DSM Engineering Plastic Products, Inc



DATA SHEET | |

|KETRON® PEEK - 1030 |

|COMPRESSION MOLDED 30% CARBON REINFORCED POLYETHERETHER KETONE |

|Property |Units |Test |Typical Average |

| | |Method |Values |

| Mechanical | | | |

|Specific Gravity, 73° F |- |ASTM D792 |1.42 |

|Tensile Strength, 73° F |psi |ASTM D638 |14,000 |

|Tensile Modulus of Elasticity, 73° F |psi |ASTM D638 |800,000 |

|Tensile Elongation (at break), 73° F |% |ASTM D638 |2.0 |

|Flexural Strength, 73° F |psi |ASTM D790 |30,000 |

|Flexural Modulus of Elasticity, 73° F |psi |ASTM D790 |1,300,000 |

|Shear Strength, 73° F |psi |ASTM D732 |11,000 |

|Compressive Strength, 10% Deformation, 73° F |psi |ASTM D695 |25,000 |

|Compressive Modulus of Elasticity, 73° F |psi |ASTM D695 |550,000 |

|Hardness, Rockwell, Scale as noted, 73° F |- |ASTM D785 |M97 (125) |

|Hardness, Durometer, Shore "D" Scale, 73° F |- |ASTM D2240 |D86 |

|Izod Impact (notched), 73° F |ft.lb./in. |ASTM D 256Type "A" |1.4 |

|Coefficient of Friction (Dry vs. Steel) Dynamic |- |PTM 55007 |0.24 |

|Limiting PV (with 4:1 safety factor applied) |ft.lbs.in.2 min. |PTM 55007 |41,000 |

|Wear Factor "k" x 10-10 |in.3-min/ft. lbs. hr. |PTM 55010 |160 |

| Thermal | | | |

|Coefficient of Linear Thermal Expansion |in./in./°F |ASTM E-831 (TMA) |1.70 x 10-5 |

|(-40°F to 300°F) | | | |

|Heat Deflection Temperature 264 psi |°F |ASTM D648 |450 |

|Tg-Glass Transition (amorphous) |°F |ASTM D3418 |N/A |

|Melting Point (crystalline) peak |°F |ASTM D3418 |644 |

|Continuous Service Temperature in Air (Max.)(1) |°F |- |480 |

|Thermal Conductivity |BTU in./(hr.ft.2 °F) |- |6.37 |

| Electrical | | | |

|Dielectric Strength, Short Term |Volts/mil |ASTM D 149 |- |

|Surface Resistivity |ohm/square |EOS/ESD S11.11 | ................
................