have found the PMSP to be water clear. Your

note = |revision to be mostly clear with bubbles only in areas of relief

note = |where the glaze has pooled. The 5-20's glaze for me was cloudy. I'm

note = |wondering if Ron Wright is getting more bubbles because he is trying

note = |to get a THICK clear? My clear gets a 4 second dip and I can't find

note = |any bubbles in it under a 1.5x magnifying glass. For anyone following

note = |this thread, all of the above glazes are given below. All are cone 6

note = |oxidation. My firing takes about 8-9 hours to bend a large cone 6 and

note = |then I soak the kiln for another half hour to hour until cone 7 is at

note = |2 o'clock. I then turn all of the switches to medium for 3 hours

note = |before shutting it off. The correct formula for Post's PMSP-4 is this

note = |one. The one posted on the database is incorrect. John Post

note = |jp6mchp@ Sterling Heights, Michigan

name = Polished Matt

index =

date = 11/15/98

source =

type = Ca Mg AlMatt

range = 5 - 6

firetype = Ox or Red

color =

vistexture =

quality = Satin Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 Spar

amount = 1600

component = Custer spar

amount = 1600

component = Spodumene

amount = 1600

component = Dolomite

amount = 1600

component = Whiting

amount = 400

component = Kaolin

amount = 1200

addition = Tin oxide

addamount = 480

note = |Nice. Val, who originated this glaze?? Glaze Type: Ca Mg AlMatt.

note = |Opacity: . Firing type: Ox or Red .

note = |

note = |

name = Powder Box Pink

index =

date = 4/3/98

source =

type =

range = 5 - 6

firetype = oxidation

color = pink

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kentucky OM #4

amount = 15.79

component = Ferro frit 3134

amount = 52.63

component = Whiting

amount = 5.26

component = Silica (300m)

amount = 26.32

addition = Bentonite

addamount = 2.11

addition = Titanium dioxide

addamount = 1.05

note = |(Mimi Obstler's Out of the Earth Into the Fire p147) Here's the

note = |recipe, fired to about cone 5.4 or 6.2 (depending on which cone you

note = |want to read). Or fired to 1200C at 50C/hr. Someone asked the other

note = |day about the billions of tiny bubbles that formed the clouds in a

note = |glaze that was supposed to be clear. I've been wondering about a

note = |similar phenomenon in a glaze that is clear to start with. I added 1%

note = |TiO2 which gives a nice blush of crystalline effects, without the

note = |yellowish orange you get from rutile. Where this glaze is thicker

note = |though and right together with the crystals/bubbles, there's a foamy

note = |texture inside the glaze. I can tell because I fire on stilts and

note = |when the stilts come off, a little circular crust of glass stays on

note = |the stilt pin and the interior of the glaze where the stilt pulled

note = |off the surface looks like froth. Foam. (P.S. is this behavior an

note = |indicator of a fit problem?) So the glaze goes onto greenware and

note = |gets put in the kiln on stilts. Fired. Tons of what I thought were

note = |crystals but maybe they really are bubbles, as revealed by the froth.

note = |The presence of some sharp-edged pinholes argues that my crystals are

note = |bubbles maybe. Conventional wisdom I: soak more or cool more slowly.

note = |Done that I: Goes up to temp at 60C/hr, soaks 25 minutes, cools at

note = |150C/hr to 900, then at 60C/hr to 700. If it gets any slower than

note = |that, won't I be a laughing stock? Conventional wisdom II: try

note = |refiring to convince yourself that it needs to soak some more. Done

note = |that II: Refired a set of pieces. Foam is still there. Some of the

note = |sharp edged pinholes have closed up. I have used this same recipe

note = |with 8% rutile (lovely effect by the way if your rutile is finely

note = |enough ground). It doesn't exhibit the same problem as far as I can

note = |see. A few pinholes where quite thick but nothing like this. So. Is

note = |this because titanium actually makes a glaze more refractory? I'm

note = |kinda puzzled about calculating how to make something melt more

note = |smoothly. Especially since it already seems totally loaded up with

note = |melter, all that boron. Thanks for any pointers to enlightenment Jan

note = |Walker Cambridge MA USA jwalker@world.

note = |

name = Purple

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = purple

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 37

component = Gerstley borate

amount = 12

component = Dolomite

amount = 6

component = Talc

amount = 14

component = Kaolin

amount = 5

component = Silica

amount = 23

component = Zinc oxide

amount = 3

addition = Cobalt carbonate

addamount = 2

note = |Brian Kemp. Singapore kempb@nievax.nie.ac.sg

note = |

name = Purple Brilliant Matt

index =

date = 12/7/96

source =

type = Mid-fire

range = 6

firetype = oxidation

color = purple

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Nepheline syenite

amount = 22.8

component = Silica

amount = 12.1

component = Strontium carbonate

amount = 36.2

component = Lithium carbonate

amount = 6

component = Kaolin

amount = 22.8

addition = Copper carbonate

addamount = 8.4

note = |We call them Brilliant Matt Purple

note = |and Brilliant Matt Turquoise. They are volatile so be very careful

note = |with your kiln shelves. There is Barium Carbonate in the recipes, so

note = |they are poisonous whilst in the raw state. As you can see they both

note = |use the same ingredients, but in different proportions. He fires to cone 6

note = |(1200/1220 C)You have to watch your application thickness to get the

note = |result you want. We have fired the BMP from 950 C to almost 1300 C

note = |with different results but always pleasantly surprised. Do not expect

note = |consistancy with these glazes.

note = |submitted by: Ralph Loewenthal e-mail: fayralph@sprintlink.co.za

name = Purple Eggplant

index =

date = 12/7/96

source =

type = Magnesium matt

range = 6

firetype =

color = purple

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 43.5

component = Flint

amount = 14.5

component = Talc

amount = 12.1

component = Gerstley borate

amount = 12.3

component = Dolomite

amount = 8.6

component = EPK

amount = 4.3

component = Manganese carbonate

amount = 4.8

addition = Bentonite

addamount = 1

addition = Cobalt carbonate

addamount = 1.9

note = |This is a semi gloss eggplant purple glaze given to me by a nice

note = |person I met at a glaze workshop: I particularly like it on the warm

note = |brown clay that I normally use. from jeanne ormsby

name = Purple Eggplant

index =

date = 12/7/96

source =

type =

range = 6

firetype = Ox. or Red.

color = purple

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 45.7

component = Flint

amount = 15.2

component = Talc

amount = 12.7

component = Gerstley borate

amount = 12.9

component = Dolomite

amount = 9

component = EPK

amount = 4.5

addition = Bentonite

addamount = 1

addition = Cobalt carbonate

addamount = 2

addition = Manganese carbonate

addamount = 5

note = |This is a semi gloss eggplant purple glaze given to me by a nice

note = |person I met at a glaze workshop: I particularly like it on the warm

note = |brown clay that I normally use. from jeanne ormsby

name = Purple Eggplant

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation

color = purple

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 45.7

component = Flint

amount = 15.2

component = Talc

amount = 12.7

component = Gerstley borate

amount = 12.9

component = Dolomite

amount = 9

component = EPK

amount = 4.5

addition = Bentonite

addamount = 1

addition = Cobalt carbonate

addamount = 2

addition = Manganese carbonate

addamount = 5

note = |This is a semi gloss eggplant purple glaze given to me by a nice

note = |person I met at a glaze workshop: I particularly like it on the warm

note = |brown clay that I normally use. from jeanne ormsby

name = Purple Elyse's Matt

index =

date = 03/06/01

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Purple

vistexture =

quality = Matt

transparency = Semi-opaque

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 3

component = Magnesium carb

amount = 3

component = Whiting

amount = 22

component = Nepheline syenite

amount = 23

component = Kaolin

amount = 20

component = Flint

amount = 29

var = |Chartreuse: 8% Drakenfield yellow (bright yellow stain)

var = | + 0.5% copper carb

var = |Deep Plum: + 10% Standard Ceramics Orchid stain

var = |Deep Purple-blue: + 8% Royal purple (Standard Ceramics).

note = |From Elyse Burja. Based on Dixon Satin.

name = Purple Emily's

index =

date = 12/30/96

source =

type = Magnesium matt

range = 6-8

firetype = Ox. or Red.

color = Blue to purple

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals = Small

bubbles = None

flow = None

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 34

component = Gerstley borate

amount = 18

component = OM#4 Ball clay

amount = 11

component = Talc

amount = 14

component = Flint

amount = 10

component = Dolomite

amount = 6

addition = Zircopax

addamount = 10

addition = Cobalt oxide

addamount = 3

note = | This is a very reliable glaze. The surface is very smooth to the

note = |touch. It would be a good glaze for color variations. We have done a

note = |small amount of testing with mason stain additions and it seems to

note = |respond well to most colors, particularly the yellow.

note = |

note = |*How long have you been using this glaze?

note = | In a college studio setting for about a year.

note = |

note = |*Where is it used?

note = | Anne Arundel Community College

note = |

note = |*Where did this recipe come from?

note = | I have two versions of this glaze. This is the best and I am not

note = |sure if it came from the Penland Pottery book or not. I don't know

note = |the source of the other one.

note = |

note = |*What do you like most about this glaze?

note = | The reliability and the feel.

note = |

note = |*Is this glaze reliable?

note = | Yes, very.

note = |

note = |*Does this glaze tend to craze/crawl/pinhole/etc.?

note = | We have had some crawling when it is applied thickly or overlapped

note = |heavily with other glazes. Controlling the thickness is essential.

note = |

note = |*How do different firing temperatures/atmospheres affect the glaze?

note = | It seems to stand up well to temperature variations. When it is

note = |hotter it will tend to go more translucent.

note = |

note = |*How does the glaze behave on different clay bodies?

note = | The color is pretty powerful. Over a stoneware body in reduction it

note = |will go a bit darker, and it will be brighter and bluer over a white

note = |body.

note = |

note = |*What consistency should the glaze be for pouring/dipping?

note = | A cream consistency, so that you can see the cutile of your fingers

note = |when a hand is dipped in the glaze.

note = |

note = |*How thickly should the glaze be applied to the pot?

note = | Medium, a full 3 second dip is adequate.

note = |

note = |*How does this glaze interact with other glazes?

note = | It breaks up nicely and goes to a navy blue when used with our clear

note = |glaze.

note = |

note = |*What is your kiln type and size?

note = | Most of our work with it has been in an Alpine 20 natural gas kiln.

note = |We have also used it in a 23" dia. L&L econo kiln. The colors in

note = |oxidation are a bit lighter, and the surface is not as smooth.

note = |

note = |*How do you typically fire?

note = | The gas schedule is just 7.5 to 8 hours to reach cone 6. We fire

note = |between cone 6 and 7. Reduction starts at cone 010, and continues to

note = |cone 6, with the dampers being opened gradually as the firing gets

note = |closer to completion, but we maintain reduction to the end. No soak.

note = |We close the dampers but don't close the burner ports. We open the

note = |kiln 36 hours later. It is usually still pretty warm a the top.

note = |

note = |*What is your water pH?

note = | very close to 7

note = |

note = |*GlazeBase Glaze*

note = | Submitted by: Rick Malmgren (RMalmgren@)

note = | Ice Cream Flavor: Bryer's Mint Chocolate Chip

note = |

note = | --------------------------------------------------------------------

note = |----

name = Purple Jeannie's

index =

date = 06/03/2005

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Purple

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 18

component = Frit 3134

amount = 14

component = Whiting

amount = 20

component = Kentucky OM #4

amount = 18

component = Silica

amount = 30

addition = Chrome oxide

addamount = 0.2

addition = Tin oxide

addamount = 3.75

addition = Cobalt carbonate

addamount = 0.6

note = |Clay Times Jan/Feb 05 p.55. Based on Raspberry Red by John Hesselberth & Ron Roy,

note = |w/change in tin + cobalt

name = Purple Matt Elyse's

index =

date = 03/22/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Purple

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 3

component = Magnesium carbonate

amount = 3

component = Whiting

amount = 22

component = Nepheline syenite

amount = 23

component = Kaolin

amount = 20

component = Flint

amount = 29

var = |Chartreuse: 8% Drakenfield yellow (bright yellow stain) + 0.5% copper carb

var = |Deep Plum: + 10% Standard Ceramics Orchid stain

var = |Deep Purple-blue: + 8% Royal purple (Standard Ceramics).

note = |From Elyse Burja

name = Purple Matt Elyse's no GB

index =

date = 03/22/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Purple

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 6.6

component = Whiting

amount = 19.1

component = Nepheline syenite

amount = 23

component = Kaolin - theoretical

amount = 16.7

component = Silica

amount = 28.8

component = Frit 3195

amount = 5.7

var = |Chartreuse: 8% Drakenfield yellow (bright yellow stain) + 0.5% copper carb

var = |Deep Plum: + 10% Standard Ceramics Orchid stain

var = |Deep Purple-blue: + 8% Royal purple (Standard Ceramics).

note = |From Elyse Burja

name = Purple semi-matte

index =

date = 01/19/2006

source =

type = Zinc matt

range = 5

firetype = Oxidation

color = Purple

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Strontium carbonate

amount = 25

component = Barium carbonate

amount = 15

component = Zinc oxide

amount = 18

component = Kaolin

amount = 25

component = Flint

amount = 17

addition = Macaloid

addamount = 1

addition = Nickel carbonate

addamount = 1.5

var = |+ 4% cobalt added to purple glaze = royal blue. Fire to cone 6 to avoid excessive

var = |matt surface.

note = |Clay Times Nov/Dec. 05 p.53 from B & R Pearson. NOT for food. Best purples are

note = |w/white slip on body. Glaze application toward thick. Rapid firing cycle (6

note = |hours). Significantly longer cycle makes glaze run, become glassy, and change

note = |toward blue.

name = purple/black Matt

index =

date = 08/01/2001

source =

type =

range = 5

firetype = Oxidation

color = purple to black

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 375

component = Cornwall Stone

amount = 125

addition = Red iron oxide

addamount = 125

note = |> ClayArt Listserv recipe < If you find this glaze useful, please

note = |consider submitting it to the GlazeBase project with full

note = |documentation. Use one of the GlazeBase submission formats available

note = |on the CeramicsWeb web page.

note = |

note = |comments: Rob Wadey (robert wadey ) 9734B -

note = |100 Ave Grande Prairie, Alberta t8V 0T6 Phone: (403) 538-3731 Fax:

note = |(403) 538.3732

name = purple/black Matt

index =

date = 08/01/2001

source =

type =

range = 5

firetype = Oxidation

color = purple to black

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 375

component = Cornwall Stone

amount = 125

addition = Red iron oxide

addamount = 125

note = |> ClayArt Listserv recipe < If you find this glaze useful, please

note = |consider submitting it to the GlazeBase project with full

note = |documentation. Use one of the GlazeBase submission formats available

note = |on the CeramicsWeb web page.

note = |

note = |comments: Rob Wadey (robert wadey ) 9734B -

note = |100 Ave Grande Prairie, Alberta t8V 0T6 Phone: (403) 538-3731 Fax:

note = |(403) 538.3732

name = Pussywillow c 5-6

index =

date = 08/24/98

source =

type =

range = 5-6

firetype = Oxidation

color = Frosty

vistexture =

quality = Satin matt

transparency = Translucent

xtals =

bubbles =

flow = Slight

durability =

flaws =

tested = tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kentucky OM #4

amount = 20

component = Kona F-4

amount = 50

component = Gerstley borate

amount = 5

component = Zinc oxide

amount = 5

component = Whiting

amount = 15

component = Flint

amount = 5

var = |Grey: 2% black nickle oxide + 1% CoO

var = |Green: 2% black nickle oxide + 4% rutile

note = |Zinc content will make this glaze brown with chrome colorants.

note = |Mottled, smooth surface.

name = Pussywillow Matt

index =

date = 11/15/99

source =

type =

range = 5

firetype = Oxidation

color = SemiOpaque Gray

vistexture =

quality = Semi-Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ball clay

amount = 20

component = Kona F-4 feldspar

amount = 50

component = Gerstley borate

amount = 5

component = Zinc oxide

amount = 5

component = Whiting

amount = 15

component = Flint

amount = 5

addition = Black nickel oxide

addamount = 2

addition = Cobalt oxide

addamount = 1

note = |From Posey Bacopoulos. Striated brown glaze. Interesting visual

note = |texture. Green: 2% Black Nickel Oxide + 4% rutile

name = Pussywillow Matte c 5-6

index =

date = 08/24/98

source =

type =

range = 5-6

firetype = Oxidation

color = Frosty

vistexture =

quality = Satin matt

transparency = Translucent

xtals =

bubbles =

flow = Slight

durability =

flaws =

tested = tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kentucky OM #4

amount = 20

component = Kona F-4

amount = 50

component = Gerstley borate

amount = 5

component = Zinc oxide

amount = 5

component = Whiting

amount = 15

component = Flint

amount = 5

var = |Grey: 2% black nickle oxide + 1% CoO

var = |Green: 2% black nickle oxide + 4% rutile

var = |Dusty Lavender: 5 deep crimson MS, 5 salmon MS, 0.2 Cobalt carb

var = |Deep purple: leave out zn, add 5 Gerst B + 10-20 Blackberry wine mason stain

var = |golden yellow: 5 golden ambrosia MS + 5 Drakenfeld yellow yellow stain (Pr)

note = |Zinc content will make this glaze brown with chrome colorants.

note = |Mottled, smooth surface. Some colors above from Shannon Nelson.

name = Pussywillow no GB

index =

date = 04/24/2004

source =

type =

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws = Crazes

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 14.2

component = Nepheline syenite

amount = 31.8

component = Whiting

amount = 15.6

component = Zinc oxide

amount = 5.1

component = Flint

amount = 18.6

component = Frit 3124

amount = 14.3

addition = Bentonite

addamount = 1

var = |Grey: 2% black nickle oxide + 1% CoO

var = |Green: 2% black nickle oxide + 4% rutile

var = |Dusty Lavender: 5 deep crimson MS, 5 salmon MS, 0.2 Cobalt carb

var = |Deep purple: leave out zn, add 5 Gerst B + 10-20 Blackberry wine mason stain

var = |golden yellow: 5 golden ambrosia MS + 5 Drakenfeld yellow yellow stain (Pr)

note = |Tested by Valerie Duncan. Nice satin surface, but crazed on her clay body.

note = |Zinc content will make this glaze brown with chrome colorants.

note = |Mottled, smooth surface. Some colors above from Shannon Nelson.

name = R-1000 matt

index =

date = 7/19/95

source =

type =

range = 6

firetype = Ox. or Red.

color = varies - see comments

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 38.7

component = Wollastonite

amount = 15.2

component = Barium carbonate

amount = 15.2

component = Gerstley borate

amount = 10.2

component = EPK

amount = 10.2

component = Silica

amount = 10.5

note = |black, brown, blue, purple, turquoise, chartreuse, coral, yellow,

note = |crimson, and green. RM-54 Black 6% Mason 6600 RM-41 Brown 10% Mason

note = |6153 RM-53 Blue 5% Mason 6313 RM-34 Purple 10% Mason 6385 5%

note = |Wollsatonite RM-37 Turquoise 10% Mason 6390 RM-47 Chartreuse 5% Mason

note = |6236 RM-55 Coral 15% Mason 6090 5% Frit 3134 10% Wollastonite RM-50

note = |Yellow 5% Mason 6481 RM-44 Crimson 10% Mason 6006 RM-42 Green 6%

note = |Mason 6219 submitted by: Jonathan Kaplan e-mail:

note = |74034.3566@ source for original recipe: Wayne Bate

note = |

name = Raspberry

index =

date = 11/03/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = red raspberry

vistexture =

quality = Gloss

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 20

component = Nepheline syenite

amount = 18

component = Frit 3134

amount = 14

component = Kentucky OM #4

amount = 18

component = Silica

amount = 30

addition = Chromium oxide

addamount = 0.2

addition = Tin oxide

addamount = 7.5

var = |deep purple +1% CoCO3 and 0.25 RIO

note = |Chrome-tin pink. p.102 Mastering Cone 6 Glazes by John Hesselberth & Ron Roy. Glaze has highest

note = |expansion/contraction of any of their glazes - almost medium expansion. Not seen to

note = |craze in their examples, but may over time.

name = Red Iron Test#^6/23 Cone Six

index =

date = 4/3/98

source =

type = Iron saturate

range = 6

firetype = Oxidation

color = iron red

vistexture =

quality = shiny glossy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = EPK

amount = 5.9

component = Flint

amount = 29.4

component = Custer feldspar

amount = 19.6

component = Talc

amount = 13.7

component = Gerstley borate

amount = 31.4

addition = Red iron oxide

addamount = 14.7

note = |Here's one I tested that I liked a great deal. Shiny Red mottled

note = |foreground. Background variations of light to medium Tans/Browns.

note = |Beautiful Glaze andrew lubow

name = Red Ketchup

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color = Red rust iron

vistexture =

quality = ?

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = EPK

amount = 4.95

component = Silica, (325 mesh)

amount = 29.7

component = Custer feldspar

amount = 19.8

component = Talc

amount = 13.86

component = Gerstley borate

amount = 31.68

addition = Red iron oxide

addamount = 14.85

note = |I tried several of the cone 6 oxidation glazes but my kiln bent the

note = |^6 witness cone only slightly. Ketchup red is wonderful--not Heinz

note = |ketchup red, more like the ketchup red from the time we had an

note = |abundance of ripe tomatoes and overcooked a batch of ketchup.

note = |However, it had a frosting of tan and the plate and bowl are great

note = |looking. The glaze tended to flake off when dry and required careful

note = |handling on non-grolleg ^6 porcelain (Standard Ceramics # 213). Has

note = |satin finish. Not tested for durability or baked beans-yet. I only

note = |hope that the frosting remains at cone 6. BTW my firing took 8 hours

note = |and the sitter had a cone 7 placed in the middle of the sitter. Kiln

note = |was quite full. Don't know why I didn't get to cone 6 on any shelf.

note = |(Obviously I failed to check the witness cone when the kiln shut

note = |off-my goof.) Any ideas from the group, please. submitted by: Bonnie

note = |Hellman e-mail: mou10man@ This glaze is identical to Randy's

note = |Red.

name = Red Pink to Purple Mauve

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 21

component = Nepheline syenite

amount = 16

component = EPK

amount = 11

component = Whiting

amount = 20

component = Silica

amount = 32

addition = Tin oxide

addamount = 5

addition = Chrome Oxide

addamount = 5

note = |One thing I will say is the 'Red pink to Purple Mauve' turned out

note = |great. It is more of a deep red-violet. I did not find it purple when

note = |applied thick but happy with it as it is. I'll mess with it and keep

note = |trying. This was fired in elect on dillo white clay. submitted by:

note = |Lori Wilkinson e-mail: lorwilk@

note = |

name = Red Randy's

index =

date = 08/01/2001

source =

type =

range = 6 - 10

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Silica

amount = 29.7

component = EPK

amount = 4.96

component = Soda feldspar

amount = 19.8

component = Talc

amount = 13.86

component = Gerstley borate

amount = 31.68

addition = Bentonite

addamount = 2

addition = Red iron oxide

addamount = 15

var = |Darker red: instead of 15 RIO add:

var = |7.5 Crocus Martis

var = |7.5 RIO

note = |comments: A very nice base comes from Randy's Red with the iron

note = |omitted. You can add up to 10% zircopax or other whitener, I would

note = |suggest 5% for starters. Works good with other colorants also. Cobalt

note = |carbonate will give a purple. Very Stable! Rose Downs submitted by:

note = |dianna rose downs

note = |

note = |Clay Times

name = RED TENMOKU

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = very dark brown

vistexture =

quality = glossy shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 80.86

component = Whiting

amount = 10.56

component = Gerstley borate

amount = 3.63

component = Lithium carbonate

amount = 4.95

addition = Red iron oxide

addamount = 10.01

note = |(Richmond Potters' Club standard, unknown origin) (a rich glossy very

note = |dark brown with a lot of life and aventurine possibilities where

note = |thick. This is also a good base glaze. The RIO can be replaced with

note = |cobalt, copper, tin, etc. for other colours, useful for overdipping

note = |or whatever.) Here are a couple of standards from the Richmond

note = |Potters Club, and a few of my own formulation that have worked well

note = |in ^6 oxidation. They aren't revolutionary (my exciting ones have

note = |things like barium in them, or are less predictable for a classroom

note = |situation) but they have been reliable, and allow for some play. They

note = |all calculate out to well within the INSIGHT limit formulas for

note = |maturity at ^6. If anyone tests these and comes up with problems, new

note = |ideas, good variations etc. could they let me know? I'll look forward

note = |to a larger list being posted to clayart. Veronica Shelford e-mail:

note = |shelford@ s-mail: P.O. Box 6-15 Thetis Island, BC V0R 2Y0

note = |Tel: (250) 246-1509

note = |

name = Red Tomato

index =

date = 12/7/96

source =

type = Iron saturate

range = 6

firetype = oxidation

color = red

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 50

component = Silica

amount = 22.73

component = Kaolin

amount = 9.09

component = Dolomite

amount = 9.09

component = Bone ash

amount = 9.09

addition = Red iron oxide

addamount = 9.09

addition = Bentonite

addamount = 1.82

note = |Brian Kemp. Singapore kempb@nievax.nie.ac.sg

name = Red Towy

index =

date = 3/26/96

source =

type = Iron saturate

range = 6

firetype = Oxidation

color = iron red

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 16

component = Talc

amount = 14

component = Gerstley borate

amount = 31

component = Bone ash

amount = 2

component = Lead bisilicate

amount = 2

component = EPK

amount = 5

component = Silica

amount = 30

addition = Red iron oxide

addamount = 15

note = |If the lead panics you, don't use it. It only makes a little

note = |difference. I do only tile, and don't spray this. I've spent the last

note = |3 years working on cone 5 iron red glazes, starting with Randy's Red,

note = |and I've found some things that work to make it redder. I started by

note = |taking each ingredient, cutting it down, and gradually adding it back

note = |till I had double the amount in the recipe. I found some adjustments

note = |that work. Then I researched adding other ingredients in various

note = |amounts, and found a couple that seem to help. My new recipe I call

note = |Towy Red, after my dog. He's a Welsh Springer Spaniel, and has spots

note = |this color. He's named after the River Towy in Wales (rhymes with

note = |Howie). Then I tried different irons. I tried black iron, yellow

note = |iron, and 5 different reds, including Spanish Red. I found that the

note = |redder it was before it was fired, the redder it would be after. The

note = |best I have found so far has been an iron from Pfizer that is bright

note = |red-orange raw. I'm almost out, and don't know where to get more. Any

note = |suggestions? The Spanish Red I got from a local supplier, and it's

note = |earthy red-brown. I've been told that what I got was not real Spanish

note = |Red. Is this true? Where can I get the real stuff? To get the red,

note = |you need a lot of calcium, and almost as much, but not more,

note = |magnesium. All of these iron reds have a very high silica/ alumina

note = |ratio, at least 20 to 1, some as high as 100 to 1. Of course they run

note = |like the Energizer Bunny, but I only use them on tile. submitted by:

note = |Paul Lewing e-mail: PJLewing@

name = Red Vals

index =

date = 4/3/98

source =

type =

range = 5 - 6

firetype = oxidation

color = tan

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Flint

amount = 29.7

component = EPK

amount = 4.95

component = Feldspar

amount = 19.8

component = Talc

amount = 13.86

component = Gerstley borate

amount = 31.68

addition = Iron oxide

addamount = 2.97

addition = Rutile

addamount = 2.97

note = |Not really red. Is actually tan. Makes for a nice base glaze. Oil

note = |Spot looks great over this one. I have spent about a year reading all

note = |of the good things you all have had to share and thought it is my

note = |turn to do some of the giving. Here are some formulas that I have

note = |gathered from the studio. I don't know who the original creators of

note = |these are. Hope you all enjoy them: sue hintz

name = Red/Gold Shaner Revision

index =

date = 08/04/2003

source =

type =

range = 5-6

firetype = Oxidation

color = red

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 30

component = Nepheline syenite

amount = 30

component = Whiting

amount = 20

component = Talc

amount = 4

component = Kaolin

amount = 9

var = |Red = bone ash 6 + iron 4

var = |Gold= rutile 4

name = Reed's Glossy Black

index =

date = 1/13/96

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 11

component = EPK

amount = 5

component = Custer feldspar

amount = 79

component = Whiting

amount = 5

addition = Copper carbonate

addamount = 4

addition = Manganese dioxide

addamount = 4

addition = Cobalt oxide

addamount = 2

note = |I have used the following glaze with an electric kiln and found good

note = |results. The glaze 'Reed's Glossy Black' needs to be put on thick and

note = |does not seem to run. submitted by: Frank Helme e-mail: fhelme@

note = |

name = Reeds Glory Black

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color = black

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 11

component = EPK

amount = 5

component = Custer feldspar

amount = 79

component = Whiting

amount = 5

addition = Copper carbonate

addamount = 4

addition = Manganese dioxide

addamount = 6

addition = Cobalt oxide

addamount = 2

addition = Red iron oxide

addamount = 1

note = |A true glossy black Tested on Dillo White clay at a full ^6.

note = |submitted by: Lori Wilkinson e-mail: lorwilk@

note = |

name = Reeds Glory Black

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color = black

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 11

component = EPK

amount = 5

component = Custer feldspar

amount = 79

component = Whiting

amount = 5

addition = Copper carbonate

addamount = 4

addition = Manganese dioxide

addamount = 6

addition = Cobalt oxide

addamount = 2

addition = Red iron oxide

addamount = 1

note = |A true glossy black Tested on Dillo White clay at a full ^6.

note = |submitted by: Lori Wilkinson e-mail: lorwilk@

note = |

name = Rhodes Ash Glaze revised

index =

date = 6/24/97

source =

type =

range = 6 - 9

firetype =

color =

vistexture =

quality = stony/ satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Hardwood ash (washed)

amount = 28

component = G-200 feldspar

amount = 36

component = Dolomite

amount = 10

component = Kentucky OM #4

amount = 21

component = EPK kaolin

amount = 5

note = |use mixed hardwood ash + CMC Last year, with a lot of help from Tom

note = |Buck and some of the other Clayart gurus, I adjusted one of the old

note = |Daniel Rhodes ash glazes. Original recipe (Cone 9-10): Mixed hard

note = |wood ash 35 Oxford spar 35 China clay 15 Talc 15 I fire in an

note = |electric kiln. I would never describe it as a foolproof glaze, but if

note = |applied with care, it's so beautiful that it just knocks out all the

note = |reliable competition. I bisque at ^06 and am now firing at ^6. I have

note = |gone to ^9, but that seems to present more problems with pinholing

note = |and crazing. Also, I wash the ash. I have also used the same recipe

note = |with unwashed ash. The difference is that I would describe the

note = |unwashed ash glaze as stony matt and the washed ash glaze as opaque

note = |satin matt. Haven't tried this recipe at a lower temperature. You

note = |might want to give it a try. marjory r. kline

note = |

name = Rhodes Turquoise

index =

date = 11/15/98

source =

type = Zn B MidRoad

range = 2 - 5

firetype = Oxidation

color = Turquoise

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Zinc oxide

amount = 1040

component = Colemanite

amount = 1040

component = Barium carbonate

amount = 480

component = Talc

amount = 480

component = Keystone spar

amount = 3200

component = Flint

amount = 1760

addition = Tin oxide

addamount = 240

addition = Copper carbonate

addamount = 160

note = | Glaze Type: Zn B MidRoad. Opacity: . Firing type: Oxidation .

note = |

name = Rich Deep Red (2300F)

index =

date = 6/24/97

source =

type =

range = 6 - 8

firetype =

color = copper red

vistexture =

quality = glossy shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 52

component = Flint

amount = 18

component = Gerstley borate

amount = 10

component = Whiting

amount = 15

component = China clay

amount = 5

addition = Tin oxide

addamount = 1

addition = Silicon carbide

addamount = 0.5

addition = Copper carbonate

addamount = 0.5

note = |Can use a calcium borate frit instead of gerstley borate (try Ferro

note = |frit 3124). (fine SiC) In the book Glazes by Emmanuel Cooper (in the

note = |Complete Potter series), Mr. Cooper states: In electric kilns

note = |reduction be achieved in the glaze by the addition of small amounts

note = |of silicon carbide. A powerful flux such as calcium borate frit or

note = |borax frit is needed to break down the silicon carbide while the

note = |glaze also needs to be sufficiently fluid to allow the gas formed to

note = |be released if a smooth surface is required. I have not personally

note = |tried this. Have fun whomever wants to.... Anne Worner

note = |

name = Robbie Srtm. Revised (VC) 92

index =

date = 6/4/96

source =

type =

range = 4 - 9

firetype = Ox. or Red.

color = Opaque Blue Green

vistexture =

quality = Rock Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 56

component = Strontium carbonate

amount = 23

component = Lithium carbonate

amount = 4

component = Ball clay

amount = 6

component = Flint

amount = 11

addition = Copper carbonate

addamount = 4

note = |Tested AU Sp '92. Pref. 4% CuCO3 - surface a bit dry. Try with 2, 4,

note = |6, 8% CuCO3. VC ed

note = |

name = Ron Roy PMSP-4

index =

date = 4/3/98

source =

type =

range = 6 - 8

firetype = oxidation

color = clear

vistexture =

quality = glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3134

amount = 21

component = Nepheline syenite

amount = 19

component = Wollastonite

amount = 20

component = EPK

amount = 16

component = Flint

amount = 24

note = |Chemical Analysis Na2O 0.21 Al2O3 0.34 SiO2 3.28 K2O 0.03 B2O3 0.22

note = |MgO 0.02 CaO 0.74 Alumina:Silica ratio is 1.00 : 9.61 Neutral:Acid

note = |ratio is 1.00 : 5.85 Alkali:Neutral:Acid ratio is 1.00 : 0.56 : 3.28

note = |Expansion coefficient: 71.1 x 10e-7 per degree C Oxides causing

note = |abnormal expansion effects: B2O3 John Post jp6mchp@ Sterling

note = |Heights, Michigan

name = Rosie's Red

index =

date = 3/26/96

source =

type =

range = 6

firetype = Ox. or Red.

color = red

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Silica

amount = 29.69

component = Kaolin

amount = 4.95

component = Kona F-4 Feldspar

amount = 19.79

component = Talc

amount = 13.92

component = Gerstley borate

amount = 31.65

addition = Red iron oxide

addamount = 15.07

note = |A friend-from out-of-town-in-need-of-a-studio threw some beautiful

note = |bowls then obtained the following glaze from the stable of trusty

note = |glazes of our local London (Ontario) Potters' Guild studio. We

note = |weighed out a 2000 gram batch. It should have turned out to be a deep

note = |glossy burgundy red; instead, to our horror, it turned out dark

note = |reddish-brown, but dry matt and somewhat orange-peeled. I fired

note = |again, thinking it had underfired ... Same result. This leads me to

note = |wonder if either: 1) My solution for weighing out large quantities on

note = |my Ohaus Triple-Beam weigh scale is at fault: I compensate for the

note = |light plastic bucket placed on the scale in lieu of the pan by

note = |suspending a small bag of pennies and paperclips on one of the front

note = |prongs then adjust to balance. How do the rest of you weigh out large

note = |batches using the Triple Beam? or 2) Could there have been something

note = |wrong with the Red Iron Oxide? I say this because the finished

note = |surface is so rough and dry and bubbly/pebbly, it almost looks as

note = |though the glaze was saturated with iron, which in my experience

note = |usually acts as a flux rather than a refractory ingredient. I would

note = |really appreciate feedback on both of these possibilities, as perhaps

note = |all the test resutls I have done using my own formulas might be based

note = |on my own possibly misguided solution for weighing (meaning that

note = |noone else would be able to reproduce any of my formulas if I were to

note = |share them) and/or also as I don't want to use this iron supply in my

note = |own formulas if it's bad. submitted by: Nancy Warren e-mail:

note = |nwarren@julian.uwo.ca

note = |

name = Rowe brown

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = brown

vistexture =

quality = semi-gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Colemanite

amount = 50

component = EPK

amount = 20

component = Flint

amount = 30

addition = Manganese dioxide

addamount = 5

addition = Red iron oxide

addamount = 10

note = |Hello Anne, This is a neat brown semi-gloss for cone 6. I beleive it

note = |came from CM, June/81 page 78. It is called Rowe brown How are things

note = |in Ontario? Frank Simons fsimons@

note = |

name = Sana Green (C6 revision)

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = yellowish green

vistexture =

quality = satin matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Feldspar

amount = 30

component = Whiting

amount = 10

component = Gerstley borate

amount = 12

component = Strontium carbonate

amount = 8

component = Magnesium carbonate

amount = 3

component = EPK

amount = 5

component = Silica

amount = 32

addition = Tin oxide

addamount = 3

addition = Copper carbonate

addamount = 5

addition = Rutile

addamount = 5

addition = Bentonite

addamount = 2

note = |Lee, This Sana Green recipe was just recently on Clayart from

note = |someone. I apologize for not remembering who put it on. I tried it

note = |and found it to be a really nice satin finish soft yellowish green

note = |that fit my clay body very well. It has a pretty low coefficient of

note = |expansion, and looks good, though not as yellowish, without the

note = |rutile. I know this doesn't add up to 100, but that's the way it was

note = |posted. Here it is. Good Luck, Paul Lewing, Seattle pjlewing@

note = |

note = |

name = Sana's Green (original formula)

index =

date = 12/7/96

source =

type =

range = 6 - 10

firetype =

color = green

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 30.01

component = Whiting

amount = 9.99

component = Colemanite

amount = 12

component = Barium carbonate

amount = 8

component = Magnesium carbonate

amount = 3

component = EPK

amount = 5

component = Silica

amount = 32

addition = Tin oxide

addamount = 3

addition = Copper carbonate

addamount = 5

addition = Rutile

addamount = 5

addition = Bentonite

addamount = 2.06

note = |A few people asked me for the *original* Sana's Green recipe, so here

note = |it is. Richard Gralnik

note = |

name = Sana's Green rev.

index =

date = 12/7/96

source =

type =

range = 4 - 7

firetype = ox. or red.

color = green

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 30.9

component = Whiting

amount = 10.3

component = Colemanite

amount = 12.4

component = Strontium carbonate

amount = 5.3

component = Magnesium carbonate

amount = 3.1

component = EPK

amount = 5.1

component = Silica

amount = 32.9

addition = Tin oxide

addamount = 3.1

addition = Copper carbonate

addamount = 5.1

addition = Rutile

addamount = 5.1

addition = Bentonite

addamount = 2.1

note = |glaze archive queen Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

note = |

name = Sandy Bronze

index =

date = 12/6/96

source =

type =

range = 6

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ball clay

amount = 100

addition = Manganese dioxide

addamount = 400

addition = Copper carbonate

addamount = 100

note = |(fire to cone 7 in sitter) Note: Thin application for best color.

note = |rafael molina-rodriguez re: blistering of this

note = |type of glazes - I've had the same problem when firing this type of

note = |glaze on the bottom of an ancient Paragon High-fire kiln ( square,

note = |top-loading ). This kiln has approximately one cone differential from

note = |top to bottom. I solved the problem of already fired pieces by

note = |refiring them in a hotter zone of the kiln. The blisters

note = |disappearred. Now I place all bronze glazed pieces at or near the top.

note = |

name = Satin Base

index =

date = 12/6/96

source =

type =

range = 6

firetype = Ox. or Red.

color = base glaze - white

vistexture =

quality = satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 24

component = Kona F-4 feldspar

amount = 19

component = Wollastonite

amount = 14

component = Talc

amount = 11

component = OM-4 ball clay

amount = 12

component = Flint, fine mesh

amount = 20

note = |use OM-4 Ball clay or equal (eg, Bell Dark) use Custer feldspar (or

note = |equal, eg, G-200 f.s.) Recently, a glaze recipe for satin black was

note = |posted here with a request for revision to C6 brown in oxidation.

note = |Here is such a recipe. C6 Base Glaze, oxidation or reduction Add 2-5%

note = |iron oxide red for browns; 1-2% Cobalt carbonate for blues; 2-4%

note = |Copper carbonate for greens. Try other colourants for variation. On

note = |some bodies, the glaze may require a 30-minute soaking. The Seger

note = |formula for the revision above is: CaO 0.51; MgO 0.24; KNaO 0.25;

note = |Al2O3 0.40; SiO2 4.10 which places the glaze in the middle of the 3-7

note = |cone range. The glaze will be glossy Ratio = 10.3 and it should fit

note = |most stoneware bodies, perhaps even some porcelaineous stonewares

note = |since the Expansion coefficient is 6.6x10-6. The original glaze as

note = |cited was relying on the high level of colourant oxides to help bring

note = |it closer to balance but it would be overfired at C9 (if the body

note = |fails to release silica to the glaze). Tom Buck Hamilton ON Canada

note = |URL

note = |

name = Satin Base

index =

date = 12/6/96

source =

type =

range = 6

firetype = Ox. or Red.

color = base glaze - white

vistexture =

quality = satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 24

component = Kona F-4 feldspar

amount = 19

component = Wollastonite

amount = 14

component = Talc

amount = 11

component = OM-4 ball clay

amount = 12

component = Flint, fine mesh

amount = 20

note = |use OM-4 Ball clay or equal (eg, Bell Dark) use Custer feldspar (or

note = |equal, eg, G-200 f.s.) Recently, a glaze recipe for satin black was

note = |posted here with a request for revision to C6 brown in oxidation.

note = |Here is such a recipe. C6 Base Glaze, oxidation or reduction Add 2-5%

note = |iron oxide red for browns; 1-2% Cobalt carbonate for blues; 2-4%

note = |Copper carbonate for greens. Try other colourants for variation. On

note = |some bodies, the glaze may require a 30-minute soaking. The Seger

note = |formula for the revision above is: CaO 0.51; MgO 0.24; KNaO 0.25;

note = |Al2O3 0.40; SiO2 4.10 which places the glaze in the middle of the 3-7

note = |cone range. The glaze will be glossy Ratio = 10.3 and it should fit

note = |most stoneware bodies, perhaps even some porcelaineous stonewares

note = |since the Expansion coefficient is 6.6x10-6. The original glaze as

note = |cited was relying on the high level of colourant oxides to help bring

note = |it closer to balance but it would be overfired at C9 (if the body

note = |fails to release silica to the glaze). Tom Buck Hamilton ON Canada

note = |URL

note = |

name = Satin Base C. Gareri

index =

date = 7/19/95

source =

type = Mid-fire

range = 4 - 8

firetype = oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 34.1

component = EPK

amount = 1.8

component = Gerstley borate

amount = 16.3

component = Silica

amount = 31.8

component = Whiting

amount = 3.9

component = Zinc oxide

amount = 6.1

component = Barium carbonate

amount = 5.9

addition = Bentonite

addamount = 2

note = |I have never ommitted Barium in this ^4-^8 oxidation glaze actually i

note = |have not used the glaze in years. But it is a great oxidation glaze

note = |and I considered using it next year at the school where I teach.

note = |However, the barium scared me. IF barium Carb can not be ommited is

note = |there a safe substitute? submitted by: Charles Gareri e-mail:

note = |cgareri@ideanet.doe.state.in.us

name = Satin Black

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color = black

vistexture =

quality = satin matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = G-200 feldspar

amount = 24.07

component = Gerstley borate

amount = 14.81

component = Silica

amount = 24.07

component = EPK

amount = 20.37

component = Dolomite

amount = 16.67

addition = Cobalt carbonate

addamount = 2.5

addition = Black iron oxide

addamount = 13.89

note = |Here is my black cone 6 ox formula. This glaze is more satin than

note = |matt, however, additions of epk should give you what you want. The

note = |expansion number for this glaze is very low, but I think there is

note = |more chance of crazing than shivering. I don't know why but probably

note = |the high iron content increases the co-e of expansion. To increase

note = |matt 2-4 more parts of epk will probably do. I have tests using this

note = |base that look like old-fashion chalk boards. submitted by: Fraser

note = |Forsythe e-mail: forsythe@

note = |

name = Satin Clear Odyssey

index =

date = 05/19/2006

source =

type =

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 60

component = Strontium carbonate

amount = 20

component = Kentucky OM #4

amount = 10

component = Silica

amount = 9

component = Lithium carbonate

amount = 1

var = |+ stain 2-12 %

note = |From Highwater Clays catalog.

name = Satin Dixon 5-6

index =

date = 02/23/99

source =

type = Magnesium matt

range = 5-6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Transparent

xtals = None

bubbles = None

flow = None

durability =

flaws =

tested = tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Gerstley borate

amount = 2.9

component = Magnesium carb

amount = 2.9

component = Whiting

amount = 22.4

component = Nepheline syenite

amount = 22.7

component = Kaolin

amount = 20.3

component = Flint

amount = 28.8

var = |Use 50 frit 50 stain to decorate on top of raw glaze like majolica. To use this,

var = |use half water, half thick CMC gum solution for better brushing.

note = |From George Bowes. Good for stains/oxides. Great for purples and pinks.

note = |% of stain is important. Test. Apply 3 coats if brushing. To brush use CMC

note = |gum solution. Cloudy if fired below cone 5. Very stable glaze, good to

note = |paint on top of w/ stains & colorants.

name = Satin Dixon no GB

index =

date = 11/25/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws = Crawls

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Magnesium carbonate

amount = 2.9

component = Whiting

amount = 22.3

component = EPK

amount = 20.3

component = Nepheline syenite

amount = 22.6

component = Flint

amount = 20

component = Frit 3124

amount = 11.7

note = |Dixon re-calculated to eliminate Gerstley Borate.

name = Satin Dixon no GB Revised

index =

date = 11/25/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws = Crawls

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 6

component = Whiting

amount = 18.9

component = Calcined kaolin

amount = 8

component = Kaolin - theoretical

amount = 12.4

component = Custer feldspar

amount = 32

component = Silica

amount = 14.4

component = Frit 3134

amount = 7.4

note = |Dixon re-calculated to eliminate Gerstley Borate.

note = |Revised again to reduce crawling. MgCO3 to dolomite. Some calcined kaolin used.

name = Satin Dixon Revised Alyssa Welch

index =

date = 02/06/2007

source =

type =

range = 6

firetype = Oxidation

color =

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 7.4

component = Frit 3124

amount = 6.2

component = Whiting

amount = 18.3

component = Nepheline syenite

amount = 20.5

component = Kaolin

amount = 20.4

component = Flint

amount = 27.2

name = Satin Gloss Butter

index =

date = 05/19/2002

source =

type =

range = 6

firetype = Oxidation

color = Yellow

vistexture =

quality =

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3134

amount = 12.5

component = Custer feldspar

amount = 36.5

component = EPK

amount = 25

component = Dolomite

amount = 14.3

component = Flint

amount = 1.5

component = Wollastonite

amount = 8.5

component = Talc

amount = 16

addition = Tin oxide

addamount = 3

addition = Rutile

addamount = 5

name = Satin Matt 4

index =

date = 11/15/98

source =

type = Ca B AlMatt

range = 5 - 6

firetype = Ox or Red

color =

vistexture =

quality = Satin Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 4000

component = Clay

amount = 4000

note = | Glaze Type: Ca B AlMatt. Opacity: . Firing type: Ox or Red .

note = |

note = |

name = Satin Matt Xavier

index =

date = 07/26/00

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 40

component = Frit 3124

amount = 9

component = Whiting

amount = 16

component = Talc

amount = 9

component = EPK

amount = 10

component = Flint

amount = 16

note = |From Gregory D Lamont . Good base for colors.

name = Satin matt charcoal brown to black

index =

date = 4/10/95

source =

type =

range = 6 - 8

firetype =

color = charcoal brown to black

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

addition = Red iron oxide

addamount = 42.86

note = |Rob Wadey (robert wadey ) 9734B - 100 Ave

note = |Grande Prairie, Alberta t8V 0T6 Phone: (403) 538-3731 Fax: (403)

note = |538.3732

note = |

name = Satin Matt G218 Conrad's

index =

date = 11/15/98

source =

type =

range = 5-9

firetype = Ox. or Red.

color = Translucent White

vistexture =

quality = Satin Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 47

component = Flint

amount = 15

component = Talc

amount = 14

component = Gerstley borate

amount = 12

component = Dolomite

amount = 8

component = Kaolin

amount = 4

name = Satin Matt Kathy King

index =

date = 10/02/2002

source =

type = Mid-fire

range = 5-6

firetype = Oxidation

color = Clear

vistexture =

quality = Waxy

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 2.94

component = Magnesium carbonate

amount = 2.94

component = Whiting

amount = 22.35

component = Nepheline syenite

amount = 22.65

component = EPK

amount = 20.3

component = Flint

amount = 20

component = Frit 3124

amount = 8.82

var = |chartreuse = + 8 Drakenfeld of Mason Praes. yellow stain + 2 copper carb

var = |med. green = 8 Drakenfeld yellow stain + 4 copper

var = |pale green = 2 pras. yellow stain + 0.5 copper carb

var = |pale yellow = 1 Drak. yellow + 0.5 Turq. Mason stain

name = Satin Matt King- Pinnell recalc

index =

date = 03/02/2003

source =

type = Mid-fire

range = 8

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3124

amount = 15.9

component = Nepheline syenite

amount = 23.7

component = Dolomite

amount = 8.2

component = Wollastonite

amount = 24.6

component = EPK

amount = 20

component = Flint

amount = 7.7

note = |Re-calc from Pete Pinnell. Original glaze seemed to 'go bad' over time. Pete thought

note = |it might be the combo of GB, Mg Carb and EPK, as well as neph sy.

name = Satin Matt V.C. Good Color

index =

date = 6/4/96

source =

type = Ba Ca Na B

range = 5 - 6

firetype = Ox or Red

color = Semi-opaque

vistexture =

quality = Satin Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 50

component = Barium carbonate

amount = 22

component = Frit 3185

amount = 8

component = Whiting

amount = 5

component = EPK

amount = 5

component = Flint

amount = 10

note = |Glaze Type: Ba Ca Na B. Firing type: Ox or Red. From Val Cushing. VC

note = |ed

name = Satin Matt white L. A.

index =

date = 11/15/98

source =

type =

range = 5

firetype = Ox. or Red.

color = Opaque White

vistexture =

quality = Satin Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 60.2

component = Flint

amount = 5.8

component = Whiting

amount = 18.2

component = Zinc oxide

amount = 10

component = EPK

amount = 5.8

addition = Opax

addamount = 4

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse. A variation on L.A. Matt.

name = Satin Matte Gray-Green Pete's

index =

date = 02/29/2004

source =

type = Lithium Matt

range = 6

firetype = Oxidation

color = gray-green

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3134

amount = 8.5

component = Nepheline syenite

amount = 26

component = Spodumene

amount = 27.3

component = Strontium carbonate

amount = 15.5

component = Grolleg

amount = 14.3

component = Silica

amount = 7

component = Lithium carbonate

amount = 1.4

note = |Variation on Pete Pinnell's Weathered Bronze w/o lithium. See Clay Times article

note = |p.19 Mar/Apr. 2004. More grey than black w/green. More satin-y than Green-Black

note = |Pete's.

name = Satin no GB

index =

date = 04/24/2004

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Waxy

transparency = Translucent

xtals =

bubbles =

flow = Slight

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 10

component = Whiting

amount = 13.3

component = Custer feldspar

amount = 36.5

component = EPK

amount = 23.5

component = Frit 3134

amount = 16.7

note = |Developed by Valerie Duncan

name = SATIN OATMEAL

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = off white

vistexture =

quality = satin matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 37.84

component = Dolomite

amount = 5.41

component = Whiting

amount = 4.86

component = Kaolin

amount = 8.65

component = Flint

amount = 12.97

component = Gerstley borate

amount = 18.38

component = Talc

amount = 11.89

addition = Titanium dioxide

addamount = 3.78

addition = Zircopax

addamount = 4.32

note = |(the club's standard oatmeal was too runny - my variation sits better

note = |and is a good base glaze. Surface waxy where thinnish, to glossy if

note = |thick. Underglaze painting shows through with softened edges. The

note = |titanium makes it reactive when over-dipped with some other glazes,

note = |and you may get areas of aventurine.) Here are a couple of standards

note = |from the Richmond Potters Club, and a few of my own formulation that

note = |have worked well in ^6 oxidation. They aren't revolutionary (my

note = |exciting ones have things like barium in them, or are less

note = |predictable for a classroom situation) but they have been reliable,

note = |and allow for some play. They all calculate out to well within the

note = |INSIGHT limit formulas for maturity at ^6. If anyone tests these and

note = |comes up with problems, new ideas, good variations etc. could they

note = |let me know? I'll look forward to a larger list being posted to

note = |clayart. Veronica Shelford e-mail: shelford@ s-mail: P.O.

note = |Box 6-15 Thetis Island, BC V0R 2Y0 Tel: (250) 246-1509

name = SATIN OATMEAL

index =

date = 6/24/97

source =

type = Magnesium matt

range = 6

firetype = Oxidation

color = off white

vistexture =

quality = Waxy

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 37.84

component = Dolomite

amount = 5.41

component = Whiting

amount = 4.86

component = Kaolin

amount = 8.65

component = Flint

amount = 12.97

component = Gerstley borate

amount = 18.38

component = Talc

amount = 11.89

addition = Titanium dioxide

addamount = 3.78

addition = Zircopax

addamount = 4.32

note = |(the club's standard oatmeal was too runny - my variation sits better

note = |and is a good base glaze. Surface waxy where thinnish, to glossy if

note = |thick. Underglaze painting shows through with softened edges. The

note = |titanium makes it reactive when over-dipped with some other glazes,

note = |and you may get areas of aventurine.) Here are a couple of standards

note = |from the Richmond Potters Club, and a few of my own formulation that

note = |have worked well in ^6 oxidation. They aren't revolutionary (my

note = |exciting ones have things like barium in them, or are less

note = |predictable for a classroom situation) but they have been reliable,

note = |and allow for some play. They all calculate out to well within the

note = |INSIGHT limit formulas for maturity at ^6. If anyone tests these and

note = |comes up with problems, new ideas, good variations etc. could they

note = |let me know? I'll look forward to a larger list being posted to

note = |clayart. Veronica Shelford e-mail: shelford@ s-mail: P.O.

note = |Box 6-15 Thetis Island, BC V0R 2Y0 Tel: (250) 246-1509

name = Satin Spodumene

index =

date = 4/21/95

source =

type =

range = 6

firetype = reduction

color = pale yellow ivory or very opaqu

vistexture =

quality = satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 30

component = Dolomite

amount = 24

component = Custer feldspar

amount = 21

component = Silica

amount = 12

component = Kaolin

amount = 9

component = Gerstley borate

amount = 4

addition = Zircopax

addamount = 5

note = |kiln type: gas Color depends upon the type of spodumene. submitted

note = |by: John Anthony e-mail: JTRAX@

note = |

name = Satin Wanamaker (Jeff Dietrich)

index =

date = 4/7/95

source =

type =

range = 6 - 7

firetype = Oxidation

color =

vistexture =

quality = Satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 18.39

component = Spodumene

amount = 11.5

component = Nepheline syenite

amount = 51.71

component = Ball clay

amount = 13.8

component = Zinc oxide

amount = 4.6

addition = Titanium dioxide

addamount = 2.3

note = |Finely Textured Satin matt - Do not apply too thick as it will

note = |bubble. I substituted Rutile for Titanium Dioxide because I didn't

note = |have any and it worked fine. Just don't double dip unless glaze if

note = |very thin. I liked how this worked over texture. They are dependable

note = |firing to firing in Cone 6 electric on dark clay. From Jeff Dietrich

note = |in Ceramics Montly, April 1991 & sent via ClayArt by Phyllis Nelson

note = |Baldwin City, Kansas E-mail: NELSON@george.bakeru.edu

name = SCVC 5

index =

date = 11/15/98

source =

type = Ca Mg

range = 5 - 6

firetype = Ox or Red

color = White

vistexture =

quality = Satin, Waxy Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 3200

component = Frit 3124

amount = 720

component = Talc

amount = 720

component = Whiting

amount = 1280

component = EPK

amount = 800

component = Flint

amount = 1280

note = | Glaze Type: Ca Mg. Opacity: ?. Firing type: Ox or Red .

note = |

note = |

name = Sea Foam

index =

date = 4/21/95

source =

type =

range = 6

firetype = Ox. or Red.

color = varies -see comments

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 Feldspar

amount = 34

component = Nepheline syenite

amount = 17

component = Whiting

amount = 12.6

component = Barium carbonate

amount = 1.6

component = Zinc oxide

amount = 6

component = Gerstley borate

amount = 3.3

component = Dolomite

amount = 2.6

component = Talc

amount = 3.3

component = Kaolin

amount = 12.3

component = Silica

amount = 7.3

note = |With 4% manganese and 0.5% Cobalt Carbonate a brown bronzey type of

note = |gun metal underneath. With 1.5% Copper Carbonate and 0.5% Cobalt

note = |Carbonate it is a blue green. With 1% copper carbonate and 6% rutile

note = |it is a terrific green with mottled yellow. This combination has been

note = |made a studio glaze and we have named it 'sea Foam' It is especially

note = |stunning on dark red clay bodies. submitted by: Debra Drencicki

note = |e-mail: DKREN@

note = |

name = Seafoam Pete's

index =

date = 02/29/2004

source =

type = Alkaline

range = 6

firetype = Oxidation

color = Green

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3134

amount = 9

component = F-4 spar

amount = 51.3

component = Strontium carbonate

amount = 25.5

component = Grolleg

amount = 13.6

addition = Copper carbonate

addamount = 5

addition = Titanium dioxide

addamount = 5

note = |Variation on Pete Pinnell's Weathered Bronze w/o lithium. See Clay Times article

note = |p.19 Mar/Apr. 2004. More of a satin-matt. Breaks white/light green. A

note = |better-behaved raw glaze w/o lithium.

name = Semi-gloss gray-brown

index =

date = 4/10/95

source =

type =

range = 5

firetype = Oxidation

color = gray- brown

vistexture =

quality = semi-gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany Slip

amount = 60

component = Nepheline syenite

amount = 40

note = |Rob Wadey (robert wadey ) 9734B - 100 Ave Grande Prairie, Alberta t8V

note = |0T6 Phone: (403) 538-3731 Fax: (403) 538.3732

note = |

name = Semi-transparent Matte

index =

date = 12/7/96

source =

type =

range = 5

firetype = oxidation

color = semi-transparent

vistexture =

quality = matte:

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 4.1

component = Frit 3195

amount = 41.54

component = G-200 Feldspar

amount = 16.92

component = EPK

amount = 6.67

component = Flint

amount = 30.77

addition = Bentonite

addamount = 2.56

note = |I got this glaze from Ceramics Monthly and when I tested it -- I

note = |thought it was wonderful, but when I put it on a few larger pieces it

note = |was awful!! I'm not quite ready to give up on it. Can someone look it

note = |over and make suggestions about the portions of chemicals? On the

note = |tests it was a semi-transparent matt. On the larger pieces it ended

note = |up black and crusty and cratery. Yuck! Any help would be appreciated.

note = |Waiting hopefully with my crusty pots. Sue sue hintz

note = |

name = SG Dryish Stone Matt

index =

date = 11/15/98

source =

type = Mg Ca Na

range = 5 - 6

firetype = Reduction

color = Peacock Blue

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Neph Sye

amount = 3360

component = Gerstley borate

amount = 960

component = Dolomite

amount = 560

component = Talc

amount = 1120

component = EPK

amount = 400

component = Flint

amount = 1600

addition = Cobalt carbonate

addamount = 40

addition = Chrome oxide

addamount = 40

addition = Iron oxide

addamount = 40

note = |Colorants listed give "Peacock Blue". Glaze Type: Mg Ca Na . Opacity:

note = |?. Firing type: Reduction .

note = |

note = |

name = SG Less Silky Test

index =

date = 10/13/97

source =

type = Magnesium matt

range = cone 5-6

firetype = Oxidation

color = Clear

vistexture =

quality = Waxy

transparency = Translucent

xtals = None

bubbles = None

flow = None

durability =

flaws =

tested = tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Gerstley borate

amount = 17.704

component = Nepheline syenite

amount = 28.462

component = Dolomite

amount = 10.704

component = Magnesium carb

amount = 4.275

component = EPK

amount = 6.588

component = Flint

amount = 32.267

var = |Add zircopax for waxy white.

note = |Frosty thick.

name = SG Silky

index =

date = 11/15/98

source =

type =

range = 5

firetype = Oxidation

color = Translucent White

vistexture =

quality = Semi-Matte or Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley

amount = 18

component = Kona F-4

amount = 40

note = |From Posey Bacopoulos. Yellow: 10% vanadium stain. Turq.: 3% copper

note = |Carb. Lavender: 0.25% cobalt carb + 2% rutile.

note = |

note = |

name = SG Silky c 5-6

index =

date = 08/24/98

source =

type =

range = 5-6

firetype = Oxidation

color = Frosty

vistexture =

quality = Satin matt

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 18

component = Flint

amount = 17

component = EPK

amount = 4

component = Talc

amount = 13

component = Dolomite

amount = 8

component = Kona F-4

amount = 40

addition = Zircopax

addamount = 10

addition = Bentonite

addamount = 2

var = |yellow: 10% vanadium stain

var = |turquoise: 3% CuCO3

var = |lavender: 0.25% CoCO3 + 2% Rutile

note = |from Posey Bacopoulos

name = SG-42 Clear Glaze

index =

date = 12/6/96

source =

type =

range = 5 - 7

firetype = Ox. or Red.

color = clear

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Pemco Frit P-626

amount = 20.58

component = Nepheline syenite

amount = 23.85

component = Wollastonite

amount = 13.85

component = Whiting

amount = 4.62

component = EPK

amount = 6.83

component = Silica, 325 mesh

amount = 30.28

addition = Bentonite

addamount = 1.92

note = |C.M.C. 1 tsp I have been off-line for several days (art fair

note = |a'comin') and upon retrieving my e-mail found several of you

note = |interested in my recipe for a cone 6 clear glaze that worked well

note = |(for me, anyway) over underglazes. (Sorry for the delay) It works

note = |over the Amaco Reward Velvet Underglazes, including reds, purples,

note = |etc. I will post the original recipe and then add my revisions. OK.

note = |The above glaze crazed on my A.R.T. #135 porcelain at cone 6. Being

note = |absolutely non-technical, I stumbled in to the following

note = |substitution: I substituted calcined kaolin (comercial name Glomax,

note = |from A.R.T.) for the EPK. I also substituted Amorphous Silica for the

note = |Flint. I don't use C.M.C. I do add Flocs...it settles out. It is

note = |glossy and very clear. My samples from two/three years ago still look

note = |good, no delayed crazing. I don't use it on anything, because I found

note = |a whole palette of glazes while I was looking for a good clear, and

note = |have lost interest in underglaze decorating. The pursuit was

note = |interesting, though ;-) I found the Pemco Frit 626 through Trinity

note = |supply in Texas. I do not know about substitutes. submitted by:

note = |Candice Roeder e-mail: CRoeder@worldnet. source for original

note = |recipe: James Chappell

note = |

name = Shaner Revision

index =

date = 03/02/2003

source =

type = Mid-fire

range = 5-6

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = cuts

amount = 30

component = Nepheline syenite

amount = 30

component = Whiting

amount = 20

component = Talc

amount = 4

var = |Red: + bone ash 6 + iron 4

var = |Gold: + rutile 4

name = Shaner Revision 1

index =

date = 11/15/98

source =

type = Ca AlMatt MidRoad

range = 5 - 6

firetype = Reduction

color = Gold

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer spar

amount = 2424

component = Nepheline Sye

amount = 2424

component = Whiting

amount = 1616

component = Talc

amount = 323

component = Kaolin

amount = 727

component = Bone ash

amount = 485

addition = Iron oxide

addamount = 323

addition = Rutile

addamount = 323

note = |Looks like Shaner Gold. Glaze Type: Ca AlMatt MidRoad. Opacity: .

note = |Firing type: Reduction .

note = |

note = |

name = Shaner Revision 2

index =

date = 11/15/98

source =

type = Ca MidRoad AlMatt

range = 5 - 6

firetype = Reduction

color = Gold

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer spar

amount = 1861

component = Nepheline Sye

amount = 2790

component = Whiting

amount = 1861

component = Talc

amount = 465

component = Kaolin

amount = 465

component = Bone ash

amount = 558

addition = Iron oxide

addamount = 372

addition = Rutile

addamount = 372

note = | Glaze Type: Ca MidRoad AlMatt. Opacity: . Firing type: Reduction .

note = |

note = |

name = Shimmer

index =

date = 7/19/95

source =

type =

range = 4 - 8

firetype =

color =

vistexture =

quality = matt to glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 44.55

component = Whiting

amount = 21.78

component = Silica

amount = 12.87

component = China clay

amount = 14.85

component = Lithium carbonate

amount = 5.94

note = |for green, add 6 gr rutile + 2 gr Cobalt Carbonate + 1 gr bentonite ,

note = |for blue add .5% Cobalt Carbonate AT cone 4-5 these glazes are a

note = |wonderful matt; higher they turn 'glossy'. I especially did not like

note = |the green at this temperature - too hard and glassy looking. These

note = |recipes came from Capilano College in North Vancouver (Canada) where

note = |I took a glaze course. submitted by: Penny Anagnostopoulos e-mail:

note = |panagnos@VCC.BC.CA

note = |

name = Shino

index =

date = 3/26/96

source =

type =

range = 6

firetype = reduction

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 40

component = Spodumene

amount = 40

component = EPK

amount = 10

component = Soda ash

amount = 10

note = |For 2 years I struggled with this concept & finally gave up. The fuel

note = |savings (?) were not worth the effort. The results don't compare to

note = |^10. I agree with Peter Pinnell- sell another mug to pay for the

note = |difference in firing costs. Due to the lower sintering point of ^6

note = |glazes- you have to start reduction fairly early- at least by

note = |stoneware standards. Try ^010 as a starting point & go from there. I

note = |also used a clay body that had a higher iron content than my present

note = |^10 body- it seemed to make a difference. submitted by: Tom Gray

note = |e-mail: tgraypots@

note = |

name = Shino Falls Creek

index =

date = 7/19/95

source =

type = Shino

range = 5 - 7

firetype = Reduction

color =

vistexture =

quality = Semi-gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Alberta slip

amount = 56.07

component = Gerstley borate

amount = 18.69

component = Kona F-4 feldspar

amount = 9.35

component = Silica

amount = 9.35

component = Lithium carbonate

amount = 6.54

addition = Superpax

addamount = 9.35

addition = Tin oxide

addamount = 4.67

note = |Last year this was published on Clayart, I have used it and I like it

note = |a lot over a red stoneware (not exactly a shino though), but I find

note = |it less pleasant over white clay. I fire it to ^6 submitted by:

note = |Michelle Lowe e-mail: mishlowe@ e-mail:

note = |mishlowe@aztec.asu.edu

name = Shino Falls Creek

index =

date = 7/19/95

source =

type = Mid-fire

range = 5 - 7

firetype = oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Alberta slip

amount = 56.1

component = Gerstley borate

amount = 18.7

component = Kona F-4 feldspar

amount = 9.4

component = Silica

amount = 9.4

component = Lithium carbonate

amount = 6.5

addition = Superpax

addamount = 9.4

addition = Tin oxide

addamount = 4.7

note = |Last year this was published on Clayart, I have used it and I like it

note = |a lot over a red stoneware (not exactly a shino though), but I find

note = |it less pleasant over white clay. I fire it to ^6 submitted by:

note = |Michelle Lowe e-mail: mishlowe@ e-mail:

note = |mishlowe@aztec.asu.edu

name = Shino type Glaze

index =

date = 9/20/95

source =

type =

range = 6

firetype =

color = translucent

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 5

component = Soda ash

amount = 4

component = Spodumene

amount = 22

component = Nepheline syenite

amount = 54

component = Kentucky OM #4

amount = 15

addition = Bentonite

addamount = 1.5

note = |best in salt or woodfire. good over iron wash. source for original

note = |recipe: Crain Edwards submitted by: Lee Love e-mail:

note = |leelove@mill2.

note = |

name = Shiny

index =

date = 11/15/98

source =

type =

range = 5

firetype = Oxidation

color = Transparent Clear

vistexture =

quality = Shiny or Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 25.5

component = Flint

amount = 3

component = Kaolin

amount = 10

component = Dolomite

amount = 10

component = Gerstley borate

amount = 20

component = Tin oxide

amount = 2.8

component = Zinc oxide

amount = 10

addition = Bentonite

addamount = 2

note = |From Posey Bacopoulos. Blue 1.4% zircopax + 1.7% cobalt + 3% rutile.

note = |Turquiose: 1.4% zircopax + 3% copper carb. + 0.1% cobalt carb.

note = |

name = Shiny cone 5-6

index =

date = 08/24/98

source =

type =

range = 5-6

firetype = Oxidation

color = Clear

vistexture =

quality = Gloss

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Kona F-4

amount = 24

component = Flint

amount = 28

component = EPK

amount = 9

component = Dolomite

amount = 9

component = Gerstley borate

amount = 18

component = Tin oxide

amount = 3

component = Zinc oxide

amount = 9

addition = Bentonite

addamount = 2

var = |Blue: 1.4% zircopax + 1.7% Co + 3% rutile

var = |turquoise: 1.4% zircopax + 3% CuCO3 + 0.1 % CoCO3 (one tenth percent)

note = |From Posey Bacopoulos

name = Shiny Transparent

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = Transparent Clear

vistexture =

quality = Glossy or shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = Petalite

amount = 40

component = Flint

amount = 10

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse.

note = |

name = Silky Black Matt

index =

date = 3/26/96

source =

type =

range = 5 - 6

firetype = Ox. or Red.

color = Opaque Black

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 7.51

component = Talc

amount = 5.42

component = Dolomite

amount = 3.34

component = Kona F-4 feldspar

amount = 16.69

component = Neph Sye

amount = 32.93

component = Whiting

amount = 7.12

component = Zinc oxide

amount = 6.45

component = EPK

amount = 12.57

component = Flint

amount = 7.96

addition = Cobalt oxide

addamount = 0.11

addition = Copper Oxide

addamount = 0.33

addition = Red iron oxide

addamount = 0.33

addition = Bentonite

addamount = 0.11

note = |from Michelle Lowe, potter in the Phoenix desert

note = |mishlowe@ mishlowe@aztec.asu.edu

note = |

name = Simple Clear Glaze

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 44.67

component = EPK

amount = 26.81

component = Silica

amount = 28.52

note = |Hope this works for ya'll. It has worked on a variety of clays for me

note = |and I have used it over underglazes. It is a cone 6 oxidation glaze.

note = |submitted by: Cindy P Russell e-mail: crussel@tenet.edu

note = |

name = Slip #1818 Kawai

index =

date = 6/3/96

source =

type = Slip

range = 6 - 10

firetype = Ox. or Red.

color = White

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 80

component = Grog (150 mesh)

amount = 20

note = |Add color to taste. I promised a while back to list this when I found

note = |it! Kawai used a lot of thick slip trailing in his work and this was

note = |given to me by one of his apprentices, Doug Lawrie. submitted by:

note = |June M. Perry e-mail: GURUSHAKTI@

name = Slip #1818 Kawai

index =

date = 6/3/96

source =

type =

range = 6 - 10

firetype =

color =

vistexture =

quality = Slip or Engobe

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 80

component = Grog (150 mesh)

amount = 20

note = |Add color to taste. I promised a while back to list this when I found

note = |it! Kawai used a lot of thick slip trailing in his work and this was

note = |given to me by one of his apprentices, Doug Lawrie. submitted by:

note = |June M. Perry e-mail: GURUSHAKTI@

name = slip Barranger

index =

date = 10/23/2002

source =

type = Slip

range = 5-6

firetype = Ox. or Red.

color = White

vistexture =

quality = unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 15

component = Ball clay

amount = 25

component = EPK

amount = 25

component = Frit 3124

amount = 10

component = Flint

amount = 25

var = |Black: rio 8 + black stain 10

var = |Blue black: Co 2 + black stain 10

var = |cream: rutile 5-6%

var = |blue-green: CrO 3 + Co 1.5

var = |pink: Pink stain 10

var = |teal: teal stain 6 + copper carb 3

var = |med blue: rutile 3 + Co 1

var = |strong green: CrO 6

var = |any stain 8-12%

name = Slip G-String Slap-On Slick Thick

index =

date = 3/26/96

source =

type =

range = 5

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 20

component = Feldspar

amount = 20

component = Silica

amount = 20

component = Ball clay

amount = 40

note = |Simple. It works. Can't be too thick. I've used OM-4, but would try

note = |Sagger xx, as the current notion seems to be that it has fewer

note = |problems. This slip will work on bisque, though needs to be thinner.

note = |The originator, Rob Forbes, applied the stuff with a three inch paint

note = |brush in thick swabs. He fired to cone 5. It is currently being used

note = |at cone 10. Enjoy - HP submitted by: Henry Pope e-mail:

note = |mikpo@et.chv.va.us

name = Slip Hands in Clay white

index =

date = 8/8/97

source =

type =

range = 6 - 11

firetype =

color = white

vistexture =

quality = engobe or slip

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 23

component = Ball clay

amount = 22

component = Feldspar

amount = 20

component = Flint

amount = 30

component = Borax

amount = 5

note = |I have been using a slip recipe that I got form HANDS IN CLAY for

note = |quite awhile. It works wonderfully..I mix up a 5 gallon pail of it,

note = |then put smaller amounts in jars and add mason stains to different

note = |jars to get the colors i want - I really don't measure, just add

note = |enough by sight until it looks right. One of those small sample

note = |packets (1/4 ounce?) usually does great in a cottage cheese container

note = |filled with the white slip. Then I brush the slip on green pots, let

note = |it dry overnight if it's humid summer in northern Wisconsin, or cover

note = |with plastic overnight if the woodstove is on...the waiting makes the

note = |carving through the slip give a nicer line I feel. Once my drawings

note = |are done, I bisque, then cover with a clear glaze and fire to cone 7

note = |or 8. the nice thing about this slip recipe is that it is good for

note = |cones 6-11, and it's true because I've used it in my electric kiln at

note = |6 and my wood kiln at 12! Joan Slack-DeBrock/River Run Pottery

note = |P.O.Box 95 McNaughton, WI 54543 715-277-2773 riverrun@

name = Slip Ozona Burgundy

index =

date = 6/24/97

source =

type = Slip

range = 6

firetype =

color = deep brick red

vistexture =

quality = unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = A.P. Green fireclay

amount = 80

component = GoldArt

amount = 20

addition = chrome oxide

addamount = 1

addition = Iron oxide

addamount = 2

note = |I've applied them to bone dry sculptural work, bisqued them and then

note = |have rubbed stains or oxides into the recesses, sponging off, then

note = |fired again for permanence. They are quite versatile. These recipes

note = |are from Zakin's book on Electric Kiln Ceramics. Some of the clays

note = |used in the recipe are coarse and the slip should not be strined. The

note = |result will be a coarse, sandy-textured surface, not for functional

note = |pieces. They may be applied by dipping, spraying or brushing. They

note = |may be applied to greenware or bisqued ware. They may be used alone

note = |or with stains and glazes. The appearance when fired is soft and

note = |sandy. Candice Roeder

name = slip Ozona gritty variations

index =

date = 6/24/97

source =

type = Slip

range = 6

firetype =

color = tan - add color

vistexture =

quality = stony slip or engobe

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = A.P. Green fireclay

amount = 70

component = GoldArt

amount = 20

component = Ball clay

amount = 10

note = |Tan Gray-green add: Chrome oxide 3 Tan Gray-blue add: Cobalt oxide 1

note = |Iron oxide 1 I've applied them to bone dry sculptural work, bisqued

note = |them and then have rubbed stains or oxides into the recesses,

note = |sponging off, then fired again for permanence. They are quite

note = |versatile. These recipes are from Zakin's book on Electric Kiln

note = |Ceramics. Some of the clays used in the recipe are coarse and the

note = |slip should not be strined. The result will be a coarse,

note = |sandy-textured surface, not for functional pieces. They may be

note = |applied by dipping, spraying or brushing. They may be applied to

note = |greenware or bisqued ware. They may be used alone or with stains and

note = |glazes. The appearance when fired is soft and sandy. Candice Roeder

note = |

name = Slip Ozona Naples Yellow

index =

date = 6/24/97

source =

type = Slip

range = 6

firetype = Oxidation

color = light ochre

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = A.P. Green fireclay

amount = 40

component = Cedar Heights Goldart

amount = 40

component = Cedar Heights Redart

amount = 12

component = Ball clay

amount = 6

component = Wollastonite

amount = 2

note = |I've applied them to bone dry sculptural work, bisqued them and then

note = |have rubbed stains or oxides into the recesses, sponging off, then

note = |fired again for permanence. They are quite versatile. These recipes

note = |are from Zakin's book on Electric Kiln Ceramics. Some of the clays

note = |used in the recipe are coarse and the slip should not be strined. The

note = |result will be a coarse, sandy-textured surface, not for functional

note = |pieces. They may be applied by dipping, spraying or brushing. They

note = |may be applied to greenware or bisqued ware. They may be used alone

note = |or with stains and glazes. The appearance when fired is soft and

note = |sandy. Candice Roeder

name = Slip Ozona Red

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = brick red

vistexture =

quality = stony slip or engobe

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = A.P. Green fireclay

amount = 60

component = Cedar Heights Goldart

amount = 15

component = Cedar Heights Redart

amount = 25

note = |I've applied them to bone dry sculptural work, bisqued them and then

note = |have rubbed stains or oxides into the recesses, sponging off, then

note = |fired again for permanence. They are quite versatile. These recipes

note = |are from Zakin's book on Electric Kiln Ceramics. Some of the clays

note = |used in the recipe are coarse and the slip should not be strained. The

note = |result will be a coarse, sandy-textured surface, not for functional

note = |pieces. They may be applied by dipping, spraying or brushing. They

note = |may be applied to greenware or bisqued ware. They may be used alone

note = |or with stains and glazes. The appearance when fired is soft and

note = |sandy. Candice Roeder

name = slip redart

index =

date = 10/23/2002

source =

type = Slip

range = 5-6

firetype = Ox. or Red.

color =

vistexture =

quality = unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Redart

amount = 84.2

component = Spodumene

amount = 10.5

component = Frit 3124

amount = 3.2

component = Lithium carbonate

amount = 2.1

note = |From Mary Barranger

name = Slip Rob's White

index =

date = 08/04/2003

source =

type = Slip

range = 5-6

firetype = Ox. or Red.

color = White

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ball clay

amount = 30

component = Kaolin

amount = 10

component = Talc

amount = 30

component = Flint

amount = 30

name = Slip Ron Meyers

index =

date = 10/06/2006

source =

type = Slip

range = 02

firetype = Ox. or Red.

color = White

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = EPK

amount = 31.3

component = Kentucky OM #4

amount = 18

component = potspar

amount = 24.9

component = Flint

amount = 17.5

addition = Zircopax Plus

addamount = 7.4

addition = Soda ash

addamount = 0.2

addition = Sodium silicate

addamount = 0.2

name = Slip Ron Meyers

index =

date = 10/06/2006

source =

type = Slip

range = 02

firetype = Ox. or Red.

color = White

vistexture =

quality = Unglazed

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = EPK

amount = 31.34

component = Kentucky OM #4

amount = 18

component = potspar

amount = 24.89

component = Flint

amount = 17.51

addition = Zircopax Plus

addamount = 7.37

addition = Soda ash

addamount = 0.23

addition = Sodium silicate

addamount = 0.23

name = Slip Rutile

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color =

vistexture =

quality = slip mottled furry texture

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 60

component = Frit 5301

amount = 40

addition = Rutile

addamount = 4

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse.

name = slip Yellow Ozona Naples

index =

date = 6/24/97

source =

type = Slip

range = 6

firetype =

color = light ochre

vistexture =

quality = stony slip or engobe

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = A.P. Green fireclay

amount = 40

component = Cedar Heights Goldart

amount = 40

component = Cedar Heights Redart

amount = 12

component = Ball clay

amount = 6

component = Wollastonite

amount = 2

note = |I've applied them to bone dry sculptural work, bisqued them and then

note = |have rubbed stains or oxides into the recesses, sponging off, then

note = |fired again for permanence. They are quite versatile. These recipes

note = |are from Zakin's book on Electric Kiln Ceramics. Some of the clays

note = |used in the recipe are coarse and the slip should not be strined. The

note = |result will be a coarse, sandy-textured surface, not for functional

note = |pieces. They may be applied by dipping, spraying or brushing. They

note = |may be applied to greenware or bisqued ware. They may be used alone

note = |or with stains and glazes. The appearance when fired is soft and

note = |sandy. Candice Roeder

name = Soft Green with Pink Flecks

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color = light green

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 67

component = Dolomite

amount = 10

component = EPK

amount = 8

component = Silica

amount = 9

component = Zinc oxide

amount = 6

addition = Copper carbonate

addamount = 3

note = |Exquisite light green gloss but no pink flecks Tested on Dillo White

note = |clay at a full ^6. submitted by: Lori Wilkinson e-mail:

note = |lorwilk@

note = |

name = SOFT MATT ONE

index =

date = 4/10/95

source =

type =

range = 5 - 6

firetype =

color =

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barium carbonate

amount = 8.18

component = Flint

amount = 11.82

component = Gerstley borate

amount = 10

component = Kaolin

amount = 10

component = Lithium carbonate

amount = 4.55

component = Nepheline syenite

amount = 49.09

component = Zinc oxide

amount = 1.82

component = Cryolite

amount = 4.55

addition = Tin oxide

addamount = 1.82

addition = Zircopax

addamount = 4.55

note = |This produces a soft white matt glaze. One might wish to substitute

note = |magnesium carbonate for the barium especially for use on functional

note = |ware. SIGNIFICANT INGREDIENTS IN THE GLAZE gertsley borate is a flux,

note = |it contributes boron and sodium to the glaze and it encourages very

note = |strong melts. Kaolin contributes silica and alumina and it has few

note = |impurities, is highly refractory, controls the glaxe flow and it is

note = |neutral in color but contributes to a mat surface. Lithium carbonate

note = |is a powerfull flux and it encourages shiny surfaces and produces

note = |glazes with strong visual textures. This glaze contains a great deal

note = |of lithium, such glazes may flake off of the ware and one should not

note = |use more then 5%. Neph syn is a feldspar, it contributes silica,

note = |alumina and powerfull fluxes to the glaze. Tin is an opacifier. Zinc

note = |is a flux and in moderate amounts it is a storng melter and

note = |encourages good glaze durability. This is a high alumina glaze which

note = |shall have a rather modest glaze flow. It will be a soft white matt

note = |or a satin matt. Without barium it may be more towards the satin matt

note = |texture. Harold J. McWHINNIE Email:Harold_J_McWHINNIE@umail.umd.edu

note = |(hm9) Phone:53125

note = |

name = SPECKLED BEIGE

index =

date = 8/8/97

source =

type =

range = 6

firetype =

color = Opaque tan

vistexture =

quality = Semi matte or satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 14.71

component = Spodumene

amount = 31.59

component = EPK

amount = 3.16

component = Dolomite

amount = 7.37

component = Talc

amount = 13.69

component = Flint

amount = 29.48

addition = Granular manganese

addamount = 0.53

addition = Manganese dioxide (milled)

addamount = 0.53

note = |I work in Cone 6 oxidation (electric) and would like to explore some

note = |speckled type glazes. My homework tells me that granular manganese

note = |dioxide (black specks) and granular illmenite (iron oxide specks) are

note = |the most common additives. BUT...are there others? And, what happens

note = |when you add a granular item to an already successful glaze? I know,

note = |test and find out. Of course a little help from my friends would

note = |expedite matters. Especially if you had a glaze to start me out on.

note = |Can Speckles get really big? (sure Dan fire in reduction) Here's a

note = |recipe that Bonnie Hellman sent me that got me thinking about this

note = |speckley business: Best Wishes Dan Saultman in Horribly Hot Colorado

note = |(100's today)

note = |

name = Speirs slip

index =

date = 6/24/97

source =

type =

range = 5 - 10

firetype =

color = base slip

vistexture =

quality = slip or engobe

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 30

component = Ball clay

amount = 25

component = Feldspar

amount = 20

component = Flint

amount = 25

note = |I have used this successfully at ^5-^10. I also usually add about l

note = |Tbls. glycerin to a 300gm batch to aid in smooth application. Some

note = |colorants I add: Pink - DeGussa 10-15% Red - DeGussa @35% Baby blue -

note = |cobalt carb 0.75 Grey blue - cobalt carb 2, RIO 2 Navy blue - cobalt

note = |carb 5, chrome 1 Black - cobalt carb 6, chrome 6, RIO 10 (I have not

note = |tried this but got it from the recipe book at Oregon School of Arts &

note = |Crafts) Olive green - chrome 6 Med. blue - cobalt carb 1, rutile 1

note = |RE: the latest info on Clayart regarding DeGussa Stain (i.e. cadmium)

note = |toxicity - I did not receive any such information when I bought the

note = |stain either. I believed it was safe because it is ENCAPSULATED. I am

note = |grateful to those who wrote to inform us. Laura in Oregon

name = Spodumene

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 47.37

component = EPK

amount = 10.53

component = Whiting

amount = 5.26

component = Dolomite

amount = 10.53

component = Spodumene

amount = 21.05

component = Soda ash

amount = 5.26

addition = Ultrox

addamount = 5.26

note = |For 2 years I struggled with this concept & finally gave up. The fuel

note = |savings (?) were not worth the effort. The results don't compare to

note = |^10. I agree with Peter Pinnell- sell another mug to pay for the

note = |difference in firing costs. Add .75 cobalt carb. for blue. This matte

note = |glaze breaks from rust to white (to blue w/ cob.) * I used chemical

note = |grade at the time- now I would probably test spod.LM. OR- replace

note = |spod. w/ soda feldspar & add redart for color Due to the lower

note = |sintering point of ^6 glazes- you have to start reduction fairly

note = |early- at least by stoneware standards. Try ^010 as a starting point

note = |& go from there. I also used a clay body that had a higher iron

note = |content than my present ^10 body- it seemed to make a difference.

note = |submitted by: Tom Gray e-mail: tgraypots@

note = |

name = Spodumene Alfred B.J. cone 6

index =

date = 6/4/96

source =

type = Magnesium matt

range = 6

firetype = Reduction

color = Tan/Brown/White

vistexture =

quality = Matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 20

component = Custer feldspar

amount = 20

component = Spodumene

amount = 20

component = Dolomite

amount = 20

component = Whiting

amount = 5

component = Kaolin

amount = 15

addition = Tin oxide

addamount = 4

note = |This is the Alfred Spodumene glaze revised to C/6. Glaze Type: Ca Mg

note = |AlMatt. Firing type: Reduction. From Val Cushing. VC ed

name = St. Helens Almond

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = almond yellow

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer spar

amount = 40

component = Zinc oxide

amount = 8.6

component = Whiting

amount = 14.9

component = EPK

amount = 11.8

component = Flint

amount = 4.7

component = Volcanic ash - Mt. St. Helens

amount = 20

addition = Rutile

addamount = 8

note = |here are two glazes I have used successfully but not put thru any

note = |analysis. I got them at an art studio where I used to take classes.

note = |They are better if layered with other glazes. Wendy Hampton

note = | from Bainbridge Island WA

note = |

name = St. Helens Blue

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = blue

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer spar

amount = 39.59

component = Flint

amount = 5.35

component = Whiting

amount = 14.08

component = EPK

amount = 11.57

component = Zinc oxide

amount = 8.17

component = Dolomite

amount = 0.44

component = Colemanite

amount = 0.88

component = Volcanic ash - Mt. St. Helens

amount = 19.92

addition = Cobalt oxide

addamount = 0.1

note = |This makes 3 gallons of glaze here are two glazes I have used

note = |successfully but not put thru any analysis. I got them at an art

note = |studio where I used to take classes. They are better if layered with

note = |other glazes. Wendy Hampton from Bainbridge Island

note = |WA

note = |

name = Stony Gray-White

index =

date = 4/21/95

source =

type =

range = 5

firetype = oxidation

color = milky, transulcent white.

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Colemanite

amount = 21.3

component = Custer feldspar

amount = 14.5

component = Ferro Frit 3134

amount = 14.9

component = Spodumene

amount = 11

component = EPK

amount = 17

component = Silica

amount = 21.3

addition = Tin oxide

addamount = 5.1

note = |I am cheap, so I use Zircopax instead of Tin. This gives a milky,

note = |translucent white. Slip decoration underneath shows well. source for

note = |original recipe: Ceramics Monthly, March '94 p.60 submitted by: Sumi

note = |Dick e-mail: Sumi@

note = |

name = Strontium Matte Pete's

index =

date = 02/29/2004

source =

type =

range = 6-10

firetype = Ox. or Red.

color = Green

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 60

component = Strontium carbonate

amount = 20

component = Grolleg

amount = 10

component = Silica

amount = 9

component = Lithium carbonate

amount = 1

addition = Copper carbonate

addamount = 5

addition = Titanium dioxide

addamount = 5

note = |From Pete Pinnell. See Clay Times Jan./Feb 2004, Mar./Apr. 2004. AKA Weathered Bronze.

name = Super Deluxe

index =

date = 3/26/96

source =

type =

range = 5 - 8

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Flint

amount = 29.7

component = EPK

amount = 4.95

component = Kona F-4 spar

amount = 19.8

component = Talc

amount = 13.86

component = Gerstley borate

amount = 31.68

addition = Red iron oxide

addamount = 26.11

note = |brown breaking to cobalt blue where thin... brick red with two coats

note = |with khaki drip marks khaki tan where thick breaking to cobalt always

note = |beautiful semimatte surfaces with wonderful drip marks and hazes...so

note = |pretty with sana green over from Mish Lowe, on IRC.

name = Superglaze

index =

date = 6/3/96

source =

type =

range = 6

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Georgia kaolin

amount = 9.9

component = Silica

amount = 18.2

component = Zirconium silicate

amount = 17.3

component = Zinc oxide

amount = 15.8

component = Lithium carbonate

amount = 8.5

component = Nepheline syenite

amount = 15

component = Whiting

amount = 15.3

note = |Here are a couple of C 6 glazes that I use with my speckled

note = |brownstone in ox. I used zircopax. A very fine, strong, white glaze

note = |with a soft sheen. Opaque. I love the white color of this glaze.

note = |Since it turns to cement when it sits, I have started adding

note = |bentonite, which helps. It works well with other glazes that have

note = |color. submitted by: Jan Henkel e-mail: jhenkel@ source

note = |for original recipe: Electric Pottery by E. Cooper.

note = |

name = Swoosh #1

index =

date = 12/6/96

source =

type =

range = 6

firetype = Ox. or Red.

color = no color

vistexture =

quality = runny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Feldspar

amount = 38.94

component = Zinc oxide

amount = 4.42

component = Colemanite

amount = 16.81

component = Dolomite

amount = 16.81

component = Whiting

amount = 1.77

component = Kaolin

amount = 4.42

component = Silica

amount = 16.81

addition = Bentonite

addamount = 2.65

note = |Apply a fluid glaze over your base glaze - but only on the rim -

note = |maybe 1/2 to 1 down. I'm sending two recipes for such a fluid glaze

note = |for you to try. I have just received these recipes and haven't yet

note = |tested them. Remember they may react differently depending on your

note = |base glaze, firing and all the other variables. An ash glaze will

note = |often have the same effect - I'm testing one now. submitted by: Geri

note = |Huntley e-mail: JHUNTLEY@cariboo.bc.ca

note = |

name = Swoosh #2

index =

date = 12/6/96

source =

type =

range = 6

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Whiting

amount = 25.87

component = Ferro Frit 3134

amount = 13.93

component = Kaolin

amount = 41.29

component = Silica

amount = 10.95

component = Custer feldspar

amount = 7.96

addition = Zircopax

addamount = 19.9

note = |Apply a fluid glaze over your base glaze - but only on the rim -

note = |maybe 1/2 to 1 down. I'm sending two recipes for such a fluid glaze

note = |for you to try. I have just received these recipes and haven't yet

note = |tested them. Remember they may react differently depending on your

note = |base glaze, firing and all the other variables. An ash glaze will

note = |often have the same effect - I'm testing one now. submitted by: Geri

note = |Huntley e-mail: JHUNTLEY@cariboo.bc.ca

note = |

name = Tamaras Blue

index =

date = 12/7/96

source =

type =

range = 6

firetype =

color = blue

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 39

component = Silica

amount = 9

component = EPK

amount = 7

component = Whiting

amount = 17

component = Zinc oxide

amount = 8

component = Volcanic ash - Mt. St. Helens

amount = 20

addition = Cobalt oxide

addamount = 1.5

note = |recipe Makes 1 gal. Good luck! Wendy from Bainbridge Island WA

note = |whampton@

note = |

name = Tan Dave's Base

index =

date = 03/02/2003

source =

type = Mid-fire

range = 5-6

firetype = Oxidation

color = Tan

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 29

component = Flint

amount = 17

component = Frit 3134

amount = 53

addition = Tin oxide

addamount = 9

addition = Red iron oxide

addamount = 3

addition = Rutile

addamount = 4

note = |Lee Shaw cone 6 recipe

name = Tan Satin Matt

index =

date = 4/21/95

source =

type =

range = 6

firetype = reduction

color = tan

vistexture =

quality = satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Zinc oxide

amount = 4.5

component = Whiting

amount = 10.01

component = Talc

amount = 2.1

component = Barium carbonate

amount = 11.01

component = F-4 Feldspar

amount = 42.04

component = EPK

amount = 8.31

component = Ball clay

amount = 8.01

component = Silica

amount = 14.01

addition = Rutile

addamount = 5.01

note = |kiln type: gas submitted by: John Anthony e-mail: JTRAX@

note = |

name = Tan SPECKLED

index =

date = 8/8/97

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = Tan

vistexture =

quality = Semi matte or satin

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 14.7

component = Spodumene

amount = 31.6

component = EPK

amount = 3.2

component = Dolomite

amount = 7.4

component = Talc

amount = 13.7

component = Flint

amount = 29.5

addition = Granular manganese

addamount = 0.5

addition = Manganese dioxide (milled)

addamount = 0.5

note = |Dan Saultman in Horribly Hot Colorado

note = |(100's today)

name = Tan Vals

index =

date = 4/3/98

source =

type =

range = 5 - 6

firetype = oxidation

color = tan

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Flint

amount = 29.7

component = EPK

amount = 4.95

component = Feldspar

amount = 19.8

component = Talc

amount = 13.86

component = Gerstley borate

amount = 31.68

addition = Iron oxide

addamount = 2.97

addition = Rutile

addamount = 2.97

note = |Makes for a nice base glaze. Oil

note = |Spot looks great over this one. sue hintz

name = TAVC

index =

date = 11/15/98

source =

type = Ca Na

range = 5 - 6

firetype = Ox or Red

color = Base is white

vistexture =

quality = Satin Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Neph Sye

amount = 3200

component = Frit 3110

amount = 720

component = Barium carbonate

amount = 720

component = Whiting

amount = 1280

component = EPK

amount = 800

component = Flint

amount = 1280

note = |For glossy deep green, add 5.0% Iron Oxide. For Tannish-grey matt,

note = |add 3.0% Rutile. Glaze Type: Ca Na. Opacity: ?. Firing type: Ox or

note = |Red .

note = |

name = Temmoku

index =

date = 3/26/96

source =

type =

range = 6

firetype = reduction

color = reddish brown/black

vistexture =

quality = gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 43.21

component = Whiting

amount = 20.99

component = EPK

amount = 9.88

component = Silica

amount = 25.93

addition = Bentonite

addamount = 3.7

addition = Red iron oxide

addamount = 19.75

note = |Here a the glazes we've found work out OK, and are currently studio

note = |shop glazes. We have noticed that a slightly heavier reduction is

note = |needed for cone 6 than in cone 9/10. submitted by: Candice Roeder

note = |e-mail: CRoeder1@

note = |

name = Temmoku Gold V's

index =

date = 11/20/97

source =

type = Mid-fire

range = 5-7

firetype = Oxidation

color = Brown

vistexture = Speckled

quality = Gloss

transparency =

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Cornwall Stone

amount = 67.8

component = Whiting

amount = 9

component = Gerstley borate

amount = 3.1

component = Lithium carbonate

amount = 6.1

component = Dolomite

amount = 7.8

component = Flint

amount = 6.2

addition = Red iron oxide

addamount = 11

note = |Gold flecks on a red-brown base. At cone 5 glossy brown w/matt gold haze.

note = |At cone 6 deep glossy chocolate w/gold flecks. At cone 7 gold

note = |disappears: dark glossy brown breaking to medium tan.

name = Ten ZA

index =

date = 4/11/95

source =

type =

range = 6

firetype =

color = black

vistexture =

quality = shiny, glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Potash feldspar

amount = 43.21

component = Kaolin

amount = 9.88

component = Silica

amount = 23.46

component = Whiting

amount = 11.11

component = Gerstley borate

amount = 12.35

addition = Iron oxide

addamount = 9.88

note = |Shiny black, ok. From Brian Kemp, (kempb@nievax.nie.ac.sg) via Rose

note = |Downs on ClayArt listserv. CLAY COLOR/TYPE: Buff Stoneware Fired at

note = |100 degrees per hour to 600 degrees, then free for all to cone 6-7.

note = |Kiln Size, Cromarty 25 cu ft. Manufactured in the UK. CONTRIBUTOR:

note = |Brian Kemp, Nanyang Technological University, Block B, Room 216, 469

note = |Bukut Timah Rd., Singapore, 1025 TEST SITE: Nanyang Technological

note = |University, Singapore

note = |

name = TENMOKU GOLD

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = dark brown w/ gold flecks

vistexture =

quality = glossy shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 67.78

component = Whiting

amount = 8.89

component = Gerstley borate

amount = 3.33

component = Lithium carbonate

amount = 6.11

component = Dolomite

amount = 7.78

component = Flint

amount = 6.11

addition = Red iron oxide

addamount = 11.11

note = |(my variation on the RPC oxidation tenmoku: this version is sugared

note = |with gold flecks - good either as a base for over-dipping, or on its

note = |own.) Here are a couple of standards from the Richmond Potters Club,

note = |and a few of my own formulation that have worked well in ^6

note = |oxidation. They aren't revolutionary (my exciting ones have things

note = |like barium in them, or are less predictable for a classroom

note = |situation) but they have been reliable, and allow for some play. They

note = |all calculate out to well within the INSIGHT limit formulas for

note = |maturity at ^6. If anyone tests these and comes up with problems, new

note = |ideas, good variations etc. could they let me know? I'll look forward

note = |to a larger list being posted to clayart. Veronica Shelford e-mail:

note = |shelford@ s-mail: P.O. Box 6-15 Thetis Island, BC V0R 2Y0

note = |Tel: (250) 246-1509

note = |

name = Tenmoku Gold V's

index =

date = 11/20/97

source =

type = Mid-fire

range = 5-7

firetype = Oxidation

color = Brown

vistexture = Speckled

quality = Gloss

transparency =

xtals = Small

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 100

component = Cornwall Stone

amount = 67.8

component = Whiting

amount = 9

component = Gerstley borate

amount = 3.1

component = Lithium carbonate

amount = 6.1

component = Dolomite

amount = 7.8

component = Flint

amount = 6.2

addition = Red iron oxide

addamount = 11

note = |Gold flecks on a red-brown base. At cone 5 glossy brown w/matt gold haze.

note = |At cone 6 deep glossy chocolate w/gold flecks. At cone 7 gold

note = |disappears: dark glossy brown breaking to medium tan.

name = TESSHA LIKE

index =

date = 8/8/97

source =

type =

range = 4 - 6

firetype =

color = iron red brown

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 45.5

component = Whiting

amount = 8.3

component = Dolomite

amount = 6

component = Silica

amount = 20

component = Zinc oxide

amount = 4

component = Kaolin

amount = 2.5

component = Gerstley borate

amount = 13.7

addition = Red iron oxide

addamount = 10

note = |Frank Martin Art Deparment/Ceranics 92nd street YM-YWHA 1395

note = |Lexington Ave NY, NY. 10128 p0tters2@

name = Test#^6/23 Cone Six Iron Red

index =

date = 4/3/98

source =

type =

range = 6

firetype =

color = iron red

vistexture =

quality = shiny glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = EPK

amount = 5.9

component = Flint

amount = 29.4

component = Custer feldspar

amount = 19.6

component = Talc

amount = 13.7

component = Gerstley borate

amount = 31.4

addition = Red iron oxide

addamount = 14.7

note = |Here's one I tested that I liked a great deal. Shiny Red mottled

note = |foreground. Background variations of light to medium Tans/Browns.

note = |Beautiful Glaze andrew lubow

name = TIZZY F

index =

date = 6/3/96

source =

type =

range = 6

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Silica

amount = 15.31

component = Ferro Frit 3134

amount = 60.2

component = Custer feldspar

amount = 10.2

component = EPK

amount = 14.29

addition = Zircopax

addamount = 10.2

note = |Howdy All - Here's a Tizzy I use with no lead. If anyone uses this

note = |glaze and does the glaze tests for color and they work, please let me

note = |know. submitted by: Capt. Mark Issenberg e-mail: ASHPOTS@

note = |

name = TMH 4

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Soda feldspar

amount = 56.1

component = Wollastonite

amount = 12.2

component = Ball clay

amount = 21.95

component = Gerstley borate

amount = 9.76

addition = Zircopax

addamount = 21.95

addition = Cobalt oxide

addamount = 2.44

note = |Tested on white stoneware. HORRIBLE GUMMY BLUE. OPAQUE. LOOKS LIKE

note = |BLUEBERRY CHEWING GUM. submitted by: Sharon LaRocca-Miranda e-mail:

note = |FMIRANDA@.OBERLIN.EDU , FMiranda@oberlin.edu source for

note = |original recipe: Zakin

note = |

name = Tomato Red

index =

date = 12/7/96

source =

type = Iron Saturate

range = 6

firetype = oxidation

color = red

vistexture =

quality = ?

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 50

component = Silica

amount = 22.7

component = Kaolin

amount = 9.1

component = Dolomite

amount = 9.1

component = Bone ash

amount = 9.1

addition = Red iron oxide

addamount = 9.1

addition = Bentonite

addamount = 1.8

note = |Brian Kemp. Singapore kempb@nievax.nie.ac.sg

name = Towy Red

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color = iron red

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 16

component = Talc

amount = 14

component = Gerstley borate

amount = 31

component = Bone ash

amount = 2

component = Lead bisilicate

amount = 2

component = EPK

amount = 5

component = Silica

amount = 30

addition = Red iron oxide

addamount = 15

note = |If the lead panics you, don't use it. It only makes a little

note = |difference. I do only tile, and don't spray this. I've spent the last

note = |3 years working on cone 5 iron red glazes, starting with Randy's Red,

note = |and I've found some things that work to make it redder. I started by

note = |taking each ingredient, cutting it down, and gradually adding it back

note = |till I had double the amount in the recipe. I found some adjustments

note = |that work. Then I researched adding other ingredients in various

note = |amounts, and found a couple that seem to help. My new recipe I call

note = |Towy Red, after my dog. He's a Welsh Springer Spaniel, and has spots

note = |this color. He's named after the River Towy in Wales (rhymes with

note = |Howie). Then I tried different irons. I tried black iron, yellow

note = |iron, and 5 different reds, including Spanish Red. I found that the

note = |redder it was before it was fired, the redder it would be after. The

note = |best I have found so far has been an iron from Pfizer that is bright

note = |red-orange raw. I'm almost out, and don't know where to get more. Any

note = |suggestions? The Spanish Red I got from a local supplier, and it's

note = |earthy red-brown. I've been told that what I got was not real Spanish

note = |Red. Is this true? Where can I get the real stuff? To get the red,

note = |you need a lot of calcium, and almost as much, but not more,

note = |magnesium. All of these iron reds have a very high silica/ alumina

note = |ratio, at least 20 to 1, some as high as 100 to 1. Of course they run

note = |like the Energizer Bunny, but I only use them on tile. submitted by:

note = |Paul Lewing e-mail: PJLewing@

note = |

name = Tracy Wilson's Clear

index =

date = 3/26/96

source =

type =

range = 5 - 6

firetype =

color = clear

vistexture =

quality = shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 45

component = Colemanite

amount = 25

component = Kaolin

amount = 15

component = Silica

amount = 15

addition = Bentonite

addamount = 3

note = |The clear was lovely over the white slip but pinholed majorly over

note = |the blue. The blue had been poured on over my cream clay body

note = |plainsman M-340. Well if anyone can let me know why the pinholing on

note = |the blue that would be great (I suspect it must be a cobalt annoyance

note = |or something because the clear glaze was o.k on the white slip and on

note = |the regular clay itself). Also if anyone has another recipe to try

note = |that would be helpful. submitted by: Cheryl Brown e-mail:

note = |cbrown@terranet.ab.ca

note = |

name = Translucent Base

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Zn Ca Na

range = 5 - 6

firetype = Ox. or Red.

color =

vistexture =

quality = Semi-Gloss Satin Celadon

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 44

component = Zinc oxide

amount = 13

component = Whiting

amount = 7

component = EPK

amount = 8

component = Flint

amount = 28

name = Translucent Deep Green

index =

date = 4/21/95

source =

type =

range = 5 - 6

firetype =

color = deep translucent green

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 50.24

component = Silica

amount = 25.12

component = Whiting

amount = 9.05

component = Dolomite

amount = 5.03

component = Gerstley borate

amount = 7.54

component = Zinc oxide

amount = 3.02

addition = Copper carbonate

addamount = 7.04

note = |originally suggested 7-10% copper carbonate. a deep green translucent

note = |that I like over white glazes, for a mottled, opaque effect. Also

note = |nice layered with cobalt blue glazes. I have found that many cone 10

note = |glazes will at least do something interesting at cone 6. Try it!

note = |source of original recipe: I adapted this off the base for Tom

note = |Coleman's cone 10 red. purple. submitted by: Sumi Dick e-mail:

note = |Sumi@

note = |

name = Transparent 1

index =

date = 11/15/98

source =

type = Ca Na

range = 5 - 6

firetype = Ox or Red

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline Sye

amount = 4445

component = Whiting

amount = 727

component = Talc

amount = 485

component = Flint

amount = 1858

component = EPK

amount = 485

note = |Other seven transparents are at end of file. Glaze Type: Ca Na .

note = |Opacity: Transparent. Firing type: Ox or Red .

note = |

note = |

name = Transparent 2

index =

date = 6/4/96

source =

type = Ca MidRoad

range = 5 - 6

firetype = Ox or Red

color = Semi-transparent

vistexture =

quality = Semi-Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 64

component = Whiting

amount = 18

component = Zinc oxide

amount = 5

component = Talc

amount = 4

component = EPK

amount = 9

note = |Glaze Type: Ca MidRoad. Firing type: Ox or Red. From Val Cushing. VC

note = |ed

note = |

name = Transparent 3

index =

date = 6/4/96

source =

type = Ca B MidRoad

range = 5 - 6

firetype = Ox or Red

color = Semi-transparent

vistexture =

quality = Semi-Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 40

component = Gerstley borate

amount = 13

component = Whiting

amount = 15

component = Zinc oxide

amount = 4

component = Flint

amount = 18

component = EPK

amount = 10

note = |Glaze Type: Ca B MidRoad. Firing type: Ox or Red. From Val Cushing.

note = |VC ed

note = |

name = Transparent 4

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca Na B

range = 5 - 6

firetype = Ox. or Red.

color = clear

vistexture =

quality = Glossy

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 47

component = Gerstley borate

amount = 47

component = EPK

amount = 4

component = Bentonite

amount = 2

note = |Shows no Boron streaking typical of high B2O3 glazes.

name = Transparent 5

index =

date = 6/4/96

source =

type = Zn Ca Na

range = 5 - 6

firetype = Ox or Red

color = Transparent

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 46

component = Whiting

amount = 8

component = Zinc oxide

amount = 10

component = Flint

amount = 28

component = EPK

amount = 8

note = |Glaze Type: Zn Ca Na. Firing type: Ox or Red. From Val Cushing. VC ed

note = |

name = Transparent 6

index =

date = 11/15/98

source =

type = Ca Zn RawLead

range = 5 - 6

firetype = Oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer spar

amount = 1840

component = Whiting

amount = 800

component = Zinc oxide

amount = 480

component = Talc

amount = 80

component = Flint

amount = 2320

component = EPK

amount = 400

component = White Lead

amount = 2080

note = |Safe Lead Glaze Glaze Type: Ca Zn RawLead. Opacity: Transparent.

note = |Firing type: Oxidation .

note = |

name = Transparent 7

index =

date = 11/15/98

source =

type = Zn Ca Pb B FritLead

range = 5 - 6

firetype = Oxidation

color = Clear

vistexture =

quality = Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3304

amount = 2800

component = Frit 3124

amount = 3200

component = Zinc oxide

amount = 800

component = EPK

amount = 1200

note = |Lead Boro-Silicate. Industrial China glaze. This glaze has a low

note = |expansion-- doesen't craze much. Glaze Type: Zn Ca Pb B FritLead.

note = |Opacity: Transparent. Firing type: Oxidation .

note = |

name = Transparent 8

index =

date = 11/15/98

source =

type = Ca B MidRoad

range = 5 - 6

firetype = Ox or Red

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Oxford spar

amount = 2640

component = Gerstley borate

amount = 1840

component = Whiting

amount = 640

component = Flint

amount = 1440

component = EPK

amount = 800

component = Barium carbonate

amount = 640

note = | Glaze Type: Ca B MidRoad. Opacity: Transparent. Firing type: Ox or

note = |Red .

note = |

name = Transparent Glossy 3

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca B

range = 5 - 6

firetype = Ox. or Red.

color = clear

vistexture =

quality = Glossy

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 40

component = Gerstley borate

amount = 18

component = Whiting

amount = 16

component = EPK

amount = 10

component = Flint

amount = 16

name = Transparent Semi-matte

index =

date = 6/3/96

source =

type =

range = 5 - 6

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 6.55

component = Nepheline syenite

amount = 18.1

component = EPK

amount = 12.12

component = Magnesium carbonate

amount = 2.24

component = Whiting

amount = 22.45

component = Flint

amount = 38.53

addition = Rutile

addamount = 1.69

note = |This version should have less crazing, but may go opaque If that

note = |happens, try adding a little (1-2%) lithium carbonate to flux it out.

note = |RB - revised for Michelle Lowe (formerly Pale Rutile Blue) 2

note = |transparent and semi matt, and NOT crazed. But no sign of the pale

note = |blue to be found. GREAT semi mat clear, left underglazes true to

note = |color really well.

name = Turquiiose/Green Crystal Nelson

index =

date = 09/17/2002

source =

type = Lithium Matte

range = 5-6

firetype = Oxidation

color = Turquoise

vistexture =

quality = Matt

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 41.5

component = Barium carbonate

amount = 27.8

component = Lithium carbonate

amount = 4.9

component = Whiting

amount = 4.9

component = Flint

amount = 14.5

component = Gerstley borate

amount = 2

component = EPK

amount = 4.5

addition = Bentonite

addamount = 2

addition = Copper carbonate

addamount = 12

var = |green: 12 copper carb + 8 RIO

note = |Translucent matte. NOT food safe due to barium content. From Shanon Nelson.

name = Turquoise

index =

date = 03/02/2003

source =

type =

range = 5-6

firetype =

color = Turquoise

vistexture =

quality = Gloss

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 33.5

component = Frit 3819

amount = 25.3

component = Flint

amount = 25.3

component = Whiting

amount = 5.6

component = Colemanite

amount = 6.5

component = Ball clay

amount = 3.8

addition = Copper carbonate

addamount = 3

addition = Bentonite

addamount = 1

note = |add CMC gum 12 tsp per 100 gms.

name = Turquoise

index =

date = 03/02/2003

source =

type =

range = 5-6

firetype =

color = Turquoise

vistexture =

quality = Gloss

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 33.5

component = Frit 3819

amount = 25.3

component = Flint

amount = 25.3

component = Whiting

amount = 5.6

component = Colemanite

amount = 6.5

component = Ball clay

amount = 3.8

addition = Copper carbonate

addamount = 3

addition = Bentonite

addamount = 1

note = |add CMC gum 12 tsp per 100 gms.

name = Turquoise Brilliant Matt

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation, reduction

color = turquoise

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 57.3

component = Silica

amount = 7.3

component = Barium carbonate

amount = 27.1

component = Lithium carbonate

amount = 2.1

component = Kaolin

amount = 6.3

addition = Copper carbonate

addamount = 4.2

note = |Whoever was looking for a Turquoise Glaze. I have 2 recipes for

note = |glazes a pottery teacher gave me. We call them Brilliant Matt Purple

note = |and Brilliant Matt Turquoise. They are volatile so be very careful

note = |with your kiln shelves. There is Barium Carbonate in the recipes, so

note = |they are poisonous whilst in the raw state. Please wear masks and

note = |gloves and if possible work at an extractor fan. I just put a normal

note = |fan pointing out the window and work behind it. I hear from

note = |production potters that Barium can leach thru your skin. Be careful

note = |and practise Good Safety Habits. As you can see they both use the

note = |same ingredients, but in different proportions. I have a friend /

note = |customer (they usually become friends) who is a production potter

note = |(with a 200 cubic foot parafin fired kiln), who uses the BMT and is

note = |delighted with it. He fires to cone 6 (1200/1220 C)You have to watch

note = |your application thickness to get the result you want. We have fired

note = |the BMP from 950 C to almost 1300 C with different results but always

note = |pleasantly surprised. Do not expect consistancy with these glazes.

note = |submitted by: Ralph Loewenthal e-mail: fayralph@sprintlink.co.za

name = Turquoise Brilliant Matt

index =

date = 12/7/96

source =

type =

range = 6

firetype = oxidation, reduction

color = turquoise

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 57.3

component = Silica

amount = 7.3

component = Barium carbonate

amount = 27.1

component = Lithium carbonate

amount = 2.1

component = Kaolin

amount = 6.3

addition = Copper carbonate

addamount = 4.2

note = |Whoever was looking for a Turquoise Glaze. I have 2 recipes for

note = |glazes a pottery teacher gave me. We call them Brilliant Matt Purple

note = |and Brilliant Matt Turquoise. They are volatile so be very careful

note = |with your kiln shelves. There is Barium Carbonate in the recipes, so

note = |they are poisonous whilst in the raw state. Please wear masks and

note = |gloves and if possible work at an extractor fan. I just put a normal

note = |fan pointing out the window and work behind it. I hear from

note = |production potters that Barium can leach thru your skin. Be careful

note = |and practise Good Safety Habits. As you can see they both use the

note = |same ingredients, but in different proportions. I have a friend /

note = |customer (they usually become friends) who is a production potter

note = |(with a 200 cubic foot parafin fired kiln), who uses the BMT and is

note = |delighted with it. He fires to cone 6 (1200/1220 C)You have to watch

note = |your application thickness to get the result you want. We have fired

note = |the BMP from 950 C to almost 1300 C with different results but always

note = |pleasantly surprised. Do not expect consistancy with these glazes.

note = |submitted by: Ralph Loewenthal e-mail: fayralph@sprintlink.co.za

name = Turquoise Glaze

index =

date = 01/19/2006

source =

type = Zinc matt

range = 5

firetype = Oxidation

color = Turquoise

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 36

component = Wollastonite

amount = 20

component = Zinc oxide

amount = 12

component = Flint

amount = 26

addition = Copper carbonate

addamount = 4

note = |should be ok for food. Clay Times Nov./Dec. p.51. From B and R Pearson.

name = Turquoise Matt

index =

date = 12/6/96

source =

type =

range = 5

firetype =

color = turquoise

vistexture =

quality = matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Strontium carbonate

amount = 26.2

component = Nepheline syenite

amount = 61.1

component = EPK

amount = 3.9

component = Flint

amount = 7

component = Lithium carbonate

amount = 1.8

addition = Copper carbonate

addamount = 4.4

addition = Bentonite

addamount = 1.8

note = |Kathy Schuetz

name = Turquoise Matt rev1

index =

date = 12/7/96

source =

type =

range = 5

firetype = oxidaition

color = turquoise

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 60

component = Strontium carbonate

amount = 25

component = Lithium carbonate

amount = 2

component = EPK

amount = 4

component = Silica

amount = 9

addition = Copper carbonate

addamount = 4

addition = Bentonite

addamount = 2

note = |The other day a matt turquoise glaze was posted on Clayart. I am

note = |suggesting that midfire potters not use this Maryland glaze for food

note = |containers. It doesn't have enough silica to keep the copper properly

note = |bound when faced with food acids. Adapting the same Seger formula,

note = |this recipe is more balanced. Only tests will show if these yield an

note = |acceptable colour and surface on your claybody. submitted by: Tom

note = |Buck e-mail: Tom.Buck@freenet.hamilton.on.ca or

note = |

note = |

name = UM Base

index =

date = 6/3/96

source =

type =

range = 6

firetype =

color = white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 64.7

component = Gerstley borate

amount = 11.8

component = Whiting

amount = 9.4

component = EPK

amount = 7.1

component = Silica

amount = 7.1

addition = Superpax

addamount = 17.7

addition = Bentonite

addamount = 3.5

note = |This is a studio glaze here at the u of m. I think it could be improved upon. It

note = |crawls a little when applied very thick,- its name is SUPER WHITE. i was just in

note = |the process of looking for other glazes to test, so let me know if you

note = |have any, thanks submitted by: Ed Brownlee e-mail: edware@umich.edu

note = |source for original recipe: University of Michigan

name = V's" Tenmoku Gold"

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color = brown w/yellow

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 67.42

component = Whiting

amount = 8.99

component = Gerstley borate

amount = 3.37

component = Lithium carbonate

amount = 6.18

component = Dolomite

amount = 7.87

component = Flint

amount = 6.18

addition = Red iron oxide

addamount = 11.24

note = |This may be the glaze you want. I got it from Veronica Shelford on

note = |Thetis Island, BC. I really like this glaze. I have used it on two

note = |different clay bodies. On a red colored high iron clay it was dark

note = |chocolate with golden flecks throughout. The stayed put and did not

note = |run. Beautiful. On Cone-5 B-mix from Laguna Clay, fired to cone 6, it

note = |ran just a bit. Georgeous effect....flecks of gold in a translucent

note = |caramel color. Some crazing. Suggest you test on vertical surfaces

note = |tall enough to significantly test the running quality. Could really

note = |make a mess on a shelf. Also, a caution about the mixture. I found

note = |that once the ingredients are mixed it needs to be used right away.

note = |If allowed to sit unused for even two or three days, 6-sided crystals

note = |begin to grow. These could be a problem, altering the glaze and the

note = |way it performs. Enjoy. John Rodgers in Alabama inua@

note = |more: Back in August, Veronica Shelford posted the following formula

note = |for V's Tenmoku Gold (cone 6 ox) to Clayart She described it as her

note = |own variation on the Richmond (BC) Potters' Club Red Tenmoku and

note = |having gold flecks on a red-brown base. I tried it on a warm brown

note = |clay body and really like the results. For me, at ^6, it is a very

note = |deep, glossy chocolate brown with gold flecks. Because of

note = |unintentional uneven temps in subsequent firings, I have found that

note = |at ^5 the glaze is rich, glossy brown with more dense patches of a

note = |more matt gold haze, and at ^7 the gold disappears and the result was

note = |glossy dark brown with breaks of medium tan on high spots. The ^5 and

note = |^7 results were obtained after adding 5% flint to the original

note = |formula to try to correct some flowing and crazing. Just thought this

note = |might be of some interest to those experimenting with Tenmoku glazes

note = |in oxidation. Cathie Feild in Maryland Ed Kraft eartharr@

note = |

name = V.C. 5

index =

date = 11/15/98

source =

type = Ca Na

range = 5 - 6

firetype = Ox or Red

color = Clear

vistexture =

quality = Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline Sye

amount = 3200

component = Gerstley borate

amount = 400

component = Whiting

amount = 1280

component = Dolomite

amount = 240

component = Zinc oxide

amount = 160

component = Frit 3124

amount = 800

component = EPK

amount = 320

component = Flint

amount = 1600

note = |Val, please name this. Glaze Type: Ca Na. Opacity: Transparent.

note = |Firing type: Ox or Red .

note = |

note = |

name = V.C. 1

index =

date = 6/4/96

source =

type = Ca Ba Na B

range = 4 - 6

firetype = Ox or Red

color = Semi-translucent to semi-opaque

vistexture =

quality = Semi-Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 Feldspar

amount = 45

component = Gerstley borate

amount = 20

component = Whiting

amount = 5

component = Barium carbonate

amount = 15

component = EPK

amount = 5

component = Flint

amount = 10

note = |Base glaze has typical boron bluish streaks which are imparted to all

note = |colorants. With 6% SnO or 12% zircopax becomes white opaque Glaze

note = |Type: Ca Ba Na B. From Val Cushing.. TESTED OK FOR FOOD. VC ed

note = |

name = V.C. 1-6

index =

date = 6/4/96

source =

type = Ca B

range = 5 - 6

firetype = Ox or Red

color = Semi-opaque

vistexture =

quality = Semi-Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3124

amount = 60

component = Gerstley borate

amount = 10

component = Flint

amount = 10

component = EPK

amount = 10

component = Whiting

amount = 10

note = |Glaze Type: Ca B. Firing type: Ox or Red From Val Cushing. VC ed

note = |

name = V.C. 2

index =

date = 6/4/96

source =

type = Ca Na

range = 4 - 6

firetype = Ox or Red

color = Semi-Opaque

vistexture =

quality = Semi Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 33

component = Whiting

amount = 16

component = Wollastonite

amount = 4

component = Dolomite

amount = 5

component = Barium carbonate

amount = 5

component = EPK

amount = 5

component = Flint

amount = 11

component = Frit 3110

amount = 21

addition = Red iron oxide

addamount = 5

addition = Lithium Carb

addamount = 6

note = |Iron gives yellow, orangish, green. Glaze Type: Ca Na. Firing type:

note = |Ox or Red From Val Cushing.TESTED OK FOR FOOD. VC ed

note = |

name = V.C. 2-6

index =

date = 6/4/96

source =

type = Na Ca Ba AlMatt

range = 5 - 6

firetype = Ox or Red

color = Semi-opaque

vistexture =

quality = Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 50

component = Barium carbonate

amount = 10

component = Frit 3124

amount = 5

component = Whiting

amount = 5

component = Petalite

amount = 5

component = EPK

amount = 10

component = Flint

amount = 15

note = |Very good for COLOR .Copper Carbonate (2.0%) produces blue green,

note = |Chrome ( 1.0%) produces yellow green. Glaze Type: Na Ca Ba AlMatt.

note = |Firing type: Ox or Red. From Val Cushing. BASE TESTED SAFE FOR FOOD

note = |VC ed

note = |

name = V.C. 3

index =

date = 6/4/96

source =

type = Ca Na

range = 4 - 6

firetype = Ox or Red

color = Semi-Opaque

vistexture =

quality = Satin

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 30

component = Whiting

amount = 10

component = Barium carbonate

amount = 10

component = EPK

amount = 10

component = Flint

amount = 10

component = Frit 3110

amount = 25

component = Zinc oxide

amount = 5

note = |Red iron (5%) gives orange yellow to green. Manganese (1.0%) gives

note = |violet pink. Glaze Type: Ca Na. Firing type: Ox or Red From Val

note = |Cushing.TESTED OK FOR FOOD. VC ed

note = |

name = V.C. 4

index =

date = 6/4/96

source =

type = Ca Na

range = 4 - 6

firetype = Ox or Red

color = Opaque

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 15

component = Whiting

amount = 10

component = Barium carbonate

amount = 10

component = EPK

amount = 10

component = Flint

amount = 10

component = Frit 3110

amount = 30

component = Petalite

amount = 10

component = Titanium dioxide

amount = 5

note = |Soda Alumina matt. Strong color from all oxides. 2% CuCO3 gives blue

note = |green. Glaze Type: Ca Na . Firing type: Ox or Red From Val Cushing.

note = |TESTED OK FOR FOOD. VC ed

note = |

name = V.C. 5

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca Na B

range = 4 - 6

firetype = Ox. or Red.

color =

vistexture =

quality = Semi-satin

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 25

component = Gerstley borate

amount = 18

component = Whiting

amount = 2

component = EPK

amount = 10

component = Flint

amount = 15

component = Zinc oxide

amount = 5

component = Frit 3124

amount = 25

addition = Tin oxide

addamount = 5

var = |2% copper gives blue green

note = |Tin causes colors to break rusty where thin.

name = V.C. 5

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca Na B

range = 4 - 6

firetype = Ox. or Red.

color =

vistexture =

quality = Semi-satin

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 25

component = Gerstley borate

amount = 18

component = Whiting

amount = 2

component = EPK

amount = 10

component = Flint

amount = 15

component = Zinc oxide

amount = 5

component = Frit 3124

amount = 25

addition = Tin oxide

addamount = 5

var = |2% copper gives blue green

note = |Tin causes colors to break rusty where thin.

name = V.C. 7

index =

date = 6/4/96

source =

type = Ca Na Mg SlipGlaze AlMatt

range = 4 - 6

firetype = Ox or Red

color = Opaque Orange to Green

vistexture =

quality = Satin Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany Slip

amount = 72

component = Cryolite

amount = 14

component = Gerstley borate

amount = 7

component = Barium Carb

amount = 7

note = |Glaze Type: Ca Na Mg Slip Glaze Al Matt. Firing type: Ox or Red From

note = |Val Cushing. TESTED OK FOR FOOD VC ed.

note = |

name = V.C. 71

index =

date = 11/25/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = White

vistexture =

quality = Satin matt

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 40

component = Frit 3124

amount = 9

component = Whiting

amount = 16

component = Talc

amount = 9

component = EPK

amount = 10

component = Flint

amount = 16

note = |From Val Cushing. Wonderful surface. Sensuous, smooth satin matte. Pearl-like.

note = |Colors keep the same character. Gorgeous base glaze.

name = V.C. 8

index =

date = 6/4/96

source =

type = Ca AlMatt

range = 4 - 6

firetype = Ox or Red

color = Semi-opaque

vistexture =

quality = Satin Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 20

component = Whiting

amount = 20

component = EPK

amount = 20

component = Flint

amount = 15

component = Frit 3124

amount = 25

note = |Glaze Type: Ca AlMatt. Firing type: Ox or Red From Val Cushing. VC ed.

note = |

name = V.C. Easy Gloss I

index =

date = 6/4/96

source =

type = Ca B AlMatt

range = 5 - 6

firetype = Ox or Red

color = Transparent

vistexture =

quality = Glossy or shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = EPK

amount = 50

note = |Glaze Type: Ca B Firing type: Ox or Red. From Val Cushing. VC ed

note = |

name = V.C. Easy Gloss II

index =

date = 6/4/96

source =

type = Ca B

range = 5 - 6

firetype = Oxidation

color = Semi-transparent bright yellow

vistexture =

quality = Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = Barnard clay

amount = 25

component = EPK

amount = 25

note = |Glaze Type: Ca B. Firing type: Oxidation From Val Cushing. VC ed

note = |

name = V.C. Easy Gloss III

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca B SlipGlaze

range = 5 - 6

firetype = Ox. or Red.

color =

vistexture =

quality = Glossy to semi-glossy

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 50

component = Albany Slip

amount = 25

component = EPK

amount = 25

note = |Base glaze is amber in oxidation, green in reduction.

name = V.C. Easy Gloss IV

index =

date = 6/4/96

source =

type = Ca Na B

range = 5 - 6

firetype = Ox or Red

color = Transparent white

vistexture =

quality = Glossy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 47

component = Gerstley borate

amount = 47

component = Ball clay

amount = 6

addition = Zircopax

addamount = 5

note = |Glaze Type: Ca Na B. Firing type: Ox or Red. From Val Cushing. VC ed

note = |

name = V.C. G 3

index =

date = 6/4/96

source =

type = Ca Zn AlMatt

range = 5 - 6

firetype = Ox or Red

color = Semi-opaque

vistexture =

quality = Satin Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 52

component = Whiting

amount = 19

component = Zinc oxide

amount = 9

component = EPK

amount = 14

component = Flint

amount = 6

note = |Glaze Type: Ca Zn AlMatt. Firing type: Ox or Red From Val Cushing. VC

note = |ed

note = |

name = V.C. G 4

index =

date = 6/4/96

source = Val Cushing VC ed. via GlazeBase

type = Ca B AshGlaze

range = 5 - 6

firetype = Reduction

color =

vistexture =

quality = Rivulet

transparency = Varies

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Apple Wood Ash

amount = 50

component = Gerstley borate

amount = 20

component = Whiting

amount = 12

component = EPK

amount = 8

component = Flint

amount = 10

note = |Typical ash looking, drippy, webby, rivulets.

name = V.C. G 5

index =

date = 6/4/96

source =

type = Ca Na

range = 5 - 6

firetype = Ox or Red

color = Semi-opaque Clear

vistexture =

quality = Semi-Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 40

component = Gerstley borate

amount = 5

component = Whiting

amount = 16

component = Dolomite

amount = 3

component = Zinc oxide

amount = 2

component = Frit 3124

amount = 10

component = EPK

amount = 4

component = Flint

amount = 20

note = |Glaze Type: Ca Na. Firing type: Ox or Red. From Val Cushing. VC ed

note = |

name = V.C. Good Color Satin Matt

index =

date = 6/4/96

source =

type = Ba Ca Na B

range = 5 - 6

firetype = Ox or Red

color = Semi-opaque

vistexture =

quality = Satin Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 Feldspar

amount = 50

component = Barium carbonate

amount = 22

component = Frit 3185

amount = 8

component = Whiting

amount = 5

component = EPK

amount = 5

component = Flint

amount = 10

note = |Glaze Type: Ba Ca Na B. Firing type: Ox or Red. From Val Cushing. VC

note = |ed

note = |

name = V.C. Karen Starshine CuAqua

index =

date = 6/4/96

source =

type =

range = 6

firetype = Ox. or Red.

color = Opaque Blue Green

vistexture =

quality = Glossy or shiny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = K-200 Feldspar

amount = 46

component = Soda ash

amount = 5

component = Gerstley borate

amount = 12

component = Whiting

amount = 10

component = Barium carbonate

amount = 5

component = Lithium carbonate

amount = 2

component = Flint

amount = 20

addition = Macaloid

addamount = 2

addition = Titanium dioxide

addamount = 4

addition = Copper carbonate

addamount = 5

note = |AU Sp '92 tested by KG in OXIDATION at C/6 on dark brown clay body -

note = |a knockout glaze! The most interesting of the Starshine series to

note = |date tho the green hue was lost. Definitely RUNNY. Good in SODA. Now

note = |- how do we get this color at C/9-10? VC ed

note = |

name = V.C. Karen Weinkauf

index =

date = 6/4/96

source =

type = Na Ca

range = 4 - 6

firetype = Oxidation

color = Transparent Clear

vistexture =

quality = Gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Frit 3110

amount = 40

component = Frit 3124

amount = 10

component = Nepheline Sye

amount = 20

component = Flint

amount = 15

component = Clay

amount = 10

component = Soda ash

amount = 5

note = |High soda glaze. Crazes. 2% CuCO3 gives blue. Glaze Type: Na Ca.

note = |Firing type: Oxidation From Val Cushing. VC ed

name = V.C. Med Temp 1

index =

date = 6/4/96

source =

type = Ca Zn Na AlMatt

range = 5 - 6

firetype = Ox or Red

color = Opaque White

vistexture =

quality = Satin Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 53

component = Whiting

amount = 18

component = Zinc oxide

amount = 8

component = EPK

amount = 15

component = Flint

amount = 6

note = |Glaze Type: Ca Zn Na AlMatt. Firing type: Ox or Red From Val Cushing.

note = |VC ed

note = |

name = V.C. Polished Matt

index =

date = 6/4/96

source =

type = Ca Mg AlMatt

range = 5 - 6

firetype = Ox or Red

color = Opaque

vistexture =

quality = Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 Feldspar

amount = 20

component = Custer feldspar

amount = 20

component = Spodumene

amount = 20

component = Dolomite

amount = 20

component = Whiting

amount = 5

component = Kaolin

amount = 15

addition = Tin oxide

addamount = 6

note = |Nice. Glaze Type: Ca Mg AlMatt. Firing type: Ox or Red. From Val

note = |Cushing. VC ed

note = |

name = V.C. Soft White Matt

index =

date = 11/15/98

source =

type = Na Li MidRoad Shino

range = 5 - 6

firetype = Ox or Red

color = White

vistexture =

quality = Matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Neph Sye

amount = 4301

component = Barium carbonate

amount = 688

component = Gerstley borate

amount = 860

component = Lithium carbonate

amount = 430

component = Cryolite

amount = 430

component = Zinc oxide

amount = 172

component = EPK

amount = 860

component = Flint

amount = 258

addition = Tin oxide

addamount = 172

addition = Zircopax

addamount = 430

note = |Over a dark firing clay it breaks a rusty brown. Lovely combination

note = |of white against orange brown. All this in oxidation. Chemically

note = |this glaze appears to be bordering on the shino type. TD Glaze Type:

note = |Na Li MidRoad Shino. Opacity: . Firing type: Ox or Red .

note = |

name = Val Cushing's SCVC5

index =

date = 3/26/96

source =

type =

range = 6

firetype =

color = Semi-opaque White

vistexture =

quality = semi-satin, waxy matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 40

component = Ferro frit 3124

amount = 9

component = Talc

amount = 9

component = Whiting

amount = 16

component = EPK

amount = 10

component = Flint

amount = 16

note = |I added .2% Epsom Salts to this to improve raw glaze suspension. This

note = |glaze produced a misty affect, which I believe Eleanora Eden(?) was

note = |after some time ago. It was applied to Miller #15 Cone 6 Porcelain

note = |bisque. I fired to Cone 6 using an Orton Cone 7 centered in kiln

note = |sitter with no Guard Cones. The glaze was much as described by V.C.

note = |The semi-opacity produces a misty appearance over underglaze. The

note = |underglaze I used in the test was Duncan C154, Cobalt Navy Blue.

note = |After painting the UG onto the bisque, I re-fired to Cone 06. The

note = |glaze was applied over this in 1 & 2 coats by dipping, then fired to

note = |Cone 6. The underglaze showed through 1 or 2 coats with a better

note = |contrast under 2 coats. Lettering painted in underglaze onto the

note = |bisque showed through the glaze quite clearly. However, carving into

note = |the porcelain (also stoneware) clay surface was completely or

note = |partially obliterated under this glaze. If you carve designs onto a

note = |pot which will be covered by this glaze, you'll need to take measures

note = |not to let the carved marks be blocked back out. (Remove or prevent

note = |the glaze from covering areas where you want the carving to show.)

note = |Wax resist is harder to work with for this glaze, so I'd consider

note = |scratching or scraping off unwanted glaze. Fired to maturity, the

note = |glaze didn't run back into letters created by scratching into the raw

note = |glaze. In fact, where the scratched-in letters appeared over the dk.

note = |blue UG, they showed up very clearly, retaining a crisp edge. They

note = |stood out better against 2 coats (rather than 1) of glaze. This looks

note = |promising as a handy way to work with lettering or linear design. I

note = |got delayed crazing from this glaze over the Miller #15. None in

note = |evidence yet over Miller #55, which is a buff-white. stoneware, Cone

note = |6-9 (this clay body doesn't perform well in microwave ovens). There

note = |also was some slight cratering of the glaze on Miller #15 where

note = |applied thickly. When 2 light coats of this glaze were poured over 2

note = |light coats of Spinach Green, it was transmuted into an attractive

note = |semi-matt, waxy Lettuce Green (voila- a vitreous tossed salad. Come

note = |to think of it, I had one of those at Red Lobster not too long ago.

note = |There was lots of sand in it.). The base for Spinach Green,

note = |originally a Richard Behrens glaze, has been used by Peter King (see

note = |CM 12/85, p.36). It has a wide Cone range, incl. Spinach Green

note = |Gerstley Borate 50 EP Kaolin 15 Flint 35 Add: Chrome Oxide, 1-2%

note = |Testing done by Joyce Jackson jjack82938@

note = |

name = Vickie's Barnard

index =

date = 7/19/95

source =

type =

range = 6 - 9

firetype =

color = chocolate brown

vistexture =

quality = glassy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Barnard clay

amount = 72.22

component = Custer feldspar

amount = 16.67

component = Whiting

amount = 11.11

note = |kiln type: electric Cone 9 and 6, clay: Plainsman M460 and H430,

note = |electric fire, applied to bisque. ALberta slip: At cone 9 Alberta by

note = |itself it makes a rich chocolate brown. It's too refractory to work

note = |at cone 6 by itself, I was told, so I didn't test it.I added 30%

note = |Gerstley borate which was the wrong thing to do, as Alberta is very

note = |glassy to begin with, but I had intended to test at cone 6 as well so

note = |I tested for both 6 and 9. I didn't really like the result at cone 6

note = |with the gerstley, as it was a frosty transparent olive green (at

note = |cone 9 it was a RUNNY transparent olive green. Adding Manganese or

note = |cobalt to the Alberta slip would probably give a really nice black.

note = |What I left out in making this one was Gerstley 10 (Rob uses

note = |Colemanite), but what I ended up with was a stony black with very

note = |tiny brown specks. Tends to crawl if too thick. Rob's recipe was

note = |great too, and that one SHOULD be thick, he says. His recipe also

note = |works on greenware, he said, but I haven't tried it yet. submitted

note = |by: Vickie Sproule e-mail: jsproule@mars.

note = |

name = Vivian's Red/Purple/Green

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = transparent green ox./reduct. r

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 46.33

component = Silica

amount = 19.8

component = Gerstley borate

amount = 13.56

component = Whiting

amount = 8.21

component = Dolomite

amount = 5.94

component = Zinc oxide

amount = 3.68

component = EPK

amount = 2.48

addition = Copper carbonate

addamount = 0.98

addition = Tin oxide

addamount = 0.98

addition = Rutile

addamount = 0.49

note = |has a tendency to run in reduction. in oxidation at cone 6 a

note = |transparent green that crackles. In reduction at cone 6 will turn

note = |blood red if heavily reduced. In reduction at cone 10 it works best,

note = |a beautiful purple. submitted by: J.D. e-mail: CLAYJUNKIE@

note = |

name = Vivikas reduction

index =

date = 3/26/96

source =

type =

range = 2 - 6

firetype = reduction

color =

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Zinc oxide

amount = 8.27

component = Colemanite

amount = 17.54

component = Barium carbonate

amount = 6.71

component = Talc

amount = 6.44

component = G-200 Feldspar

amount = 38.56

component = Silica

amount = 22.48

note = |Add 1% Bentonite. Color Variations: A: Add 2% Copper Oxide B: For

note = |blue Add 1% Cobalt Oxide C: Nickel Oxide 1% D: For blue-grey add

note = |Nickel Oxide 1%, Cobalt Oxide 1% submitted by: GURUSHAKTI@

note = |

name = Wanamaker Satin (Jeff Dietrich)

index =

date = 4/7/95

source =

type =

range = 6 - 7

firetype =

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Dolomite

amount = 18.39

component = Spodumene

amount = 11.5

component = Nepheline syenite

amount = 51.71

component = Ball clay

amount = 13.8

component = Zinc oxide

amount = 4.6

addition = Titanium dioxide

addamount = 2.3

note = |Finely Textured Satin matt - Do not apply too thick as it will

note = |bubble. I substituted Rutile for Titanium Dioxide because I didn't

note = |have any and it worked fine. Just don't double dip unless glaze if

note = |very thin. I liked how this worked over texture. They are dependable

note = |firing to firing in Cone 6 electric on dark clay. From Jeff Dietrich

note = |in Ceramics Montly, April 1991 & sent via ClayArt by Phyllis Nelson

note = |Baldwin City, Kansas E-mail: NELSON@george.bakeru.edu

note = |

name = Warwick Martin

index =

date = 10/06/2002

source =

type = Mid-fire

range = 6

firetype = Oxidation

color =

vistexture =

quality = Semi-gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wollastonite

amount = 19.9

component = Kona F-4 feldspar

amount = 43.4

component = EPK

amount = 16.8

component = Frit 3134

amount = 19.9

addition = Rutile

addamount = 6

note = |Nice shiny(but not too shiny)base for colorants

name = Waxy #3

index =

date = 04/24/2004

source =

type =

range = 6

firetype = Oxidation

color = White

vistexture =

quality = Waxy

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws = Crazes

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 33.6

component = Whiting

amount = 20.2

component = Flint

amount = 17.3

component = Frit 3195

amount = 28.9

addition = Bentonite

addamount = 1

note = |Developed by Valerie Duncan. Nice waxy surface, goes to whitish when thick.

note = |Crazed on her clay body.

name = Waxy base

index =

date = 12/22/2002

source =

type = Mid-fire

range = 6-10

firetype = Oxidation

color =

vistexture =

quality = Waxy

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 41

component = Silica

amount = 20

component = Gerstley borate

amount = 12

component = Dolomite

amount = 7

component = Kaolin

amount = 5

note = |As a result of seeing, Reading and being fascinated By Carleton Ball book, I fall

note = |in love with the waxy glazes. I had one before but never used it correctly. I tested

note = | a glaze was posted y John Post in 19997: A decorative glaze: WAXY WHITE^6 TO ^10

note = | The result:

note = |The glaze looks to me like the glazes (as they look in the book and the net of

note = |Japanese tea bowls) some decorative pinholes not fully mature, but enough to make

note = |it a wonderful glaze please see it in:

note = |

note = |If it does not open the last slide in:

note = |

note = | Seger Weight%

note = |KNO 0.218 6.67%

note = |CaO 0.332 6.97%

note = |MgO 0.450 6.78%

note = |Al2O3 0.257 9.81%

note = |B2O3 0.147 3.83%

note = |SiO2 2.933 65.94%

note = |K2O 0.134 4.71%

note = |Na2O 0.084 1.96%

note = |Al:Si 11.40

note = |Expan. 6.56

note = |ST 358.96

note = |The last slide,the one in the LEFT

note = |Ababi

note = |

note = |Ababi Sharon

note = |Glaze addict

note = |Kibbutz Shoval Israel

name = Waxy Kevin's

index =

date = 11/27/2001

source =

type = Magnesium matt

range = 6

firetype = Oxidation

color = Clear

vistexture =

quality = Satin matt

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 75

component = Zinc oxide

amount = 2

component = Dolomite

amount = 5

component = Whiting

amount = 3

component = EPK

amount = 7

component = Flint

amount = 9

note = |From Kevin Snipes. Over black slip made w/copper, slip bleeds green.

name = Weathered Bronze

index =

date = 11/15/98

source =

type = Strontium matt

range = 6

firetype = Oxidation

color = Green

vistexture =

quality = Satin matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Tested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Lithium carbonate

amount = 1

component = Strontium carbonate

amount = 20

component = Nepheline syenite

amount = 60

component = Ball clay

amount = 10

component = Flint

amount = 6

addition = Titanium dioxide

addamount = 5

addition = Copper carbonate

addamount = 5

var = |Periwinkle: 1.5% cobalt carb. + 4% copper carb.

note = |From Pete Pinnell via Posey Bacopoulos. Soft satiny goldish green.See article Clay

note = |Times Jan/Feb 04 p.17. This is the same glaze as Strontium Matte Pete Pinnell, a cone

note = |10 glaze. Not using colorants, or using refractory colorants can make this glaze

note = |underfired at cone 6.

name = WG White

index =

date = 4/3/98

source =

type =

range = 5 - 6

firetype = oxidation

color = white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Feldspar

amount = 34.48

component = Gerstley borate

amount = 11.49

component = Zinc oxide

amount = 11.49

component = Dolomite

amount = 17.24

component = Flint

amount = 25.29

note = |Nice white, get pastel colors when adding cobol or copper carb. Slips

note = |show through very nicely. I have spent about a year reading all of

note = |the good things you all have had to share and thought it is my turn

note = |to do some of the giving. Here are some formulas that I have gathered

note = |from the studio. I don't know who the original creators of these are.

note = |Hope you all enjoy them sue hintz

note = |

name = White

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = white base

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 34.9

component = Gerstley borate

amount = 31.5

component = Silica

amount = 19.8

component = Kaolin

amount = 5.9

component = Zinc oxide

amount = 4.9

component = Whiting

amount = 3

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse. Add 4% Copper carb for mottled blue green. Add 1/2% cobalt

note = |carb. + 1% Manganese dioxide + 1% red iron oxide for rich blue.

note = |

name = white Axner

index =

date = 9/20/95

source =

type = Mid-fire

range = 6 - 7

firetype = oxidation

color = white

vistexture =

quality = Semi-Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 39.78

component = Silica

amount = 19.55

component = Gerstley borate

amount = 12.61

component = Dolomite

amount = 6.84

component = Kaolin

amount = 4.4

component = Talc

amount = 12.41

component = Lithium carbonate

amount = 3.42

component = Borax

amount = 0.98

addition = Zircopax

addamount = 11.73

addition = Bentonite

addamount = 0.98

note = |Here is a cone 6-7 oxidation white glaze I have had a lot of success

note = |with. I've had lots of success adding colorants to this glaze, and at

note = |cone 7, it has a very nice texture. At cone 6 it is kind of flat.

note = |submitted by: Judy at Axner e-mail: AXNER@

name = white Axner

index =

date = 9/20/95

source =

type =

range = 6 - 7

firetype = Oxidation

color = white

vistexture =

quality = Semi-Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 39.78

component = Silica

amount = 19.55

component = Gerstley borate

amount = 12.61

component = Dolomite

amount = 6.84

component = Kaolin

amount = 4.4

component = Talc

amount = 12.41

component = Lithium carbonate

amount = 3.42

component = Borax

amount = 0.98

addition = Zircopax

addamount = 11.73

addition = Bentonite

addamount = 0.98

note = |Here is a cone 6-7 oxidation white glaze I have had a lot of success

note = |with. I've had lots of success adding colorants to this glaze, and at

note = |cone 7, it has a very nice texture. At cone 6 it is kind of flat.

note = |submitted by: Judy at Axner e-mail: AXNER@

name = White Base UM

index =

date = 6/3/96

source =

type = Mid-fire

range = 6

firetype = Oxidation

color = white

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 64.7

component = Gerstley borate

amount = 11.8

component = Whiting

amount = 9.4

component = EPK

amount = 7.1

component = Silica

amount = 7.1

addition = Superpax

addamount = 17.7

addition = Bentonite

addamount = 3.5

note = |This is a studio glaze here at the u of m. It crawls a little

note = |when applied very thick,- its name is SUPER WHITE. i was just in the

note = |process of looking for other glazes to test, so let me know if you

note = |have any, thanks submitted by: Ed Brownlee e-mail: edware@umich.edu

note = |source for original recipe: University of Michigan

name = White base yee vian shin 1

index =

date = 4/21/95

source =

type =

range = 6

firetype = Oxidation

color = White

vistexture =

quality = texture, mottled

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 35

component = Wollastonite

amount = 12

component = Lithium carbonate

amount = 2.7

component = Zinc oxide

amount = 5.8

component = Strontium carbonate

amount = 10.7

component = EPK

amount = 17.4

component = Silica

amount = 16.4

addition = Zircopax Plus

addamount = 5

note = |texture - sea shell kind of texture with pattern when reflected by

note = |light. with 5% zircopax, white. add colorants like mason stain or

note = |whatever oxide you want to create what color you want. when you fired

note = |this, you can apply it thick. submitted by: yee vian shin aka Frankie

note = |Yeevia e-mail: yeevi2@acc.wuacc.edu

name = White Cornball

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color = white

vistexture =

quality = Matt

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 49.2

component = Kentucky OM #4

amount = 23

component = Talc

amount = 7.3

component = Whiting

amount = 7.7

component = Barium carbonate

amount = 12.8

note = |I'm not taking responsibility for anyone using these glazes, etc.

note = |Something is probably toxic. They are examples of my research and

note = |they work out in formulation. Which is what they are examples of. So

note = |go formulate your own non-toxic glazes, if that is possible. It's

note = |probably bad for the environment too. Email me with questions as to

note = |household performance, as that may be indicative of other problems.

note = |The badly crazed surfaces are not considered to be a continous-non

note = |porous sanitary surfaces. Eric Hansen, Lawrence, Kansas

note = |wabi_sabi@

name = White Gloss

index =

date = 12/7/96

source =

type =

range = 4 - 5 - 6 - 7 - 8

firetype = oxidation

color = white

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Spodumene

amount = 12.59

component = Nepheline syenite

amount = 29.95

component = Whiting

amount = 11.37

component = Flint

amount = 27.51

component = Gerstley borate

amount = 8.93

component = Dolomite

amount = 5.69

component = Zinc oxide

amount = 3.96

addition = Bentonite

addamount = 1.52

addition = Zircopax

addamount = 10.15

note = |For Pat Chesney- I use a gloss white glaze that it supposed to mature

note = |at cone 4 -8. I fire it to 6-7, so I haven't personally tested it at

note = |4. I got the recipe from Eastern Ill. Univ. Hope this helps. from

note = |rebecca mott

name = White Happy

index =

date = 02/03/2006

source =

type = Magnesium matt

range = 6

firetype = Oxidation

color = White

vistexture =

quality = Waxy

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 50

component = Ball clay

amount = 12

component = Dolomite

amount = 20

component = Bone ash

amount = 10

component = Lithium carbonate

amount = 8

addition = Rutile

addamount = 4

addition = Zircopax

addamount = 4

var = |Can substitute titanium dioxide for less creamy, whiter glaze.

note = |From Shannon Nelson.

name = White Kona

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color = white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 46.3

component = Cornwall Stone

amount = 46.3

component = Wollastonite

amount = 1.2

component = Barium carbonate

amount = 3.8

component = Zinc oxide

amount = 2.5

note = |Eric Hansen, Lawrence, Kansas

note = |wabi_sabi@

name = White Liner Cushing

index =

date = 08/04/2003

source =

type =

range = 5-6

firetype = Oxidation

color = White

vistexture =

quality = Gloss

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 64

component = Whiting

amount = 18

component = Zinc oxide

amount = 5

component = Talc

amount = 5

component = EPK

amount = 9

addition = Zircopax Plus

addamount = 10

name = White Liner Val Cushing

index =

date = 03/02/2003

source =

type = Mid-fire

range = 5-6

firetype = Ox. or Red.

color = White

vistexture =

quality = Gloss

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 64

component = Whiting

amount = 18

component = Zinc oxide

amount = 5

component = Talc

amount = 5

component = EPK

amount = 9

addition = Zircopax

addamount = 10

name = White Matt

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = Opaque White

vistexture =

quality = Matte

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Cornwall Stone

amount = 12.5

component = Spodumene

amount = 12.5

component = Barium carbonate

amount = 12.5

component = Dolomite

amount = 12.5

component = Talc

amount = 12.5

component = Zinc oxide

amount = 12.5

component = Kaolin

amount = 12.5

component = Flint

amount = 12.5

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse. (Ever wonder if you could make a glaze with equal parts of

note = |everything? RB)

note = |

name = White Matt V.C. Soft

index =

date = 11/15/98

source =

type = Na Li MidRoad Shino

range = 5 - 6

firetype = Ox or Red

color = White

vistexture =

quality = Satin matt

transparency = Transparent

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Neph Sye

amount = 53.8

component = Barium carbonate

amount = 8.6

component = Gerstley borate

amount = 10.8

component = Lithium carbonate

amount = 5.4

component = Cryolite

amount = 5.4

component = Zinc oxide

amount = 2.2

component = EPK

amount = 10.8

component = Flint

amount = 3.2

addition = Tin oxide

addamount = 2.2

addition = Zircopax

addamount = 5.4

note = |Over a dark firing clay it breaks a rusty brown. Lovely combination

note = |of white against orange brown. All this in oxidation. Chemically

note = |this glaze appears to be bordering on the shino type. TD Glaze Type:

note = |Na Li MidRoad Shino. Opacity: . Firing type: Ox or Red .

name = White Matte

index =

date = 4/21/95

source =

type =

range = 6

firetype = Oxidation

color = White

vistexture =

quality = matt

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 38.7

component = Wollastonite

amount = 15.2

component = Barium carbonate

amount = 15.2

component = Silica

amount = 10.5

component = EPK

amount = 10.2

component = Gerstley borate

amount = 10.2

note = |kiln type: gas very white in oxidation, duller in reduction submitted

note = |by: John Anthony e-mail: JTRAX@

name = White Matte

index =

date = 4/21/95

source =

type =

range = 6

firetype = reduction

color = very white

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 38.7

component = Wollastonite

amount = 15.2

component = Barium carbonate

amount = 15.2

component = Silica

amount = 10.5

component = EPK

amount = 10.2

component = Gerstley borate

amount = 10.2

note = |kiln type: gas very white in oxidation, duller in reduction submitted

note = |by: John Anthony e-mail: JTRAX@

name = White Opaque (Blue)

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = army green/dark blue

vistexture =

quality = shiny, gloss

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 50

component = Zinc oxide

amount = 10.8

component = Whiting

amount = 18.6

component = EPK

amount = 14.7

component = Silica

amount = 5.9

addition = Rutile

addamount = 3

addition = Cobalt carbonate

addamount = 2.5

note = |An interesting combination of army green/dark blue. The recipe was

note = |given to me by a friend and is called White Opaque. She said to add

note = |2.5% cobalt for a great shiny dark blue. or LEAVE OUT THE RUTILE FOR

note = |A SHINY DARK BLUE The only thing she forgot to tell me was to leave

note = |out the rutile. I now know that Rutile makes cobalt go green as the

note = |result was a glaze that went a dingy army green on my light clay

note = |(Standard 112), but on the Standard 266 dark brown it was dark blue

note = |in the background with a diffuse green overcast, almost like a tiny

note = |green crystal pattern, very attractive. submitted by: Julia Moore

note = |e-mail: DIRTYBIRD5@

note = |

name = White Ozona

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = stony white

vistexture =

quality = stony slip or engobe

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = A.P. Green fireclay

amount = 70

component = Cedar Heights Goldart

amount = 20

component = Ball clay

amount = 10

note = |I've applied them to bone dry sculptural work, bisqued them and then

note = |have rubbed stains or oxides into the recesses, sponging off, then

note = |fired again for permanence. They are quite versatile. These recipes

note = |are from Zakin's book on Electric Kiln Ceramics. Some of the clays

note = |used in the recipe are coarse and the slip should not be strined. The

note = |result will be a coarse, sandy-textured surface, not for functional

note = |pieces. They may be applied by dipping, spraying or brushing. They

note = |may be applied to greenware or bisqued ware. They may be used alone

note = |or with stains and glazes. The appearance when fired is soft and

note = |sandy. Candice Roeder

name = White Paul's

index =

date = 6/24/97

source =

type =

range = 6

firetype =

color = white

vistexture =

quality =

transparency = Semi-opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Gerstley borate

amount = 15.7

component = Talc

amount = 8.6

component = Whiting

amount = 12

component = Custer feldspar

amount = 43

component = EPK

amount = 8.6

component = Flint

amount = 12.1

addition = Zircopax

addamount = 8.1

note = |There's a White that i tested from Ceramics Monthly Answers to

note = |Potters Questions. I have done tests with it but haven't used it yet

note = |on anything major. It appeared to be something I would like. I want

note = |to work more with it when I get the time. Cheryl Fisher Sarasota, FL

note = |cfisher995@

name = white Satin Matt L. A.

index =

date = 11/15/98

source =

type = Zinc matt

range = 5

firetype = Ox. or Red.

color = White

vistexture =

quality = Satin Matte

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 60.2

component = Flint

amount = 5.8

component = Whiting

amount = 18.2

component = Zinc oxide

amount = 10

component = EPK

amount = 5.8

addition = Opax

addamount = 4

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse. A variation on L.A. Matt.

name = White Slip Glaze

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 36.4

component = Frit 5301

amount = 54.5

component = Zinc oxide

amount = 9.1

addition = Bentonite

addamount = 2.7

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse. Can be used on greenware.

note = |

note = |

name = White Super

index =

date = 12/6/96

source =

type =

range = 6

firetype = oxidation

color = white

vistexture =

quality = ?

transparency = Opaque

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 64.7

component = Gerstley borate

amount = 11.8

component = Whiting

amount = 9.4

component = EPK

amount = 7.1

component = Silica

amount = 7.1

addition = Superpax

addamount = 17.6

note = |^6 in sitter- average bend; on buff stoneware; no soaking. a lttle

note = |dry where thin. nice rich white where thick. looks like it almost

note = |started to crawl wher thickest. good fit.overglazes look real good

note = |wher thin, but seperate wher base is thicker, probably because of

note = |ball clay in o.g. s . submitted by: Ed Brownlee e-mail:

note = |edware@umich.edu

name = White Super

index =

date = 12/6/96

source =

type =

range = 6

firetype = oxidation

color = white

vistexture =

quality = ?

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kona F-4 feldspar

amount = 55

component = Gerstley borate

amount = 10

component = Whiting

amount = 8

component = EPK

amount = 6

component = Silica

amount = 6

component = Superpax

amount = 15

note = |^6 in sitter- average bend; on buff stoneware; no soaking. a lttle

note = |dry where thin. nice rich white where thick. looks like it almost

note = |started to crawl wher thickest. good fit.overglazes look real good

note = |wher thin, but seperate wher base is thicker, probably because of

note = |ball clay in o.g. s . submitted by: Ed Brownlee e-mail:

note = |edware@umich.edu

name = White Waxy

index =

date = 08/01/2001

source =

type =

range = 6 - 10

firetype = Ox. or Red.

color = very white

vistexture =

quality = fat waxy satin matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kingman feldspar

amount = 41

component = Silica

amount = 20

component = Talc

amount = 15

component = Gerstley borate

amount = 12

component = Dolomite

amount = 7

component = EPK

amount = 5

note = |> ClayArt Listserv recipe < If you find this glaze useful, please

note = |consider submitting it to the GlazeBase project with full

note = |documentation. Use one of the GlazeBase submission formats available

note = |on the CeramicsWeb web page.

note = |

note = |comments: a nice, fat , matte very-white. Due to the magnesium the

note = |talc, this glaze has that peculiar property of turning cobalt purple.

note = |Can use Custer instead of Kingman and use 15 gr ( instead of 12 gr)

note = |of Gerstley Borate for cone 6 glaze.

name = White Waxy

index =

date = 6/24/97

source =

type =

range = 6

firetype = Ox. or Red.

color = white

vistexture =

quality = waxy

transparency = Translucent

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Custer feldspar

amount = 43

component = Gerstley borate

amount = 15.7

component = Flint

amount = 12.1

component = Whiting

amount = 12

component = Talc

amount = 8.6

component = EPK

amount = 8.6

note = |I use it in reduction but I have had some luck with it in oxidation

note = |too. Sarah Barnes

name = White WG

index =

date = 4/3/98

source =

type =

range = 5 - 6

firetype = oxidation

color = white

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Feldspar

amount = 34.48

component = Gerstley borate

amount = 11.49

component = Zinc oxide

amount = 11.49

component = Dolomite

amount = 17.24

component = Flint

amount = 25.29

note = |Nice white, get pastel colors when adding cobol or copper carb. Slips

note = |show through very nicely. I have spent about a year reading all of

note = |the good things you all have had to share and thought it is my turn

note = |to do some of the giving. Here are some formulas that I have gathered

note = |from the studio. I don't know who the original creators of these are.

note = |Hope you all enjoy them sue hintz

name = Wood Ash Look

index =

date = 08/01/2001

source =

type =

range = 6

firetype = oxidation

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro frit 3195

amount = 230

component = Whiting

amount = 170

component = EPK

amount = 100

note = |> ClayArt Listserv recipe < If you find this glaze useful, please

note = |consider submitting it to the GlazeBase project with full

note = |documentation. Use one of the GlazeBase submission formats available

note = |on the CeramicsWeb web page.

note = |

note = |comments: hi. I have a recipe for a fake wood ash at cone 6

note = |oxidation. It does run in those rivulets. I added 3% copper

note = |carbonate but I am sure some other colorants would be worth a try.

note = |submitted by: Suzanne Fuqua e-mail: Suzanne511@

note = |

name = yee vian shin 1

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = with 5% zircopax, white

vistexture =

quality = texture, mottled

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 34.95

component = Wollastonite

amount = 12.04

component = Lithium carbonate

amount = 2.65

component = Zinc oxide

amount = 5.84

component = Strontium carbonate

amount = 10.68

component = EPK

amount = 17.43

component = Silica

amount = 16.42

note = |texture - sea shell kind of texture with pattern when reflected by

note = |light. with 5% zircopax, white. add colorants like mason stain or

note = |whatever oxide you want to create what color you want. when you fired

note = |this, you can apply it thick. submitted by: yee vian shin aka Frankie

note = |Yeevia e-mail: yeevi2@acc.wuacc.edu

note = |

name = Yellow Bright

index =

date = 11/15/98

source =

type = Mid-fire

range = 2 - 5

firetype = Ox. or Red.

color = bright yellow

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 30

component = Frit 5301

amount = 70

addition = Bentonite

addamount = 3

addition = Vanadium stain

addamount = 10

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse.

name = Yellow green slip glaze

index =

date = 11/15/98

source =

type =

range = 2 - 5

firetype = Ox. or Red.

color = yellow green

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Albany slip

amount = 60

component = Frit 5301

amount = 40

addition = Copper carbonate

addamount = 2

note = |From a University of Georgia class handout on glaze & clay from Andy

note = |Nasisse.

note = |

note = |

name = Yellow Ochre Glaze

index =

date = 02/26/2002

source =

type = Zinc matt

range = 6

firetype = Ox. or Red.

color =

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Kaolin

amount = 29

component = Frit 3110

amount = 26

component = Zinc oxide

amount = 17

component = Flint

amount = 16

component = Lithium carbonate

amount = 4

addition = Red iron oxide

addamount = 4

addition = Tin oxide

addamount = 4

addition = Yellow ochre

addamount = 0.5

addition = Copper carbonate

addamount = 0.4

note = |from Mary Barranger

name = Yellow Seto Leach

index =

date = 4/3/98

source =

type =

range = 6

firetype = oxidation

color = yellow

vistexture =

quality =

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Wood ash

amount = 66.67

component = Custer feldspar

amount = 33.33

addition = Yellow ochre

addamount = 33.33

note = |comments: Seems to be better on

note = |porcelain. Some- times bright yellow, sometimes browner depends on

note = |mineral content of the ash which varies from wood to wood. Darker and

note = |more opaque where thin goes to almost black. Yellow where thicker.

note = |Keep glaze thin or you will be scraping shelves. Becomes transparent

note = |yellowish brown and very fluid when thickly applied. The mid way

note = |thin/thick of application is mottled like a salt fired piece and is

note = |satin matte. But I got great reds, yellows, browns, blacks on pieces

note = |where it's thinner. To make tiny rivers of ash I make the same glaze

note = |substituting Red Art for the Ochre and trail it on with a slip trail

note = |bulb. Caution: use rubber gloves with unwashed ash glazes or face the

note = |possibility of contact dermatitis. It will mildly burn the skin. I

note = |keep Cornhuskers lotion and Hydrocortisone cream around the house

note = |anyway. I layer it with a glossy, glassy glaze that by itself has its

note = |own problems like keeping me up at night to the sound of loudly

note = |cooling and crazing *pings* I use a glaze with wood ash. I don't wash

note = |the ash, but I do screen it. The woodash has to be soft, white,

note = |fluffy. Not from a wood kiln! That kind is sintered and won't get the

note = |best results. You can tell it will feel crispy at first. I'm not

note = |taking responsibility for anyone using these glazes, etc. Something

note = |is probably toxic. They are examples of my research and they work out

note = |in formulation. Which is what they are examples of. So go formulate

note = |your own non-toxic glazes, if that is possible. It's probably bad for

note = |the environment too. Email me with questions as to household

note = |performance, as that may be indicative of other problems. The badly

note = |crazed surfaces are not considered to be a continous-non porous

note = |sanitary surfaces. Eric Hansen, Lawrence, Kansas

note = |wabi_sabi@

name = Yellow Woo

index =

date = 4/21/95

source =

type =

range = 6

firetype =

color = deep yellow

vistexture =

quality = matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested =

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 42.51

component = Strontium carbonate

amount = 23.93

component = Dolomite

amount = 15.45

component = Silica

amount = 9.05

component = Kaolin

amount = 9.05

addition = Zircopax

addamount = 19.28

addition = Red iron oxide

addamount = 3.58

addition = Bentonite

addamount = 4.77

addition = Epsom salts

addamount = 1.19

note = |kiln type: gas nice deep yellow with brown spotting over iron bearing

note = |clay when thin. Waxier and paler when thick. submitted by: John

note = |Anthony e-mail: JTRAX@

name = Zakin K15-1

index =

date = 6/3/96

source =

type =

range = 6

firetype = oxidation

color = dark blue

vistexture =

quality = semi -matt

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Nepheline syenite

amount = 40

component = Dolomite

amount = 18

component = Silica

amount = 18

component = Kaolin

amount = 12

component = Bone ash

amount = 6

component = Lithium carbonate

amount = 2

component = Zinc oxide

amount = 4

addition = Copper carbonate

addamount = 2

note = |Tested on white Stoneware. THIS IS A DARK BLUE GLAZE, NICE TEXTURE,

note = |WORKS WELL THIN. SEMI-MATT. IF THICK THEN IT'S GLOSS AND REALLY BLUE

note = |(should sell like crazy...) submitted by: Sharon LaRocca-Miranda

note = |e-mail: FMIRANDA@.OBERLIN.EDU , FMiranda@oberlin.edu source

note = |for original recipe: Zakin

note = |

name = Zakin's GK ash

index =

date = 08/01/2001

source =

type =

range = 5 - 6

firetype = Ox. or Red.

color =

vistexture =

quality = ash runny

transparency =

xtals =

bubbles =

flow =

durability =

flaws =

tested = Untested

imagefile =

notefile =

limform =

by_vol = n

batchsize = 0

component = Ferro frit 3124

amount = 90.9

component = Magnesium carbonate

amount = 35.3

component = Nepheline syenite

amount = 50.5

component = Strontium carbonate

amount = 55.5

component = Spodumene

amount = 75.8

component = EPK

amount = 50.5

component = Whiting

amount = 65.7

component = Wood ash

amount = 75.8

addition = Opax

addamount = 60.6

addition = Bentonite

addamount = 10.1

note = |> ClayArt Listserv recipe < If you find this glaze useful, please

note = |consider submitting it to the GlazeBase project with full

note = |documentation. Use one of the GlazeBase submission formats available

note = |on the CeramicsWeb web page.

note = |

note = |comments: Use unwashed fireplace ash. Doesn't add to 100 because of

note = |the strontium/barium substitution, the bentonite, and the ash. This

note = |may be closer to cone 5 than cone 6 but seems to work over a range of

note = |a couple cones. This is Zakin's GK base with 15% unwashed, mixed

note = |fireplace ashes, with strontium substituted for barium and superpax

note = |for opax. By itself over porcelain, the glaze is not particularly

note = |interesting. But other glazes on top of it run and drip and blend

note = |together nicely. I've found that if I glaze the lower 2/3 or 3/4 of a

note = |pot with a well-behaved glossy glaze, brush a coat of this ZGK ash

note = |glaze on the top 1/3 or so and then brush or dip some third glaze on

note = |top of the ash glaze, I get a nice pattern of runs that don't go off

note = |the bottom of the pot onto the kiln shelf (usually). Different glazes

note = |give different kinds of runs and bands of different glazes are

note = |interesting too. The few times I tried a matte glaze on the bottom,

note = |the pots cracked. Could have been coincidence. But I've been sticking

note = |with glossy glazes on the bottom since then. submitted by: Janet

note = |Price e-mail: jprice@kzoo.edu

note = |

................
................